CN103382094A - Anti-corrosion anti-erosion heat-preservation mortar - Google Patents
Anti-corrosion anti-erosion heat-preservation mortar Download PDFInfo
- Publication number
- CN103382094A CN103382094A CN2013103142419A CN201310314241A CN103382094A CN 103382094 A CN103382094 A CN 103382094A CN 2013103142419 A CN2013103142419 A CN 2013103142419A CN 201310314241 A CN201310314241 A CN 201310314241A CN 103382094 A CN103382094 A CN 103382094A
- Authority
- CN
- China
- Prior art keywords
- parts
- erosion
- anticorrosion
- corrosion
- weight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses an anti-corrosion anti-erosion heat-preservation mortar. The anti-corrosion anti-erosion heat-preservation mortar is made of raw materials of, by weight, 4-6 parts of polypropylene fiber, 300-400 parts of common Portland cement, 80-100 parts of expanded perlite powder, 5-7 parts of white latex, 1-2 parts of epoxy soybean oil, 5-7 parts of modified straw ash, 1-2 parts of molasses calcium, 8-15 parts of river sand, 0.05-0.2 part of organosilicone, 1-2 parts of methacrylic acid, 0.1-0.3 part of aluminum stearate, 0.1-0.3 part of barium stearate, 0.1-0.2 part of tert-butyl benzoate, 3.8-5 parts of sodium hydroxide, 1-2 parts of chitosan, 0.04-0.06 part of hydroxyethyl cellulose, 0.04-0.06 part of sodium persulfate, 0.2-0.4 part of calcium metasilicate and 0.1-0.2 part of sodium benzoate. The anti-corrosion anti-erosion heat-preservation mortar has a strong anti-corrosion anti-erosion capacity, a water reducing function and a prolonged service life.
Description
Technical field
The present invention relates to the thermal insulation mortar field, is exactly a kind of anticorrosion anti-erosion thermal insulation mortar.
Background technology
Thermal insulation mortar is take various light materials as aggregate, take cement as gelating material, admixes some property-modifying additives, mixes and a kind of premixing dry-mix of making through manufacturing enterprise.Be mainly used in building exterior wall heat preserving, have the advantages such as easy construction, good endurance.
Summary of the invention
The object of the present invention is to provide a kind of anticorrosion anti-erosion thermal insulation mortar
Above-mentioned purpose realizes by following scheme:
a kind of anticorrosion anti-erosion thermal insulation mortar, it is characterized in that: it is that raw material by following weight parts makes: polypropylene fibre 4-6, ordinary Portland cement 300-400, swelling perlite powder 80-100, white glue with vinyl 5-7, epoxy soybean oil 1-2, modified straw ashes 5-7, sugar calcium 1-2, river sand 8-15, organosilicon 0.05-0.2, methacrylic acid 1-2, aluminum stearate 0.1-0.3, barium stearate 0.1-0.3, the special fourth 0.1-0.2 of phenylformic acid, sodium hydroxide 3.8-5, chitosan 1-2, Natvosol 0.04-0.06, Potassium Persulphate 0.04-0.06, Calucium Silicate powder 0.2-0.4, Sodium Benzoate 0.1-0.2, suitable quantity of water.
Described a kind of anticorrosion anti-erosion thermal insulation mortar is characterized in that:
The preparation method is:
(1) the stalk ashes being put into concentration is that the acetic acid solution of 5-8% soaked 8-10 hour, take out, deionized water wash, oven dry adds the polyoxyethylene nonylphenol ether of the silane coupling agent KH530, the 0.1-0.2% that are equivalent to its weight 0.8-1.5%, the antioxidant 2246 of 1-2%, the tetraethoxy of 1-2%, and appropriate water, under 800-1000rpm after high-speed stirring 10-15 minute, take out, oven dry namely gets the modified straw ashes standby;
(2) the special fourth of epoxy soybean oil, sugared calcium, river sand, organosilicon, methacrylic acid, aluminum stearate, barium stearate, phenylformic acid mixing by weight, add again and be equivalent to above-mentioned raw materials gross weight 2-3 water doubly, stirred 10-20 minute under 30-35 ℃, get anticorrosion annex solution standby;
(3) with ordinary Portland cement, swelling perlite powder, modified straw ashes mixing, then add anticorrosion annex solution, stir; Add again surplus stock, stirred 20-30 minute under 25-35 ℃, and get final product.
