CN103360741B - 抗老化pc-pet塑料合金 - Google Patents

抗老化pc-pet塑料合金 Download PDF

Info

Publication number
CN103360741B
CN103360741B CN201310294928.0A CN201310294928A CN103360741B CN 103360741 B CN103360741 B CN 103360741B CN 201310294928 A CN201310294928 A CN 201310294928A CN 103360741 B CN103360741 B CN 103360741B
Authority
CN
China
Prior art keywords
pet
aging
polyblend
mah
compatilizer
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201310294928.0A
Other languages
English (en)
Other versions
CN103360741A (zh
Inventor
黄美蓉
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
SHANTOU LONGQI PLASTIC PRODUCTS CO., LTD.
Original Assignee
Shanghai Qiucheng New Material Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shanghai Qiucheng New Material Technology Co Ltd filed Critical Shanghai Qiucheng New Material Technology Co Ltd
Priority to CN201310294928.0A priority Critical patent/CN103360741B/zh
Publication of CN103360741A publication Critical patent/CN103360741A/zh
Application granted granted Critical
Publication of CN103360741B publication Critical patent/CN103360741B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种抗老化PC-PET塑料合金，由下述组分按重量份组成：60-80份PC、15-25份PET、2-4份相容剂、0.5-1.5份抗老化剂。本发明的抗老化PC-PET塑料合金具有优异的耐低温性能、冲击强及热变形温度高、力学性能及尺寸稳定性好的特点，可广泛应用于家电、电子电器、建材、汽车等领域，且具有优秀的热老化性能，适合在极端高温环境下使用。

