CN103382291A - 一种耐高热汽车分电器盖 - Google Patents

一种耐高热汽车分电器盖 Download PDF

Info

Publication number
CN103382291A
CN103382291A CN201310260348XA CN201310260348A CN103382291A CN 103382291 A CN103382291 A CN 103382291A CN 201310260348X A CN201310260348X A CN 201310260348XA CN 201310260348 A CN201310260348 A CN 201310260348A CN 103382291 A CN103382291 A CN 103382291A
Authority
CN
China
Prior art keywords
parts
raw material
mixed
powder
automobile distributor
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201310260348XA
Other languages
English (en)
Inventor
王进
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ANHUI QIAITE ELECTRONIC TECHNOLOGY Co Ltd
Original Assignee
ANHUI QIAITE ELECTRONIC TECHNOLOGY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ANHUI QIAITE ELECTRONIC TECHNOLOGY Co Ltd filed Critical ANHUI QIAITE ELECTRONIC TECHNOLOGY Co Ltd
Priority to CN201310260348XA priority Critical patent/CN103382291A/zh
Publication of CN103382291A publication Critical patent/CN103382291A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种耐高热汽车分电器盖，它是由下述重量份的原料组成的PET树脂100-105、ABS高胶粉15-20、热稳定剂5-6、空心玻璃微珠3-5、蓖麻油酸锌2-4、间苯二甲酸酯2-3、云母粉1-2、脲基丙基三乙氧基硅烷1-2、碳纤维4-5、均苯四酸二酐1-2、乙二醇单丁醚1-2、乙醇1-2、改性助剂3-5超细硫酸钡2-3；本发明原料中增加热稳定剂，大大改善了其耐热性能，可以在200℃环境下长期使用。

Description

一种耐高热汽车分电器盖
技术领域
    本发明主要涉及一种分电器盖，尤其涉及一种耐高热汽车分电器盖。
背景技术
    PET是乳白色或浅黄色高度结晶性的聚合物，表面平滑而有光泽。耐蠕变、抗疲劳性、耐摩擦性好，磨耗小而硬度高，具有热塑性塑料中最大的韧性；电绝缘性能好，受温度影响小，但耐电晕性较差。无毒、耐气候性、抗化学药品稳定性好，吸水率低，耐弱酸和有机溶剂，但不耐热水浸泡，不耐碱。PET树脂的玻璃化温度较高，结晶速度慢，模塑周期长，成型周期长，成型收缩率大，尺寸稳定性差，结晶化的成型呈脆性，耐热性低等；传统生产的汽车分电器盖大多用ABS高胶粉增强改进PET的热变形温度等不良性能，但是汽车分电器盖还是会经常出现裂缝、损毁等，影响了车的正常使用，容易造成安全隐患，因此一种新的、高性能的分电器盖对于汽车事业的发展是很有必要的。
发明内容
本发明目的就是为了提供一种耐高热汽车分电器盖。
本发明是通过以下技术方案实现的：
一种耐高热汽车分电器盖，它是由下述重量份的原料组成的：
PET树脂 100-105、ABS高胶粉15-20、热稳定剂 5-6、空心玻璃微珠3-5、蓖麻油酸锌2-4、间苯二甲酸酯2-3、云母粉1-2、脲基丙基三乙氧基硅烷1-2、碳纤维4-5、均苯四酸二酐1-2、乙二醇单丁醚1-2、乙醇1-2、改性助剂3-5超细硫酸钡2-3；
所述的热稳定剂是由重量比为6-7:1-2的亚磷酸双酚A 酯和二盐基亚磷酸铅混合组成；
所述的改性助剂是由下述重量份的原料组成的：
氯化聚乙烯70-80、eva树脂4-5、氮化铝粉5-6、脂肪酸聚乙二醇酯1-2、硼化铬0.2-0.4、液体石蜡1-2；
将上述脂肪酸聚乙二醇酯与氮化铝粉搅拌混合，加入eva树脂，升高温度至80-90℃，保温1-2小时，加入剩余各原料，1000-1200转/分分散10-15分钟，球磨，烘干，过筛，得2-3μm的颗粒。
一种耐高热汽车分电器盖的制备方法，包括以下步骤：
将上述乙二醇单丁醚与乙醇混合，搅拌溶解后加热至80-90℃，加入云母粉、蓖麻油酸锌，充分搅拌，送入高速混合机中混制3-5分钟，转速为600-700转/分；将ABS高胶粉、碳纤维、均苯四酸二酐、改性助剂混合，充分搅拌后，加热到100-110℃，保温1-2小时，冷却至常温，400-500转/分分散3-4分钟；将上述处理后的各原料与剩余原料混合，搅拌均匀，送入双螺杆挤出机，经双螺杆挤出机挤出，注塑成型。
本发明的优点是：
    本发明原料中增加热稳定剂，大大改善了其耐热性能，可以在200℃环境下长期使用。
具体实施方式
实施例1
一种耐高热汽车分电器盖，它是由下述重量份（公斤）的原料组成的：
PET树脂105、ABS高胶粉20、热稳定剂 6、空心玻璃微珠5、蓖麻油酸锌4、间苯二甲酸酯2、云母粉2、脲基丙基三乙氧基硅烷1、碳纤维5、均苯四酸二酐2、乙二醇单丁醚2、乙醇2、改性助剂3、超细硫酸钡3；
所述的热稳定剂是由重量比为7:2的亚磷酸双酚A 酯和二盐基亚磷酸铅混合组成；
所述的改性助剂是由下述重量份的原料组成的：
氯化聚乙烯80、eva树脂5、氮化铝粉6、脂肪酸聚乙二醇酯2、硼化铬0.4、液体石蜡2；
将上述脂肪酸聚乙二醇酯与氮化铝粉搅拌混合，加入eva树脂，升高温度至90℃，保温2小时，加入剩余各原料， 1200转/分分散15分钟，球磨，烘干，过筛，得3μm的颗粒。
一种耐高热汽车分电器盖的制备方法，包括以下步骤：
将上述乙二醇单丁醚与乙醇混合，搅拌溶解后加热至90℃，加入云母粉、蓖麻油酸锌，充分搅拌，送入高速混合机中混制5分钟，转速为700转/分；将ABS高胶粉、碳纤维、均苯四酸二酐、改性助剂混合，充分搅拌后，加热到110℃，保温2小时，冷却至常温， 500转/分分散4分钟；将上述处理后的各原料与剩余原料混合，搅拌均匀，送入双螺杆挤出机，经双螺杆挤出机挤出，注塑成型。
性能测试：
热变形温度：236℃；
拉伸强度：147.1MPa；
弯曲强度：209MPa；
阻燃性，UL94测定：将用本发明工艺方法制得的试样点燃，把火焰移开后试样在10s内快速自熄，无燃烧的熔体滴落，结果为VO。

