CN103483829A - 一种耐高温阻燃硅橡胶及其制备方法 - Google Patents

一种耐高温阻燃硅橡胶及其制备方法 Download PDF

Info

Publication number
CN103483829A
CN103483829A CN201310461092.9A CN201310461092A CN103483829A CN 103483829 A CN103483829 A CN 103483829A CN 201310461092 A CN201310461092 A CN 201310461092A CN 103483829 A CN103483829 A CN 103483829A
Authority
CN
China
Prior art keywords
mass parts
silicon
rubber
silicone rubber
silicon rubber
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201310461092.9A
Other languages
English (en)
Inventor
郝冬冬
张薇薇
徐文俊
施贤斌
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
JIANGSU TIANCHENG SILICON CO Ltd
Original Assignee
JIANGSU TIANCHENG SILICON CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by JIANGSU TIANCHENG SILICON CO Ltd filed Critical JIANGSU TIANCHENG SILICON CO Ltd
Priority to CN201310461092.9A priority Critical patent/CN103483829A/zh
Publication of CN103483829A publication Critical patent/CN103483829A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种耐高温阻燃硅橡胶及其制备方法，所述耐高温阻燃硅橡胶按质量份数计组成为：100质量份甲基乙烯基硅橡胶生胶、30-50质量份气相白炭黑、3-6质量份二甲基二甲氧基硅烷、3-6质量份羟基硅油、0.2-0.6质量份乙烯基三甲氧基硅烷、0.2-0.4质量份硬脂酸、20-30质量份十溴二苯乙烷、1-2质量份氧化铈。本发明制备的硅橡胶经过实际检测具有良好的阻燃性能，同时具有较好的耐高温特性、硬度、强度和加工性能，完全能够满足耐高温阻燃电缆的使用要求。

