CN103382295A - 一种耐低温汽车分电器盖 - Google Patents

一种耐低温汽车分电器盖 Download PDF

Info

Publication number
CN103382295A
CN103382295A CN2013102603916A CN201310260391A CN103382295A CN 103382295 A CN103382295 A CN 103382295A CN 2013102603916 A CN2013102603916 A CN 2013102603916A CN 201310260391 A CN201310260391 A CN 201310260391A CN 103382295 A CN103382295 A CN 103382295A
Authority
CN
China
Prior art keywords
parts
low
mixed
raw material
ethylene glycol
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2013102603916A
Other languages
English (en)
Inventor
王进
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ANHUI QIAITE ELECTRONIC TECHNOLOGY Co Ltd
Original Assignee
ANHUI QIAITE ELECTRONIC TECHNOLOGY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ANHUI QIAITE ELECTRONIC TECHNOLOGY Co Ltd filed Critical ANHUI QIAITE ELECTRONIC TECHNOLOGY Co Ltd
Priority to CN2013102603916A priority Critical patent/CN103382295A/zh
Publication of CN103382295A publication Critical patent/CN103382295A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种耐低温汽车分电器盖，它是由下述重量份的原料组成的PET树脂95-105、线性低密度聚乙烯13-19、低温改良剂3-4、玻璃微珠2-3、大理石粉3-4、氧化锌0.3-0.5、马来酸酐-丙烯酸共聚物2-3、二甲基丙烯酸乙二醇酯1-2、双(二辛氧基焦磷酸酯基)乙撑钛酸酯1-2、乙二醇3-4、二苯胺1-2、氨丙基三乙氧基硅烷1-2、改性助剂3-4；本发明生产的分电器盖耐寒性好，适合于高寒地区使用。

Description

一种耐低温汽车分电器盖
技术领域
    本发明主要涉及一种分电器盖，尤其涉及一种耐低温汽车分电器盖。
背景技术
    PET是乳白色或浅黄色高度结晶性的聚合物，表面平滑而有光泽。耐蠕变、抗疲劳性、耐摩擦性好，磨耗小而硬度高，具有热塑性塑料中最大的韧性；电绝缘性能好，受温度影响小，但耐电晕性较差。无毒、耐气候性、抗化学药品稳定性好，吸水率低，耐弱酸和有机溶剂，但不耐热水浸泡，不耐碱。PET树脂的玻璃化温度较高，结晶速度慢，模塑周期长，成型周期长，成型收缩率大，尺寸稳定性差，结晶化的成型呈脆性，耐热性低等；传统生产的汽车分电器盖大多用线性低密度聚乙烯增强改进PET的热变形温度等不良性能，但是汽车分电器盖还是会经常出现裂缝、损毁等，影响了车的正常使用，容易造成安全隐患，因此一种新的、高性能的分电器盖对于汽车事业的发展是很有必要的。
发明内容
本发明目的就是为了提供一种耐低温汽车分电器盖。
本发明是通过以下技术方案实现的：
一种耐低温汽车分电器盖，它是由下述重量份的原料组成的：
PET树脂 95-105、线性低密度聚乙烯13-19、低温改良剂 3-4、玻璃微珠2-3、大理石粉3-4、氧化锌0.3-0.5、马来酸酐-丙烯酸共聚物2-3、二甲基丙烯酸乙二醇酯1-2、双(二辛氧基焦磷酸酯基)乙撑钛酸酯1-2、乙二醇3-4、二苯胺1-2、氨丙基三乙氧基硅烷1-2、改性助剂3-4；
所述的低温改良剂是由重量比为3-4:2-3的聚烯烃弹性体8200与环氧硬脂酸辛酯混合组成；
所述的改性助剂是由下述重量份的原料组成的：
氯化聚乙烯70-80、eva树脂4-5、氮化铝粉5-6、脂肪酸聚乙二醇酯1-2、硼化铬0.2-0.4、液体石蜡1-2；
将上述脂肪酸聚乙二醇酯与氮化铝粉搅拌混合，加入eva树脂，升高温度至80-90℃，保温1-2小时，加入剩余各原料，1000-1200转/分分散10-15分钟，球磨，烘干，过筛，得2-3μm的颗粒。
一种耐低温汽车分电器盖的制备方法，包括以下步骤：
将上述二甲基丙烯酸乙二醇酯、氨丙基三乙氧基硅烷与大理石粉混合，预热到70-80℃，送入高速混合机中混制3-5分钟，转速为500-600转/分；将线性低密度聚乙烯、低温改良剂、氧化锌、改性助剂混合，加热到90-100℃，保温1-2小时，滴加乙二醇，滴加完毕后，冷却至常温，低速500-700转/分分散6-8分钟；将上述处理后的各原料与剩余原料混合，搅拌均匀，送入双螺杆挤出机，经双螺杆挤出机挤出，注塑成型。
本发明的优点是：
    本发明生产的分电器盖耐寒性好，适合于高寒地区使用。
具体实施方式
实施例1
一种耐低温汽车分电器盖，它是由下述重量份（公斤）的原料组成的：
PET树脂 105、线性低密度聚乙烯19、低温改良剂4、玻璃微珠3、大理石粉4、氧化锌0.5、马来酸酐-丙烯酸共聚物3、二甲基丙烯酸乙二醇酯2、双(二辛氧基焦磷酸酯基)乙撑钛酸酯2、乙二醇4、二苯胺2、氨丙基三乙氧基硅烷2、改性助剂3；
所述的低温改良剂是由重量比为4:3的聚烯烃弹性体8200与环氧硬脂酸辛酯混合组成；
所述的改性助剂是由下述重量份的原料组成的：
氯化聚乙烯80、eva树脂5、氮化铝粉6、脂肪酸聚乙二醇酯2、硼化铬0.4、液体石蜡2；
将上述脂肪酸聚乙二醇酯与氮化铝粉搅拌混合，加入eva树脂，升高温度至90℃，保温1小时，加入剩余各原料， 1200转/分分散15分钟，球磨，烘干，过筛，得3μm的颗粒。
一种耐低温汽车分电器盖的制备方法，包括以下步骤：
将上述二甲基丙烯酸乙二醇酯、氨丙基三乙氧基硅烷与大理石粉混合，预热到80℃，送入高速混合机中混制5分钟，转速为600转/分；将线性低密度聚乙烯、低温改良剂、氧化锌、改性助剂混合，加热到100℃，保温2小时，滴加乙二醇，滴加完毕后，冷却至常温，低速700转/分分散8分钟；将上述处理后的各原料与剩余原料混合，搅拌均匀，送入双螺杆挤出机，经双螺杆挤出机挤出，注塑成型。
性能测试：
热变形温度：211℃；
拉伸强度：145.2MPa；
弯曲强度：203MPa；
阻燃性，UL94测定：将用本发明工艺方法制得的试样点燃，把火焰移开后试样在10s内快速自熄，无燃烧的熔体滴落，结果为VO。

