CN103352182B - Nb-V-Ag-Pd系铁基非晶合金薄带及其制备方法 - Google Patents

Nb-V-Ag-Pd系铁基非晶合金薄带及其制备方法 Download PDF

Info

Publication number
CN103352182B
CN103352182B CN201310213198.7A CN201310213198A CN103352182B CN 103352182 B CN103352182 B CN 103352182B CN 201310213198 A CN201310213198 A CN 201310213198A CN 103352182 B CN103352182 B CN 103352182B
Authority
CN
China
Prior art keywords
amorphous
amorphous alloy
annulus
thin ribbon
heat treatment
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201310213198.7A
Other languages
English (en)
Other versions
CN103352182A (zh
Inventor
王军松
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Chuzhou Hangyou Electric Co., Ltd.
Original Assignee
QUANJIAO JUNHONG SOFT MAGNETIC MATERIALS CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by QUANJIAO JUNHONG SOFT MAGNETIC MATERIALS CO Ltd filed Critical QUANJIAO JUNHONG SOFT MAGNETIC MATERIALS CO Ltd
Priority to CN201310213198.7A priority Critical patent/CN103352182B/zh
Publication of CN103352182A publication Critical patent/CN103352182A/zh
Application granted granted Critical
Publication of CN103352182B publication Critical patent/CN103352182B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种Nb-V-Ag-Pd系铁基非晶合金薄带，其特征在于：其组成各元素的原子百分比为：Nb1-1.2、V3.5-3.6、Zr0.06-0.09、Li1.2-1.4、Ba0.06-0.08、Ag3-5、Pd2.1-2.3、Gd0.02-0.04、Dy0.20-0.28、Fe余量。本发明制备非晶带材与常规的非晶带材制备方法相似，本申请以Nb-V-Ag-Pd为基础掺杂材料，添加Zr、Li、Ba等其它成分，优化热处理工艺，明显改善非晶合金带材的应力分配，使得本发明非晶合金材料具有优良的韧性、良好的塑性、优异的软磁性能和良好的非晶形成能力，可广泛应用于各种非晶薄带圆环材料。

