CN103351769B - 一种丙烯酸酯单组份防水涂料 - Google Patents

一种丙烯酸酯单组份防水涂料 Download PDF

Info

Publication number
CN103351769B
CN103351769B CN201310330081.7A CN201310330081A CN103351769B CN 103351769 B CN103351769 B CN 103351769B CN 201310330081 A CN201310330081 A CN 201310330081A CN 103351769 B CN103351769 B CN 103351769B
Authority
CN
China
Prior art keywords
component
water
paint
waterproofing paint
acrylate mono
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN201310330081.7A
Other languages
English (en)
Other versions
CN103351769A (zh
Inventor
刘绍贵
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
XIAMEN LIKASAM WATERPROOF ENGINEERING Co Ltd
Original Assignee
XIAMEN LIKASAM WATERPROOF ENGINEERING Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by XIAMEN LIKASAM WATERPROOF ENGINEERING Co Ltd filed Critical XIAMEN LIKASAM WATERPROOF ENGINEERING Co Ltd
Priority to CN201310330081.7A priority Critical patent/CN103351769B/zh
Publication of CN103351769A publication Critical patent/CN103351769A/zh
Application granted granted Critical
Publication of CN103351769B publication Critical patent/CN103351769B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种丙烯酸酯单组份防水涂料,它由以下重量比的组分组成:丙烯酸乳液50~70,防腐剂0.02~0.04,重质碳酸钙5~7,钛白粉10~20,增稠剂0.1~0.3,二丁酯3~6,氨中和剂0.04~0.06,纤维素2~4,消泡剂0.01~0.03,水6~8,填充料1~2。本发明以纯丙烯酸酯乳液加入优质p填料,助剂配置而成的单组份高聚物水性防水涂料,它具有良好的抗渗性、粘结力及柔性,整体的弹性和延伸率,能实现涂覆防水涂料在混凝土出现2-3mm宽开裂而不渗水的效果。

