CN103485503A - Stable interior wall decorative material and method for manufacturing same - Google Patents
Stable interior wall decorative material and method for manufacturing same Download PDFInfo
- Publication number
- CN103485503A CN103485503A CN201310421163.2A CN201310421163A CN103485503A CN 103485503 A CN103485503 A CN 103485503A CN 201310421163 A CN201310421163 A CN 201310421163A CN 103485503 A CN103485503 A CN 103485503A
- Authority
- CN
- China
- Prior art keywords
- layer
- pvc
- micropore
- ornament materials
- indoor wall
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a stable interior wall decorative material which comprises a fiber cloth\glass fiber layer. An upper PVC (polyvinyl chloride) layer and a lower PVC layer are arranged on the upper side and the lower side of the fiber cloth\glass fiber layer, the upper PVC layer comprises a surface abrasion-resistant layer and a microporous cell layer, and the microporous cell layer is arranged between the surface abrasion-resistant layer and the fiber cloth\glass fiber layer; the lower PVC layer is a foam layer, the upper PVC layer further comprises a surface coating layer, and the surface abrasion-resistant layer is arranged between the surface coating layer and the microporous cell layer. The invention further discloses a method for manufacturing the stable interior wall decorative material. The stable interior wall decorative material and the method have the advantages that the high-performance fiber cloth\glass fiber layer is compounded with PVC materials, so that the stability and the strength of the product can be improved, the stable interior wall decorative material is excellent in characteristics such as flame retardance, heat insulation, damp proofing, sound insulation and mildew proofing, and is long in service life, and patterns on the surface of the product are rich and varied.
Description
Technical field
The invention belongs to building materials field, relate to specifically a kind of novel stable type indoor wall ornament materials, the invention still further relates to a kind of production technology of this material.
Background technology
At present, more common indoor wall ornament materials mainly is divided into several large classes on the market: wallpaper class, coating class, stone materials and cloth art class etc.Use coating to account for 70% of inner wall decoration, occupied the leading position in market, the problems such as that but coating often easily occurs in long-term use procedure is mouldy, delamination, and the color of its decorative effect is single, can't realize the decorative effect of decorative pattern, and also have the disadvantages such as washing property of erasable is low, so abandoned by the finishing of some personalizations gradually.Wallpaper class material cost is relatively more expensive than emulsion paint, construction level and quality are not easy to control, product structure is that the layers of material different by the coefficient of expansion is combined into one, still have mouldy, alice in its use procedure, the phenomenon such as flame retardant effect is poor, life cycle is short, some wallpaper color fastness are poor, are unable to bear scouring, the place that especially daylight often irradiates, time has been grown and has had the phenomenon of fading, and range of application is subject to larger restriction.A kind of decorative material for internal wall of cloth art class material for starting at home in recent years to prevail.But its flame-retarding characteristic, the easy shortcoming such as dirty, have got long long way to go apart from customer's generally approval.The stone materials material is due to its radiativity, and construction is complicated, expensive, general application that can be not a large amount of in wall decoration.So the customer is in the urgent need to a kind of indoor wall ornament materials, not only safety and environmental protection but also durable in use.
Summary of the invention
The object of the invention is to the problem for above-mentioned existence, a kind of stable type indoor wall ornament materials is provided, by high-performance fiber cloth glass layer and PVC material carry out compound, construction stability is better, heat stability and intensity are high, possess the characteristics such as excellent fire-retardant, insulation, protection against the tide, mildew-resistant, long service life, the pattern of product surface is rich and varied.
In order to realize the foregoing invention purpose, the technical solution used in the present invention is as follows:
A kind of stable type indoor wall ornament materials, have cloth glass layer, cloth the both sides up and down of glass layer, be upper PVC layer and lower PVC layer.
Described upper PVC layer is surface wear-resistant layer and micropore alveolar layer, the micropore alveolar layer surface wear-resistant layer and cloth between glass layer;
Described lower PVC layer is foaming layer.
