CN103478940A - Production method of water-proof, oil-resistant and flame-retardant children's clothing fabric - Google Patents
Production method of water-proof, oil-resistant and flame-retardant children's clothing fabric Download PDFInfo
- Publication number
- CN103478940A CN103478940A CN201310192669.0A CN201310192669A CN103478940A CN 103478940 A CN103478940 A CN 103478940A CN 201310192669 A CN201310192669 A CN 201310192669A CN 103478940 A CN103478940 A CN 103478940A
- Authority
- CN
- China
- Prior art keywords
- children
- fabric
- waterproof
- retardant
- synthetic fibre
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a production method of a water-proof, oil-resistant and flame-retardant children's clothing fabric. According to the production method, terylene is used as a base texture, and polysulfonamide is used as a flocked yarn, wherein the materials are woven by using a double tricot machine and are slit to form a flocked fabric. The polysulfonamide is dyed by using a disperse dye carrier method; finally, the polysulfonamide warp knitted fabric is subjected to padding-baking finishing by using an HS1100 fluorine-containing water-proof, oil-resistant and soil resistant finishing agent. The children's clothing fabric produced by the method has lasting and stable flame retardance and superior water-repellent and oil-repellent effects; the water-repellent grade can still reach grade 10 and the oil-repellent grade can reach grade 7-8 after standard washing is performed for five times.
Description
Technical field
The present invention relates to a kind of fabric plus material producing method, particularly relate to a kind of production method of being weaved the children's garment fabric with the dirty fire resistance of waterproof and oilproof that then warp arranges later by double rib warp loom.
Background technology
Children's natural disposition is active, the dirts such as common addle and oil stain on clothes.Children curiosity is strong, constantly is familiar with and accepts extraneous fangle, and observe things is main mainly with perception simultaneously, and the sense organ that gay colours can stimulate the people.Therefore, children generally can like bright color.In addition, the head of a family likes child neatly clean, pay attention to hygiene, but bright brisk color is stained with the dirts such as addle and oil stain, if cleaning is unclean, will directly affect attractive in appearance.Although children curiosity is strong, like constantly being familiar with and accepting extraneous fangle, when observing, lack protection consciousness.According to US Consumer Product Safety Commission (CPSC) statistics, the U.S. recalls 22 batches of garments for children in 2011 altogether, wherein because fire resistance is underproof just 5 batches, account for total batch 22.7%.Therefore, be necessary the production technology of current children's garment fabric is improved or optimized in conjunction with the deficiency of existing fabric according to people's demand.
Summary of the invention
The production method that the purpose of this invention is to provide the dirty fire-retardant children's garment fabric of a kind of waterproof and oilproof, the fabric of being produced by the method, aspect the dirty fire resistance of waterproof and oilproof, having larger lifting and improvement, has met the requirement of people to the children's garment fabric.
The technical solution adopted in the present invention is such: the dirty fire-retardant children's garment fabric plus material producing method of a kind of waterproof and oilproof comprises the comprehensive Design of following three aspects:
1, raw material design: raw material adopts fragrant sulfone synthetic fibre and terylene.Virtue sulfone synthetic fibre is fastened the high-temperature fibre of sea market textile scientific research institute and Shanghai Synthetic Fibre Inst independent research and development, belong to p-aramid fiber series, formal name used at school PPSU terephthalamide fiber, owing to there being strong electrophilic sulfuryl group on macromolecular main chain, by two key conjugations of phenyl ring, make it than aramid fiber 1313, there is more excellent molecular structure performance.
Virtue sulfone synthetic fibre has excellent heat resistance and heat endurance, and the strength retention ratio when 250 ℃ and 300 ℃ is respectively 70% and 50%, even under the high temperature of 350 ℃, still keeps 38% intensity; The strength retention ratio of processing in the hot-air of 250 ℃ and 200 ℃ after 100h is respectively 80% and 90%; Polysulphonamide fiber is placed in to 300 ℃ of hot-airs, and its shrinkage factor is only 0.5%-1.0% and 2.0%.Fibre strength 3.0-4.5g/d, elongation at break 20%-25%, initial modulus 760kg/mm
2, proportion 1.416g/cm
3.
The fire resistance of virtue sulfone synthetic fibre is outstanding, and limited oxygen index LOI value is up to 33.Because the high protective value of polysulphonamide fiber comes from the molecular structure of self, rather than obtain by chemical treatment, therefore, the product solar heat protection fire protecting performance lasting stability that adopts polysulphonamide fiber to make.
2, tissue design: consider that the higher and fabric wearing process medium staple yarn of fragrant sulfone synthetic fibre cost is exposed outside, therefore organize the employing terylene, the suede yarn adopts fragrant sulfone synthetic fibre.
3, rear arrangement: fabric is carried out to the dirty arrangement of waterproof and oilproof, promote the added value of fabric.
By adopting the previous designs scheme, the invention has the beneficial effects as follows: the fabric of producing has the dirty performance of good waterproof and oilproof, fire resistance lasting stability.
