CN103395184A - Organic feather biodegradable plastic - Google Patents

Organic feather biodegradable plastic Download PDF

Info

Publication number
CN103395184A
CN103395184A CN2013103245792A CN201310324579A CN103395184A CN 103395184 A CN103395184 A CN 103395184A CN 2013103245792 A CN2013103245792 A CN 2013103245792A CN 201310324579 A CN201310324579 A CN 201310324579A CN 103395184 A CN103395184 A CN 103395184A
Authority
CN
China
Prior art keywords
feather
parts
organic
expanded
characterized
Prior art date
Application number
CN2013103245792A
Other languages
Chinese (zh)
Other versions
CN103395184B (en
Inventor
张很文
Original Assignee
张很文
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 张很文 filed Critical 张很文
Priority to CN201310324579.2A priority Critical patent/CN103395184B/en
Publication of CN103395184A publication Critical patent/CN103395184A/en
Application granted granted Critical
Publication of CN103395184B publication Critical patent/CN103395184B/en

Abstract

The invention provides organic feather biodegradable plastic. The organic feather biodegradable plastic is prepared from the follow raw materials in parts by weight: 30-70 parts of puffing feather meal, 15-45 parts of a plasticizer, 3-5 parts of a calcium zinc stabilizer, 5-10 parts of a softening agent and 5-10 parts of water. The organic feather biodegradable plastic provided by the invention has the advantages that the obtained plastic quality is good, the plastic is degraded and has no harm to environment, and the organic feather biodegradable plastic develops a new pathway for the utilization of bird feathers and has great economic values and market prospects.

Description

A kind of organic feather degradative plastics

Technical field

The invention belongs to field of plastics manufacture, specifically a kind of organic feather degradative plastics.

Background technology

China's fowl plumage aboundresources, mainly contain two approach to the comprehensive utilization of fowl feather at present, and the one, in fowl feather resource, sub-fraction is used for being processed into down products; The 2nd, a part of fowl feather, by different post processings, is made the fowl plumage and is added feed, and with replace imported fish meal protein feed, but current production rate is little; Also having a considerable amount of fowl feathers to be used as waste material abandons.Its reason is the long processing time of fowl plumage feed, is of low nutritive value, and cost is high.With the feather processing plastic, also do not report at present.

?

Summary of the invention

In order to solve the problems of the technologies described above, the invention provides a kind of organic feather degradative plastics.

A kind of organic feather degradative plastics, is characterized in that its raw material by following parts by weight makes: 30-70 parts of expanded feather meals; 15-45 parts, plasticizer; 3-5 parts of calcium zinc stabilizers; 5-10 parts of flexibilizing agents, 5-10 parts, water.

Described a kind of organic feather degradative plastics, is characterized in that its raw material by following parts by weight makes: 40-60 parts of expanded feather meals; 25-35 parts, plasticizer; 4 parts of calcium zinc stabilizers; 6-8 parts of flexibilizing agents, 6-8 parts, water.

Described a kind of organic feather degradative plastics, is characterized in that its raw material by following parts by weight makes: 50 parts of expanded feather meals; 30 parts, plasticizer; 4 parts of calcium zinc stabilizers; 7 parts of flexibilizing agents, 8 parts, water.

Described a kind of organic feather degradative plastics, it is characterized in that described expanded feather meal adopts the mixture of chicken feather, drake feather, pig hair as raw material, wherein the weight percentage of chicken feather, drake feather, pig hair is respectively chicken feather 40%-60%, drake feather 20%-40%, pig hair 15%-25%.

Described a kind of organic feather degradative plastics, is characterized in that described plasticizer is trimethyl citrate, triethyl citrate or ATBC.

Described a kind of organic feather degradative plastics is characterized in that described expanded feather meal adopts the production method that comprises the steps:

1) mixture material of chicken feather, drake feather, pig hair is pulverized by pulverizer;

2) by the feed arrangement charging;

3) moisture that adds mixture material weight 15%-30% carries out modified, and boiler working pressure is 2Mpa, and the modified time is 5-10min;

4) adopt single screw extrusion type bulking process to carry out expanded.

Organic feather degradative plastics of the present invention, the plastic quality that obtains is good, can degrade, and environmental sound, opened up new approach for the utilization of fowl feather, has great economic worth and market prospects.

?

The specific embodiment

Embodiment 1

Composition of raw materials:

40 parts of expanded feather meals; 35 parts of triethyl citrates; 4 parts of calcium zinc stabilizers; 8 parts of flexibilizing agents, 6 parts, water.Wherein the mixture of expanded feather meal employing chicken feather, drake feather, pig hair is as raw material, and wherein the weight percentage of chicken feather, drake feather, pig hair is respectively chicken feather 40%, drake feather 40%, pig hair 20%.

