CN103409762B - Metal detergent and preparation method thereof - Google Patents
Metal detergent and preparation method thereof Download PDFInfo
- Publication number
- CN103409762B CN103409762B CN201310309922.6A CN201310309922A CN103409762B CN 103409762 B CN103409762 B CN 103409762B CN 201310309922 A CN201310309922 A CN 201310309922A CN 103409762 B CN103409762 B CN 103409762B
- Authority
- CN
- China
- Prior art keywords
- parts
- metal detergent
- preparation
- magnesiumcarbonate
- oxyethane
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a kind of metal detergent and preparation method thereof.By the raw material of following parts by weight; Sodium dodecylbenzene sulfonate 8-10 part, sodium bicarbonate 2-6 part, magnesiumcarbonate 10-12 part, tertiary sodium phosphate 4-6 part, basic zirconium chloride 2-9 part, butyl stearate 5-10 part, propylene glycol 10-15 part, oxyethane 20-22 part, zinc peroxide 10-20 part, water 30-40 part.Metal detergent of the present invention can remove the dirt that metallic surface etc. is difficult to remove easily, exposes in atmosphere, can keep 30 days non-corrosives, and cost is low after metal cleaning.
Description
Technical field
The present invention relates to a kind of sanitising agent, particularly relate to a kind of metal detergent and preparation method thereof.
Background technology
Sanitising agent is a kind of cleaning product being used for washing clothes or the thing such as implement or clean furniture of liquid state.It adopts various new tensio-active agent, strong detergency, and rinsing is easy, non-stimulated to skin.The most suitable washing kitchen tools, furniture, and fruit, melon and vegetable.Sanitising agent primarily of tensio-active agent, sterilant, rumbling compound, that the green technology such as agent and unique bright factor high-tech is seen through in import is formulated; There is the characteristics such as powerful scrubbing power and seepage force, sterilizing power and polishing bright property.Thoroughly can remove rapidly the tough stains in all kinds of ceramic tile surface, gap.Unique seepage force and the polishing light factor more can remove lime scale rapidly, cement scale, spackling dirt, scale, and electric welding prints, aluminium cut, coin marking, black dirt, mould dirt, incrustation scale, all kinds of paint, all kinds of glue, all kinds of heavy oil is dirty, when it is coated in cleaning of objects surface, is combined or melts with dirt.But the dirt on general sanitising agent not easily clean metal surface, and easily corrosion is caused to metal.
Summary of the invention
For the deficiencies in the prior art, the invention provides a kind of metal detergent and preparation method thereof, effectively can remove the greasy dirt of metallic surface, and not easily corroding metal.
Described metal detergent, comprises the raw material of following parts by weight; Sodium dodecylbenzene sulfonate 8-10 part, sodium bicarbonate 2-6 part, magnesiumcarbonate 10-12 part, tertiary sodium phosphate 4-6 part, basic zirconium chloride 2-9 part, butyl stearate 5-10 part, propylene glycol 10-15 part, oxyethane 20-22 part, zinc peroxide 10-20 part, water 30-40 part.
The preparation method of above-mentioned metal detergent, comprise the following steps: add water and basic zirconium chloride in a kettle., heating for dissolving, add Sodium dodecylbenzene sulfonate under stirring, maintain the temperature at 100 DEG C, the time is at 0.5-1 hour, stop heating, then add sodium bicarbonate, magnesiumcarbonate, tertiary sodium phosphate, butyl stearate, propylene glycol, oxyethane, zinc peroxide, stir.
The invention has the beneficial effects as follows, the dirt that metallic surface etc. is difficult to remove can be removed easily, expose in atmosphere after metal cleaning, 30 days non-corrosives can be kept, and cost is low.
Embodiment
Below by specific embodiment, the present invention is further described in detail.