Described cloth glass layer be terylene, nylon, cotton and numb material cloth glass fiber.
Adopt tatting technique, glass fiber or terylene, nylon, cotton and fiber crops are manufactured to embryo cloth.
The material composition of described surface wear-resistant layer is 25%-55% PVC, 20%-60% environment-friendly plasticizer, 0.5%-5% environmental protection stabilizing agent, other auxiliary agent of 5%-40%.
Surface wear-resistant layer is that the PVC of the high abrasion loss material that is mixed makes.The high polymerization degree resin that wherein PVC material selection polymerization K value is greater than 70.The wear-resisting PVC layer possesses excellent protection against the tide, mildew-resistant characteristic, abrasion resistance, anti-flammability.
The material composition of described micropore alveolar layer is 20%-60% PVC, 20%-50% environment-friendly plasticizer, 0.5%-5% environmental protection stabilizing agent, other auxiliary agent of 5%-40%.
The suitable EPVC used as expanded material of PVC material selection wherein.
The material composition of described foaming layer is 20%-70% PVC rubber plastic foam material, 15%-60% environment-friendly plasticizer, 0.5%-5% environmental protection stabilizing agent, other auxiliary agent of 2%-40%.
Micropore alveolar layer and foaming layer provide excellent sound-absorption and heat-insulation characteristic for material.
The foam structure of material uniqueness, coefficient of thermal conductivity is little, and heat preservation and energy conservation effects is good.Material self can digest the phenomenons such as warpage that minimal stress brings, opposite joint cracking, foaming, delamination.Foam structure design makes product have sufficient elasticity, feels more after comfortable and can also effectively reduce the injury caused because accidentally colliding with, and especially can effectively protect the external corner of metope.
Described PVC rubber plastic foam material composition is:
60～100 parts, PVC powder;
2～8 parts of AC blowing agents;
1～7 part of antimony oxide flame retardant;
1～6 part of environmental protection stabilizing agent;
0～120 part of filler;
Environment-friendly plasticizer 40～100;
Described PVC powder is the Corvic that suspension method or emulsion method are produced; Described filler is inorganic mineral material.
Adopt PVC to have excellent water repellency, the vacuum dehydration performance is less than 10%, can farthest reduce the heat-insulating property caused because of the material water suction and descend; Add the wide spectrum anti-fungus material in modified formula, reach the effect of fungus-resistant; After foaming by high temperature, form closed loose structure, the effect of the heat conductivility of material itself and closed pore Air, make independently air structure unit of product formation, due to the gas molecule spacing farthest, heat conductivility is minimum, this structure has guaranteed the insulation capacity of material; Afterwards, composite and flexible cloth or glass fiber material again on perforated foams.
Described filler is preferably calcium carbonate, kaolin, French chalk, magnalium compound, wooden molding powder.
Described other auxiliary agent is environment-friendly foaming agent, surfactant, fire retardant or filler; Described environment-friendly plasticizer is non-adjacent benzene class plasticizing agent:
TOTM (TEHTM), as: the different monooctyl ester of trimellitic acid three;
Hexamoll DINCH, as: cyclohexane 1,2-bis-base diisononyl esters;
The ATBC series products, as: ATBC-tributyl 2-acetylcitrate, BHTC-butyryl citric acid tri-n-hexyl ester;
DEHA (DOA), as: dioctyl adipate;
DOTP, as: DOTP; ESO, as: epoxidized soybean oil.
Described upper PVC layer also has the top finishing layer, and surface wear-resistant layer is between described top finishing layer and micropore alveolar layer, and the top finishing layer is processed through the Bio-pruf coating.
Described top finishing layer is that polyurethane, acrylate material make.
The high performance resin of acrylate material selection yellowing resistance, adhesive power excellence wherein.
Process through the Bio-pruf coating on surface, and Escherichia coli, staphylococcus aureus, Candida albicans are had to good inhibitory action, by the method detection of " the anti-mould determination method of GB1741-79 paint film ".Bacteriostasis property can reach more than 98% common bacteria bacteriostasis rate in 72 hours, guarantees that this ornament materials has the fungicidal properties effect.
