CN103450752A - 防霉调湿涂料及其制备方法 - Google Patents

防霉调湿涂料及其制备方法 Download PDF

Info

Publication number
CN103450752A
CN103450752A CN2013103683195A CN201310368319A CN103450752A CN 103450752 A CN103450752 A CN 103450752A CN 2013103683195 A CN2013103683195 A CN 2013103683195A CN 201310368319 A CN201310368319 A CN 201310368319A CN 103450752 A CN103450752 A CN 103450752A
Authority
CN
China
Prior art keywords
parts
powder
modified zeolite
preparation
mould
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
CN2013103683195A
Other languages
English (en)
Inventor
庄亚东
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
WUJIANG WUHUA HARDWARE PRODUCTS CO Ltd
Original Assignee
WUJIANG WUHUA HARDWARE PRODUCTS CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by WUJIANG WUHUA HARDWARE PRODUCTS CO Ltd filed Critical WUJIANG WUHUA HARDWARE PRODUCTS CO Ltd
Priority to CN2013103683195A priority Critical patent/CN103450752A/zh
Publication of CN103450752A publication Critical patent/CN103450752A/zh
Withdrawn legal-status Critical Current

Abstract

防霉调湿涂料及其制备方法，防霉调湿涂料包括按照质量份数计的如下原料：苯乙烯-丙烯酸酯乳液100-130份、改性沸石粉30-40份、海泡石粉10-20份、竹炭粉15-23份、纳米二氧化钛1-5份、滑石粉5-10份、丙二醇1-1.5份、分散剂Orotan11241.5-2份、十二碳醇酯2-5份、羟乙基纤维素1-1.8份、水150-160份。本发明具有良好的防霉性和调湿功能，其对金黄色葡萄球菌的抑菌率可达99.95%，对大肠杆菌的抑菌率可达99.98%，吸湿实验效果良好，对甲醛的净化率可达95%。

Description

防霉调湿涂料及其制备方法
技术领域
本发明属于涂料领域，具体涉及一种防霉调湿涂料及其制备方法。
背景技术
随着涂料行业的迅猛发展，涂料的功能也不断完善，室内涂料对涂料的安全性要求较高。目前环保型涂料备受人们青睐，越来越多的涂料具有有益人体健康的性能。现已有防霉、净化空气、调湿涂料的报道，其主要以吸附性矿物质为调湿材料，再在组分中配以抗菌剂防霉剂，以达到所述效果。但因其采用的吸湿材料未经改性，其调湿能力仍有待提高。
综上所述，如何克服现有技术的不足已成为现有涂料领域亟待解决的问题。
发明内容
本发明的目的是克服现有技术的不足而提出一种防霉调湿涂料及其制备方法，本发明以改性沸石取代防霉剂和吸湿材料，可有效调节室内湿度，净化室内空气。
本发明的技术方案如下：
防霉调湿涂料，包括按照质量份数计的如下原料：苯乙烯-丙烯酸酯乳液100-130份、改性沸石粉30-40份、海泡石粉10-20份、竹炭粉15-23份、纳米二氧化钛1-5份、滑石粉5-10份、丙二醇1-1.5份、分散剂Orotan1124 1.5-2份、十二碳醇酯2-5份、羟乙基纤维素1-1.8份、水150-160份，其中，改性沸石为稀土改性沸石，制备方法为：将氯化亚铈溶于水中，搅拌均匀后，调节pH为11，将粉碎后的沸石加入其中，浸渍15h后，过滤水洗至中性，干燥于500℃下焙烧4h，即得稀土改性沸石，改性时氯化镧沸石的质量比为1:20。
防霉调湿涂料的制备方法：按照质量配比，将羟乙基纤维素加入水中搅拌均匀，后依次加入丙二醇、分散剂Orotan1124、十二碳醇酯，搅拌均匀后加入改性沸石粉、海泡石粉、竹炭粉、纳米二氧化钛、滑石粉混合使之分散均匀，即可得本发明所述成品。
有益效果：本发明具有良好的防霉性和调湿功能，其对金黄色葡萄球菌的的抑菌率可达99.95%，对大肠杆菌的抑菌率可达99.98%，吸湿实验效果良好，25℃下相对湿度为80%时，吸湿量可达15%；吸湿饱和后，25℃下相对湿度为40%时，放湿量可达10%，其对甲醛的净化率可达95%。
具体实施方式
本发明所述改性沸石粉、海泡石粉、竹炭粉的粒径为200目，所述苯乙烯-丙烯酸酯乳液购自广州沃顿化工有限公司，固含量为49%-51%。
下面结合具体实施方式对本发明作进一步详细说明。
实施例1
防霉调湿涂料，包括按照质量份数计的如下原料：苯乙烯-丙烯酸酯乳液100份、改性沸石粉30份、海泡石粉10份、竹炭粉15份、纳米二氧化钛1份、滑石粉5份、丙二醇1份、分散剂Orotan1124 1.5份、十二碳醇酯2份、羟乙基纤维素1份、水150份。
改性沸石为稀土改性沸石，其制备方法为：将氯化亚铈溶于水中，搅拌均匀后，调节pH为11，将粉碎后的沸石加入其中，浸渍15h后，过滤水洗至中性，干燥于500℃下焙烧4h，即得稀土改性沸石，改性时氯化镧沸石的质量比为1:20。
本发明制备方法：按照质量配比，将羟乙基纤维素加入水中搅拌均匀，后依次加入丙二醇、分散剂Orotan1124、十二碳醇酯，搅拌均匀后加入改性沸石粉、海泡石粉、竹炭粉、纳米二氧化钛、滑石粉混合使之分散均匀，加入苯乙烯-丙烯酸酯乳液，搅匀，即可得本发明所述成品。
实施例2
防霉调湿涂料，包括按照质量份数计的如下原料：苯乙烯-丙烯酸酯乳液130份、改性沸石粉40份、海泡石粉20份、竹炭粉23份、纳米二氧化钛5份、滑石粉10份、丙二醇1.5份、分散剂Orotan1124 2份、十二碳醇酯5份、羟乙基纤维素1.8份、水160份。
改性沸石为稀土改性沸石，其制备方法同实施例1。
本发明制备方法同实施例1，各原料及配比如上所述。
实施例3
防霉调湿涂料，包括按照质量份数计的如下原料：苯乙烯-丙烯酸酯乳液125份、改性沸石粉36份、海泡石粉16份、竹炭粉20份、纳米二氧化钛3份、滑石粉8份、丙二醇1.3份、分散剂Orotan1124 1.7份、十二碳醇酯3份、羟乙基纤维素1.5份、水152份。
改性沸石为稀土改性沸石，其制备方法同实施例1。
本发明制备方法同实施例1，各原料及配比如上所述。
 
