CN103450751A - Antibacterial wet-wiping-resistant interior wall coating - Google Patents
Antibacterial wet-wiping-resistant interior wall coating Download PDFInfo
- Publication number
- CN103450751A CN103450751A CN2013103676914A CN201310367691A CN103450751A CN 103450751 A CN103450751 A CN 103450751A CN 2013103676914 A CN2013103676914 A CN 2013103676914A CN 201310367691 A CN201310367691 A CN 201310367691A CN 103450751 A CN103450751 A CN 103450751A
- Authority
- CN
- China
- Prior art keywords
- parts
- interior wall
- wiping
- proof
- wall coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses an antibacterial wet-wiping-resistant interior wall coating. The coating comprises the following raw materials in parts by mass: 40-50 parts of styrene-acrylic emulsion, 0.5-1 part of acrylic emulsion, 12-18 parts of silica powder, 7-12 parts of titanium dioxide, 0.1-0.2 part of ethyl vanillin, 1-2 parts of Texanol ester alcohol, 0.2-0.5 parts of dispersant, 5-6 parts of polyethylene glycol 200, 0.1-0.2 part of antifoaming agent and 80-90 parts of deionized water, wherein the dispersant is one or two of HPMA (Hydroxypropyl Methacrylate) and zinc stearate, and the antifoaming agent is polyoxyethylene octylphenol ether. The interior wall coating disclosed by the invention is good in bacterial resistance, wet-wiping resistance and adhesion, and can be widely applied to various indoor coatings.
Description
Technical field
The invention belongs to paint field, be specifically related to a kind of inner-wall antibacterial moisture-proof obliterating material.
Background technology
Inner wall decoration is a very important link of building decoration, has part coating inferior to be used to the application interior wall, and organic volatile wherein has very important detrimentally affect to HUMAN HEALTH.To environment and human body, friendly and well behaved health type multi-functional coating is the trend of following paint development.Existing interior wall coating is of a great variety, Various Functions, but its over-all properties still can not meet user demand, and its performance tends to attend to one thing and lose sight of another.
In sum, how to overcome the deficiencies in the prior art and become existing paint field problem demanding prompt solution.
Summary of the invention
The objective of the invention is to overcome the deficiencies in the prior art and propose a kind of inner-wall antibacterial moisture-proof obliterating material, the present invention has good antimicrobial property and wet scrub resistance, facilitates daily cleaning.
Technical scheme of the present invention is as follows:
Inner-wall antibacterial moisture-proof obliterating material comprises the following raw material according to the mass fraction meter: benzene emulsion 40-50 part, ACRYLIC EMULSION 0.5-1 part, silicon powder 12-18 part, titanium dioxide 7-12 part, vanillal 0.1-0.2 part, Texanol alcohol ester 1-2 part, dispersion agent 0.2-0.5 part, Macrogol 200 5-6 part, defoamer 0.1-0.2 part, deionized water 80-90 part.
Described dispersion agent is one or both in HPMA and Zinic stearas.
Described defoamer is polyoxyethylene octylphenol ether.
Preparation method of the present invention: according to the quality proportioning, add the deionized water of 80% formula ratio in paint mixing tank, stir and add ACRYLIC EMULSION, stir, add vanillal, Texanol alcohol ester, dispersion agent, defoamer, stir, add successively silicon powder, titanium dioxide, add Macrogol 200 after stirring, stir evenly, after disperseing, grinding, add benzene emulsion, stir 30min, add the residue deionized water and stirring even, obtain.
Beneficial effect: the present invention has good antimicrobial property and wet-rub resistance energy, and sticking power is good, to colibacillary antibiotic rate, can reach more than 99.85%, to the antibiotic rate of streptococcus aureus, can reach more than 99.92%, and moisture-proof is wiped number of times and can be reached 3100 times.
Embodiment
Benzene emulsion solid content of the present invention is 48 ± 2%.
Below in conjunction with embodiment, the present invention is described in further detail.
Embodiment 1
Inner-wall antibacterial moisture-proof obliterating material comprises the following raw material according to the mass fraction meter: benzene emulsion 40-50 part, 0.5 part of ACRYLIC EMULSION, 12 parts of silicon powders, 7 parts of titanium dioxides, 0.1 part of vanillal, 1 part of Texanol alcohol ester, 0.2 part of HPMA, 5 parts of Macrogol 200s, 0.1 part of polyoxyethylene octylphenol ether, 80 parts of deionized waters.
Preparation method of the present invention: according to the quality proportioning, add the deionized water of 80% formula ratio in paint mixing tank, stir and add ACRYLIC EMULSION, stir, add vanillal, Texanol alcohol ester, HPMA, polyoxyethylene octylphenol ether, stir, add successively silicon powder, titanium dioxide, add Macrogol 200 after stirring, stir evenly, after disperseing, grinding, add benzene emulsion, stir 30min, add the residue deionized water and stirring even, obtain.
Embodiment 2
Inner-wall antibacterial moisture-proof obliterating material comprises the following raw material according to the mass fraction meter: benzene emulsion 40-50 part, 1 part of ACRYLIC EMULSION, 18 parts of silicon powders, 12 parts of titanium dioxides, 0.2 part of vanillal, 2 parts of Texanol alcohol esters, 0.5 part of Zinic stearas, 6 parts of Macrogol 200s, 0.2 part of polyoxyethylene octylphenol ether, 90 parts of deionized waters.
Preparation method of the present invention is with embodiment 1, and each component raw material as mentioned above.
Embodiment 3
Inner-wall antibacterial moisture-proof obliterating material comprises the following raw material according to the mass fraction meter: 45 parts of benzene emulsions, 0.6 part of ACRYLIC EMULSION, 16 parts of silicon powders, 10 parts of titanium dioxides, 0.15 part of vanillal, 1.6 parts of Texanol alcohol esters, 0.3 part of HPMA, 0.1 part of Zinic stearas, 5.4 parts of Macrogol 200s, 0.16 part of polyoxyethylene octylphenol ether, 85 parts of deionized waters.
Preparation method of the present invention is with embodiment 1, and each component raw material as mentioned above.
By gained end properties test of the present invention, it reaches more than 99.85% colibacillary antibiotic rate, to the antibiotic rate of streptococcus aureus, can reach more than 99.92%, and moisture-proof is wiped number of times and can be reached 3100 times, sticking power is 1 grade, and VOC and heavy metal content detect and all reach national standard.
Above-described embodiment is only the explanation to product of the present invention; not the present invention is made to any pro forma restriction; within not breaking away from technical scheme scope of the present invention, any technology contents that utilizes above-mentioned announcement is made the equivalent of simple transformation, all belongs to protection scope of the present invention.
Claims (3)
1. inner-wall antibacterial moisture-proof obliterating material, it is characterized in that, comprise the following raw material according to the mass fraction meter: benzene emulsion 40-50 part, ACRYLIC EMULSION 0.5-1 part, silicon powder 12-18 part, titanium dioxide 7-12 part, vanillal 0.1-0.2 part, Texanol alcohol ester 1-2 part, dispersion agent 0.2-0.5 part, Macrogol 200 5-6 part, defoamer 0.1-0.2 part, deionized water 80-90 part.
2. inner-wall antibacterial moisture-proof obliterating material according to claim 1, is characterized in that, described dispersion agent is one or both in HPMA and Zinic stearas.
3. inner-wall antibacterial moisture-proof obliterating material according to claim 1, is characterized in that, described defoamer is polyoxyethylene octylphenol ether.