CN103497606A - 一种汽车车身及保险杠修补用消痕剂及其制备方法 - Google Patents
一种汽车车身及保险杠修补用消痕剂及其制备方法 Download PDFInfo
- Publication number
- CN103497606A CN103497606A CN201310478365.0A CN201310478365A CN103497606A CN 103497606 A CN103497606 A CN 103497606A CN 201310478365 A CN201310478365 A CN 201310478365A CN 103497606 A CN103497606 A CN 103497606A
- Authority
- CN
- China
- Prior art keywords
- parts
- solvent
- agent
- aromatic hydrocarbon
- disappears
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
一种汽车车身及保险杠修补用消痕剂及其制备方法,该消痕剂由以下重量份的组分组成:羟基丙烯酸树脂8~12份,芳香烃溶剂35~45份,酯类溶剂35~45份,酮类溶剂8~12份,流平剂0.1~0.3份;所述羟基丙烯酸树脂的羟值60~90mgKOH/g;所述芳香烃溶剂的溶解度参数8.9~9.3,沸点80~145℃;所述酯类溶剂为沸点70~100℃、120~140℃、190~220℃三个挥发段的溶剂的混合物,三者的质量配比为1~2:1~2:1。本发明还包括所述汽车车身及保险杠修补用消痕剂的制备方法。本发明具有良好的修补外观和打磨性,能使修补区域与原漆之间在外观、颜色、耐磨性等方面无明显差异。
Description
技术领域
本发明涉及一种汽车车身及保险杠修补用消痕剂及其制备方法。
背景技术
目前,市场上汽车车身及保险杠修补用消痕剂,常由几种溶解性、极性、挥发性不尽相同的溶剂组合而成,主要应用于溶剂型涂料的车身修补,其不仅施工工艺要求高,而且修补后的漆膜干瘪、粗糙,极易打磨抛光露底,修补区域极易出现接口痕,修补外观难以满足生产及消费者要求。
发明内容
本发明所要解决的技术问题是,提供一种具有良好的修补外观和打磨性,能使修补区域与原漆之间在外观、颜色、耐磨性等方面无明显差异的汽车车身及保险杠修补用消痕剂及其制备方法。
本发明解决其技术问题所采用的技术方案是:
本发明之汽车车身及保险杠修补用消痕剂,由以下重量份的组分组成:羟基丙烯酸树脂8~12份(优选9~11份),芳香烃溶剂35~45份(优选38~42份),酯类溶剂35~45份(优选38~42份),酮类溶剂8~12份(优选9~11份),流平剂0.1~0.3份(优选0.15~0.25份);
所述羟基丙烯酸树脂为羟值60~90mgKOH/g(原液)的羟基丙烯酸树脂;
所述芳香烃溶剂为溶解度参数8.9~9.3,沸点80~145℃的芳香烃溶剂;
所述酯类溶剂为沸点70~100℃、120~140℃、190~220℃三个挥发段的溶剂的混合物,三者的质量配比为1~2:1~2:1。
进一步,所述芳香烃溶剂为甲苯、二甲苯中的一种或两者的混合物。
进一步,所述酯类溶剂为乙酸乙酯、乙酸丁酯和乙二醇丁醚醋酸酯的混合物等。
进一步,所述酮类溶剂为溶解度参数8.6~9.9,沸点60~80℃的酮类溶剂,如:甲酮、甲乙酮中的一种或两者的混合物。
进一步,所述流平剂为氟改性的丙烯酸酯类流平剂,如:台湾德谦的Levelol 837、埃夫卡EFKA 3777等。
本发明之汽车车身及保险杠修补用消痕剂的制备方法,包括以下步骤:
(1)按以下重量配比称取各组分原料:羟基丙烯酸树脂8~12份,芳香烃溶剂35~45份,酯类溶剂35~45份,酮类溶剂8~12份,流平剂0.1~0.3份;
(2)将所称取的羟基丙烯酸树脂、芳香烃溶剂、酯类溶剂、酮类溶剂、流平剂依次加入调和釜,搅拌均匀,即成。
本发明之汽车车身及保险杠修补用消痕剂,采用中羟值羟基丙烯酸树脂,并对溶剂进行优化组合(包括选择溶解度参数与羟基丙烯酸树脂的溶解度参数接近的芳香烃溶剂,选择三个挥发段的酯类溶剂溶剂-主要是满足消痕剂施工过程中在涂料中的溶解、流平及烘烤针孔弊病预防),赋予消痕剂良好的修补外观和打磨性,同时有效解决深色涂料接头痕的技术难题。
与现有技术相比,本发明具有以下优点:
(1)加入少量的羟基丙烯酸共聚物溶液树脂,确保修补后漆膜在耐打磨、耐抛光性、外观等方面满足修补要求;
(2)通过芳香烃溶剂、酯类溶剂、酮类溶剂的搭配组合,使消痕剂具备优异的接痕消除能力,确保修补区域之间完美过渡;
(3)成本较低,适用性广泛,可应用于溶剂型、水性涂料的修补用途。
具体实施方式
以下结合实施例对本发明作进一步说明。
实施例1
本实施例之汽车车身及保险杠修补用消痕剂,由以下重量份的组分组成:羟基丙烯酸树脂10份(佛山高明同德AC1106,羟值83mgKOH/g(原液)),芳香烃溶剂40份(甲苯20份,二甲苯20份),酯类溶剂40份(乙酸乙酯15份,乙酸丁酯15份,乙二醇丁醚醋酸酯10份),酮类溶剂10份(甲酮5份,甲乙酮5份),流平剂0.2份(台湾德谦Levelol 837)。
制备方法,包括以下步骤:
(1)按以下重量配比称取各组分原料:羟基丙烯酸树脂10份,芳香烃溶剂40份,酯类溶剂40份,酮类溶剂10份,流平剂0.2份;
(2)将所称取的羟基丙烯酸树脂、芳香烃溶剂、酯类溶剂、酮类溶剂、流平剂依次加入调和釜,搅拌均匀,即成。
实施例2
本实施例之汽车车身及保险杠修补用消痕剂,由以下重量份的组分组成:羟基丙烯酸树脂10份(台湾德谦FS3270,羟值73.9mgKOH/g(原液)),芳香烃溶剂40份(甲苯20份,二甲苯20份),酯类溶剂40份(乙酸乙酯15份,乙酸丁酯15份,乙二醇丁醚醋酸酯10份),酮类溶剂10份(甲酮5份,甲乙酮5份),流平剂0.2份(埃夫卡EFKA 3777)。
制备方法同实施例1。
实施例3
本实施例之汽车车身及保险杠修补用消痕剂,由以下重量份的组分组成:羟基丙烯酸树脂10份(纽佩斯Setalux 1184—ss-51,羟值66mgKOH/g(原液)),芳香烃溶剂40份(二甲苯40份),酯类溶剂40份(乙酸乙酯15份,乙酸丁酯15份,乙二醇丁醚醋酸酯10份),酮类溶剂10份(甲乙酮10份),流平剂0.2份(埃夫卡EFKA 3777)。
制备方法同实施例1。
比较例1
本比较例之汽车车身及保险杠修补用消痕剂,由以下重量份的组分组成:羟基丙烯酸树脂10份(台湾德谦FS2050,羟值33mgKOH/g(原液)),芳香烃溶剂40份(甲苯20份,二甲苯20份),酯类溶剂40份(乙酸乙酯15份,乙酸丁酯15份,乙二醇丁醚醋酸酯10份),酮类溶剂10份(甲酮5份,甲乙酮5份),流平剂0.2份(台湾德谦Levelol 837)。
制备方法同实施例1。
比较例2
本比较例之汽车车身及保险杠修补用消痕剂,由以下重量份的组分组成:羟基丙烯酸树脂10份(纽佩斯Setalux 1208,羟值148.5mgKOH/g(原液)),芳香烃溶剂40份(甲苯20份,二甲苯20份),酯类溶剂40份(乙酸乙酯15份,乙酸丁酯15份,乙二醇丁醚醋酸酯10份),酮类溶剂10份(甲酮5份,甲乙酮5份),流平剂0.2份(台湾德谦Levelol 837)。
制备方法同实施例1。
比较例3