Material environment friendly aspect of performance of the present invention, this product indices is much better than the GB-18585-2001 standard.Obtain country's " nonhazardous (green) indoor hardware fitting " certificate, meet the environmental protection standard requirement of indoor hardware fitting fully.
Through national fire-proof construction material quality examination center, check: this product indices all meets the regulation requirement of nonflammable material, reaches GB8624 B-s2, d0, t1 level.
Product is to possess the special pigment of rating for light fastness preferably, and rating for light fastness reaches 7 grades of ISO105B02 standards, and anti-look change, anti-aging, compare longer service life with the traditional decoration material.
The cleaning performance aspect: the macromolecule raw material are processed through special process, effectively intercept infiltration, acid and alkali-resistance, antistatic, possess water resistance, be difficult for dust suction.Impervious and the pH resistance test by national experiment of building material center.Not mouldy, alice not, and can as floor tile, repeatedly clean.Need not sweep, antistatic performance makes it away from dust.
Insulation, heat-proof quality, through national building materials inspection center's detection detection to its coefficient of thermal conductivity according to (GB/T17794-2008), meet the requirement of country about energy-conserving product.
Due to adding of fiber stabilized zone, make the telescopic resilience of material further reduce, reach in 0.2%, be difficult for producing construction joint in work progress, in follow-up use procedure, can not cause because of the variation of ambient temperature Material shrinkage to form gap, reach the Expected Results of house ornamentation, finishing work.
When producing raw material, buying controls the content's index of content of beary metal, pernicious gas and volatile matter well; In factory formula, considered to add the environmental protection flame retardant material, could environmental protection and fire-retardant thereby produce product.
Control the internal stress parameter of product well when producing, thereby produce product, just can prevent the phenomenons such as material generation warpage, foaming, delamination.
A kind of production method of described stable type indoor wall ornament materials comprises the following steps:
1) by a kind of automatic recipe maker, respectively according to surface wear-resistant layer, micropore alveolar layer, foaming layer and cloth the formula of glass layer carry out the preparation of thickener; Color by the PVC thickener of surface wear-resistant layer, micropore alveolar layer according to the client requires proportionally to carry out adding of color;
2) adopt the blade coating production technology, scraping coating line, by the thickener blade coating of surface wear-resistant layer on release liners; Release liners is carried out the oven dry of surface wear-resistant layer by delivering into baking oven;
3) painting of carrying out the micropore alveolar layer at the next board of coating line is scraped, by cloth glass layer naturally put down on the thickener that is covered in the micropore alveolar layer; Stick cloth material after glass layer again along with release liners enters baking oven, dried;
4) on the next board of coating line, by the thickener of foaming layer be coated on cloth on glass layer, then along with release liners is sent into, baking oven is dried and the foaming of material;
5) product is peeled off from release liners, sent into print surface coatings operation;
6) printing process carries out the printing of decorative pattern coatings to product wearing layer surface, is made into the required pattern of client, finally sends into packing and the inspection process of product, selects qualified products.
Compared with prior art, the invention has the beneficial effects as follows:
The present invention by cloth glass layer is compound joins in the PVC house decorative material, make the stability of material better, be difficult for producing and shrink, solved the problem that pure PVC ornament materials easily gaps because of exterior temperature change, after construction, metope is integral, the linking seam that does not have wallpaper class material there will be; Construction stability is better, and heat stability and intensity are high;
2. by the design of the rational formula of PVC wearing layer and foaming layer, the product thickness specification is thicker than the common wallpaper with base cloth far away, and product thickness can reach 1.5 ~ 2.0mm, can effectively realize that product is fire-retardant, moistureproof, mildew-resistant, heat insulation characteristic;
3. by the screening of the feature of environmental protection to formula materials, can adapt to the requirement of country for the house decorative material limits of harmful substances fully, long service life, the pattern of product surface is rich and varied, indoor wall ornament materials for middle and high end is effective supplementing, and the functional of its excellence is also the building material classification of encourage growth in country's 12 planning.
