CN103496851A - 黑色微晶玻璃板材及其生产方法 - Google Patents
黑色微晶玻璃板材及其生产方法 Download PDFInfo
- Publication number
- CN103496851A CN103496851A CN201310441664.7A CN201310441664A CN103496851A CN 103496851 A CN103496851 A CN 103496851A CN 201310441664 A CN201310441664 A CN 201310441664A CN 103496851 A CN103496851 A CN 103496851A
- Authority
- CN
- China
- Prior art keywords
- parts
- minutes
- glass
- glass sheet
- crystallization
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
原料名称 | 菱镁矿 | 花岗石 | 磷酸二氢钙 | 重钙 | 锰矿 |
重量(Kg) | 94 | 348.6 | 17.7 | 27.5 | 36.8 |
化学成份 | 花岗石 | 重钙 | 铁红 | 菱镁矿 | 磷酸二氢钙 |
Na2O | 3.706 | 0 | 0 | 0.043 | 0 |
MgO | 0.2687 | 0 | 0 | 42.7094 | 0 |
Al2O3 | 11.7 | 0 | 0 | 0.2678 | 0 |
SiO2 | 77.306 | 0 | 0 | 1.3426 | 0 |
P2O5 | 0.0193 | 0 | 0 | 0.023 | 51 |
K2O | 4.721 | 0 | 0 | 0.015 | 0 |
CaO | 0.398 | 54.88 | 0 | 4.4148 | 17 |
Fe2O3 | 0.967 | 0 | 98 | 0.092 | 0 |
Na2O | MgO | Al2O3 | SiO2 | P2O5 | K2O | CaO | TiO2 | MnO | Fe2O3 |
2.85 | 9.04 | 9.03 | 59.56 | 2.00 | 3.62 | 5.06 | 0.04 | 0.03 | 8.65 |
原料名称 | 菱镁矿 | 花岗石 | 磷酸二氢钙 | 重钙 | 锰矿 |
重量(Kg) | 88.7 | 348.7 | 19.5 | 30.4 | 35.8 |
Na2O | MgO | Al2O3 | SiO2 | P2O5 | K2O | CaO | TiO2 | MnO | Fe2O3 |
2.85 | 8.54 | 9.03 | 59.56 | 2.20 | 3.62 | 5.56 | 0.04 | 0.03 | 8.45 |
Claims (2)