CN103361800A - Quickly-dyed yarn or fabric with camaieu effect and processing and application of yarn or fabric - Google Patents
Quickly-dyed yarn or fabric with camaieu effect and processing and application of yarn or fabric Download PDFInfo
- Publication number
- CN103361800A CN103361800A CN2012101036514A CN201210103651A CN103361800A CN 103361800 A CN103361800 A CN 103361800A CN 2012101036514 A CN2012101036514 A CN 2012101036514A CN 201210103651 A CN201210103651 A CN 201210103651A CN 103361800 A CN103361800 A CN 103361800A
- Authority
- CN
- China
- Prior art keywords
- fiber
- yarn
- fabric
- resin
- dye
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to a quickly-dyed yarn or fabric with a camaieu effect and a manufacturing method of the yarn or the fabric. The quickly-dyed yarn or the fabric with the camaieu effect is characterized in that a fiber subjected to resin finishing and a fiber not subjected to the resin finishing, a bleached fiber or a boiling-off fiber are spun into a yarn by different spinning technologies, baked and then dyed to form the yarn with the camaieu effect, or white fabric woven by yarns subjected to the resin finishing and the fibers not subjected to the resin finishing or the bleached fibers is baked and then dyed to form the fabric with the camaieu effect. The yarn or the white fabric produced by the technological method can be subjected to once dyeing to form the yarn or the fabric with a special flower gray effect and a camaieu changing style, and the yarn or the fabric can serve as an excellent raw material of a high-grade undergarment, a T-shirt, sportswear and the like.
Description
Technical field
The present invention relates to a kind of yarn that can dye and have fast camaieu effect or fabric and preparation method thereof and use.
Background technology
Cellulose fibre is by RESIN FINISH, and after baking, molecular resin can at fibrous inside and surface-crosslinked, obviously improve the performance of fabric.Because the resin crosslinks through baking formation has good persistence, general washing can't be removed it, and dye molecule is difficult to enter into fibrous inside in dyeing course, therefore the fiber of resin treatment is not painted substantially or slight staining.
The fiber of resin treatment is evenly mixed and spinning with special ratios and untreatment fiber or bleached fiber, use the cellulose dyeing common dyes, such as REACTIVE DYES, direct dyes, SULPHUR DYES or soluble vat dye etc., resultant yarn is dyeed, can have the Fancy Yarns of the dim sense outward appearance of " spending ash ".Wherein, under the ordinary stain condition, untreatment fiber or bleached fiber can normally be colored, and the fiber of resin treatment is not painted substantially or slight staining, therefore, be untreated by change or the degree of bleached fiber composition can be regulated the depth of Fancy Yarns color.
Summary of the invention
The object of the present invention is to provide a kind of yarn that can dye and have fast camaieu effect or fabric and preparation method thereof, the yarn that can dye and have fast camaieu effect of the present invention or fabric be for will be through resin treatment fiber and yarn, the resin treatment yarn of different spinning styles or the white fabrics that further is made into again without the different proportionings of resin treatment fiber, and dialogue dyed yarn line or white fabrics dye and get again after baking.
To achieve these goals, the present invention adopts following technical scheme:
A kind of yarn or fabric that can dye and have fast camaieu effect, the described yarn that can dye and have fast camaieu effect for will without fiber, bleached fiber or the kiering fiber of resin treatment be spun into white yarn through the fiber mixing of resin treatment by the spinning process of different spinning styles, with the acquisition of dyeing again behind the white drying yarn that obtains; The described fabric that can dye and have fast camaieu effect for will without fiber, bleached fiber or the kiering fiber of resin treatment be spun into white yarn through the fiber mixing of resin treatment by the spinning process of different spinning styles, the white yarn that obtains is made into first white fabrics, obtains after drying, the dyeing successively again.
Yarn or the fabric that can dye and have fast camaieu effect of the present invention, its dark part or the corresponding fiber of dark point are fiber, bleached fiber or the kiering fiber without resin treatment, and its light-colored part or the corresponding fiber of light color point are the fiber through resin treatment.Be generally dark part and echo mutually yarn or the fabric that forms camaieu effect with light-colored part, dark point echoes yarn or the fabric that forms camaieu effect mutually with the light color point.
Better, described fiber without resin treatment, bleached fiber, kiering fiber and be one or more cellulose fibres through the composition of the fiber of resin treatment.