Description

一种丙烯酸酯单组份防水涂料
技术领域
[0001] 本发明涉及一种防水涂料,具体来说是一种丙烯酸酯单组份防水涂料,属于建筑 材料技术领域。
背景技术
[0002] 要在建筑物表面上,经溶剂或水分的挥发或两种组分的化学反应形成一层薄膜, 使建筑物表面与水隔绝,从而起到防水、密封的作用,这些涂刷的粘稠液体称为防水涂料。 在一些军事工程、机械地坑、隧道、游泳池、水池、地下室、供水管排灌闸粘贴瓷片以及屋面、 卫生间、阳台、管道接口的混凝土结构位置,尽管是涂覆有常规的防水涂料,但是,混凝土一 旦出现裂缝,仍然出现裂缝处漏水现象,原因在于现有常见的防水涂料的抗渗性差、粘结力 较弱、柔性差,整体的弹性和延伸率较差,为此,本申请人认为有必要对现有的防水涂料进 行改进,充分提高防水涂料的整体性能,以填补国内涂覆防水涂料在混凝土出现2-3mm宽 开裂而不渗水的空白。
发明内容
[0003] 本发明的目的在于克服现有防水涂料性能差的问题,提供一种丙烯酸酯单组份防 水涂料,它具有良好的抗渗性、粘结力及柔性,整体的弹性和延伸率,能实现涂覆防水涂料 在混凝土出现2-3_宽开裂而不渗水的效果。
[0004] 本发明的目的是通过以下技术方案来实现的:一种丙烯酸酯单组份防水涂料,其 特征在于:它由以下重量比的组分组成:
[0005] 丙烯酸乳液 50~70
[0006] 防腐剂 0· 02 ~0· 04
[0007] 重质碳酸钙 5~7
[0008] 钛白粉 10~20
[0009] 增稠剂 0· 1~0· 3
[0010] 二丁酯 3~6
[0011] 氨中和剂 0.04~0.06
[0012] 纤维素 2~4
[0013] 消泡剂 0.01 ~0.03
[0014] 填充料 1~2
[0015] 水 6 ~8.
[0016] 具体来说,所述重质碳酸钙的颗粒大小为1500目。
[0017] 具体来说,所述钛白粉的颗粒大小为3000目。
[0018] 期间,钛白粉是填充料,作用是不沉淀,颗粒目数越大,浮力大,就不沉淀;二丁酯 是用于增加弹性,防止开裂;氨中和剂是用于调节稳定性能;纤维素是用于增稠,粘接作 用。
[0019] 本发明所述的丙烯酸酯单组份防水涂料,是以纯丙烯酸酯乳液加入优质填料,助 剂配置而成的单组份高聚物水性防水涂料,它与常规的防水涂料相比,具有以下优点:
[0020] (1)本产品是单组份水性涂料,无毒,无味绿色环保。
[0021] (2)该涂料具有优良的弹性及延伸率,断裂伸长率大于或等于500,抗渗性好,粘 结力强,独特的整体无接缝,而且使用本产品后,混凝土出现2-3mm的裂缝,不会渗水,填补 了防水涂料混凝土出现新开裂而不渗水的空白。
[0022] (3)耐低温柔性好低温柔性/绕(10mm棒)零下40摄氏度无裂纹。
[0023] (4)拉伸强度大于或等于2. 0MP3,耐老化,使用寿命长,可根据需要配制各种颜 色,兼有装饰与防水的效果。
具体实施方式
[0024] 下面结合实施例进一步描述本发明的技术方案,但要求保护的范围并不局限于所 述。
[0025] 实施例1
[0026] 本实施例所述的丙烯酸酯单组份防水涂料,它由以下重量比的组分组成:
[0027] 丙烯酸乳液 50
[0028] 防腐剂 0· 04
[0029] 1500目的重质碳酸钙 5
[0030] 3000目的钛白粉 20
[0031] 增稠剂 0· 1
[0032] 二丁酯 6
[0033] 氨中和剂 0.04
[0034] 纤维素 4
[0035] 消泡剂 0· 01
[0036] 水 8
[0037] 填充料 1
[0038] 实施例2
[0039] 本实施例所述的丙烯酸酯单组份防水涂料,它由以下重量比的组分组成:
[0040] 丙烯酸乳液 70
[0041] 防腐剂 0.02
[0042] 1500目的重质碳酸钙 7
[0043] 3000目的钛白粉 10
[0044] 增稠剂 0· 3
[0045] 二丁酯 3
[0046] 氨中和剂 0.06
[0047] 纤维素 2
[0048] 消泡剂 0· 03
[0049] 水 6
[0050] 填充料 1. 5
[0051] 实施例3
[0052] 本实施例所述的丙烯酸酯单组份防水涂料,它由以下重量比的组分组成:
[0053] 丙烯酸乳液 63
[0054] 防腐剂 0· 03
[0055] 1500目的重质碳酸钙 6
[0056] 3000目的钛白粉 15
[0057] 增稠剂 0· 21
[0058] 二丁酯 5
[0059] 氨中和剂 0.05
[0060] 纤维素 3
[0061] 消泡剂 0.01
[0062] 水 7. 7
[0063] 填充料 1.9
[0064] 实施例4
[0065] 本实施例所述的丙烯酸酯单组份防水涂料,它由以下重量比的组分组成:
[0066] 丙烯酸乳液 55
[0067]防腐剂 0· 035
[0068] 1500目的重质碳酸钙 5. 6
[0069] 3000目的钛白粉 18
[0070] 增稠剂 0· 15
[0071] 二丁酯 5.6
[0072] 氨中和剂 0.045
[0073] 纤维素 3. 5
[0074] 消泡剂 0· 02
[0075] 水 7
[0076] 填充料 2
[0077] 实施例5
[0078] 本实施例所述的丙烯酸酯单组份防水涂料,它由以下重量比的组分组成:
[0079] 丙烯酸乳液 68
[0080]防腐剂 0· 025
[0081] 1500目的重质碳酸钙 6.5
[0082] 3000目的钛白粉 12
[0083] 增稠剂 0· 26
[0084] 二丁酯 4
[0085] 氨中和剂 0.056
[0086] 纤维素 2. 5
[0087]消泡剂 0· 012
[0088] 水 6. 5
[0089] 填充料 2
[0090] 对以上各实施例制得的丙烯酸酯单组份防水涂料,对其进行物理性能检测,得下 表:
Figure CN103351769BD00061
[0091]
[0092]
[0093] 从上表得知,本发明所述的丙烯酸酯单组份防水涂料,其确实具有良好的抗渗性、 粘结力及柔性效果,整体的弹性和延伸率,进而实现涂覆防水涂料在混凝土出现开裂而不 渗水的效果。

Claims (1)

1. 一种丙締酸醋单组份防水涂料,其特征在于:它由W下重量比的组分组成:丙締酸乳液 50~70 防腐剂 0. 02~0. 04 1500目的重质碳酸巧 5~7 3000目的铁白粉 10~20 增稠剂 0.1~0.3 二下醋 3~6 氨中和剂 0.04~0.06 纤维素 2~4 消泡剂 0. 01~0. 03 填充料 1~2 水 6~8。
CN201310330081.7A 2013-08-01 2013-08-01 一种丙烯酸酯单组份防水涂料 Expired - Fee Related CN103351769B (zh)