CN103420652A - Cement-based waterproof tile adhesives material and preparation method thereof - Google Patents
Cement-based waterproof tile adhesives material and preparation method thereof Download PDFInfo
- Publication number
- CN103420652A CN103420652A CN2012101633981A CN201210163398A CN103420652A CN 103420652 A CN103420652 A CN 103420652A CN 2012101633981 A CN2012101633981 A CN 2012101633981A CN 201210163398 A CN201210163398 A CN 201210163398A CN 103420652 A CN103420652 A CN 103420652A
- Authority
- CN
- China
- Prior art keywords
- cement
- tile adhesives
- adhesives material
- based waterproof
- dry
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a cement-based waterproof tile adhesives material. The tile adhesives material is composed of the following components by weight: 40% of Portland cement 52.5, 58% of dry silica sand, 1% of latex powder, and 1% of a naphthalene superplasticizer. A preparation method of the tile adhesives material comprises the following steps: putting the 40% of Portland cement 52.5 and the 58% of dry silica sand into a closed dry sand mixer and stirring completely; and after full stirring, putting the 1% of latex powder and the 1% of naphthalene superplasticizer into the closed dry sand mixer, stirring completely, then obtaining the cement-based waterproof tile adhesives material, and packing the tile adhesives material with moistureproof and airpermeable packages. The tile adhesives material has the following advantages: a wide application range, convenient use, high bonding intensity, waterproof property, low shrinkage, and cracking resistance.
Description
Technical field
The present invention relates to a kind of cement-based waterproof type tile paste material, this product is applicable to the indoor and outdoor tile paste, and mosaic is pasted, concrete, brick structures, ground putty, floor leveling thick-layer construction etc.
Background technology
No matter be indoor or outdoor at present; the use range of ceramic tile is in continuous expansion; the use of ceramic tile makes the adhesive material of ceramic tile in continuous raising; current ceramic tile often can encounter in taping process that sticking strength is not high, adhesive material easily shrinks; cause ceramic tile easily drop or come off; mostly the water resistance of tile paste material is insuperior, causes the phenomenon generation that is pasted not strongly solid at later stage ceramic tile and adhesive material.
Summary of the invention
For achieving the above object, cement-based waterproof tile paste material of the present invention is comprised of following weight proportion:
52.5 silicate cement 40%, dry silica sand 58%, latex powder 1%, naphthalene water reducer 1%.
The particle diameter of described dry silica sand is between 0.1mm-0.3mm.
The preparation method of cement-based waterproof tile paste material is as follows:
Step 1: 52.5 silicate cements 40% and dry silica sand 58% are dropped in airtight dry sand mixing tank, fully stir, after stirring.
Step 2: again latex powder 1%, naphthalene water reducer 1% are dropped in above-mentioned airtight dry sand mixing tank, make cement-based waterproof tile paste material after mixing.
Step 3: adopt moistureproof ventilative the packing.
The present invention compared with prior art, has following obvious advantage and beneficial effect:
1) applied range, this product is applicable to following environment: indoor and outdoor tile paste, mosaic stickup, concrete, brick structures, ground putty, floor leveling, thick-layer construction;
2) cohesive strength is high, and single component is easy to use, only need add water;
3) waterproof, low-shrinkage, cracking resistance.
Embodiment
Below in conjunction with specific embodiment, the present invention is illustrated:
Now take that to produce 1000 kilograms of cement-based waterproof tile paste materials be example: 580 kilograms of 400 kilograms of 52.5 silicate cements and dry silica sands are dropped in airtight dry sand mixing tanks, fully stir, after stirring; Again 10 kilograms of 10 kilograms of latex powder, naphthalene water reducer are dropped in above-mentioned airtight dry sand mixing tank, make cement-based waterproof tile paste material after mixing; Then adopt moistureproof ventilative the packing.Adopting 10 kilograms of every bag of protection against the tide to breathe freely is packed.
Material usage:
Water and powder weight mixture ratio are 2.6-2.8:10
Technical data:
Product appearance: grey powder
Condition of storage: be stored in shady and cool arid region, guard against damp.
Quality guaranteed period: the original packing quality guaranteed period is 12 months
Packing: 10 kilograms/bag
Operation instruction
1. processing base level: guarantee basal plane clean, firm, dustless and loose particles, grease or other impurity.Before tiling, fresh concrete, brick structures, putty and screed-coat should first solidify 28 days or without shrinking, can construct (remarks: be sure not this product of construction on the gypsum basal plane)
2. stir: powder is added in clean water gradually, and be stirred to without the uniform thickness slurry of powder ball.The weight mixture ratio of water and powder is 2.6-2.8:10, and mixture waits 5 minutes, slightly does stirring and constructs.Available low-speed machinery/electric stirring
3. construction: with spatula or ruler, blend mixture is taped against on basal plane, so share the horizontal combing ceramic tile of dentation spatula and paste, place ceramic tile (in ceramic tile glues the applicable time), gently toward pressing down and slightly move left and right ceramic tile, guarantee laminating fully.The darker ceramic tile for the sticking veneer recess first is coated with this product of one deck and fits fully guaranteeing on bonding plane.As the applicable time has crossed or porcelain
Brick pastes dry, removes ceramic tile and glues and again construct with virgin material.
Construction precautions: temperature lower time of drying of corresponding prolongation during construction, construction temperature is not less than 5
Degree centigrade;
Finally it should be noted that: above embodiment is only in order to illustrate the present invention and unrestricted technical scheme described in the invention; Therefore, although this specification sheets has been described in detail the present invention with reference to each above-mentioned embodiment,, those of ordinary skill in the art should be appreciated that still and can modify or be equal to replacement the present invention; And all do not break away from technical scheme and the improvement thereof of the spirit and scope of invention, it all should be encompassed in the middle of claim scope of the present invention.
Claims (1)
1. cement-based waterproof tile paste material is characterized in that: following weight proportion, consist of:
52.5 silicate cement----------------40%
Dry silica sand------------------------58%
Latex powder------------------------1%
Naphthalene water reducer--------------------1%
The particle diameter of described dry silica sand is between 0.1mm-0.3mm;
Its preparation method is as follows:
Step 1: 52.5 silicate cements 40% and dry silica sand 58% are dropped in airtight dry sand mixing tank, fully stir, after stirring;
Step 2: again latex powder 1%, naphthalene water reducer 1% are dropped in above-mentioned airtight dry sand mixing tank, make cement-based waterproof tile paste material after mixing;
Step 3: adopt moistureproof ventilative the packing.