CN103436134A - 一种熔融突起型反光涂料 - Google Patents
一种熔融突起型反光涂料 Download PDFInfo
- Publication number
- CN103436134A CN103436134A CN2013103691204A CN201310369120A CN103436134A CN 103436134 A CN103436134 A CN 103436134A CN 2013103691204 A CN2013103691204 A CN 2013103691204A CN 201310369120 A CN201310369120 A CN 201310369120A CN 103436134 A CN103436134 A CN 103436134A
- Authority
- CN
- China
- Prior art keywords
- coating
- fused
- light reflecting
- protruding light
- reflecting coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明属于涂料技术领域,尤其涉及一种熔融突起型反光涂料。本发明公开了一种熔融突起型反光涂料,由以下组分及重量百分比组成:C5石油树脂:15%-20%,颜料:1%-10%,填料:65%-80%,反光玻璃珠:1%-6%,助剂:2%-8%。本发明的有益效果:1、开放交通快,一般15分钟内开放;2、汽车行驶在该涂层上,会发出振荡涂料特有的声音,提醒司机,有效地增加了安全性。
Description
技术领域
本发明属于涂料技术领域,尤其涉及一种熔融突起型反光涂料。
背景技术
涂料是一种材料,这种材料可以用不同的施工工艺涂覆在物件表面,形成粘附牢固、具有一定强度、连续的固态薄膜。这样形成的膜通称涂膜,又称漆膜或涂层。目前涂料的应用领域非常广泛,比如家庭装修用涂料、交通路面用涂料。在交通用涂料中主要是用于路面标记用。目前使用的交通用涂料,在使用的时候干燥慢,从而使得交通开放慢,影响交通。而且目前使用的交通用涂料在做好交通标记后,汽车行驶到标记上时并不会产生异声,从而不会对司机起到提醒作用。
发明内容
本发明的目的在于解决以上所述的技术问题,提供一种熔融突起型反光涂料,其技术方案如下:
一种熔融突起型反光涂料,其特征在于,由以下组分及重量百分比组成:
C5石油树脂 15%-20%
颜料 1%-10%
填料 65%-80%
反光玻璃珠 1%-6%
助剂 2%-8%。
优选方式为,所述的颜料为钛白粉或耐热铬黄。
优选方式为,所述的填料为重钙和石英砂。
本发明的生产和施工:将以上组分按工艺要求逐一加入搅拌混合均匀,包装。 施工时 ,将以上涂料加入热熔釜中,加热到200℃,通过振荡标线机涂敷于路面,冷却后即可通车。
本发明所述的C5石油树脂是脂肪族树脂,不含苯环和不饱和键,耐候性良好;
本发明的助剂包括成型剂、增塑剂、防沉剂、抗粘连剂等。助剂赋予涂料触变性,对形成稳定形状起关键作用。
本发明的有益效果:
1、开放交通快,一般15分钟内开放;
2、汽车行驶在该涂层上,会发出振荡涂料特有的声音,提醒司机,有效地增加了安全性。
具体实施方式
下面具体说明实施例:
实施例一:
一种熔融突起型反光涂料,其特征在于,由以下组分及重量百分比组成:
C5石油树脂 16%
颜料 5%
填料 70%
反光玻璃珠 2.5%
助剂 6.5%
优选方式为,所述的颜料为钛白粉或耐热铬黄。
优选方式为,所述的填料为重钙和石英砂。
本发明的生产和施工:将以上组分按工艺要求逐一加入搅拌混合均匀,包装。 施工时 ,将以上涂料加入热熔釜中,加热到200℃,通过振荡标线机涂敷于路面,冷却后即可通车。
实施例二:
一种熔融突起型反光涂料,其特征在于,由以下组分及重量百分比组成:
C5石油树脂 15%
颜料 1%
填料 80%
反光玻璃珠 2%
助剂 2%。
本发明的生产和施工:将以上组分按工艺要求逐一加入搅拌混合均匀,包装。 施工时 ,将以上涂料加入热熔釜中,加热到200℃,通过振荡标线机涂敷于路面,冷却后即可通车。
实施例三:
C5石油树脂 20%
颜料 10%
填料 65%
反光玻璃珠 1%
助剂 4%。
本发明的生产和施工:将以上组分按工艺要求逐一加入搅拌混合均匀,包装。 施工时 ,将以上涂料加入热熔釜中,加热到200℃,通过振荡标线机涂敷于路面,冷却后即可通车。
Claims (3)
1.一种熔融突起型反光涂料,其特征在于,由以下组分及重量百分比组成:
C5石油树脂 15%-20%
颜料 1%-10%
填料 65%-80%
反光玻璃珠 1%-6%
助剂 2%-8%。
2.如权利要求1所述的熔融突起型反光涂料,其特征在于,所述的颜料为钛白粉或耐热铬黄。
3.如权利要求1所述的熔融突起型反光涂料,其特征在于,所述的填料为重钙和石英砂。