CN103408244A - 云母纸的制造方法 - Google Patents
云母纸的制造方法 Download PDFInfo
- Publication number
- CN103408244A CN103408244A CN2013102840428A CN201310284042A CN103408244A CN 103408244 A CN103408244 A CN 103408244A CN 2013102840428 A CN2013102840428 A CN 2013102840428A CN 201310284042 A CN201310284042 A CN 201310284042A CN 103408244 A CN103408244 A CN 103408244A
- Authority
- CN
- China
- Prior art keywords
- mica
- parts
- powder
- grog
- paper
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种云母纸的制造方法,由下列重量份的原料制成:云母90-100、硼酸1-2、氯化石蜡2-3、凹凸棒土5-8、海泡石粉3-4、明胶4-5、聚乙烯吡咯烷酮1-2、尿素3-4、过硫酸铵1-2、水适量;本发明增加氯化石蜡,增加了云母纸的防水性、绝缘性,又保持了天然云母抗击穿、隔热等优点,本发明制得的云母纸电气强度和拉伸强度好。
Description
技术领域
本发明涉及云母纸生产技术领域,特别涉及一种云母纸的制造方法。
背景技术
云母是一种自然生成的层状硅酸盐类矿物, 具有优良的物理性能和电气性以及在高温状态下仍保持以上性能的特性, 它具有完全的化学惰性和不易燃性, 最重要的是它具有抗高电压、耐电晕放电和防辐射的特性。
云母纸是以碎云母片(白云母、金云母、人工合成云母)为原料,用化学制浆或水力机械制浆在圆网造纸机较慢的车速下抄成纸卷, 再分切成卷筒纸或平板纸, 云母纸保持了天然云母的优良性能, 且厚度均匀、介电强度波动范围小、电晕起始电压高而稳定;其介质损耗的电压特性比片云母绝缘稳定得多, 导热性良好。
但目前生产云母纸工艺单一,采用生粉或熟粉生产,云母纸的电气强度和拉伸强度不理想,需要研究新的生产工艺。
发明内容
本发明的目的是提供一种云母纸的制造方法。
本发明的技术方案如下:
一种云母纸的制造方法,其特征在于:由下列重量份的原料制成:云母90-100、硼酸1-2、氯化石蜡2-3、凹凸棒土5-8、海泡石粉3-4、明胶4-5、聚乙烯吡咯烷酮1-2、尿素3-4、过硫酸铵1-2、水适量;
包括以下步骤:
(1) 将云母在700-800℃下高温煅烧,煅烧1-2 小时得云母熟料;
(2) 将熟料加上相当于熟料重量3-4%的硅烷偶联剂KH550、2-3%的三聚磷酸钠,研成粉末,得50-120目粉末;
(3) 将熟料粉末与其它剩余原料混合加水,至含水量为40-50%,加热至80-90℃,搅拌反应1-2小时;
(4) 将步骤(3)浆料稀释至熟料含量3-4%,加入相当于熟料粉末重量4-5%的碳化硅粉,搅拌分散均匀,圆网抄纸;
(5) 烘干:所得纸在烘缸中烘干至含水量0.2~0.5% 即得成品
本发明增加氯化石蜡,增加了云母纸的防水性、绝缘性,又保持了天然云母抗击穿、隔热等优点,本发明制得的云母纸电气强度和拉伸强度好。
具体实施方式
一种云母纸的制造方法,由下列重量份(公斤)的原料制成:云母90、硼酸2、氯化石蜡2、凹凸棒土8、海泡石粉3、明胶5、聚乙烯吡咯烷酮1、尿素4、过硫酸铵2、水适量;
包括以下步骤:
(1) 将云母在700-800℃下高温煅烧,煅烧1-2 小时得云母熟料;
(2) 将熟料加上相当于熟料重量4%的硅烷偶联剂KH550、2%的三聚磷酸钠,研成粉末,得50-120目粉末;
(3) 将熟料粉末与其它剩余原料混合加水,至含水量为40-50%,加热至80-90℃,搅拌反应1-2小时;
(4) 将步骤(3)浆料稀释至熟料含量3-4%,加入相当于熟料粉末重量4-5%的碳化硅粉,搅拌分散均匀,圆网抄纸;
(5) 烘干:所得纸在烘缸中烘干至含水量0.2~0.5% 即得成品。
经检测,本发明制得的云母纸,拉伸强度为2.3KN/m,击穿电压44KV/mm。
Claims (1)
1.一种云母纸的制造方法,其特征在于:由下列重量份的原料制成:云母90-100、硼酸1-2、氯化石蜡2-3、凹凸棒土5-8、海泡石粉3-4、明胶4-5、聚乙烯吡咯烷酮1-2、尿素3-4、过硫酸铵1-2、水适量;
包括以下步骤:
(1)将云母在700-800℃下高温煅烧,煅烧1-2 小时得云母熟料;
(2)将熟料加上相当于熟料重量3-4%的硅烷偶联剂KH550、2-3%的三聚磷酸钠,研成粉末,得50-120目粉末;
(3)将熟料粉末与其它剩余原料混合加水,至含水量为40-50%,加热至80-90℃,搅拌反应1-2小时;
(4)将步骤(3)浆料稀释至熟料含量3-4%,加入相当于熟料粉末重量4-5%的碳化硅粉,搅拌分散均匀,圆网抄纸;
(5)烘干:所得纸在烘缸中烘干至含水量0.2~0.5% 即得成品。