The accompanying drawing explanation
Fig. 1 is stable type indoor wall ornament materials cross-sectional view of the present invention;
Fig. 2 is the production procedure sketch of material of the present invention;
Wherein, mark in figure: 1 is the top finishing layer, and 2 is surface wear-resistant layer, and 3 is the micropore alveolar layer, and 4 is Xian Weibu glass layer, and 5 is foaming layer.
The specific embodiment
Below in conjunction with the specific embodiment, foregoing invention content of the present invention is described in further detail.
But this should be interpreted as to the scope of the above-mentioned theme of the present invention only limits to following embodiment.Without departing from the idea case in the present invention described above, according to ordinary skill knowledge and customary means, make various replacements and change, all should comprise within the scope of the invention.
embodiment 1
The described stable type indoor wall of the present embodiment ornament materials has 5 layers, and layers of material is:
The top finishing layer of outermost layer for processing through the Bio-pruf coating.
The material composition of surface wear-resistant layer is 42% PVC, 20% environment-friendly plasticizer, 4% environmental protection stabilizing agent, 34% other auxiliary agent.
The material composition of micropore alveolar layer is 50% PVC, 30% environment-friendly plasticizer, 3% environmental protection stabilizing agent, 17% other auxiliary agent.
Cloth the material composition of glass layer be nylon fiber.
The material composition of foaming layer is 40% PVC rubber plastic foam material, 50% environment-friendly plasticizer, 3% environmental protection stabilizing agent, 7% other auxiliary agent.
Described PVC rubber plastic foam material composition is:
65 parts, PVC powder;
5 parts of AC blowing agents;
7 parts of antimony oxide flame retardants;
4 parts of environmental protection stabilizing agents;
20 parts of fillers;
60 parts of environment-friendly plasticizers;
Described PVC powder, be suspension method produce Corvic; Described plasticizing agent is cyclohexane 1,2-bis-base diisononyl esters; Described filler is calcium carbonate.
embodiment 2
The described stable type indoor wall of the present embodiment ornament materials has 5 layers, and layers of material is:
The top finishing layer of outermost layer for processing through the Bio-pruf coating.
The material composition of surface wear-resistant layer is 25% PVC, 50% environment-friendly plasticizer, 3% environmental protection stabilizing agent, 22% other auxiliary agent.
The material composition of micropore alveolar layer is 30% PVC, 40% environment-friendly plasticizer, 0.5% environmental protection stabilizing agent, 29.5% other auxiliary agent.
Cloth the material composition of glass layer be glass fiber.
The material composition of foaming layer is 70% PVC rubber plastic foam material, 20% environment-friendly plasticizer, 1% environmental protection stabilizing agent, 9% other auxiliary agent.
Described PVC rubber plastic foam material composition is:
90 parts, PVC powder;
6 parts of AC blowing agents;
5 parts of antimony oxide flame retardants;
3 parts of environmental protection stabilizing agents;
100 parts of environment-friendly plasticizers;
Described PVC powder, be emulsion method produce Corvic; Described plasticizing agent is citrate plasticizer.
embodiment 3
The described stable type indoor wall of the present embodiment ornament materials has 5 layers, and layers of material is:
The top finishing layer of outermost layer for processing through the Bio-pruf coating.
The material composition of surface wear-resistant layer is 40% PVC, 29% environment-friendly plasticizer, 2% environmental protection stabilizing agent, 29% other auxiliary agent.
The material composition of micropore alveolar layer is 60% PVC, 20% environment-friendly plasticizer, 2% environmental protection stabilizing agent, 18% other auxiliary agent.
Cloth the material composition of glass layer be numb material fiber.
The material composition of foaming layer is 22% PVC rubber plastic foam material, 60% environment-friendly plasticizer, 0.5% environmental protection stabilizing agent, 17.5% other auxiliary agent.