Claims (2)

1.一种耐低温汽车分电器盖，其特征在于它是由下述重量份的原料组成的：
PET树脂 95-105、线性低密度聚乙烯13-19、低温改良剂 3-4、玻璃微珠2-3、大理石粉3-4、氧化锌0.3-0.5、马来酸酐-丙烯酸共聚物2-3、二甲基丙烯酸乙二醇酯1-2、双(二辛氧基焦磷酸酯基)乙撑钛酸酯1-2、乙二醇3-4、二苯胺1-2、氨丙基三乙氧基硅烷1-2、改性助剂3-4；
所述的低温改良剂是由重量比为3-4:2-3的聚烯烃弹性体8200与环氧硬脂酸辛酯混合组成；
所述的改性助剂是由下述重量份的原料组成的：
氯化聚乙烯70-80、eva树脂4-5、氮化铝粉5-6、脂肪酸聚乙二醇酯1-2、硼化铬0.2-0.4、液体石蜡1-2；
将上述脂肪酸聚乙二醇酯与氮化铝粉搅拌混合，加入eva树脂，升高温度至80-90℃，保温1-2小时，加入剩余各原料，1000-1200转/分分散10-15分钟，球磨，烘干，过筛，得2-3μm的颗粒。
2.一种如权利要求1所述的耐低温汽车分电器盖的制备方法，其特征在于包括以下步骤：
将上述二甲基丙烯酸乙二醇酯、氨丙基三乙氧基硅烷与大理石粉混合，预热到70-80℃，送入高速混合机中混制3-5分钟，转速为500-600转/分；将线性低密度聚乙烯、低温改良剂、氧化锌、改性助剂混合，加热到90-100℃，保温1-2小时，滴加乙二醇，滴加完毕后，冷却至常温，低速500-700转/分分散6-8分钟；将上述处理后的各原料与剩余原料混合，搅拌均匀，送入双螺杆挤出机，经双螺杆挤出机挤出，注塑成型。
CN2013102603916A 2013-06-26 2013-06-26 一种耐低温汽车分电器盖 Pending CN103382295A (zh)