Description

一种耐高温阻燃硅橡胶及其制备方法
技术领域
本发明涉及硅橡胶技术领域，具体涉及一种耐高温阻燃硅橡胶及其制备方法。
背景技术
硅橡胶具备良好的耐高低温、耐臭氧、耐候性、绝缘性及生产惰性等很多优异的性能，在国民经济的各个领域有着广泛的应用。气相白炭黑填充、卤素材料作为阻燃剂的硅橡胶具有较好的电绝缘、阻燃特性以及其优异的加工成型性能决定了它可以作为电缆使用。但是要应用在特殊的环境下，如高温环境，该硅橡胶的耐高温性能和阻燃性能就达不到要求，因此，研究耐高温阻燃硅橡胶具有十分积极的意义。
发明内容
本发明的目的是提供一种耐高温阻燃硅橡胶及其制备方法，解决现有技术中卤系阻燃硅橡胶不耐高温的缺点。
为解决上述问题，本发明采用以下技术方案：
一种耐高温阻燃硅橡胶，按质量份计组成为：
Figure BDA0000390920280000011
其中，所述甲基乙烯基硅橡胶生胶粘均分子量为60-80万，乙烯基摩尔为0.05%-0.15%。
所述气相白炭黑比表面积200-300m2/g。
所述羟基硅油羟基质量百分比为4-8%，粘度为25-50mPa.s。
上述耐高温阻燃硅橡胶的制备方法，包括如下步骤：
步骤一、将100质量份甲基乙烯基硅橡胶生胶加入到捏合机中搅拌2-4分钟；
步骤二、将30-50质量份气相白炭黑、3-6质量份二甲基二甲氧基硅烷、3-6质量份羟基硅油和0.2-0.4质量份硬脂酸分若干次加入到步骤一得到的甲基乙烯基硅橡胶生胶中，每次加入后搅拌均匀，得到硅橡胶混炼胶；
步骤三、将步骤二得到的硅橡胶混炼胶室温捏合0.5-1h，之后升温到140-160℃，抽真空至真空度为0.05-0.08kPa，降温至70-90℃，出胶，得到混炼硅橡胶；
步骤四、将0.2-0.6质量份乙烯基三甲氧基硅烷、20-30质量份十溴二苯乙烷、1-2质量份氧化铈分若干次加入到步骤三得到的混炼硅橡胶中，每次加入后搅拌均匀，升温到110-130℃，抽真空至真空度为0.05-0.08kPa，出胶，冷却至室温得到所述耐高温阻燃硅橡胶。
步骤二中，所述若干次为3-6次。
步骤四中，所述若干次为3-6次。
本发明的有益效果：
1、卤系阻燃硅橡胶不耐高温，本发明在此基础上增加了氧化铈作为耐高温添加剂，可以有效提高此款硅胶的温度使用范围，且有良好的阻燃性能。
2、本发明制备的硅橡胶经过实际检测具有良好的阻燃性能，同时具有较好的耐高温特性、硬度、强度和加工性能，完全能够满足耐高温阻燃电缆的使用要求。
具体实施方式
下面结合实施例对本发明做更进一步的解释。下列实施例仅用于说明本发明，但并不用来限定本发明的实施范围。
一种耐高温阻燃硅橡胶，按质量份计组成为：
Figure BDA0000390920280000021
Figure BDA0000390920280000031
所述甲基乙烯基硅橡胶生胶粘均分子量为60-80万，乙烯基摩尔含量为0.05%-0.15%，以下实施例采用的是江苏天辰硅材料有限公司生产的110-2生胶。所述气相白炭黑比表面积200-300m2/g；所述羟基硅油羟基质量百分比为4-8%，粘度为25-50mPa.s，以下实施例采用的是道康宁PMX-0930；以下实施例采用的硬脂酸是硬脂酸1801。
上述耐高温阻燃硅橡胶的制备方法，包括如下步骤：
步骤一、将100质量份甲基乙烯基硅橡胶生胶加入到捏合机中搅拌2-4分钟；
步骤二、将30-50质量份气相白炭黑、3-6质量份二甲基二甲氧基硅烷、3-6质量份羟基硅油和0.2-0.4质量份硬脂酸分3-6次加入到步骤一得到的甲基乙烯基硅橡胶生胶中，每次加入后搅拌均匀，得到硅橡胶混炼胶；
步骤三、将步骤二得到的硅橡胶混炼胶室温捏合0.5-1h，之后升温到140-160℃，抽真空至真空度为0.05-0.08kPa，降温至70-90℃，出胶，得到混炼硅橡胶；
步骤四、将0.2-0.6质量份乙烯基三甲氧基硅烷、20-30质量份十溴二苯乙烷、1-2质量份氧化铈分3-6次加入到步骤三得到的混炼硅橡胶中，每次加入后搅拌均匀，升温到110-130℃，抽真空至真空度为0.05-0.08kPa，出胶，冷却至室温得到所述耐高温阻燃硅橡胶。
本发明制备的低永久变形耐油硅橡胶在使用过程中可再加入硫化剂硫化，在170摄氏度下硫化5分钟，200摄氏度二次硫化4小时。
实施例1
步骤一、将100质量份甲基乙烯基硅橡胶生胶加入到捏合机中搅拌3分钟；
步骤二、将35质量份气相白炭黑、3质量份二甲基二甲氧基硅烷、3质量份羟基硅油和0.3质量份硬脂酸分4次加入到步骤一得到的甲基乙烯基硅橡胶生胶中，每次加入后充分搅拌，得到硅橡胶混炼胶；
步骤三、将步骤二得到的硅橡胶混炼胶室温捏合0.5h，之后升温到150℃，抽真空至真空度为0.06kPa，通冷却水降温80℃，出胶，得到混炼硅橡胶；
步骤四、将0.4质量份乙烯基三甲氧基硅烷、28质量份十溴二苯乙烷和1质量份氧化铈分4次加入步骤三得到的混炼硅橡胶中，升温到120℃，抽真空至真空度0.06kPa，出胶，冷却至室温得到所述耐高温阻燃硅橡胶。
将本实施例制备得到的耐高温阻燃硅橡胶，在170摄氏度下硫化5分钟后，测试得到结果如下：
Figure BDA0000390920280000041
实施例2
步骤一、将100质量份甲基乙烯基硅橡胶生胶加入到捏合机中搅拌3分钟；
步骤二、将40质量份气相白炭黑、4质量份二甲基二甲氧基硅烷、4质量份羟基硅油和0.4质量份硬脂酸分4次加入到步骤一得到的甲基乙烯基硅橡胶生胶中，每次加入后充分搅拌，得到硅橡胶混炼胶；
步骤三、将步骤二得到的硅橡胶混炼胶室温捏合1h，之后升温到150℃，抽真空至真空度为0.07kPa，通冷却水降温80℃，出胶，得到混炼硅橡胶；
步骤四、将0.4质量份乙烯基三甲氧基硅烷、25质量份十溴二苯乙烷和1质量氧化铈分4次加入到步骤三得到的混炼硅橡胶中，升温到120℃，抽真空至真空度0.07kPa，出胶，冷却至室温得到所述耐高温阻燃硅橡胶。
将本实施例制备得到的耐高温阻燃硅橡胶，在170摄氏度下硫化5分钟后，测试得到结果如下：
Figure BDA0000390920280000042
实施例3
步骤一、将100质量份甲基乙烯基硅橡胶生胶加入到捏合机中搅拌2分钟；
步骤二、将30质量份气相白炭黑、3质量份二甲基二甲氧基硅烷、3质量份羟基硅油和0.2质量份硬脂酸分3次加入到步骤一得到的甲基乙烯基硅橡胶生胶中，每次加入后充分搅拌，得到硅橡胶混炼胶；
步骤三、将步骤二得到的硅橡胶混炼胶室温捏合0.5h，之后升温到140℃，抽真空至真空度为0.05kPa，通冷却水降温70℃，出胶，得到混炼硅橡胶；
步骤四、将0.2质量份乙烯基三甲氧基硅烷、20质量份十溴二苯乙烷和1质量份氧化铈分3次加入步骤三得到的混炼硅橡胶中，升温到110℃，抽真空至真空度0.05kPa，出胶，冷却至室温得到所述耐高温阻燃硅橡胶。
将本实施例制备得到的耐高温阻燃硅橡胶，在170摄氏度下硫化5分钟后，测试得到结果如下：
Figure BDA0000390920280000051
实施例4
步骤一、将100质量份甲基乙烯基硅橡胶生胶加入到捏合机中搅拌4分钟；
步骤二、将50质量份气相白炭黑、6质量份二甲基二甲氧基硅烷、6质量份羟基硅油和0.4质量份硬脂酸分6次加入到步骤一得到的甲基乙烯基硅橡胶生胶中，每次加入后充分搅拌，得到硅橡胶混炼胶；
步骤三、将步骤二得到的硅橡胶混炼胶室温捏合1h，之后升温到160℃，抽真空至真空度为0.08kPa，通冷却水降温90℃，出胶，得到混炼硅橡胶；
步骤四、将0.6质量份乙烯基三甲氧基硅烷、30质量份十溴二苯乙烷和2质量份氧化铈分6次加入步骤三得到的混炼硅橡胶中，升温到130℃，抽真空至真空度0.08kPa，出胶，冷却至室温得到所述耐高温阻燃硅橡胶。
将本实施例制备得到的耐高温阻燃硅橡胶，在170摄氏度下硫化5分钟后，测试得到结果如下：
Figure BDA0000390920280000052