Described PVC rubber plastic foam material composition is:
60 parts, PVC powder;
7 parts of AC blowing agents;
2 parts of antimony oxide flame retardants;
6 parts of environmental protection stabilizing agents;
70 parts of fillers;
70 parts of environment-friendly plasticizers;
Described PVC powder, be suspension method produce Corvic; Described plasticizing agent is the TOTM plasticizing agent; Described filler is the magnalium compound.
embodiment 4
The described stable type indoor wall of the present embodiment ornament materials has 5 layers, and layers of material is:
The top finishing layer of outermost layer for processing through the Bio-pruf coating.
The material composition of surface wear-resistant layer is 55% PVC, 35.5% environment-friendly plasticizer, 0.5% environmental protection stabilizing agent, 9% other auxiliary agent.
The material composition of micropore alveolar layer is 35% PVC, 24% environment-friendly plasticizer, 1% environmental protection stabilizing agent, 40% other auxiliary agent.
Cloth the material composition of glass layer be polyster fibre.
The material composition of foaming layer is 28% PVC rubber plastic foam material, 35% environment-friendly plasticizer, 2% environmental protection stabilizing agent, 35% other auxiliary agent.
Described PVC rubber plastic foam material composition is:
80 parts, PVC powder;
8 parts of AC blowing agents;
6 parts of antimony oxide flame retardants;
2 parts of environmental protection stabilizing agents;
100 parts of fillers;
40 parts of environment-friendly plasticizers;
Described PVC powder, be emulsion method produce Corvic; Described plasticizing agent is dioctyl adipate; Described filler is kaolin.
embodiment 5
The described stable type indoor wall of the present embodiment ornament materials has 5 layers, and layers of material is:
The top finishing layer of outermost layer for processing through the Bio-pruf coating.
The material composition of surface wear-resistant layer is 35% PVC, 20% environment-friendly plasticizer, 5% environmental protection stabilizing agent, 40% other auxiliary agent.
The material composition of micropore alveolar layer is 40% PVC, 50% environment-friendly plasticizer, 5% environmental protection stabilizing agent, 5% other auxiliary agent.
Cloth the material composition of glass layer be cotton fiber.
The material composition of foaming layer is 60% PVC rubber plastic foam material, 15% environment-friendly plasticizer, 5% environmental protection stabilizing agent, 20% other auxiliary agent.
Described PVC rubber plastic foam material composition is:
100 parts, PVC powder;
3 parts of AC blowing agents;
4 parts of antimony oxide flame retardants;
2 parts of environmental protection stabilizing agents;
40 parts of fillers;
100 parts of environment-friendly plasticizers;
Described PVC powder, be emulsion method produce Corvic; Described plasticizing agent is DOTP; Described filler is French chalk.
embodiment 6
The described stable type indoor wall of the present embodiment ornament materials has 5 layers, and layers of material is:
The top finishing layer of outermost layer for processing through the Bio-pruf coating.
The material composition of surface wear-resistant layer is 50% PVC, 41% environment-friendly plasticizer, 4% environmental protection stabilizing agent, 5% other auxiliary agent.
The material composition of micropore alveolar layer is 20% PVC, 45% environment-friendly plasticizer, 1% environmental protection stabilizing agent, 34% other auxiliary agent.
Cloth the material composition of glass layer be nylon fiber.
The material composition of foaming layer is 20% PVC rubber plastic foam material, 38% environment-friendly plasticizer, 2% environmental protection stabilizing agent, 40% other auxiliary agent.
Described PVC rubber plastic foam material composition is:
70 parts, PVC powder;
6 parts of AC blowing agents;
1 part of antimony oxide flame retardant;
5 parts of environmental protection stabilizing agents;
120 parts of fillers;
80 parts of environment-friendly plasticizers;
Described PVC powder, be suspension method produce Corvic; Described plasticizing agent is epoxidized soybean oil; Described filler is calcium carbonate.
embodiment 7
The described stable type indoor wall of the present embodiment ornament materials has 5 layers, and layers of material is:
The top finishing layer of outermost layer for processing through the Bio-pruf coating.
