CN103395184B - A kind of Organic feather biodegradable plastic - Google Patents
A kind of Organic feather biodegradable plastic Download PDFInfo
- Publication number
- CN103395184B CN103395184B CN201310324579.2A CN201310324579A CN103395184B CN 103395184 B CN103395184 B CN 103395184B CN 201310324579 A CN201310324579 A CN 201310324579A CN 103395184 B CN103395184 B CN 103395184B
- Authority
- CN
- China
- Prior art keywords
- feather
- parts
- expanded
- organic
- biodegradable plastic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention provides a kind of Organic feather biodegradable plastic, it is made up of the raw material of following parts by weight: expanded feather meal 30-70 parts; 15-45 parts, plasticizer; Calcium zinc stabilizer 3-5 parts; Flexibilizing agent 5-10 parts, 5-10 parts, water.Organic feather biodegradable plastic of the present invention, the plastic quality obtained is good, can degrade, environmental sound, and the utilization for fowl feather opens new approach, has great economic worth and market prospects.
Description
Technical field
The invention belongs to field of plastics manufacture, specifically a kind of Organic feather biodegradable plastic.
Background technology
China's fowl plumage aboundresources, mainly contains two approach to the comprehensive utilization of fowl feather at present, and one is that in fowl feather resource, sub-fraction is used for being processed into down products; Two be a part of fowl feather by different post processings, make fowl plumage add feed, with alternative imported fish meal protein feed, but current production rate is little; A considerable amount of fowl feather is also had to be abandoned by as waste material.Its reason is the long processing time of fowl plumage feed, is of low nutritive value, and cost is high.Also do not report at present with feather processing plastic.
Summary of the invention
In order to solve the problems of the technologies described above, the invention provides a kind of Organic feather biodegradable plastic.
A kind of Organic feather biodegradable plastic, is characterized in that it is made up of the raw material of following parts by weight: expanded feather meal 30-70 parts; 15-45 parts, plasticizer; Calcium zinc stabilizer 3-5 parts; Flexibilizing agent 5-10 parts, 5-10 parts, water.
Described a kind of Organic feather biodegradable plastic, is characterized in that it is made up of the raw material of following parts by weight: expanded feather meal 40-60 parts; 25-35 parts, plasticizer; Calcium zinc stabilizer 4 parts; Flexibilizing agent 6-8 parts, 6-8 parts, water.
Described a kind of Organic feather biodegradable plastic, is characterized in that it is made up of the raw material of following parts by weight: expanded feather meal 50 parts; 30 parts, plasticizer; Calcium zinc stabilizer 4 parts; Flexibilizing agent 7 parts, 8 parts, water.
Described a kind of Organic feather biodegradable plastic, it is characterized in that described expanded feather meal adopts the mixture of chicken feather, drake feather, pig hair as raw material, wherein the weight percentage of chicken feather, drake feather, pig hair is respectively chicken feather 40%-60%, drake feather 20%-40%, pig hair 15%-25%.
Described a kind of Organic feather biodegradable plastic, is characterized in that described plasticizer is trimethyl citrate, triethyl citrate or ATBC.
Described a kind of Organic feather biodegradable plastic, is characterized in that described expanded feather meal adopts the production method comprised the steps:
1) mixture material of chicken feather, drake feather, pig hair is pulverized by pulverizer;
2) by feed arrangement charging;
3) moisture adding mixture material weight 15%-30% carries out modified, and boiler working pressure is 2Mpa, and conditioning period is 5-10min;
4) singe screw extrusion type puffing technique is adopted to carry out expanded.
Organic feather biodegradable plastic of the present invention, the plastic quality obtained is good, can degrade, environmental sound, and the utilization for fowl feather opens new approach, has great economic worth and market prospects.
Detailed description of the invention
Embodiment 1
Composition of raw materials:
Expanded feather meal 40 parts; Triethyl citrate 35 parts; Calcium zinc stabilizer 4 parts; Flexibilizing agent 8 parts, 6 parts, water.Wherein expanded feather meal adopts the mixture of chicken feather, drake feather, pig hair as raw material, and wherein the weight percentage of chicken feather, drake feather, pig hair is respectively chicken feather 40%, drake feather 40%, pig hair 20%.