Further, described fiber without resin treatment, bleached fiber, kiering fiber and all be selected from cotton fiber, viscose, Modal fibre, flax fibre and the tencel fiber etc. one or more through the fiber of resin treatment.
Better, described fiber without resin treatment, bleached fiber or kiering fiber are (0.5-99.5) % with percentage by weight through the fiber of resin treatment: (0.5-99.5) %.Preferably, both percentage by weights are (5-95) %: (5-95) %.
Better, described fiber through resin treatment gets for cellulose fibre is carried out RESIN FINISH under the bulk fibre state.Wherein, described resin comprises resin finishing agent, catalyst, bleeding agent and water, and the main component of described resin is:
Resin finishing agent 10-300 grams per liter; Be preferably the 30-150 grams per liter;
Catalyst 0.5-50 grams per liter; Be preferably the 3-30 grams per liter;
Bleeding agent 0.1-10 grams per liter; Be preferably the 1-3 grams per liter;
When adopting RESIN FINISH, adopt 1: 1-1: 50 bath raio, in 1-70 ℃ water-bath, place the resin dipping after 1-80 minute cellulose fibre, take out dewatered drying and get final product.Preferably, adopt 1: 5-1: 10 bath raio.
Preferably, the temperature of described water-bath is 20-70 ℃, and the time of dipping is 20-60 minute.
Further, described resin finishing agent is the resin finishing agent of cross-linking type, as: 2D resin, etherified 2D resin, polyurethanes crosslinking agent etc.Described resin finishing agent is preferably the SOFTENER PRB Arkofix PCLN lip c resin finishing agent of Ke Laien.
Further, described catalyst is halide, sulfate etc.; Described halide is preferably magnesium chloride.
Further, described bleeding agent is anion-permeable membrane agent or nonionic penetrant commonly used; Preferably, described bleeding agent is selected from the JFC bleeding agent of development of evil in febrile disease chemical industry Zhejiang Province Chuanhua Co., Ltd.
Better, the spinning process of described different spinning styles is the spinning process of common style, the spinning process of AB yarn style, the spinning process of slub yarn style or the spinning process of kinckebocker yarn style etc.
Common style of the present invention is as adopting the common spinning process of RING SPINNING, described AB yarn style can adopt match network spinning process, the spinning process of described slub yarn style is as adopting the frequency conversion spinning process of RING SPINNING, and the spinning process of described kinckebocker yarn style is as adopting the spinning process of RING SPINNING or open-end spinning.
Better, described white yarn or the drying condition of white fabrics before dyeing are and bake 0.5-5 minute under 100-180 ℃.
Preferably, described white yarn and the drying condition of white fabrics before dyeing are and bake 2-4 minute under 140-160 ℃.
Better, described white yarn and white fabrics all adopt one-step method dyeing, and the dyestuff that adopts during dyeing is REACTIVE DYES, direct dyes, SULPHUR DYES or soluble vat dye.Owing to adopting homochromy dyestuff during dyeing, therefore forming yarn or the fabric of camaieu effect.
Bath raio during one-step method dyeing of the present invention, as be generally (1: 3)-(1: 50); The percentage by weight of the dyestuff in the dye liquor, as be generally 0.01-20.0%.
Yarn or the fabric that can dye and have fast camaieu effect of the present invention, the main REACTIVE DYES that adopts dyes to the white fabrics after baking, as COLOR FASTNESS etc. is had specific (special) requirements, also can use other dyestuff (such as direct dyes, SULPHUR DYES or soluble vat dye etc.), colouring method adopts normal dyeing to get final product.
The white yarn and the white fabrics that adopt process of the present invention to obtain can be used for disposable dyeing and dye and have special yarn and the fabric of spending grey effect, homochromy depth change style.In addition, this has special yarn and the fabric of spending grey effect, is the excellent raw material of the products such as producing high-grade underwear, T-shirt, Casual Wear.
The specific embodiment
Further set forth the present invention below in conjunction with specific embodiment, should be understood that these embodiment only are used for explanation the present invention and are not used in restriction protection scope of the present invention.
Resin finishing agent among following each embodiment is that the resin finishing agent of cross-linking type is the SOFTENER PRB Arkofix PCLN lip c resin finishing agent of Ke Laien; Catalyst is magnesium chloride; Bleeding agent is the JFC bleeding agent of development of evil in febrile disease chemical industry Zhejiang Province Chuanhua Co., Ltd.Below the percentage composition of each fiber be weight percentage.