The material composition of surface wear-resistant layer is 32% PVC, 60% environment-friendly plasticizer, 1% environmental protection stabilizing agent, 7% other auxiliary agent.
The material composition of micropore alveolar layer is 55% PVC, 35% environment-friendly plasticizer, 2% environmental protection stabilizing agent, 8% other auxiliary agent.
Cloth the material composition of glass layer be polyster fibre.
The material composition of foaming layer is 50% PVC rubber plastic foam material, 44% environment-friendly plasticizer, 4% environmental protection stabilizing agent, 2% other auxiliary agent.
Described PVC rubber plastic foam material composition is:
80 parts, PVC powder;
2 parts of AC blowing agents;
2 parts of antimony oxide flame retardants;
1 part of environmental protection stabilizing agent;
80 parts of fillers;
50 parts of environment-friendly plasticizers;
Described PVC powder, be emulsion method produce Corvic; Described plasticizing agent is the different monooctyl ester of trimellitic acid three; Described filler is wooden molding powder.
embodiment 8
The described stable type indoor wall of the present embodiment ornament materials has 5 layers, and layers of material is:
The top finishing layer of outermost layer for processing through the Bio-pruf coating.
The material composition of surface wear-resistant layer is 55% PVC, 21% environment-friendly plasticizer, 0.5% environmental protection stabilizing agent, 23.5% other auxiliary agent.
The material composition of micropore alveolar layer is 47% PVC, 29% environment-friendly plasticizer, 4% environmental protection stabilizing agent, 20% other auxiliary agent.
Cloth the material composition of glass layer be flaxen fiber.
The material composition of foaming layer is 65% PVC rubber plastic foam material, 25% environment-friendly plasticizer, 5% environmental protection stabilizing agent, 5% other auxiliary agent.
Described PVC rubber plastic foam material composition is:
75 parts, PVC powder;
7 parts of AC blowing agents;
3 parts of antimony oxide flame retardants;
5 parts of environmental protection stabilizing agents;
60 parts of fillers;
90 parts of environment-friendly plasticizers;
Described PVC powder, be emulsion method produce Corvic; Described plasticizing agent is the ATBC-tributyl 2-acetylcitrate; Described filler is kaolin.
embodiment 9
The formula of above each embodiment, according to following steps production:
1) by a kind of automatic recipe maker, respectively according to surface wear-resistant layer, micropore alveolar layer, foaming layer and cloth the formula of glass layer carry out the preparation of thickener; Color by the PVC thickener of surface wear-resistant layer, micropore alveolar layer according to the client requires proportionally to carry out adding of color;
2) adopt the blade coating production technology, scraping coating line, by the thickener blade coating of surface wear-resistant layer on release liners; Release liners is carried out the oven dry of surface wear-resistant layer by delivering into baking oven;
3) painting of carrying out the micropore alveolar layer at the next board of coating line is scraped, by cloth glass layer naturally put down on the thickener that is covered in the micropore alveolar layer; Stick cloth material after glass layer again along with release liners enters baking oven, dried;
4) on the next board of coating line, by the thickener of foaming layer be coated on cloth on glass layer, then along with release liners is sent into, baking oven is dried and the foaming of material;
5) product is peeled off from release liners, sent into print surface coatings operation;
6) printing process carries out the printing of decorative pattern coatings to product wearing layer surface, is made into the required pattern of client, finally sends into packing and the inspection process of product, selects qualified products.
In sum, stability of material of the present invention is good, is difficult for producing shrinking, and temperature influence is little, and after construction, metope is integral, and construction stability is better, and heat stability and intensity are high; This material is thicker than the common wallpaper with base cloth, can effectively realize that product is fire-retardant, moistureproof, mildew-resistant, heat insulation characteristic; Formula is all environment-friendly materials, can adapt to the requirement of country for the house decorative material limits of harmful substances fully, long service life, and the pattern of product surface is rich and varied.
