CN103496030A - 一种混凝土印字砖的加工工艺 - Google Patents
一种混凝土印字砖的加工工艺 Download PDFInfo
- Publication number
- CN103496030A CN103496030A CN201310428890.1A CN201310428890A CN103496030A CN 103496030 A CN103496030 A CN 103496030A CN 201310428890 A CN201310428890 A CN 201310428890A CN 103496030 A CN103496030 A CN 103496030A
- Authority
- CN
- China
- Prior art keywords
- brick
- lettering
- mould
- cooling
- compound
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种混凝土印字砖的加工工艺,该工艺包括以下工艺步骤:1)取料、2)搅拌、3)预热、4)制模、5)压制、6)冷却、7)定型、8)养护、9)盛放、10)检验。本发明具有步骤安排合理和方便制造等优点,能在混凝土砖表面印字,并保证砖的成型质量。
Description
技术领域
本发明涉及墙体材料加工技术领域,具体的说是一种混凝土印字砖的加工工艺。
背景技术
目前,随着节能、环保的理念的不断推广,对墙体材料也带来了一定的影响,现有的工厂大多采用矿渣作为墙体材料(如混凝土砖)的主要填充料,不仅实现了废物再利用,避免了资源的浪费,降低了生产的成本,还在一定程度上提高了混凝土砖的性能。对于混凝土砖,在砖上印字可以用以对砖的类型、性能进行区分,而如何在砖上印字成为困扰人们的难题,若采用传统的印字方法,在印字后,砖上的砂土就会出现脱落,成型质量较差。
发明内容
本发明所要解决的技术问题在于提供一种步骤安排合理的、方便制造的,能在混凝土砖表面印字并保证砖成型质量的加工工艺,即一种混凝土印字砖的加工工艺。
本发明所要解决的技术问题采用以下技术方案来实现:
一种混凝土印字砖的加工工艺,该工艺包括以下工艺步骤:
1)取料:根据实际掺配比例,从水泥容器、石粉容器、砂容器、黑粉容器内依次称取一定量的水泥、石粉、砂、黑粉;
2)搅拌:将步骤1)取出的料投放进搅拌机内,并添加一定量的粘接剂,然后搅拌50-60分钟,添加粘接剂是为了在压制时,能够确保各材料间的粘接力度,从而有效的放置成型后砂土的脱落,为印字的顺利进行提供保障;
3)预热:对步骤2)搅拌后的混合料进行预热,温度控制在45-55摄氏度,并保持混合料具有一定的湿度,预热处理能够保持各材料的相关性能,并为压制提供一个成型温度,能够保证成型后的砖的强度;
4)制模:将需要印的字雕刻在模具上,并在模具上开设一定量的空冷通道和水冷通道,为了方便在模具山架设空冷和水冷设备;
5)压制:利用步骤4)刻好的模具对步骤3)预热后的混合料进行压制,并利用振动的方式将混合料振实,振动的频率控制在80-100Hz,从而保证砖成型后具有一定的紧实度;
6)冷却:采用步骤4)中模具上的空冷与水冷相结合的方式对步骤5)压制后的模具进行冷却,直至冷却至室温,采用空冷与水冷相结合的方式,能够加速模具的冷却,提高冷却的效率,并利用冷却使印字砖成型;
7)定型:继续压制1-2分钟,保证印字砖的充分定型,定型处理是为了保证砖成型后不会出现砂土脱落的现象;
8)养护:将成型后的印字砖放置在养护房内,养护时间为一天,养护期间每隔40-50分钟喷一次水雾;
9)盛放:将步骤8)养护后的印字砖露天放置,盛放时间为28天,且盛放期间,每天淋水次数不少于2次;