Bath raio when the one-step method among following each embodiment dyes is (1: 10); The percentage by weight of the dyestuff in the dye liquor is 1.0%.
Embodiment 1:
Select 100 kilograms of cotton bulk fibres, after conventional kiering or bleaching pre-treatment, again 60 kilograms cotton bulk fibre being put into bath raio is 1: 10, contain in the solution of 80 grams per liter resin finishing agents, 10 grams per liter magnesium chlorides, bleeding agent 2 grams per liters, be warmed up to 60 ℃ of dippings after 30 minutes, dewatered drying obtains the resin treatment fiber.Resin treatment fiber with 60% (60 kilograms) and 40% bleached fiber or kiering fiber (40 kilograms) evenly mixes and be spun into white yarn with the spinning process of common style, then be made into common white plain cloth, under 160 ℃, bake 2 minutes.The white plain cloth is used red reactive dyes 3BS and is dyeed by normal colouring method, can get the fabric of the resultful red depth effect of tool.
The white yarn that obtains is baked 2 minutes under 160 ℃, then adopt red reactive dyes 3BS to dye by normal colouring method, can get the yarn of the resultful red depth effect of tool.
Embodiment 2:
Select 100 kilograms of model bulk fibres, after conventional kiering pre-treatment, again 85 kilograms model bulk fibre being put into bath raio is 1: 8, contain in the solution of 100 grams per liter resin finishing agents, 12 grams per liter magnesium chlorides, bleeding agent 2 grams per liters, be warmed up to 60 ℃ of dippings after 45 minutes, dewatered drying obtains the resin treatment fiber.Resin treatment fiber with 85% (85 kilograms) and 15% white Modal fibre (15 kilograms) evenly mix and are spun into white yarn with the spinning process of slub yarn style, then be made into common white plain cloth, under 160 ℃, bake 2 minutes.The white plain cloth is used blue SULPHUR DYES Diresul Blue RDT-3R 80 and is dyeed by normal colouring method, can get the fabric of the resultful blue depth effect of tool.
The white yarn that obtains is baked 2 minutes under 160 ℃, then adopt blue SULPHUR DYES Diresul Blue RDT-3R80 to dye by normal colouring method, can get the yarn of the resultful blue depth effect of tool.
Embodiment 3:
Select 100 kilograms of sky silk bulk fibres, after conventional kiering pre-treatment, again 50 kilograms sky silk bulk fibre being put into bath raio is 1: 15, contain in the solution of 30 grams per liter resin finishing agents, 3 grams per liter magnesium chlorides, bleeding agent 2 grams per liters, be warmed up to 50 ℃ of dippings after 60 minutes, dewatered drying obtains the resin treatment fiber.Resin treatment fiber with 50% (50 kilograms) and 50% silk fiber on daytime (50 kilograms) evenly mix, and are spun into white yarn with the spinning process of AB yarn style, then are made into common white plain cloth, bake 2 minutes under 160 ℃.The white plain cloth is used yellow direct dyes K-CF and is dyeed by normal colouring method, can get the fabric of the resultful yellow depth effect of tool.
The white yarn that obtains is baked 2 minutes under 160 ℃, then adopt yellow direct dyes K-CF to dye by normal colouring method, can get the yarn of the resultful yellow depth effect of tool.
Embodiment 4:
Select each 50 kilograms of cotton bulk fibre and numb bulk fibres, respectively after conventional kiering pre-treatment, putting into respectively bath raio is 1: 10, contain in the solution of 50 grams per liter resin finishing agents, 6 grams per liter magnesium chlorides, bleeding agent 2 grams per liters, be warmed up to 70 ℃ of dippings after 20 minutes, dewatered drying obtains respectively resin treatment cotton fiber and resin treatment flax fibre.Resin treatment cotton fiber with 30% (30 kilograms) and 30% resin treatment flax fibre (30 kilograms) evenly mix with 40% bleached cotton fiber (40 kilograms) and are spun into white yarn with the spinning process of common style, then be made into common white plain cloth, under 160 ℃, bake 2 minutes.The white plain cloth is used black and active dye super black R and is dyeed by normal colouring method, can get the fabric of the resultful black depth of tool effect.
The white yarn that obtains is baked 2 minutes under 160 ℃, then adopt black and active dye super black R to dye by normal colouring method, can get the yarn of the resultful black depth of tool effect.
