CN103450723A - 一种耐老化耐腐蚀超净工作台涂层 - Google Patents
一种耐老化耐腐蚀超净工作台涂层 Download PDFInfo
- Publication number
- CN103450723A CN103450723A CN2013103667012A CN201310366701A CN103450723A CN 103450723 A CN103450723 A CN 103450723A CN 2013103667012 A CN2013103667012 A CN 2013103667012A CN 201310366701 A CN201310366701 A CN 201310366701A CN 103450723 A CN103450723 A CN 103450723A
- Authority
- CN
- China
- Prior art keywords
- parts
- resistant
- ageing
- coating
- bechtop
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明涉及一种耐老化耐腐蚀超净工作台涂层,涂层由以下成分按照重量比组成:对苯二甲酯环氧树脂31~34份、丙烯酸异辛酯13~16份、氟硅酸钾为7~12份、碳酸二辛酯为9~12份、三硫代碳酸酯4~7份、硼镁石粉13~14份、环氧硬脂酸辛酯6~11份。制备得到的超净工作台涂层可应用于超净工作台中,具有耐老化耐腐蚀的优势。
Description
技术领域
本发明涉及一种超净工作台涂层,特别是涉及一种耐老化耐腐蚀超净工作台涂层。
背景技术
净化车间中经常需要用到超净工作台,超净工作台也被称作生物安全柜,可以保证空间内的洁净度。超净工作台在应用过程中,为了保证空间的洁净度,需要对超净工作台进行紫外灭菌,同时在超净工作台上进行操作时,如果涉及到有机试剂或酸碱试剂时,又对超净工作台的抗腐蚀性提出了要求,因此需要开发一种可应用在超净工作台表面的涂层,保证超净工作台的正常运转。
发明内容
要解决的技术问题:净化车间中超净工作台耐腐蚀和耐老化性能差的问题。
技术方案:本发明公开了一种耐老化耐腐蚀超净工作台涂层,其特征在于涂层由以下成分按照重量比组成:对苯二甲酯环氧树脂31~34份、丙烯酸异辛酯13~16份、氟硅酸钾为7~12份、碳酸二辛酯为9~12份、三硫代碳酸酯4~7份、硼镁石粉13~14份、环氧硬脂酸辛酯6~11份。制备上述涂层方法:取对苯二甲酯环氧树脂31~34kg、丙烯酸异辛酯13~16kg、氟硅酸钾为7~12kg、碳酸二辛酯为9~12kg、三硫代碳酸酯4~7kg、硼镁石粉13~14kg、环氧硬脂酸辛酯6~11kg。将搅拌罐温度调至90℃,压力为常压,将上述各成分按重量倒入搅拌罐中,使用搅拌桨搅拌2h,转速为160rpm。搅拌结束后,待冷却至常温得涂层液。
有益效果:通过本发明配方和方法制备得到的涂层液在应用到超净工作台上后,具有非常良好的耐紫外线老化和耐腐蚀的效果。在紫外照射500h后依然保持了原有状态和性能,未有老化现象产生。另外可耐30wt%氢氧化钠溶液30天不发生变化,可耐50wt%醋酸溶液20天不发生变化。
具体实施方式
实施例1
取对苯二甲酯环氧树脂34kg、丙烯酸异辛酯16kg、氟硅酸钾为7kg、碳酸二辛酯为9kg、三硫代碳酸酯4kg、硼镁石粉14kg、环氧硬脂酸辛酯6kg。将搅拌罐温度调至90℃,压力为常压,将上述各成分按重量倒入搅拌罐中,使用搅拌桨搅拌2h,转速为160rpm。搅拌结束后,待冷却至常温得涂层液。
实施例2
取对苯二甲酯环氧树脂31kg、丙烯酸异辛酯13kg、氟硅酸钾为9kg、碳酸二辛酯为10kg、三硫代碳酸酯7kg、硼镁石粉13kg、环氧硬脂酸辛酯9kg。将搅拌罐温度调至90℃,压力为常压,将上述各成分按重量倒入搅拌罐中,使用搅拌桨搅拌2h,转速为160rpm。搅拌结束后,待冷却至常温得涂层液。
实施例3
取对苯二甲酯环氧树脂32kg、丙烯酸异辛酯15kg、氟硅酸钾为12kg、碳酸二辛酯为12kg、三硫代碳酸酯6kg、硼镁石粉14kg、环氧硬脂酸辛酯11kg。将搅拌罐温度调至90℃,压力为常压,将上述各成分按重量倒入搅拌罐中,使用搅拌桨搅拌2h,转速为160rpm。搅拌结束后,待冷却至常温得涂层液。
耐老化耐腐蚀测试及结果
取制备得到的实施例1、实施例2、实施例3的涂层液喷涂在不锈钢表面,喷涂厚度为1mm,喷涂后将喷有涂层的不锈钢在温度为70℃下烘干,烘干后进行耐老化和耐腐蚀测试。耐老化选用紫外灯进行照射,紫外灯距涂层距离为1m,照射波长为320nm,照射时间为500h。将喷有涂层的不锈钢放入至30%氢氧化钠溶液中放置30天,再另外放入50%醋酸溶液中放置20天。
实验结果表明,三个实施例产品在紫外照射500h后喷有涂层的不锈钢未有发生变化,没有老化现象产生。另外在30wt%氢氧化钠溶液中30天未发生变化,在50wt%醋酸溶液中20天未发生变化。
Claims (5)
1.一种耐老化耐腐蚀超净工作台涂层,其特征在于涂层由以下成分按照重量比组成:对苯二甲酯环氧树脂31~34份、丙烯酸异辛酯13~16份、氟硅酸钾为7~12份、碳酸二辛酯为9~12份、三硫代碳酸酯4~7份、硼镁石粉13~14份、环氧硬脂酸辛酯6~11份。
2.根据权利要求1所述的一种耐老化耐腐蚀超净工作台涂层,其特征在于成分组成中对苯二甲酯环氧树脂为31份。
3.根据权利要求1所述的一种耐老化耐腐蚀超净工作台涂层,其特征在于成分组成中丙烯酸异辛酯为13份。
4.根据权利要求1所述的一种耐老化耐腐蚀超净工作台涂层,其特征在于成分组成中氟硅酸钾为7份。
5.根据权利要求1所述的一种耐老化耐腐蚀超净工作台涂层,其特征在于成分组成中碳酸二辛酯为12份。