CN1034357C - 一种防水透汽服装面料的制造方法 - Google Patents
一种防水透汽服装面料的制造方法 Download PDFInfo
- Publication number
- CN1034357C CN1034357C CN94113980A CN94113980A CN1034357C CN 1034357 C CN1034357 C CN 1034357C CN 94113980 A CN94113980 A CN 94113980A CN 94113980 A CN94113980 A CN 94113980A CN 1034357 C CN1034357 C CN 1034357C
- Authority
- CN
- China
- Prior art keywords
- film
- hydrophobic
- water
- garment
- membrane
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
一种防水透汽服装面料的制造方法其特征在于服装面料为纤维织物与憎水透汽膜直接复合而成，复合面料不需亲水处理，憎水透汽膜用低分子量树脂制备，膜的弹性用回缩法获得，其复合服装面料的透汽量＞4000g/m2天，制作简便，成本低廉，防水透汽服能防雨、透汽性好，穿着舒适，晴雨天都能穿，即使在大暴雨或者大运动量的人同样有舒适感，不渗漏，透汽性好，并有抗折、拉、皱和耐洗涤性能，是一种功能独特、人人喜爱的服装。
Description
本发明公开了防水透汽服装面料的制造方法，属生活必需品服装类发明。
每个人都希望自己穿的服装能晴雨两用，雨天不但能防水还能透汽，将身上的汗水汽扩张到衣服外面，不论晴天、阴天、雨天各种环境穿都舒适，这就要求有一种高透汽量、高防水性能，并抗折、皱，有些还要求有弹性的高性能服装面料。用硅酮、氟碳和其他憎水剂处理的织物以及近来发展推出的高聚物涂层，虽然透汽良好，但一经摩擦、折、皱、拉伸等便渗水，耐水压也很低≯400mm水柱，而且寿命很短，洗涤几次便失去防水性能，专利EP0110626和USP4194041是用聚四氟乙烯膜作憎水透汽层于亲水膜及织物复合制造成防水透汽服装面料，能达到静水压250mm，20分钟无水渗漏，透汽量＞1000g/m2，天，最好时可达＞2000g/m2，天，但它一定要在憎水层的一面，即而料的衬里面复合有亲水膜，如用聚醚—聚尿烷、聚全氟磺酸等亲水物制造的亲水膜。这种亲水层制备非常复杂，甚至需在PTFE膜表面进行聚合或与其接枝聚合，亲水层厚度达170μ。通常真正防雨的实际要求为：耐静水压1400mm，特大暴雨要求大于2000mm。透汽量＞1000g/m2，天，大运动量要求＞3500-4000g/m2，天。显然上述二个专利所得的产品是不能满足要求的。
本发明的目的是提供一种防雨和透汽量也好的服装面料的制造方法，即使在大暴雨、对大运动量人也能具有防雨和透汽量的要求，穿着舒适，其静水压＞6000mm、透汽量＞4000g/m2，天。同时也不必复合亲水材料、制作简单、成本低廉。
为达到本发明且的，本发明采用的憎水膜是按中国申请专利941120570“用聚四氟乙烯制备多孔膜”制备的PTFE透汽膜，透汽量＞4000g/m2，天，水触角＞90°，国外专利制备透汽膜的原料必须用超高分了量树脂。这种要求非常高，实际上是不可得到，而941120570专利制备的透汽膜是用普通制造密封生料带的低分子量树脂，方法简便，容易得到，用低分子量树脂制备的膜，膜的横向能扩张＞5倍，最高能达到40倍，透汽量在5000-10000g/m2，天，静水压6000mm2小时不渗漏，说明膜的孔径小，孔率非常高，能充分保证透汽量，因此服装面料复合时不需对膜和纤维织物进行亲水处理，粘合剂也不必用亲水透汽胶，只要使用普通胶粘剂即可。面料制成服装，在穿着过程中会遇到折、拉、皱以及洗涤等情况，因此需要将憎水膜处理成有弹性，EP0110626制备弹性膜是扩张超过绕曲点5％，但绕曲点随温度不同而变化很大，同时仅仅超过绕曲点5％要想保持弹性，定型不能过度，否则会失去弹性，定型不够，虽能保持弹性但复合物尺寸易变形，洗涤时易脱胶，影响寿命。本发明采用回缩法制取弹性膜，即是将膜进行扩张→定型→回缩程序的操作方法。下面通过实施例对本发明作详细说明。
实施例1
弹性膜制备，本发明用回缩法圆满解决了这个问题。取未扩张的生料带24×24cm，四边用夹子夹好，按生料带压延方向拉伸2倍至72cm，再在横向扩张10倍至264cm，定型后再让横向回缩至178cm，纵向保持72cm不变，此时制得的膜具有非常良好的弹性，平均100转弹性复原性＞50％，而复合物从各方向受力都能复原。
弹性膜、无弹性膜与纤维织物复合，其主要性能测试见下表一：表一
| 项目 | 无弹性膜复合 | 弹性膜复合 |
| 透气量 | 4805.9g/m2，天 | 4653.25g/m2，天 |
| 静水压600MM 2小时 | 无渗漏 | 无渗漏 |
| 耐洗性(洗衣机洗涤30次) | 脱胶 | 不脱胶 |
从上述方法及表一中可看出，用回缩法即用扩张→定型→回缩的处理方法，制得的弹性膜复合后对其透汽量静水压基本无影响，透汽量仍＞4000g/m2，天，符合大运动量人的穿着要求，洗涤30次后仍不脱胶，适合做服装的要求。
实施例2
用弹性膜与帆布、涤纶布、棉布、丝绸等织物粘合，其透汽量的测式见表二：表二
| 复合材料种类 | 透汽量g/m2，天 |
| 细帆布-平纹布 | 4055.6 |
| 尼龙绸 | 4054.36 |
| 涤纶布-平纹布 | 4139.81 |
| 平纹布-平纹布 | 4505.9 |
| 涤纶布-平纹布 | 4149 |
| 膜 | 4604.6 |
从表二中可看出膜与各种织物复合后，其透气量损失很少，每一种复合材料其透气量都大于4000g/m2，天，符合大运动量的透气量要求值3500-4000g/m2，天。因此各类织物的复合衣料穿着应是很舒适的。
本发明的服装衣料具有制作简便，成本低廉，服装能防雨透汽好，穿着有舒适感。即使在大暴雨、大运动量的人穿着同样有不渗漏，透汽性能好，穿着舒适并有抗折、拉、皱和耐洗涤的要求，因此是一种功能独特服装，会受到人们的喜爱。
Claims (2)
1.一种防水透汽服装面料的制造方法，其特征在于服装面料为纤维织物与憎水透汽膜直接复合而成，复合面料不需亲水处理，憎水透汽膜用低分子量树脂制备，膜的弹性用回缩法获得，膜其透汽量＞5000g/m2，天，静水压＞6000mm水柱2小时不渗漏。
2.根据权利要求书1所述的防水透汽服装面料的制造方法，其特征在于的回缩法是将憎水透汽膜进行扩张→定型→回缩程序的操作方法，即将膜横向扩张5倍至40倍后定型，然后再让其自然回缩。