CN103382102A - 一种低温烧结镍锌铜软磁铁氧体材料及其制备方法 - Google Patents

一种低温烧结镍锌铜软磁铁氧体材料及其制备方法 Download PDF

Info

Publication number
CN103382102A
CN103382102A CN2013102589355A CN201310258935A CN103382102A CN 103382102 A CN103382102 A CN 103382102A CN 2013102589355 A CN2013102589355 A CN 2013102589355A CN 201310258935 A CN201310258935 A CN 201310258935A CN 103382102 A CN103382102 A CN 103382102A
Authority
CN
China
Prior art keywords
hour
temperature
soft magnetic
zinc
magnetic ferrite
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2013102589355A
Other languages
English (en)
Other versions
CN103382102B (zh
Inventor
肖宪书
文庆华
张俊
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
BENGBU CITY GAOHUA ELECTRONIC Co Ltd
Original Assignee
BENGBU CITY GAOHUA ELECTRONIC Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by BENGBU CITY GAOHUA ELECTRONIC Co Ltd filed Critical BENGBU CITY GAOHUA ELECTRONIC Co Ltd
Priority to CN201310258935.5A priority Critical patent/CN103382102B/zh
Publication of CN103382102A publication Critical patent/CN103382102A/zh
Application granted granted Critical
Publication of CN103382102B publication Critical patent/CN103382102B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种低温烧结镍锌铜软磁铁氧体材料及其制备方法，其特征在于：主成分按摩尔份计包括：23.5-25molFe2O3、19-19.5molMnO、6-6.5molZnO、2.3-2.5molNiO、4.3-4.5molCuO，主成分中添加的改性杂质按照占所述低温烧结镍锌铜软磁铁氧体材料的重量百分比计包括：480-520ppmCaCO3、380-420ppmNiO、410-420ppmBi2O3、80-120ppm硼化钨、80-120ppmV；本发明的优点在于能够为叠层片式电感器提供稳定性更好、致密度更高、磁导率更高的低温烧结镍锌铜软磁铁氧体材料，而且不增加生产周期和成本，适合工业化推广。

Description

一种低温烧结镍锌铜软磁铁氧体材料及其制备方法
技术领域
本发明涉及磁性材料技术领域，具体地，本发明涉及一种低温烧结镍锌铜软磁铁氧体材料及其制备方法。
背景技术
磁通密度高铁氧体磁粉、磁芯是实现程控通讯、数字技术、网络通讯彩电等电子设备中用作电感器、滤波器、脉冲变压器等产品使其小型化、轻量化必不可少的电子材料，不断提高磁性材料中的磁通密度，一直是从事该专业的工程技术人员和生产厂商的追求，且材料的性能指标，如损耗、频率特性、居里温度等都不尽人意。
发明内容
本发明的目的是提供一种低温烧结镍锌铜软磁铁氧体材料及其制备方法。
本发明所采用的技术方案是：  
    一种低温烧结镍锌铜软磁铁氧体材料，其特征在于,主成分按摩尔份计包括：23.5-25molFe2O3、19-19.5molMnO、6-6.5molZnO、2.3-2.5molNiO、4.3-4.5molCuO,主成分中添加的改性杂质按照占所述低温烧结镍锌铜软磁铁氧体材料的重量百分比计包括：480-520ppmCaCO3、380-420ppmNiO、410-420ppm Bi2O3、80-120ppm硼化钨、80-120ppm V；
    所述的低温烧结镍锌铜软磁铁氧体材料的制备方法，其特征在于包括以下步骤：
   （1）配料：将主成分进行配料，并添加改性杂质；
   （2）一次烧结：配料混合在870℃-920℃的条件下预烧2-3小时得预烧料；
   （3）球磨：将预烧料放入砂磨机中，同时加入相当于配料0.6-1.0wt%聚乙烯醇、1.2-1.6wt%分散料、适量去离子水进行砂磨90-120分钟，得浆料，并烘干；
   （4）压制成型：将烘干的粉料加入1.2-1.8wt%的聚乙烯醇、0.2-0.4wt%的硬酯酸锌，造粒，装入模具，在75-85Mpa压力下压制成坯件，自然晾干；
   （5）二次烧结：将磁芯毛坯放入氮气气氛保护推板窑内，在氧含量为0.6%-0.8%的氮气氛中烧结，烧结先以160-180℃/小时的升温速率升至700-720℃；再调整氧含量为1-2%，以100-120℃/小时的升温速率由1200-1250℃，保温2-3小时，再以60-80℃/小时的升温速率升至1370-1420℃，保温烧结5-6小时；然后降温，调整氧含量0.3%-0.4%，先以80-100℃/小时的降温速率降温至720-750℃，再以200-250℃/小时的降温速率降温至室温。
步骤（3）中所述的分散料由以下重量份的原料制得：聚乙烯醇3-4、硬脂酸锌2-3、Bi2O30.2-0.3、氨丙基三乙氧基硅烷0.5-0.8、氮化铝1-1.3、Nb2O5 0.3-0.5、硫酸钡1.2-1.4、石油磺酸钠0.6-0.9；
制备方法是：将各物料混合，研磨分散均匀即可。
    本发明的优点在于能够为叠层片式电感器提供稳定性更好、致密度更高、磁导率更高的低温烧结镍锌铜软磁铁氧体材料，而且不增加生产周期和成本，适合工业化推广。
具体实施方式    
    一种低温烧结镍锌铜软磁铁氧体材料，主成分按摩尔份计包括：25molFe2O3、19.5molMnO、6molZnO、2.5molNiO、4.5molCuO,主成分中添加的改性杂质按照占所述低温烧结镍锌铜软磁铁氧体材料的重量百分比计包括：520ppmCaCO3、380ppmNiO、420ppm Bi2O3、120ppm硼化钨、120ppm V；
    所述的低温烧结镍锌铜软磁铁氧体材料的制备方法，其特征在于包括以下步骤：
   （1）配料：将主成分进行配料，并添加改性杂质；
   （2）一次烧结：配料混合在870℃-920℃的条件下预烧2-3小时得预烧料；
   （3）球磨：将预烧料放入砂磨机中，同时加入相当于配料0.6-1.0wt%聚乙烯醇、1.2-1.6wt%分散料、适量去离子水进行砂磨90-120分钟，得浆料，并烘干；
   （4）压制成型：将烘干的粉料加入1.2-1.8wt%的聚乙烯醇、0.2-0.4wt%的硬酯酸锌，造粒，装入模具，在75-85Mpa压力下压制成坯件，自然晾干；
   （5）二次烧结：将磁芯毛坯放入氮气气氛保护推板窑内，在氧含量为0.6%-0.8%的氮气氛中烧结，烧结先以160-180℃/小时的升温速率升至700-720℃；再调整氧含量为1-2%，以100-120℃/小时的升温速率由1200-1250℃，保温2-3小时，再以60-80℃/小时的升温速率升至1370-1420℃，保温烧结5-6小时；然后降温，调整氧含量0.3%-0.4%，先以80-100℃/小时的降温速率降温至720-750℃，再以200-250℃/小时的降温速率降温至室温；
步骤（3）中所述的分散料由以下重量份（公斤）的原料制得：聚乙烯醇4、硬脂酸锌3、Bi2O30.3、氨丙基三乙氧基硅烷0.8、氮化铝1、Nb2O5 0.5、硫酸钡1.4、石油磺酸钠0.9；
制备方法是：将各物料混合，研磨分散均匀即可。
通过上述实施例制得的软磁铁氧体磁芯的性能数据：
序号 技术指标名称 技术指标 备注
1 初始磁导率（25±3℃） 8300±25%  
2 功率损耗（100Kc、200mT）单位：KW/m3 613(25±2℃), 305(100±2℃)  
3 饱和磁通密度mT（100℃） 493  
4 居里温度℃ >265  