Embodiment 1
A kind of metal detergent is made up of the raw material of following parts by weight; Sodium dodecylbenzene sulfonate 8 parts, sodium bicarbonate 2 parts, 10 parts, magnesiumcarbonate, tertiary sodium phosphate 4 parts, basic zirconium chloride 2 parts, butyl stearate 5 parts, propylene glycol 10 parts, 20 parts, oxyethane, zinc peroxide 10 parts, 30 parts, water.
The preparation method of above-mentioned metal detergent: add water and basic zirconium chloride in a kettle., heating for dissolving, Sodium dodecylbenzene sulfonate is added under stirring, maintain the temperature at 100 DEG C, time, at 0.5 hour, stops heating, then adds sodium bicarbonate, magnesiumcarbonate, tertiary sodium phosphate, butyl stearate, propylene glycol, oxyethane, zinc peroxide, stir.
Embodiment 2
A kind of metal detergent is made up of the raw material of following parts by weight; Sodium dodecylbenzene sulfonate 10 parts, sodium bicarbonate 6 parts, 12 parts, magnesiumcarbonate, tertiary sodium phosphate 6 parts, basic zirconium chloride 9 parts, butyl stearate 10 parts, propylene glycol 15 parts, 22 parts, oxyethane, zinc peroxide 20 parts, 40 parts, water.
The preparation method of above-mentioned metal detergent: add water and basic zirconium chloride in a kettle., heating for dissolving, Sodium dodecylbenzene sulfonate is added under stirring, maintain the temperature at 100 DEG C, time, at 1 hour, stops heating, then adds sodium bicarbonate, magnesiumcarbonate, tertiary sodium phosphate, butyl stearate, propylene glycol, oxyethane, zinc peroxide, stir.
Embodiment 3
A kind of metal detergent is made up of the raw material of following parts by weight; Sodium dodecylbenzene sulfonate 9 parts, sodium bicarbonate 4 parts, 11 parts, magnesiumcarbonate, tertiary sodium phosphate 5 parts, basic zirconium chloride 6 parts, butyl stearate 8 parts, propylene glycol 12 parts, 21 parts, oxyethane, zinc peroxide 15 parts, 35 parts, water.
The preparation method of above-mentioned metal detergent: add water and basic zirconium chloride in a kettle., heating for dissolving, Sodium dodecylbenzene sulfonate is added under stirring, maintain the temperature at 100 DEG C, time, at 0.8 hour, stops heating, then adds sodium bicarbonate, magnesiumcarbonate, tertiary sodium phosphate, butyl stearate, propylene glycol, oxyethane, zinc peroxide, stir.
After tested, the present invention can remove iron, aluminium, the dirt on copper surface or booty easily, and the metal exposed after adopting embodiment 1,2,3 to clean in atmosphere, see the following form by the time of getting rusty.
| Unit: sky | Embodiment 1 | Embodiment 2 | Embodiment 3 |
| Iron | 30 | 33 | 35 |
| Aluminium | 37 | 40 | 38 |
| Copper | 40 | 50 | 45 |
In addition, the invention is not restricted to above-mentioned embodiment, as long as not exceeding in scope of the present invention, various mode can be taked to implement the present invention.
Claims (2)
1. a metal detergent, is characterized in that: the raw material comprising following parts by weight; Sodium dodecylbenzene sulfonate 8-10 part, sodium bicarbonate 2-6 part, magnesiumcarbonate 10-12 part, tertiary sodium phosphate 4-6 part, basic zirconium chloride 2-9 part, butyl stearate 5-10 part, propylene glycol 10-15 part, oxyethane 20-22 part, zinc peroxide 10-20 part, water 30-40 part.
2. the preparation method of metal detergent according to claim 1, it is characterized in that comprising the following steps: add water and basic zirconium chloride in a kettle., heating for dissolving, add Sodium dodecylbenzene sulfonate under stirring, maintain the temperature at 100 DEG C, the time is at 0.5-1 hour, stop heating, then add sodium bicarbonate, magnesiumcarbonate, tertiary sodium phosphate, butyl stearate, propylene glycol, oxyethane, zinc peroxide, stir.