Embodiment 5:
Select 100 kilograms of cotton bulk fibres, after conventional kiering or bleaching pre-treatment, again 5 kilograms cotton bulk fibre being put into bath raio is 1: 10, contain in the solution of 80 grams per liter resin finishing agents, 10 grams per liter magnesium chlorides, bleeding agent 3 grams per liters, be warmed up to 60 ℃ of dippings after 30 minutes, dewatered drying obtains the resin treatment fiber.Resin treatment fiber with 5% (5 kilograms) and 95% bleached fiber (95 kilograms) evenly mix and are spun into white yarn with the spinning process of common style, then are made into common white plain cloth, bake 2 minutes under 160 ℃.The white plain cloth is used red reactive dyes 3BS and is dyeed by normal colouring method, can get the fabric of the resultful red depth effect of tool.
The white yarn that obtains is baked 2 minutes under 160 ℃, then adopt red reactive dyes 3BS to dye by normal colouring method, can get the yarn of the resultful red depth effect of tool.
Embodiment 6:
Select 100 kilograms of model bulk fibres, after conventional kiering pre-treatment, again 95 kilograms model bulk fibre being put into bath raio is 1: 20, contain in the solution of 120 grams per liter resin finishing agents, 30 grams per liter magnesium chlorides, bleeding agent 8 grams per liters, be warmed up to 60 ℃ of dippings after 45 minutes, dewatered drying obtains the resin treatment fiber.Resin treatment fiber with 95% (95 kilograms) and 5% white Modal fibre (5 kilograms) evenly mix and are spun into white yarn with the spinning process of slub yarn style, then are made into common white plain cloth, bake 2 minutes under 160 ℃.The white plain cloth is used blue SULPHUR DYES Diresul Blue RDT-3R 80 and is dyeed by normal colouring method, can get the fabric of the resultful blue depth effect of tool.
The white yarn that obtains is baked 2 minutes under 160 ℃, then adopt blue SULPHUR DYES Diresul Blue RDT-3R80 to dye by normal colouring method, can get the yarn of the resultful blue depth effect of tool.
Embodiment 7:
Select 100 kilograms of sky silk bulk fibres, after conventional kiering pre-treatment, again 50 kilograms sky silk bulk fibre being put into bath raio is 1: 15, contain in the solution of 30 grams per liter resin finishing agents, 3 grams per liter magnesium chlorides, bleeding agent 1 grams per liter, be warmed up to 20 ℃ of dippings after 60 minutes, dewatered drying obtains the resin treatment fiber.Resin treatment fiber with 50% and 50% silk fiber on daytime evenly mix, and are spun into white yarn with the spinning process of AB yarn style, then are made into common white plain cloth, bake 4 minutes under 140 ℃.The white plain cloth is used yellow direct dyes K-CF and is dyeed by normal colouring method, can get the fabric of the resultful yellow depth effect of tool.
The white yarn that obtains is baked 4 minutes under 140 ℃, then adopt yellow direct dyes K-CF to dye by normal colouring method, can get the yarn of the resultful yellow depth effect of tool.
Embodiment 8:
Select each 50 kilograms of cotton bulk fibre and numb bulk fibres, respectively after conventional kiering pre-treatment, putting into respectively bath raio is 1: 12, contain in the solution of 50 grams per liter resin finishing agents, 6 grams per liter magnesium chlorides, bleeding agent 2 grams per liters, be warmed up to 70 ℃ of dippings after 20 minutes, dewatered drying obtains the resin treatment fiber.Resin treatment cotton fiber with 30% and 30% resin treatment flax fibre evenly mix with 40% bleached cotton fiber and are spun into white yarn with the spinning process of common style, then are made into common white plain cloth, bake 3 minutes under 150 ℃.The white plain cloth is used black and active dye super black R and is dyeed by normal colouring method, can get the fabric of the resultful black depth of tool effect.
The white yarn that obtains is baked 3 minutes under 150 ℃, then adopt black and active dye super black R to dye by normal colouring method, can get the yarn of the resultful black depth of tool effect.
Embodiment 9:
Select 100 kilograms of cotton bulk fibres, after conventional kiering or bleaching pre-treatment, putting it into bath raio is 1: 10 again, contain in the solution of 150 grams per liter resin finishing agents, 15 grams per liter magnesium chlorides, bleeding agent 5 grams per liters, be warmed up to 60 ℃ of dippings after 30 minutes, dewatered drying obtains the resin treatment fiber.Resin treatment fiber with 5% and 95% bleached fiber evenly mix and are spun into white yarn with the spinning process of common style, then are made into common white plain cloth, bake 2 minutes under 160 ℃.The white plain cloth is used red reactive dyes 3BS and is dyeed by normal colouring method, can get the fabric of the resultful red depth effect of tool.