10)检验:对步骤9)盛放后的印字砖进行抽检,检查强度、硬度和质量是否达标,并观察印字处有无裂痕。
本发明的有益效果是:本发明具有步骤安排合理和方便制造等优点,能在混凝土砖表面印字,并保证砖的成型质量。
具体实施方式
为了使本发明实现的技术手段、创作特征、达成目的与功效易于明白了解,下面对本发明进一步阐述。
一种混凝土印字砖的加工工艺,该工艺包括以下工艺步骤:
1)取料:根据实际掺配比例,从水泥容器、石粉容器、砂容器、黑粉容器内依次称取一定量的水泥、石粉、砂、黑粉;
2)搅拌:将步骤1)取出的料投放进搅拌机内,并添加一定量的粘接剂,然后搅拌50-60分钟,添加粘接剂是为了在压制时,能够确保各材料间的粘接力度,从而有效的放置成型后砂土的脱落,为印字的顺利进行提供保障;
3)预热:对步骤2)搅拌后的混合料进行预热,温度控制在45-55摄氏度,并保持混合料具有一定的湿度,预热处理能够保持各材料的相关性能,并为压制提供一个成型温度,能够保证成型后的砖的强度;
4)制模:将需要印的字雕刻在模具上,并在模具上开设一定量的空冷通道和水冷通道,为了方便在模具山架设空冷和水冷设备;
5)压制:利用步骤4)刻好的模具对步骤3)预热后的混合料进行压制,并利用振动的方式将混合料振实,振动的频率控制在80-100Hz,从而保证砖成型后具有一定的紧实度;
6)冷却:采用步骤4)中模具上的空冷与水冷相结合的方式对步骤5)压制后的模具进行冷却,直至冷却至室温,采用空冷与水冷相结合的方式,能够加速模具的冷却,提高冷却的效率,并利用冷却使印字砖成型;
7)定型:继续压制1-2分钟,保证印字砖的充分定型,定型处理是为了保证砖成型后不会出现砂土脱落的现象;
8)养护:将成型后的印字砖放置在养护房内,养护时间为一天,养护期间每隔40-50分钟喷一次水雾;
9)盛放:将步骤8)养护后的印字砖露天放置,盛放时间为28天,且盛放期间,每天淋水次数不少于2次;
10)检验:对步骤9)盛放后的印字砖进行抽检,检查强度、硬度和质量是否达标,并观察印字处有无裂痕。
按照上述工艺步骤实施,即可完成对印字砖的生产制造。
以上显示和描述了本发明的基本原理、主要特征和本发明的优点。本行业的技术人员应该了解,本发明不受上述实施例的限制,上述实施例和说明书中描述的只是本发明的原理,在不脱离本发明精神和范围的前提下,本发明还会有各种变化和改进,这些变化和改进都落入要求保护的本发明范围内。本发明要求保护范围由所附的权利要求书及其等效物界定。
Claims (1)
1.一种混凝土印字砖的加工工艺,其特征在于:该工艺包括以下工艺步骤:
1)取料:根据实际掺配比例,从水泥容器、石粉容器、砂容器、黑粉容器内依次称取一定量的水泥、石粉、砂、黑粉;
2)搅拌:将步骤1)取出的料投放进搅拌机内,并添加一定量的粘接剂,然后搅拌50-60分钟;
3)预热:对步骤2)搅拌后的混合料进行预热,温度控制在45-55摄氏度,并保持混合料具有一定的湿度;
4)制模:将需要印的字雕刻在模具上,并在模具上开设一定量的空冷通道和水冷通道;
5)压制:利用步骤4)刻好的模具对步骤3)预热后的混合料进行压制,并利用振动的方式将混合料振实,振动的频率控制在80-100Hz;
6)冷却:采用步骤4)中模具上的空冷与水冷相结合的方式对步骤5)压制后的模具进行冷却,直至冷却至室温;
7)定型:继续压制1-2分钟,保证印字砖的充分定型;
8)养护:将成型后的印字砖放置在养护房内,养护时间为一天,养护期间每隔40-50分钟喷一次水雾;
9)盛放:将步骤8)养护后的印字砖露天放置,盛放时间为28天,且盛放期间,每天淋水次数不少于2次;
10)检验:对步骤9)盛放后的印字砖进行抽检,检查强度、硬度和质量是否达标,并观察印字处有无裂痕。