Expanded feather meal adopts following production method:

1) mixture material of chicken feather, drake feather, pig hair is pulverized by pulverizer;

2) by the feed arrangement charging;

3) moisture that adds mixture material weight 15% carries out modified, and boiler working pressure is 2Mpa, and the modified time is 5min;

4) adopt single screw extrusion type bulking process to carry out expanded.

By each raw material mix, dispersed, adopt extruding-out process to carry out plastic processing and obtain plastic product.

Embodiment 2

Composition of raw materials:

50 parts of expanded feather meals; 30 parts of triethyl citrates; 4 parts of calcium zinc stabilizers; 7 parts of flexibilizing agents, 8 parts, water.Wherein the mixture of expanded feather meal employing chicken feather, drake feather, pig hair is as raw material, and wherein the weight percentage of chicken feather, drake feather, pig hair is respectively chicken feather 50%, drake feather 35%, pig hair 15%.

Expanded feather meal adopts following production method:

1) mixture material of chicken feather, drake feather, pig hair is pulverized by pulverizer;

2) by the feed arrangement charging;

3) moisture that adds mixture material weight 20% carries out modified, and boiler working pressure is 2Mpa, and the modified time is 7min;

4) adopt single screw extrusion type bulking process to carry out expanded.

By each raw material mix, dispersed, adopt extruding-out process to carry out plastic processing and obtain plastic product.

Embodiment 3

Composition of raw materials:

60 parts of expanded feather meals; 25 parts of triethyl citrates; 4 parts of calcium zinc stabilizers; 6 parts of flexibilizing agents, 8 parts, water.Wherein the mixture of expanded feather meal employing chicken feather, drake feather, pig hair is as raw material, and wherein the weight percentage of chicken feather, drake feather, pig hair is respectively chicken feather 60%, drake feather 20%, pig hair 20%.

Expanded feather meal adopts following production method:

1) mixture material of chicken feather, drake feather, pig hair is pulverized by pulverizer;

2) by the feed arrangement charging;

3) moisture that adds mixture material weight 30% carries out modified, and boiler working pressure is 2Mpa, and the modified time is 10min;

4) adopt single screw extrusion type bulking process to carry out expanded.

By each raw material mix, dispersed, adopt extruding-out process to carry out plastic processing and obtain plastic product.

Through detecting, the plastics that embodiment 1-3 obtains all meet the industry standard of national regulation.

The foregoing is only preferred embodiment of the present invention, not in order to limit the present invention, all any modifications of doing within the spirit and principles in the present invention, be equal to and replace and improvement etc., within all being included in protection scope of the present invention.

Claims (6)

1. organic feather degradative plastics, is characterized in that its raw material by following parts by weight makes: 30-70 parts of expanded feather meals; 15-45 parts, plasticizer; 3-5 parts of calcium zinc stabilizers; 5-10 parts of flexibilizing agents, 5-10 parts, water.
2. a kind of organic feather degradative plastics as claimed in claim 1, is characterized in that its raw material by following parts by weight makes: 40-60 parts of expanded feather meals; 25-35 parts, plasticizer; 4 parts of calcium zinc stabilizers; 6-8 parts of flexibilizing agents, 6-8 parts, water.
3. a kind of organic feather degradative plastics as claimed in claim 1, is characterized in that its raw material by following parts by weight makes: 50 parts of expanded feather meals; 30 parts, plasticizer; 4 parts of calcium zinc stabilizers; 7 parts of flexibilizing agents, 8 parts, water.
4. a kind of organic feather degradative plastics as claimed in claim 1, it is characterized in that described expanded feather meal adopts the mixture of chicken feather, drake feather, pig hair as raw material, wherein the weight percentage of chicken feather, drake feather, pig hair is respectively chicken feather 40%-60%, drake feather 20%-40%, pig hair 15%-25%.
5. a kind of organic feather degradative plastics as claimed in claim 1, is characterized in that described plasticizer is trimethyl citrate, triethyl citrate or ATBC.
6. a kind of organic feather degradative plastics as claimed in claim 4 is characterized in that described expanded feather meal adopts the production method that comprises the steps:
1) mixture material of chicken feather, drake feather, pig hair is pulverized by pulverizer;
2) by the feed arrangement charging;
3) moisture that adds mixture material weight 15%-30% carries out modified, and boiler working pressure is 2Mpa, and the modified time is 5-10min;
4) adopt single screw extrusion type bulking process to carry out expanded.
CN201310324579.2A 2013-07-30 2013-07-30 A kind of Organic feather biodegradable plastic CN103395184B (en)