CN103360752B - 抗老化ppo-abs塑料合金 - Google Patents

抗老化ppo-abs塑料合金 Download PDF

Info

Publication number
CN103360752B
CN103360752B CN201310300427.9A CN201310300427A CN103360752B CN 103360752 B CN103360752 B CN 103360752B CN 201310300427 A CN201310300427 A CN 201310300427A CN 103360752 B CN103360752 B CN 103360752B
Authority
CN
China
Prior art keywords
ppo
aging
plastic alloy
abs plastic
abs
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201310300427.9A
Other languages
English (en)
Other versions
CN103360752A (zh
Inventor
黄美蓉
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Guangdong Yuhao New Material Technology Co.,Ltd.
Original Assignee
Shanghai Qiucheng New Material Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shanghai Qiucheng New Material Technology Co Ltd filed Critical Shanghai Qiucheng New Material Technology Co Ltd
Priority to CN201310300427.9A priority Critical patent/CN103360752B/zh
Publication of CN103360752A publication Critical patent/CN103360752A/zh
Application granted granted Critical
Publication of CN103360752B publication Critical patent/CN103360752B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种抗老化PPO-ABS塑料合金，由下述组分按重量份组成：100份PPO、10-20份ABS、4-8份GPPS、0.5-1.5份抗老化剂。本发明的抗老化PPO-ABS塑料合金，相对于PPO，冲击强度显著提高，成型加工性能好，提高了耐溶剂性、改进了制品表面光泽及电镀性，主要用于制造电子电器零部件、汽车零部件、办公机械及纺纱管。