本比较例之汽车车身及保险杠修补用消痕剂,由以下重量份的组分组成:羟基丙烯酸树脂10份(纽佩斯Setalux 1184—ss-51,羟值66mgKOH/g(原液)),芳香烃溶剂40份(甲苯20份,二甲苯20份),酯类溶剂40份(己二酸二甲酯15份,丁二酸二甲酯15份,戊二酸二甲酯10份),酮类溶剂10份(甲酮5份,甲乙酮5份),流平剂0.2份(台湾德谦Levelol 837)。
制备方法同实施例1。
[消痕剂性能评价步骤]
测试汽车车身及保险杠修补用消痕剂接口痕消除、耐磨性等性能,取一块含有电泳、中涂、面漆复合涂层的汽车钢板,采用3M 800#砂纸打磨该实验板直至中涂层,然后采用湖南湘江关西开发的LS-10低温色漆(不添加固化剂)进行打磨层的修补(涂料根据试板颜色而定),修补色漆完成后闪干3-5min,然后喷涂湖南湘江关西开发的HK-7000 快干型低温修补清漆(加固化剂),紧接着在喷涂完修补清漆的涂层边缘喷涂消痕剂,流平5min后,采用烤灯或者红外灯烘烤(60-80℃,30min),烘烤结束后采用3M 1000#砂纸打磨,并采用3M抛光蜡抛光。消痕剂性能评价项目,见表1。
注:第1-3项属常规性能、储存稳定性的检测项目;4-5项为修补性的综合评价项目。HKSTM检测方法为湖南湘江关西测试方法;ES-X63122 4.3.4为三菱汽车公司企业标准。
消痕剂性能检测结果,见表2、表3。
评价结果:从表2可知,实施例1-3均具有优异的贮藏稳定性,由于所实验的树脂为中低羟值的羟基丙烯酸树脂,干燥速度适中,具有优异的修补外观和优异的耐磨性能,同时具备优异的接痕消除能力。
相反,比较例1中,由于台湾德谦树脂FS2050羟值含量过低,烘烤时交联速度快,内聚力较高,涂膜脆性大,涂膜外观显得干瘪,且打磨抛光时漆膜易露底。
比较例2中,纽佩斯丙烯酸树脂Setalux 1208羟值过高,148.5mgKOH/g,反应速度过慢,喷涂完的接口水难以固化,烘烤后修补边界处有非常明显的接口痕迹,不能满足修补要求,特别是不能适应水性产品的修补。
比较例3中,酯类溶剂沸点过高,己二酸甲酯、丁二酸甲酯、戊二酸甲酯的沸点在200~240℃之间,挥发速度慢,施工时极易流挂,且修补完成后,烘烤难以干燥,抛光打磨时,修补区域极易粘附打磨灰,出现蒙光、成片颗粒等异常。
Claims (6)
1.一种汽车车身及保险杠修补用消痕剂,其特征在于,由以下重量份的组分组成:羟基丙烯酸树脂8~12份,芳香烃溶剂35~45份,酯类溶剂35~45份,酮类溶剂8~12份,流平剂0.1~0.3份;
所述羟基丙烯酸树脂为羟值60~90mgKOH/g的羟基丙烯酸树脂;
所述芳香烃溶剂为溶解度参数8.9~9.3,沸点80~145℃的芳香烃溶剂;
所述酯类溶剂为沸点70~100℃、120~140℃、190~220℃三个挥发段的溶剂的混合物,三者的质量配比为1~2:1~2:1。
2.根据权利要求1所述的汽车车身及保险杠修补用消痕剂,其特征在于:所述芳香烃溶剂为甲苯、二甲苯中的一种或两者的混合物。
3.根据权利要求1或2所述的汽车车身及保险杠修补用消痕剂,其特征在于:所述酯类溶剂为乙酸乙酯、乙酸丁酯和乙二醇丁醚醋酸酯的混合物。
4.根据权利要求1或2所述的汽车车身及保险杠修补用消痕剂,其特征在于:所述酮类溶剂为溶解度参数8.6~9.9,沸点60~80℃的酮类溶剂。
5.根据权利要求1或2所述的汽车车身及保险杠修补用消痕剂,其特征在于:所述流平剂为氟改性的丙烯酸酯类流平剂。
6.一种如权利要求1所述的汽车车身及保险杠修补用消痕剂的制备方法,其特征在于,包括以下步骤:
(1)按以下重量配比称取各组分原料:羟基丙烯酸树脂8~12份,芳香烃溶剂35~45份,酯类溶剂35~45份,酮类溶剂8~12份,流平剂0.1~0.3份;
(2)将所称取的羟基丙烯酸树脂、芳香烃溶剂、酯类溶剂、酮类溶剂、流平剂依次加入调和釜,搅拌均匀,即成。