The accompanying drawing explanation
Accompanying drawing 1 is the gauze pad motion diagram of fabric of the present invention.
Accompanying drawing 2 is the dyeing flow curve figure of fabric of the present invention.
The specific embodiment
The present invention, by raw material, fabric construction and the comprehensive Design that arranges afterwards 3 aspects, has proposed the production method of the dirty fire-retardant children's garment fabric of a kind of waterproof and oilproof.Its technological process is: raw material---through braiding, make---cut open width---dyeing---water and oil repellant is dirty to be arranged---dry---bristle---scald light---cropping---typing is hung---check---clot---packing---warehouse-in, wherein through braiding make, dyeing and the dirty arrangement of water and oil repellant be critical process.
(1) through braiding, make:
Machine: the RD6DPLM double rib warp loom, plane No.: E22, the machine fabric width: 130 inches, machine speed: 600r/min, trick plate spacing 10mm.
Raw material: A:150D terylene
B:100D virtue sulfone synthetic fibre
Warping radical: GB1:6*445A
GB2：6*445A
GB3：6*445B
GB4：6*445B
GB5：6*445A
GB6：6*445A
Organize, pass: GB1:0-1-1-1/3-2-2-2/0-1-1-1/3-2-2-2//completely wear
GB2:2-1-1-1/0-1-1-1/2-1-1-1/0-1-1-1//completely wear
GB3:0-1-0-0/0-0-0-1/0-0-0-1/0-1-0-0//completely wear
GB4:0-0-0-1/0-1-0-0/0-1-0-0/0-0-0-1//completely wear
GB5:1-1-2-1/1-1-0-1/1-1-2-1/1-1-0-1//completely wear
GB6:1-1-0-1/2-2-3-2/1-1-0-1/2-2-3-2//completely wear
Warp run-in: GB1:2980mm/rack
GB2：1920mm/rack
GB3：10080mm/rack
GB4：10080mm/rack
GB5：1920mm/rack
GB6：2980mm/rack
The fabric technological parameter: the finished product horizontal stroke is close: 8.7wpc, finished product is vertical close: 13cpc, grammes per square metre: 450g/m
2.
(2) dyeing: adopt the disperse dyes support methods to be dyeed.Technological process is: pre-treatment, and---------soap---washing---dries in washing in dyeing.The dyeing prescription is:
The red R-5BL of disperse dyes (omf): 3%
Carrier Levegalc (ml/L): 40
High temperature levelling agent (%): 1
Value in Dyeing Process: 5
Temperature (℃): 110
Time (min): 40
Bath raio: 1: 20
(3) water and oil repellant is dirty arranges: adopt the fluorine-containing waterproof and oilproof anti-soil agent of HS1100, fragrant sulfone synthetic fibre WARP-KNITTING is rolled and cures arrangement.Technological process: deionized water immersion-natural air drying---soak one and roll (pick-up rate 70%)-dry (100 ℃ of * 2min)-bake.The process conditions of finishing agent to fragrant sulfone synthetic fibre fabric water and oil repellent finish: finishing agent consumption 40g/l, 190 ℃ of baking temperatures, bake time 5min.
Claims (4)
1. the dirty fire-retardant children's garment fabric plus material producing method of a waterproof and oilproof, comprise fragrant sulfone synthetic fibre and terylene are cutd open to width formation lint by making through braiding, dyed and postfinishing process step again, it is characterized in that: through braiding, organize with making and adopt terylene, the suede yarn adopts fragrant sulfone synthetic fibre, after fabric slitting, fragrant sulfone synthetic fibre is dyeed, finally with the waterproof and oilproof anti-soil agent, fuzz fabric is arranged.
2. the production method of the dirty fire-retardant children's garment fabric of waterproof and oilproof according to claim 1, it is characterized in that fragrant sulfone synthetic fibre that the suede yarn adopts fastens the high-temperature fibre of sea market textile scientific research institute and Shanghai Synthetic Fibre Inst independent research and development, belong to p-aramid fiber series, formal name used at school PPSU terephthalamide fiber, owing to there being strong electrophilic sulfuryl group on macromolecular main chain, by two key conjugations of phenyl ring, make it than aramid fiber 1313, there is more excellent molecular structure performance.Virtue sulfone synthetic fibre has excellent heat resistance and heat endurance, and fire resistance is outstanding, and limited oxygen index LOI value is up to 33.Because the high protective value of polysulphonamide fiber comes from the molecular structure of self, rather than obtain by chemical treatment, therefore, the product solar heat protection fire protecting performance lasting stability that adopts polysulphonamide fiber to make.
3. the production method of the dirty fire-retardant children's garment fabric of waterproof and oilproof according to claim 1, is characterized in that adopting the disperse dyes support methods to be dyeed.
4. the production method of the dirty fire-retardant children's garment fabric of waterproof and oilproof according to claim 1, is characterized in that with the fluorine-containing waterproof and oilproof anti-soil agent of HS1100, fragrant sulfone synthetic fibre WARP-KNITTING being rolled and baking arrangement.