Claims (2)

1.一种低温烧结镍锌铜软磁铁氧体材料，其特征在于,主成分按摩尔份计包括：23.5-25molFe2O3、19-19.5molMnO、6-6.5molZnO、2.3-2.5molNiO、4.3-4.5molCuO,主成分中添加的改性杂质包括：480-520ppmCaCO3、380-420ppmNiO、410-420ppm Bi2O3、80-120ppm硼化钨、80-120ppm V。
2.根据权利要求1所述的低温烧结镍锌铜软磁铁氧体材料的制备方法，其特征在于包括以下步骤：
（1）配料：将主成分进行配料，并添加改性杂质；
（2）一次烧结：配料混合在870℃-920℃的条件下预烧2-3小时得预烧料；
（3）球磨：将预烧料放入砂磨机中，同时加入相当于配料0.6-1.0wt%聚乙烯醇、1.2-1.6wt%分散料、适量去离子水进行砂磨90-120分钟，得浆料，并烘干；
（4）压制成型：将烘干的粉料加入1.2-1.8wt%的聚乙烯醇、0.2-0.4wt%的硬酯酸锌，造粒，装入模具，在75-85Mpa压力下压制成坯件，自然晾干；
（5）二次烧结：将磁芯毛坯放入氮气气氛保护推板窑内，在氧含量为0.6%-0.8%的氮气氛中烧结，烧结先以160-180℃/小时的升温速率升至700-720℃；再调整氧含量为1-2%，以100-120℃/小时的升温速率由1200-1250℃，保温2-3小时，再以60-80℃/小时的升温速率升至1370-1420℃，保温烧结5-6小时；然后降温，调整氧含量0.3%-0.4%，先以80-100℃/小时的降温速率降温至720-750℃，再以200-250℃/小时的降温速率降温至室温；
    步骤（3）中所述的分散料由以下重量份的原料制得：聚乙烯醇3-4、硬脂酸锌2-3、Bi2O30.2-0.3、氨丙基三乙氧基硅烷0.5-0.8、氮化铝1-1.3、Nb2O5 0.3-0.5、硫酸钡1.2-1.4、石油磺酸钠0.6-0.9；
制备方法是：将各物料混合，研磨分散均匀即可。
CN201310258935.5A 2013-06-26 2013-06-26 一种低温烧结镍锌铜软磁铁氧体材料及其制备方法 Expired - Fee Related CN103382102B (zh)