CN103421230A - Hdpe和pc复合的抗菌塑料合金 - Google Patents

Hdpe和pc复合的抗菌塑料合金 Download PDF

Info

Publication number
CN103421230A
CN103421230A CN2013103195134A CN201310319513A CN103421230A CN 103421230 A CN103421230 A CN 103421230A CN 2013103195134 A CN2013103195134 A CN 2013103195134A CN 201310319513 A CN201310319513 A CN 201310319513A CN 103421230 A CN103421230 A CN 103421230A
Authority
CN
China
Prior art keywords
hdpe
plastic alloy
density polyethylene
high density
composite antibacterial
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2013103195134A
Other languages
English (en)
Inventor
黄丽红
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
SHANGHAI YINGZHI RUBBER PLASTIC PRODUCT CO Ltd
Original Assignee
SHANGHAI YINGZHI RUBBER PLASTIC PRODUCT CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by SHANGHAI YINGZHI RUBBER PLASTIC PRODUCT CO Ltd filed Critical SHANGHAI YINGZHI RUBBER PLASTIC PRODUCT CO Ltd
Priority to CN2013103195134A priority Critical patent/CN103421230A/zh
Publication of CN103421230A publication Critical patent/CN103421230A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种HDPE和PC复合的抗菌塑料合金，由下述组分按重量份组成：100份HDPE，30-40份PC，10-20份增容剂HDPE-g-MAH，0.6-0.8份抗菌剂。本发明的HDPE和PC复合的抗菌塑料合金，抗菌效果优异。

Description

HDPE和PC复合的抗菌塑料合金
技术领域
本发明涉及一种塑料合金，尤其涉及一种HDPE和PC复合的抗菌塑料合金。
背景技术
高密度聚乙烯（High Density Polyethylene，简称为“HDPE”），是一种结晶度高、非极性的热塑性树脂。原态HDPE的外表呈乳白色，在微薄截面呈一定程度的半透明状。是一种结晶度高、非极性的热塑性树脂。高密度聚乙烯为无毒、无味、无臭的白色颗粒，熔点约为130℃，相对密度为0.941～0.960。它具有良好的耐热性和耐寒性，化学稳定性好，还具有较高的刚性和韧性，机械强度好。
PC，聚碳酸酯，是分子链中含有碳酸酯基的高分子聚合物，五大工程塑料中增长速度最快的通用工程塑料。
然而，目前的HDPE和PC复合的塑料合金抗菌性能并不佳。
发明内容
针对现有技术中存在的上述不足，本发明所要解决的技术问题是提供一种HDPE和PC复合的抗菌塑料合金。
本发明所要解决的技术问题是通过如下技术方案实现的：
HDPE和PC复合的抗菌塑料合金，由下述组分按重量份组成：100份HDPE，30-40份PC，10-20份增容剂HDPE-g-MAH，0.6-0.8份抗菌剂。
所述增容剂HDPE-G-MAH为高密度聚乙烯与马来酸酐接枝物。
所述抗菌剂，由下述组分按重量份组成：磷酸锆10-30份、氧化银20-40份、壳聚糖10-30份、2-噻唑基-4-苯并咪唑20-40份。
磷酸锆，英文名：Phosphoric acid,zirconium(4+)salt(2:1)，CAS Number：13772-29-7。
氧化银，CAS Number:20667-12-3。
壳聚糖，英文名：Chitosan，CAS Number：9012-76-4。
2-噻唑基-4-苯并咪唑，英文名称：2-(4-thiazolyl)benzimidazole，CASNumber：148-79-8。
将磷酸锆、氧化银、壳聚糖和2-噻唑基-4-苯并咪唑搅拌混合均匀，即可制得所述抗菌剂。
可以采用本行业通用方法进行制备本发明的HDPE和PC复合的抗菌塑料合金，例如：按配比称取各组分，混合均匀后，熔融混炼、挤出造粒，即获得所述HDPE和PC复合的抗菌塑料合金。
本发明的HDPE和PC复合的抗菌塑料合金，抗菌效果优异。
具体实施方式
实施例1
按照表1中对应实施例1数据称取各原料，混合均匀后，熔融混炼、挤出造粒，即获得所述HDPE和PC复合的抗菌塑料合金。
表1：原料配方表   单位：公斤
实施例1 实施例2 实施例3 实施例4 实施例5
HDPE树脂 100 100 100 100 100
PC树脂 35 35 35 35 35
增容剂HDPE-g-MAH 15 15 15 15 15
磷酸锆 0.14 / 0.35 0.14 0.14
氧化银 0.21 0.35 / 0.21 0.21
壳聚糖 0.14 0.14 0.14 / 0.35
2-噻唑基-4-苯并咪唑 0.21 0.21 0.21 0.35 /
HDPE树脂选用台湾塑胶公司牌号9001的HDPE树脂。
PC树脂选用日本帝人公司牌号1250Y的注塑级PC树脂。
实施例2-4
分别按照表1中对应实施例2-4数据称取各原料。采用实施例1所述的方法制备所述HDPE和PC复合的抗菌塑料合金。
测试例1
对各实施例制备而得的塑料合金进行抗菌性能测试。
抗菌测试标准：QB/T2591-2003A《抗菌塑料抗菌性能试验方法和抗菌效果》。检测用菌：大肠杆菌（Escherichia coli）ATCC25922，金黄色葡萄球菌（Staphy lococcus aureus）ATCC6538。
表2：塑料合金抗菌性能测试表
大肠杆菌抗菌率，% 金黄色葡萄球菌抗菌率，%
实施例1 87.2 88.4
实施例2 86.5 87.6
实施例3 85.7 87.2
实施例4 86.2 86.8
本发明的塑料合金，在添加抗菌剂后，力学性能几乎没有影响。采用特定原料及配比的抗菌剂，起到协同增效抗菌的作用。

Claims (2)

1.HDPE和PC复合的抗菌塑料合金，其特征在于，由下述组分按重量份组成：100份HDPE，30-40份PC，10-20份增容剂HDPE-g-MAH，0.6-0.8份抗菌剂。
2.如权利要求1所述的HDPE和PC复合的抗菌塑料合金，其特征在于，所述抗菌剂，由下述组分按重量份组成：磷酸锆10-30份、氧化银20-40份、壳聚糖10-30份、2-噻唑基-4-苯并咪唑20-40份。
CN2013103195134A 2013-07-26 2013-07-26 Hdpe和pc复合的抗菌塑料合金 Pending CN103421230A (zh)