Beneficial effect of the present invention is: the present invention has very strong anticorrosion corrosion resistance, has simultaneously the diminishing function, can extend its work-ing life.Sugar calcium is a kind of good water reducer, greatly improves water-reducing rate.
Embodiment
A kind of anticorrosion anti-erosion thermal insulation mortar, it is that raw material by following weight parts (kg) makes: polypropylene fibre 6, ordinary Portland cement 300, swelling perlite powder 100, white glue with vinyl 7, epoxy soybean oil 2, modified straw ashes 7, sugared calcium 2, river sand 15, organosilicon 0.2, methacrylic acid 2, aluminum stearate 0.3, barium stearate 0.3, the special fourth 0.2 of phenylformic acid, sodium hydroxide 5, chitosan 1, Natvosol 0.06, Potassium Persulphate 0.06, Calucium Silicate powder 0.4, Sodium Benzoate 0.2, suitable quantity of water.
Described a kind of anticorrosion anti-erosion thermal insulation mortar,
The preparation method is:
(1) the stalk ashes being put into concentration is that 7% acetic acid solution soaked 10 hours, take out, deionized water wash, oven dry adds the silane coupling agent KH530 that is equivalent to its weight 0.8%, 0.2% polyoxyethylene nonylphenol ether, 2% antioxidant 2246,2% tetraethoxy, and appropriate water, under 1000rpm, high-speed stirring is after 10 minutes, take out, oven dry namely gets the modified straw ashes standby;
(2) the special fourth of epoxy soybean oil, sugared calcium, river sand, organosilicon, methacrylic acid, aluminum stearate, barium stearate, phenylformic acid mixing by weight, add again the water that is equivalent to 3 times of above-mentioned raw materials gross weights, stirred 20 minutes under 32 ℃, get anticorrosion annex solution standby;
(3) with ordinary Portland cement, swelling perlite powder, modified straw ashes mixing, then add anticorrosion annex solution, stir; Add again surplus stock, stirred 30 minutes under 35 ℃, and get final product.
The products obtained therefrom test result is as follows:
Claims (2)
1. anticorrosion anti-erosion thermal insulation mortar, it is characterized in that: it is that raw material by following weight parts makes: polypropylene fibre 4-6, ordinary Portland cement 300-400, swelling perlite powder 80-100, white glue with vinyl 5-7, epoxy soybean oil 1-2, modified straw ashes 5-7, sugar calcium 1-2, river sand 8-15, organosilicon 0.05-0.2, methacrylic acid 1-2, aluminum stearate 0.1-0.3, barium stearate 0.1-0.3, the special fourth 0.1-0.2 of phenylformic acid, sodium hydroxide 3.8-5, chitosan 1-2, Natvosol 0.04-0.06, Potassium Persulphate 0.04-0.06, Calucium Silicate powder 0.2-0.4, Sodium Benzoate 0.1-0.2, suitable quantity of water.
2. a kind of anticorrosion anti-erosion thermal insulation mortar according to claim 1 is characterized in that:
The preparation method is:
(1) the stalk ashes being put into concentration is that the acetic acid solution of 5-8% soaked 8-10 hour, take out, deionized water wash, oven dry adds the polyoxyethylene nonylphenol ether of the silane coupling agent KH530, the 0.1-0.2% that are equivalent to its weight 0.8-1.5%, the antioxidant 2246 of 1-2%, the tetraethoxy of 1-2%, and appropriate water, under 800-1000rpm after high-speed stirring 10-15 minute, take out, oven dry namely gets the modified straw ashes standby;
(2) the special fourth of epoxy soybean oil, sugared calcium, river sand, organosilicon, methacrylic acid, aluminum stearate, barium stearate, phenylformic acid mixing by weight, add again and be equivalent to above-mentioned raw materials gross weight 2-3 water doubly, stirred 10-20 minute under 30-35 ℃, get anticorrosion annex solution standby;
(3) with ordinary Portland cement, swelling perlite powder, modified straw ashes mixing, then add anticorrosion annex solution, stir; Add again surplus stock, stirred 20-30 minute under 25-35 ℃, and get final product.