Claims (2)

1.一种耐高热汽车分电器盖，其特征在于它是由下述重量份的原料组成的：
PET树脂 100-105、ABS高胶粉15-20、热稳定剂 5-6、空心玻璃微珠3-5、蓖麻油酸锌2-4、间苯二甲酸酯2-3、云母粉1-2、脲基丙基三乙氧基硅烷1-2、碳纤维4-5、均苯四酸二酐1-2、乙二醇单丁醚1-2、乙醇1-2、改性助剂3-5超细硫酸钡2-3；
所述的热稳定剂是由重量比为6-7:1-2的亚磷酸双酚A 酯和二盐基亚磷酸铅混合组成；
所述的改性助剂是由下述重量份的原料组成的：
氯化聚乙烯70-80、eva树脂4-5、氮化铝粉5-6、脂肪酸聚乙二醇酯1-2、硼化铬0.2-0.4、液体石蜡1-2；
将上述脂肪酸聚乙二醇酯与氮化铝粉搅拌混合，加入eva树脂，升高温度至80-90℃，保温1-2小时，加入剩余各原料，1000-1200转/分分散10-15分钟，球磨，烘干，过筛，得2-3μm的颗粒。
2.一种如权利要求1所述的耐高热汽车分电器盖的制备方法，其特征在于包括以下步骤：
将上述乙二醇单丁醚与乙醇混合，搅拌溶解后加热至80-90℃，加入云母粉、蓖麻油酸锌，充分搅拌，送入高速混合机中混制3-5分钟，转速为600-700转/分；将ABS高胶粉、碳纤维、均苯四酸二酐、改性助剂混合，充分搅拌后，加热到100-110℃，保温1-2小时，冷却至常温，400-500转/分分散3-4分钟；将上述处理后的各原料与剩余原料混合，搅拌均匀，送入双螺杆挤出机，经双螺杆挤出机挤出，注塑成型。
CN201310260348XA 2013-06-26 2013-06-26 一种耐高热汽车分电器盖 Pending CN103382291A (zh)