将本发明所得成品性能测试：
1、吸湿性：将本发明成品于40℃下真空干燥5h后，进行吸湿实验，温度25℃，相对湿度80%，吸湿量可达15%，吸湿饱和后，25℃，相对湿度40%下放湿，放湿量可达10%。
2、空气净化效果：将本发明涂层置于密封舱内，舱内甲醛浓度5mg/m3，24h后测定密封舱内甲醛浓度，计算本发明成品对舱内甲醛的净化率可达95%。
3、防霉抗菌性能：用贴膜方法检测本发明成品防霉抗菌性能，其对金黄色葡萄球菌的的抑菌率可达99.95%，对大肠杆菌的抑菌率可达99.98%。
上述实施例仅是对本发明产品的说明，并非对本发明做出任何形式上的限制，在不脱离本发明的技术方案范围之内，任何利用上述揭示的技术内容作出简单变换的等同方案，均属本发明的保护范围。

Claims (2)

1.防霉调湿涂料，其特征在于，包括按照质量份数计的如下原料：苯乙烯-丙烯酸酯乳液100-130份、改性沸石粉30-40份、海泡石粉10-20份、竹炭粉15-23份、纳米二氧化钛1-5份、滑石粉5-10份、丙二醇1-1.5份、分散剂Orotan1124 1.5-2份、十二碳醇酯2-5份、羟乙基纤维素1-1.8份、水150-160份，其中，改性沸石为稀土改性沸石，制备方法为：将氯化亚铈溶于水中，搅拌均匀后，调节pH为11，将粉碎后的沸石加入其中，浸渍15h后，过滤水洗至中性，干燥于500℃下焙烧4h，即得稀土改性沸石，改性时氯化镧沸石的质量比为1:20。
2.如权利要求1所述的防霉调湿涂料的制备方法，其特征在于，由以下步骤制备而得：按照质量配比，将羟乙基纤维素加入水中搅拌均匀，后依次加入丙二醇、分散剂Orotan1124、十二碳醇酯，搅拌均匀后加入改性沸石粉、海泡石粉、竹炭粉、纳米二氧化钛、滑石粉混合使之分散均匀，即可得本发明所述成品。
CN2013103683195A 2013-08-22 2013-08-22 防霉调湿涂料及其制备方法 Withdrawn CN103450752A (zh)