CN103449781A - 一种赤泥发泡轻质保温板及其制备方法 - Google Patents

一种赤泥发泡轻质保温板及其制备方法 Download PDF

Info

Publication number
CN103449781A
CN103449781A CN2013103200683A CN201310320068A CN103449781A CN 103449781 A CN103449781 A CN 103449781A CN 2013103200683 A CN2013103200683 A CN 2013103200683A CN 201310320068 A CN201310320068 A CN 201310320068A CN 103449781 A CN103449781 A CN 103449781A
Authority
CN
China
Prior art keywords
parts
red mud
thermal
minute
insulation
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2013103200683A
Other languages
English (en)
Other versions
CN103449781B (zh
Inventor
彭庆付
孟玲琳
王清伟
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ANHUI ZHONGKUNYUAN NEW BUILDING MATERIALS Co Ltd
Original Assignee
ANHUI ZHONGKUNYUAN NEW BUILDING MATERIALS Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ANHUI ZHONGKUNYUAN NEW BUILDING MATERIALS Co Ltd filed Critical ANHUI ZHONGKUNYUAN NEW BUILDING MATERIALS Co Ltd
Priority to CN201310320068.3A priority Critical patent/CN103449781B/zh
Publication of CN103449781A publication Critical patent/CN103449781A/zh
Application granted granted Critical
Publication of CN103449781B publication Critical patent/CN103449781B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种赤泥发泡轻质保温板，它是由下述重量份的原料组成的：普通硅酸盐水泥100-110、赤泥40-50、膨润土10-20、凹凸棒土10-20、硅藻土10-20、硅酸钙10-13、气相白炭黑2-3、白乳胶6-8、异丙醇3-4、甘油2-3、乙撑双硬脂酰胺1-2、聚酰胺蜡微粉3-4、松香2-3、聚乙二醇4002-3、二氯甲烷1-2、丙烯酸甲酯2-3、聚氧丙烯甘油醚2-3、十二烷基苯磺酸钠2-3、氧化聚乙烯蜡2-4、N-(β-氨乙基)-γ-氨丙基三甲氧基硅烷1-2、二甲基硅油0.3-0.4、过氧化钾0.1-0.3、水适量。本发明的保温板具有质轻、隔热保温及防水等特点，适用于建筑外墙保温，是一种应用前景广阔的保温材料；通过本发明的工艺预先得到的浆料增强了各料之间的粘合性和相容性，进一步增强了成型板材的回弹性和压缩强度。