Expanded feather meal adopts following production method:
1) mixture material of chicken feather, drake feather, pig hair is pulverized by pulverizer;
2) by feed arrangement charging;
3) moisture adding mixture material weight 15% carries out modified, and boiler working pressure is 2Mpa, and conditioning period is 5min;
4) singe screw extrusion type puffing technique is adopted to carry out expanded.
By each raw material mix, dispersed, adopt extruding-out process to carry out plastic processing and obtain plastic product.
Embodiment 2
Composition of raw materials:
Expanded feather meal 50 parts; Triethyl citrate 30 parts; Calcium zinc stabilizer 4 parts; Flexibilizing agent 7 parts, 8 parts, water.Wherein expanded feather meal adopts the mixture of chicken feather, drake feather, pig hair as raw material, and wherein the weight percentage of chicken feather, drake feather, pig hair is respectively chicken feather 50%, drake feather 35%, pig hair 15%.
Expanded feather meal adopts following production method:
1) mixture material of chicken feather, drake feather, pig hair is pulverized by pulverizer;
2) by feed arrangement charging;
3) moisture adding mixture material weight 20% carries out modified, and boiler working pressure is 2Mpa, and conditioning period is 7min;
4) singe screw extrusion type puffing technique is adopted to carry out expanded.
By each raw material mix, dispersed, adopt extruding-out process to carry out plastic processing and obtain plastic product.
Embodiment 3
Composition of raw materials:
Expanded feather meal 60 parts; Triethyl citrate 25 parts; Calcium zinc stabilizer 4 parts; Flexibilizing agent 6 parts, 8 parts, water.Wherein expanded feather meal adopts the mixture of chicken feather, drake feather, pig hair as raw material, and wherein the weight percentage of chicken feather, drake feather, pig hair is respectively chicken feather 60%, drake feather 20%, pig hair 20%.
Expanded feather meal adopts following production method:
1) mixture material of chicken feather, drake feather, pig hair is pulverized by pulverizer;
2) by feed arrangement charging;
3) moisture adding mixture material weight 30% carries out modified, and boiler working pressure is 2Mpa, and conditioning period is 10min;
4) singe screw extrusion type puffing technique is adopted to carry out expanded.
By each raw material mix, dispersed, adopt extruding-out process to carry out plastic processing and obtain plastic product.
Through detecting, the plastics that embodiment 1-3 obtains all meet the professional standard of national regulation.
The foregoing is only preferred embodiment of the present invention, not in order to limit the present invention, all any amendments done within the spirit and principles in the present invention, equivalent replacement and improvement etc., be all included within protection scope of the present invention.
Claims (4)
1. an Organic feather biodegradable plastic, is characterized in that it is made up of the raw material of following parts by weight: expanded feather meal 30-70 parts; 15-45 parts, plasticizer; Calcium zinc stabilizer 3-5 parts; Flexibilizing agent 5-10 parts, 5-10 parts, water, described expanded feather meal adopts the mixture of chicken feather, drake feather, pig hair as raw material, and wherein the weight percentage of chicken feather, drake feather, pig hair is respectively chicken feather 40%-60%, drake feather 20%-40%, pig hair 15%-25%;
Described expanded feather meal adopts the production method comprised the steps:
1) mixture material of chicken feather, drake feather, pig hair is pulverized by pulverizer;
2) by feed arrangement charging;
3) moisture adding mixture material weight 15%-30% carries out modified, and boiler working pressure is 2Mpa, and conditioning period is 5-10min;
4) singe screw extrusion type puffing technique is adopted to carry out expanded.
2. a kind of Organic feather biodegradable plastic as claimed in claim 1, is characterized in that it is made up of the raw material of following parts by weight: expanded feather meal 40-60 parts; 25-35 parts, plasticizer; Calcium zinc stabilizer 4 parts; Flexibilizing agent 6-8 parts, 6-8 parts, water.
3. a kind of Organic feather biodegradable plastic as claimed in claim 1, is characterized in that it is made up of the raw material of following parts by weight: expanded feather meal 50 parts; 30 parts, plasticizer; Calcium zinc stabilizer 4 parts; Flexibilizing agent 7 parts, 8 parts, water.
4. a kind of Organic feather biodegradable plastic as claimed in claim 1, is characterized in that described plasticizer is trimethyl citrate, triethyl citrate or ATBC.