Description

抗老化PC-PET塑料合金
技术领域
本发明涉及一种塑料合金，尤其涉及一种抗老化PC-PET塑料合金。
背景技术
PET塑料是英文Polyethylene terephthalate的缩写，简称PET或PETP。中文意思是：聚对苯二甲酸类塑料，主要包括聚对苯二甲酸乙二酯PET和聚对苯二甲酸丁二酯PBT。PET塑料分子结构高度对称，具有一定的结晶取向能力，故而具有较高的成膜性和成性。PET塑料具有很好的光学性能和耐候性，非晶态的PET塑料具有良好的光学透明性。另外PET塑料具有优良的耐磨耗摩擦性和尺寸稳定性及电绝缘性。
聚碳酸酯(简称PC)是分子链中含有碳酸酯基的高分子聚合物，根据酯基的结构可分为脂肪族、芳香族、脂肪族-芳香族等多种类型。其中由于脂肪族和脂肪族-芳香族聚碳酸酯的机械性能较低，从而限制了其在工程塑料方面的应用。目前仅有芳香族聚碳酸酯获的了工业化生产。由于聚碳酸酯结构上的特殊性，现已成为五大工程塑料中增长速度最快的通用工程塑料。
PC的优点是室温刚而韧，但高温的情况下，热变形严重。缺点是应力开裂，粘度大；PET长期使用温度可达120度，电绝缘性优良，甚至在高温高频下，其电性能仍较好，但耐电晕性较差，抗蠕变性，耐疲劳性、尺寸稳定性都很好；PC-PET塑料合金保留了两者的优点。
然而，目前的PC-PET塑料合金抗老化性能并不佳。
发明内容
针对现有技术中存在的上述不足，本发明所要解决的技术问题是提供一种抗老化PC-PET塑料合金，具有良好的抗老化性能。
本发明所要解决的技术问题是通过如下技术方案实现的：
一种抗老化PC-PET塑料合金，由下述组分按重量份组成：60-80份PC、15-25份PET、2-4份相容剂、0.5-1.5份抗老化剂。
所述抗老化剂，由下述组分按重量份组成：30-50份4,4’-硫代双(6-叔丁基-3-甲基苯酚)、30-50份1,1,3-三(2-甲基-4-羟基-5-叔丁苯基)丁烷、10-30份硫代二丙酸双十八醇酯。
4,4’-硫代双(6-叔丁基-3-甲基苯酚)，CAS号：96-69-5，英文名：4,4'-Thio-bis(6-tert-butyl-m-methyl phenol)。
1,1,3-三(2-甲基-4-羟基-5-叔丁苯基)丁烷，CAS号:1843-03-4，4,4',4''-(1-methyl-1-propanyl-3-ylidene)tris[2-(1,1-dimethylethyl)-5-methyl-Phenol。
硫代二丙酸双十八醇酯，英文名：Distearyl thiodipropionate，CAS号：693-36-7。
将4,4’-硫代双(6-叔丁基-3-甲基苯酚)、1,1,3-三(2-甲基-4-羟基-5-叔丁苯基)丁烷和硫代二丙酸双十八醇酯搅拌混合均匀，即可制得该抗老化剂。
所述相容剂为SMA、PP-g-MA、PP-g-AA、EAA、PS-g-PMMA、PS-g-MAH、PP-g-Pa6、PS-b-PMMA、PS-b-PBA、PE-g-ST、PP-g-ST、ABS-g-MAH、PP-g-MAH、EVA、SEBS、SEBS-g-MAH或PE-g-MAH。
可以采用本行业通用方法进行制备本发明的抗老化PC-PET塑料合金，例如：按配比称取各组分，混合均匀后，熔融混炼、挤出造粒，即获得所述抗老化PC-PET塑料合金。
具体的，可以为按配比称取各组分，在混合机中，室温下控制转速在300-400转/分钟，混合5-10分钟，取出后转入螺杆挤出机中，在225-245℃温度下挤出造粒，即获得所述抗老化PC-PET塑料合金。
显然，在本发明中为提高产品的其他性能，还可以适应性地添加其他助剂，如阻燃剂、着色剂和抗静电剂等。
发明人通过大量实验得出，将4,4’-硫代双(6-叔丁基-3-甲基苯酚)、1,1,3-三(2-甲基-4-羟基-5-叔丁苯基)丁烷和硫代二丙酸双十八醇酯三种抗老化剂进行合理复配使用，协同增效，抗老化效果明显。
本发明的抗老化PC-PET塑料合金具有优异的耐低温性能、冲击强及热变形温度高、力学性能及尺寸稳定性好的特点，可广泛应用于家电、电子电器、建材、汽车等领域，且具有优秀的热老化性能，适合在极端高温环境下使用。
具体实施方式
实施例1
按照表1中对应实施例1数据称取各原料。将各组分加入到高速混合机中，室温下控制转速在300-400转/分钟，混合5-10分钟，取出后转入螺杆挤出机中，在225-245℃温度下挤出造粒，获得抗老化PC-PET塑料合金。
表1：抗老化PC-PET塑料合金配方表   单位：公斤
实施例1 实施例2 实施例3 实施例4
PC树脂 70 70 70 70
PET树脂 20 20 20 20
相容剂SMA 3 3 3 3
4,4’-硫代双(6-叔丁基-3-甲基苯酚) 0.4 0.8 / 0.5
1,1,3-三(2-甲基-4-羟基-5-叔丁苯基)丁烷 0.4 / 0.8 0.5
硫代二丙酸双十八醇酯 0.2 0.2 0.2 /
PC树脂选用日本帝人公司牌号1250Y的注塑级PC树脂；
PET树脂选用美国杜邦公司牌号545BK的PET树脂；
相容剂SMA，学名苯乙烯-马来酸酐共聚物。SMA树脂系苯乙烯与马来酸酐的无规共聚物，是国际二十世纪七十年代开发成功的耐热性高分子品种，主要充当高分子产品的相容剂，属于苯乙烯系列专用树脂之一。
实施例2-4
分别按照表1中对应实施例2-4数据称取各原料。采用实施例1所述的方法制备所述抗老化PC-PET塑料合金。
测试例1
根据热氧老化实验标准GB/T7141-2008，对制得的塑料进行人工加速老化实验（90℃，500h），并分别测定该塑料人工加速老化前后的拉伸强度、悬臂梁缺口冲击强度。
拉伸强度保持率=（人工加速老化后的拉伸强度-人工加速老化前的拉伸强度）÷人工加速老化前的拉伸强度×100%。
冲击强度保持率=（人工加速老化后的悬臂梁缺口冲击强度-人工加速老化前的悬臂梁缺口冲击强度）÷人工加速老化前的悬臂梁缺口冲击强度×100%。
表2：塑料抗老化性能测试表（90℃，500h）
拉伸强度保持率，% 悬臂梁缺口冲击强度保持率，%
实施例1 82.9 81.5
实施例2 81.3 80.8
实施例3 81.1 81.0
实施例4 81.6 80.4

Claims (2)

1.一种抗老化PC-PET塑料合金，其特征在于，由下述组分按重量份组成：60-80份PC、15-25份PET、2-4份相容剂、0.5-1.5份抗老化剂；
所述抗老化剂由下述组分按重量份组成：30-50份4,4’-硫代双(6-叔丁基-3-甲基苯酚)、30-50份1,1,3-三(2-甲基-4-羟基-5-叔丁苯基)丁烷、10-30份硫代二丙酸双十八醇酯。
2.如权利要求1所述的抗老化PC-PET塑料合金，其特征在于：所述相容剂为SMA、PP-g-MA、PP-g-AA、EAA、PS-g-PMMA、PS-g-MAH、PP-g-PA6、PS-b-PMMA、PS-b-PBA、PE-g-ST、PP-g-ST、ABS-g-MAH、PP-g-MAH、EVA、SEBS、SEBS-g-MAH或PE-g-MAH。
CN201310294928.0A 2013-07-14 2013-07-14 抗老化pc-pet塑料合金 Active CN103360741B (zh)