Description

一种赤泥发泡轻质保温板及其制备方法
技术领域
本发明主要涉及一种赤泥发泡轻质保温板，属于建筑材料领域。
背景技术
赤泥发泡轻质保温板是指使用发泡水泥技术制造的保温板，传统的赤泥发泡轻质保温板主料是水泥，加入双氧水、硬钙、粉煤灰和水泥发泡剂融合发泡而成，发泡水泥保温板是目前墙体保温和墙体保温防火隔离带最理想的保温材料，其优点是：导热系数低，保温效果好，不燃烧，防水，与墙体粘结力强，强度高，无毒害放射物质，环保。
发明内容
本发明目的就是提供一种赤泥发泡轻质保温板及其制备方法。
本发明是通过以下技术方案实现的：
一种赤泥发泡轻质保温板，它是由下述重量份的原料组成的：
普通硅酸盐水泥100-110、赤泥40-50、膨润土10-20、凹凸棒土10-20、硅藻土10-20、硅酸钙10-13、气相白炭黑2-3、白乳胶6-8、异丙醇3-4、甘油2-3、乙撑双硬脂酰胺1-2、聚酰胺蜡微粉3-4、松香2-3、聚乙二醇400 2-3、二氯甲烷1-2、丙烯酸甲酯2-3、聚氧丙烯甘油醚2-3、十二烷基苯磺酸钠2-3、氧化聚乙烯蜡2-4、N-(β-氨乙基)-γ-氨丙基三甲氧基硅烷1-2、二甲基硅油0.3-0.4、过氧化钾0.1-0.3、水适量。
一种赤泥发泡轻质保温板的制备方法，包括以下步骤：
（1）将上述聚氧丙烯甘油醚与气相白炭黑混合，充分搅拌，加热至120-150℃，加入丙烯酸甲酯，保温静置2-3小时，降低温度至40-50℃，滴加聚乙二醇400，滴加完毕后，在搅拌条件下依次加入白乳胶、过氧化钾，600-800转/分搅拌10-16分钟，加入N-(β-氨乙基)-γ-氨丙基三甲氧基硅烷，常温搅拌10-15分钟，得浆料；
（2）将上述快普通硅酸盐水泥、赤泥、膨润土、凹凸棒土、硅藻土、硅酸钙混合加入到搅拌机中，搅拌速度为60-80 转/ 分，搅拌时间15-20 分钟，得水泥混料；
（3）将40-50℃的水加入到搅拌机中，湿搅拌2-3分钟，与上述十二烷基苯磺酸钠混合，通过发泡剂发泡，得泡沫料；
（4）将上述得到的泡沫料与水泥混料混合，泡沫料的体积占水泥混料重量的含量为：4-6升/千克；40-50转/分搅拌20-30分钟，得预混料；
（5）将得到的预混料与上述浆料和剩余各原料混合，充分搅拌后送入模具内浇注成形，经脱模、养护、干燥后即得所述赤泥发泡轻质保温板。
本发明的优点是：
本发明的保温板具有质轻、隔热保温及防水等特点，适用于建筑外墙保温，是一种应用前景广阔的保温材料；通过本发明的工艺预先得到的浆料增强了各料之间的粘合性和相容性，进一步增强了成型板材的回弹性和压缩强度。
具体实施方式
实施例1
一种赤泥发泡轻质保温板，它是由下述重量份（公斤）的原料组成的：
普通硅酸盐水泥110、赤泥50、膨润土20、凹凸棒土20、硅藻土20、硅酸钙10-13、气相白炭黑3、白乳胶8、异丙醇4、甘油3、乙撑双硬脂酰胺2、聚酰胺蜡微粉4、松香2、聚乙二醇400 3、二氯甲烷2、丙烯酸甲酯3、聚氧丙烯甘油醚3、十二烷基苯磺酸钠3、氧化聚乙烯蜡2、N-(β-氨乙基)-γ-氨丙基三甲氧基硅烷2、二甲基硅油0.4、过氧化钾0.3、水适量。
一种如权利要求1所述的赤泥发泡轻质保温板的制备方法，其特征在于包括以下步骤：
（1）将上述聚氧丙烯甘油醚与气相白炭黑混合，充分搅拌，加热至150℃，加入丙烯酸甲酯，保温静置3小时，降低温度至50℃，滴加聚乙二醇400，滴加完毕后，在搅拌条件下依次加入白乳胶、过氧化钾，800转/分搅拌16分钟，加入N-(β-氨乙基)-γ-氨丙基三甲氧基硅烷，常温搅拌15分钟，得浆料；
（2）将上述快普通硅酸盐水泥、赤泥、膨润土、凹凸棒土、硅藻土、硅酸钙混合加入到搅拌机中，搅拌速度为80 转/ 分，搅拌时间20分钟，得水泥混料；
（3）将50℃的水加入到搅拌机中，湿搅拌3分钟，与上述十二烷基苯磺酸钠混合，通过发泡剂发泡，得泡沫料；
（4）将上述得到的泡沫料与水泥混料混合，泡沫料的体积占水泥混料重量的含量为：6升/千克；50转/分搅拌30分钟，得预混料；
（5）将得到的预混料与上述浆料和剩余各原料混合，充分搅拌后送入模具内浇注成形，经脱模、养护、干燥后即得所述赤泥发泡轻质保温板。
性能测试：
Figure BDA0000357886481

Claims (2)

1.一种赤泥发泡轻质保温板，其特征在于它是由下述重量份的原料组成的：
普通硅酸盐水泥100-110、赤泥40-50、膨润土10-20、凹凸棒土10-20、硅藻土10-20、硅酸钙10-13、气相白炭黑2-3、白乳胶6-8、异丙醇3-4、甘油2-3、乙撑双硬脂酰胺1-2、聚酰胺蜡微粉3-4、松香2-3、聚乙二醇400 2-3、二氯甲烷1-2、丙烯酸甲酯2-3、聚氧丙烯甘油醚2-3、十二烷基苯磺酸钠2-3、氧化聚乙烯蜡2-4、N-(β-氨乙基)-γ-氨丙基三甲氧基硅烷1-2、二甲基硅油0.3-0.4、过氧化钾0.1-0.3、水适量。
2.一种如权利要求1所述的赤泥发泡轻质保温板的制备方法，其特征在于包括以下步骤：     （1）将上述聚氧丙烯甘油醚与气相白炭黑混合，充分搅拌，加热至120-150℃，加入丙烯酸甲酯，保温静置2-3小时，降低温度至40-50℃，滴加聚乙二醇400，滴加完毕后，在搅拌条件下依次加入白乳胶、过氧化钾，600-800转/分搅拌10-16分钟，加入N-(β-氨乙基)-γ-氨丙基三甲氧基硅烷，常温搅拌10-15分钟，得浆料；
（2）将上述快普通硅酸盐水泥、赤泥、膨润土、凹凸棒土、硅藻土、硅酸钙混合加入到搅拌机中，搅拌速度为60-80 转/ 分，搅拌时间15-20 分钟，得水泥混料；
（3）将40-50℃的水加入到搅拌机中，湿搅拌2-3分钟，与上述十二烷基苯磺酸钠混合，通过发泡剂发泡，得泡沫料；
（4）将上述得到的泡沫料与水泥混料混合，泡沫料的体积占水泥混料重量的含量为：4-6升/千克；40-50转/分搅拌20-30分钟，得预混料；
（5）将得到的预混料与上述浆料和剩余各原料混合，充分搅拌后送入模具内浇注成形，经脱模、养护、干燥后即得所述赤泥发泡轻质保温板。
CN201310320068.3A 2013-07-27 2013-07-27 一种赤泥发泡轻质保温板及其制备方法 Active CN103449781B (zh)