Description

抗老化PPO-ABS塑料合金
技术领域
本发明涉及一种塑料合金，尤其涉及一种抗老化PPO-ABS塑料合金。
背景技术
聚苯醚，简称PPO，英文名：Polyphenylene Oxide，是世界五大通用工程塑料之一。它具有刚性大、耐热性高、难燃、强度较高电性能优良等优点。另外，聚苯醚还具有耐磨、无毒、耐污染等优点。PPO的介电常数和介电损耗在工程塑料中是最小的品种之一，几乎不受温度、湿度的影响，可用于低、中、高频电场领域。PPO的负荷变形温度可达190℃以上，脆化温度为-170℃。PPO材料作为世界五大通用工程塑料之一，无毒，相对密度小，是五大通用工程塑料中密度最小的,具有良好的机械强度，抗蠕变性，耐应力松弛，抗疲劳强度高。
ABS树脂（丙烯腈-苯乙烯-丁二烯共聚物，ABS是Acrylonitrile ButadieneStyrene的首字母缩写）是一种强度高、韧性好、易于加工成型的热塑型高分子材料结构。
ABS是本世纪40年代发展起来的通用热塑性工程塑料，是一个综合力学性能十分优秀的塑料品种，不仅具有良好的刚性、硬度和加工流动性，而且具有高韧性特点，可以注塑、挤出或热成型。
然而，目前的PPO-ABS塑料合金抗老化性能并不佳。
发明内容
针对现有技术中存在的上述不足，本发明所要解决的技术问题是提供一种抗老化PPO-ABS塑料合金，具有良好的抗老化性能。
本发明所要解决的技术问题是通过如下技术方案实现的：
一种抗老化PPO-ABS塑料合金，由下述组分按重量份组成：100份PPO、10-20份ABS、4-8份GPPS、0.5-1.5份抗老化剂。
所述抗老化剂，由下述组分按重量份组成：30-50份4,4’-硫代双(6-叔丁基-3-甲基苯酚)、30-50份1,1,3-三(2-甲基-4-羟基-5-叔丁苯基)丁烷、10-30份硫代二丙酸双十八醇酯。
4,4’-硫代双(6-叔丁基-3-甲基苯酚)，CAS号：96-69-5，英文名：4,4'-Thio-bis(6-tert-butyl-m-methyl phenol)。
1,1,3-三(2-甲基-4-羟基-5-叔丁苯基)丁烷，CAS号:1843-03-4，4,4',4''-(1-methyl-1-propanyl-3-ylidene)tris[2-(1,1-dimethylethyl)-5-methyl-Phenol。
硫代二丙酸双十八醇酯，英文名：Distearyl thiodipropionate，CAS号：693-36-7。
将4,4’-硫代双(6-叔丁基-3-甲基苯酚)、1,1,3-三(2-甲基-4-羟基-5-叔丁苯基)丁烷和硫代二丙酸双十八醇酯搅拌混合均匀，即可制得该抗老化剂。
可以采用本行业通用方法进行制备本发明的抗老化PPO-ABS塑料合金，例如：按配比称取各组分，混合均匀后，熔融混炼、挤出造粒，即获得所述抗老化PPO-ABS塑料合金。
具体的，可以为按配比称取各组分，在混合机中，室温下控制转速在300-400转/分钟，混合5-10分钟，取出后转入螺杆挤出机中，在250-260℃温度下挤出造粒，即获得所述抗老化PPO-ABS塑料合金。
显然，在本发明中为提高产品的其他性能，还可以适应性地添加其他助剂，如阻燃剂、着色剂和抗静电剂等。
发明人通过大量实验得出，将4,4’-硫代双(6-叔丁基-3-甲基苯酚)、1,1,3-三(2-甲基-4-羟基-5-叔丁苯基)丁烷和硫代二丙酸双十八醇酯三种抗老化剂进行合理复配使用，协同增效，抗老化效果明显。
本发明的抗老化PPO-ABS塑料合金，相对于PPO，冲击强度显著提高，成型加工性能好，提高了耐溶剂性、改进了制品表面光泽及电镀性，主要用于制造电子电器零部件、汽车零部件、办公机械及纺纱管，且具有优秀的热老化性能，适合在极端高温环境下使用。
具体实施方式
实施例1
按照表1中对应实施例1数据称取各原料。将各组分加入到高速混合机中，室温下控制转速在350转/分钟，混合8分钟，取出后转入螺杆挤出机中，在255℃温度下挤出造粒，获得抗老化PPO-ABS塑料合金。
表1：抗老化PPO-ABS塑料合金配方表单位：公斤
实施例1 实施例2 实施例3 实施例4
PPO树脂 100 100 100 100
ABS树脂 15 15 15 15
GPPS树脂 6 6 6 6
4,4’-硫代双(6-叔丁基-3-甲基苯酚) 0.4 0.8 / 0.5
1,1,3-三(2-甲基-4-羟基-5-叔丁苯基)丁烷 0.4 / 0.8 0.5
硫代二丙酸双十八醇酯 0.2 0.2 0.2 /
PPO树脂采用沙伯基础公司牌号为N190X-701的PPO树脂。
ABS树脂选用吉林石化公司牌号0215A的ABS树脂。
GPPS选用台湾台化公司牌号GP5250的通用聚苯乙烯。
实施例2-4
分别按照表1中对应实施例2-4数据称取各原料。采用实施例1所述的方法制备所述抗老化PPO-ABS塑料合金。
测试例1
根据热氧老化实验标准GB/T7141-2008，对制得的塑料进行人工加速老化实验（90℃，500h），并分别测定该塑料人工加速老化前后的拉伸强度、悬臂梁缺口冲击强度。
拉伸强度保持率=（人工加速老化后的拉伸强度-人工加速老化前的拉伸强度）÷人工加速老化前的拉伸强度×100%。
冲击强度保持率=（人工加速老化后的悬臂梁缺口冲击强度-人工加速老化前的悬臂梁缺口冲击强度）÷人工加速老化前的悬臂梁缺口冲击强度×100%。
表2：塑料抗老化性能测试表（90℃，500h）
拉伸强度保持率，% 悬臂梁缺口冲击强度保持率，%
实施例1 83.8 81.7
实施例2 81.9 80.5
实施例3 82.7 80.8
实施例4 82.4 80.2

Claims (1)

1.一种抗老化PPO-ABS塑料合金，其特征在于，由下述组分按重量份组成：100份PPO、10-20份ABS、4-8份GPPS、0.5-1.5份抗老化剂；
所述抗老化剂由下述组分按重量份组成：30-50份4,4’-硫代双(6-叔丁基-3-甲基苯酚)、30-50份1,1,3-三(2-甲基-4-羟基-5-叔丁苯基)丁烷、10-30份硫代二丙酸双十八醇酯。
CN201310300427.9A 2013-07-15 2013-07-15 抗老化ppo-abs塑料合金 Active CN103360752B (zh)