The white yarn that obtains is baked 2 minutes under 160 ℃, then adopt red reactive dyes 3BS to dye by normal colouring method, can get the yarn of the resultful red depth effect of tool.
Claims (12)
1. yarn or fabric that can dye and have fast camaieu effect, the described yarn that can dye and have fast camaieu effect for will without fiber, bleached fiber or the kiering fiber of resin treatment be spun into white yarn through the fiber mixing of resin treatment by the spinning process of different spinning styles, with the acquisition of dyeing again behind the white drying yarn that obtains; The described fabric that can dye and have fast camaieu effect for will without fiber, bleached fiber or the kiering fiber of resin treatment be spun into white yarn through the fiber mixing of resin treatment by the spinning process of different spinning styles, the white yarn that obtains is made into first white fabrics, obtains after drying, the dyeing successively again.
2. yarn or the fabric that can dye and have fast camaieu effect as claimed in claim 1, it is characterized in that, the dark part of the described yarn that can dye and have fast camaieu effect or fabric or the corresponding fiber of dark point are fiber, bleached fiber or kiering fiber without resin treatment, and its light-colored part or the corresponding fiber of light color point are the fiber through resin treatment.
3. yarn or the fabric that can dye and have fast camaieu effect as claimed in claim 1, it is characterized in that described fiber without resin treatment, bleached fiber, kiering fiber and be one or more cellulose fibres through the composition of the fiber of resin treatment.
4. yarn or the fabric that can dye and have fast camaieu effect as claimed in claim 3, it is characterized in that described fiber without resin treatment, bleached fiber, kiering fiber and all be selected from cotton fiber, viscose, Modal fibre, flax fibre and the tencel fiber one or more through the fiber of resin treatment.
5. yarn or the fabric that can dye and have fast camaieu effect as claimed in claim 1, it is characterized in that, described fiber without resin treatment, bleached fiber or kiering fiber are (0.5-99.5) % with percentage by weight through the fiber of resin treatment: (0.5-99.5) %.
6. yarn or the fabric that can dye and have fast camaieu effect as claimed in claim 1 is characterized in that, described fiber through resin treatment gets for cellulose fibre is carried out RESIN FINISH under the bulk fibre state; Wherein, described resin comprises resin finishing agent, catalyst, bleeding agent and water, and the main component of described resin is:
Resin finishing agent 10-300 grams per liter;
Catalyst 0.5-50 grams per liter;
Bleeding agent 0.1-10 grams per liter;
When adopting RESIN FINISH, adopt 1: 1-1: 50 bath raio, in 1-70 ℃ water-bath, place the resin dipping after 1-80 minute cellulose fibre, take out dewatered drying and get final product.
7. yarn or the fabric that can dye and have fast camaieu effect as claimed in claim 1 is characterized in that, described resin finishing agent is the resin finishing agent of cross-linking type; Described catalyst is selected from halide and sulfate; Described bleeding agent is anion-permeable membrane agent or nonionic penetrant.
8. yarn or the fabric that can dye and have fast camaieu effect as claimed in claim 7 is characterized in that, the resin finishing agent of described cross-linking type is selected from 2D resin, etherified 2D resin and polyurethanes crosslinking agent; Described halide is selected from magnesium chloride; Described bleeding agent is selected from the JFC bleeding agent.
9. yarn or the fabric that can dye and have fast camaieu effect as claimed in claim 1, it is characterized in that, the spinning process of described different spinning styles is the spinning process of common style, the spinning process of AB yarn style, the spinning process of slub yarn style or the spinning process of kinckebocker yarn style.
10. yarn or the fabric that can dye and have fast camaieu effect as claimed in claim 1 is characterized in that, described white yarn or the drying condition of white fabrics before dyeing are and bake 0.5-5 minute under 100-180 ℃.
11. yarn or the fabric that can dye and have fast camaieu effect as claimed in claim 1 is characterized in that, described white yarn and white fabrics all adopt one-step method dyeing; The dyestuff that adopts during dyeing is REACTIVE DYES, direct dyes, SULPHUR DYES or soluble vat dye.
12. such as the application as high-grade underwear, T-shirt, Casual Wear raw material of the arbitrary described yarn that can dye and have fast camaieu effect of claim 1-11 or fabric.