Claims (10)
1. a stable type indoor wall ornament materials, it is characterized in that: having Xian Weibu glass layer, in the both sides up and down of Xian Weibu glass layer, is upper PVC layer and lower PVC layer.
2. stable type indoor wall ornament materials according to claim 1, it is characterized in that: described upper PVC layer is surface wear-resistant layer and micropore alveolar layer, the micropore alveolar layer surface wear-resistant layer and cloth between glass layer;
Described lower PVC layer is foaming layer.
3. according to stable type indoor wall ornament materials according to claim 2, it is characterized in that: described cloth glass layer be terylene, nylon, cotton and numb material cloth glass fiber.
4. according to stable type indoor wall ornament materials according to claim 2, it is characterized in that: the material composition of described surface wear-resistant layer is 25%-55% PVC, 20%-60% environment-friendly plasticizer, 0.5%-5% environmental protection stabilizing agent, other auxiliary agent of 5%-40%.
5. according to stable type indoor wall ornament materials according to claim 2, it is characterized in that: the material composition of described micropore alveolar layer is 20%-60% PVC, 20%-50% environment-friendly plasticizer, 0.5%-5% environmental protection stabilizing agent, other auxiliary agent of 5%-40%.
6. according to stable type indoor wall ornament materials according to claim 2, it is characterized in that: the material composition of described foaming layer is 20%-70% PVC rubber plastic foam material, 15%-60% environment-friendly plasticizer, 0.5%-5% environmental protection stabilizing agent, other auxiliary agent of 2%-40%.
7. according to stable type indoor wall ornament materials according to claim 6, it is characterized in that: described PVC rubber plastic foam material composition is:
60～100 parts, PVC powder;
2～8 parts of AC blowing agents;
1～7 part of antimony oxide flame retardant;
1～6 part of environmental protection stabilizing agent;
0～120 part of filler;
Environment-friendly plasticizer 40～100;
Described PVC powder is the Corvic that suspension method or emulsion method are produced; Described filler is inorganic mineral material.
8. according to the described stable type indoor wall of claim 4-7 any one ornament materials, it is characterized in that: described other auxiliary agent is environment-friendly foaming agent, surfactant, fire retardant or filler; Described environment-friendly plasticizer is non-adjacent benzene class plasticizing agent.
9. stable type indoor wall ornament materials according to claim 2, it is characterized in that: described upper PVC layer also has the top finishing layer, surface wear-resistant layer is between described top finishing layer and micropore alveolar layer, and described top finishing layer is processed through the Bio-pruf coating.
10. the production method of the described stable type indoor wall of claim 2 or 9 ornament materials is characterized in that: comprise the following steps:
1) by a kind of automatic recipe maker, the formula according to surface wear-resistant layer, micropore alveolar layer, foaming layer carries out the preparation of thickener respectively; Color by the PVC thickener of surface wear-resistant layer, micropore alveolar layer according to the client requires proportionally to carry out adding of color;
2) adopt the blade coating production technology, scraping coating line, by the thickener blade coating of surface wear-resistant layer on release liners; Release liners is carried out the oven dry of surface wear-resistant layer by delivering into baking oven;
3) painting of carrying out the micropore alveolar layer at the next board of coating line is scraped, by cloth glass layer naturally put down on the thickener that is covered in the micropore alveolar layer; Stick cloth material after glass layer again along with release liners enters baking oven, dried;
4) on the next board of coating line, by the thickener of foaming layer be coated on cloth on glass layer, then along with release liners is sent into, baking oven is dried and the foaming of material;
5) product is peeled off from release liners, sent into print surface coatings operation;
6) printing process carries out the printing of decorative pattern coatings to product wearing layer surface, is made into the required pattern of client, finally sends into packing and the inspection process of product, selects qualified products.