Claims (6)

1.一种耐高温阻燃硅橡胶，其特征在于，按质量份计组成为：
其中，所述甲基乙烯基硅橡胶生胶粘均分子量为60-80万，乙烯基摩尔含量为0.05%-0.15%。
2.根据权利要求1所述的耐高温阻燃硅橡胶，其特征在于，所述气相白炭黑比表面积200-300m2/g。
3.根据权利要求1所述的耐高温阻燃硅橡胶，其特征在于，所述羟基硅油羟基质量百分比为4-8%，粘度为25-50mPa.s。
4.权利要求1或2或3所述的耐高温阻燃硅橡胶的制备方法，其特征在于，包括如下步骤：
步骤一、将100质量份甲基乙烯基硅橡胶生胶加入到捏合机中搅拌2-4分钟；
步骤二、将30-50质量份气相白炭黑、3-6质量份二甲基二甲氧基硅烷、3-6质量份羟基硅油和0.2-0.4质量份硬脂酸分若干次加入到步骤一得到的甲基乙烯基硅橡胶生胶中，每次加入后搅拌均匀，得到硅橡胶混炼胶；
步骤三、将步骤二得到的硅橡胶混炼胶室温捏合0.5-1h，之后升温到140-160℃，抽真空至真空度为0.05-0.08kPa，降温至70-90℃，出胶，得到混炼硅橡胶；
步骤四、将0.2-0.6质量份乙烯基三甲氧基硅烷、20-30质量份十溴二苯乙烷、1-2质量份氧化铈分若干次加入到步骤三得到的混炼硅橡胶中，每次加入后搅拌均匀，升温到110-130℃，抽真空至真空度为0.05-0.08kPa，出胶，冷却至室温得到所述耐高温阻燃硅橡胶。
5.根据权利要求4所述的低永久变形耐油硅橡胶的制备方法，其特征在于，步骤二中，所述若干次为3-6次。
6.根据权利要求4所述的低永久变形耐油硅橡胶的制备方法，其特征在于，步骤四中，所述若干次为3-6次。
CN201310461092.9A 2013-09-30 2013-09-30 一种耐高温阻燃硅橡胶及其制备方法 Pending CN103483829A (zh)