Description

Nb-V-Ag-Pd系铁基非晶合金薄带及其制备方法
技术领域
本发明涉及磁性功能材料领域，特别涉及一种性能优良的铁基非晶态合金薄带及其制备方法，可广泛用于各种非晶薄带圆环材料。
背景技术
现有变压器磁芯多采用硅钢片制作，其虽然具有较高的饱和磁感(2.0T)，但中频损耗大，能耗高。非晶合金开始用于变压器非晶薄带圆环材料，但其饱和磁感小于硅钢，应用受限，因此，开发一种具有高饱和磁感和低中频损耗的非晶合金薄带材料，是变压器非晶薄带圆环材料的研究重点。
发明内容
本发明的目的是提供一种Nb-V-Ag-Pd系铁基非晶合金薄带及其制备方法，其具有高饱和磁感和低中频损耗。
本发明提供了如下技术方案：
一种Nb-V-Ag-Pd系铁基非晶合金薄带，其特征在于：其组成各元素的原子百分比为：Nb1-1.2、V3.5-3.6、Zr0.06-0.09、Li1.2-1.4、Ba0.06-0.08、Ag3-5、Pd2.1-2.3、Gd0.02-0.04、Dy0.20-0.28、Fe余量。
所述的Nb-V-Ag-Pd系铁基非晶合金薄带的制备方法，包括按各元素原子百分比配料，加热到1200-1500℃，熔化并制备成熔融合金；在CO2和N2混合气氛保护下，将熔融合金喷射到铜辊上快速急冷，得到非晶态合金薄带并卷绕成圆环；混合气氛的比例CO2：N2=1：2-3；其特征在于：将得到的非晶薄带圆环放在第一热处理炉中，第一热处理炉中放置所述非晶薄带圆环的部分外加纵向脉冲磁场，频率为1-2Hz，磁场强度1.2-1.5T；抽真空后至小于5Pa，再充氩气至0.2-0.4MPa，以6-8℃/分钟速率，升温至280-300℃，保温15-20分钟；继续以8-10℃/分钟速率，升温460-490℃，保温25-30分钟；停止加热，调整磁场频率为3-5Hz磁场强度0.5-0.8T，待非晶薄带圆环冷却至50℃以下，从热处理炉取出。
本发明制备非晶带材与常规的非晶带材制备方法相似，本申请以Nb-V-Ag-Pd为基础掺杂材料，添加Zr、Li、Ba等其它成分，优化热处理工艺，明显改善非晶合金带材的应力分配，使得本发明非晶合金材料具有优良的韧性、良好的塑性、优异的软磁性能和良好的非晶形成能力，可广泛应用于各种非晶薄带圆环材料。
具体实施方式
Nb-V-Ag-Pd系铁基非晶合金薄带，其组成各元素的原子百分比为：Nb1、V3.5、Zr0.09、Li1.4、Ba0.08、Ag5、Pd2.3、Gd0.04、Dy0.28、Fe余量。
Nb-V-Ag-Pd系铁基非晶合金薄带的制备方法，包括按各元素原子百分比配料，加热到1200-1500℃，熔化并制备成熔融合金；在CO2和N2混合气氛保护下，将熔融合金喷射到辊速为22-28m/s铜辊上快速急冷，得到宽度为5±0.2mm、厚度为28±5μm的非晶薄带。将非晶薄带卷绕成圆环，内径1厘米，外径2.5厘米；混合气氛的比例CO2：N2=1：2；本发明依次进行以下步骤：
将得到的非晶薄带圆环放在第一热处理炉中，第一热处理炉中放置所述非晶薄带圆环的部分外加纵向脉冲磁场，频率为1-2Hz，磁场强度1.2-1.5T；抽真空后至小于5Pa，再充氩气至0.35MPa，以6-8℃/分钟速率，升温至280-300℃，保温18分钟；继续以8-10℃/分钟速率，升温460-490℃，保温25-30分钟；停止加热，调整磁场频率为5Hz磁场强度0.5T，待非晶薄带圆环冷却至50℃以下，从热处理炉取出。
性能检测：
测试条件为磁感1.1T，频率为50Hz，记为P11/50。合金的饱和磁感应强度Bs采用静态磁性能测量仪，以磁场为800A/m下的磁感应强度作为合金的饱和磁感应强度Bs，合金的矫顽力Hc采用B-H磁滞回线测试仪测得。
本发明饱和磁感应强度Bs为1.9T，矫顽力Hc在2.9A/m，损耗P11/50在0.30W/kg，断裂应变εf在0.028以上，韧脆转变温度TDB均在150℃以上。

Claims (1)

1.一种Nb-V-Ag-Pd系铁基非晶合金薄带，其特征在于：其组成各元素的原子百分比为：Nb1-1.2、V3.5-3.6、Zr0.06-0.09、Li1.2-1.4、Ba0.06-0.08、Ag3-5、Pd2.1-2.3、Gd0.02-0.04、Dy0.20-0.28、Fe余量；
所述的Nb-V-Ag-Pd系铁基非晶合金薄带的制备方法，包括按各元素原子百分比配料，加热到1200-1500℃，熔化并制备成熔融合金；在CO2和N2混合气氛保护下，将熔融合金喷射到铜辊上快速急冷，得到非晶态合金薄带并卷绕成圆环；混合气氛的比例CO2：N2=1：2-3；将得到的非晶薄带圆环放在第一热处理炉中，第一热处理炉中放置所述非晶薄带圆环的部分外加纵向脉冲磁场，频率为1-2Hz，磁场强度1.2-1.5T；抽真空后至小于5Pa，再充氩气至0.2-0.4MPa，以6-8℃/分钟速率，升温至280-300℃，保温15-20分钟；继续以8-10℃/分钟速率，升温460-490℃，保温25-30分钟；停止加热，调整磁场频率为3-5Hz磁场强度0.5-0.8T，待非晶薄带圆环冷却至50℃以下，从热处理炉取出。
CN201310213198.7A 2013-05-31 2013-05-31 Nb-V-Ag-Pd系铁基非晶合金薄带及其制备方法 Active CN103352182B (zh)