CN103351554A - 低吸水的聚氯乙烯电缆料 - Google Patents
低吸水的聚氯乙烯电缆料 Download PDFInfo
- Publication number
- CN103351554A CN103351554A CN2013103070622A CN201310307062A CN103351554A CN 103351554 A CN103351554 A CN 103351554A CN 2013103070622 A CN2013103070622 A CN 2013103070622A CN 201310307062 A CN201310307062 A CN 201310307062A CN 103351554 A CN103351554 A CN 103351554A
- Authority
- CN
- China
- Prior art keywords
- parts
- polyvinyl chloride
- cable material
- chloride cable
- low suction
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种低吸水的聚氯乙烯电缆料,属于高分子复合材料技术领域。其是由以下重量份数的原料构成:聚氯乙烯树脂50~55份;邻苯二甲酸二辛酯8~12份;对苯二甲酸二辛酯10~15份;乙烯与醋酸乙烯共聚物5~8;氯化石蜡6~12份;处理的碳酸钙14~20份;稳定剂1.3~1.9份。提供的低吸水的聚氯乙烯电缆料具有电性能优异,强度高,阻燃好的特点,并且还具有低吸水性。
Description
技术领域
本发明属于高分子复合材料技术领域,具体涉及一种低吸水的聚氯乙烯电缆料。
背景技术
聚氯乙烯电缆由于价格低,加工方便,机械性能以及电性能优异,因而被广泛用于通信电缆领域,但是行业内为减低成本,往往过度地添加矿物填料,从而导致在实际使用中因电缆吸潮而致使电性能及耐电压性能下降,甚至引发安全事故。因而有必要加以改进,为此,本申请人作了反复而有益的尝试,终于形成了下面将要介绍的技术方案。
发明内容
本发明的任务在于提供一种强度高、电性能优异和吸水率低的低吸水的聚氯乙烯电缆料。
本发明的任务是这样来完成的,一种低吸水的聚氯乙烯电缆料,其是由以下重量份数的原料构成:
在本发明的一个实施例中,所述的聚氯乙烯树脂为聚合度为130的聚氯乙烯粉。
在本发明的另一个实施例中,所述的邻苯二甲酸二辛酯为酯含量为99%以上并且水分含量小于0.1%邻苯二甲酸二辛酯。
在本发明的又一个实施例中,所述的对苯二甲酸二辛酯为酯含量大于99.5%并且水分含量小于0.1%的对苯二甲酸二辛酯。
在本发明的再一个实施例中,所述的乙烯与醋酸乙烯共聚物为醋酸乙烯含量为28%的乙烯与醋酸乙烯共聚物。
在本发明的还有一个实施例中,所述的氯化石蜡为氯含量为70%的氯化石蜡。
在本发明的更而一个实施例中,所述的处理的碳酸钙是指:100份碳酸钙在60℃下用4份乙烯基三甲氧基硅烷处理,其中乙烯基三甲氧基硅烷是经过酒精稀释的,酒精与乙烯基三甲氧基硅烷的重量比为1:1。
在本发明的进而一个实施例子中,所述的稳定剂为铅锌稳定剂,其中硬脂酸锌与硬脂酸铅的重量比为4:6。
本发明提供的低吸水的聚氯乙烯电缆料具有电性能优异,强度高,阻燃好的特点,并且还具有低吸水性。
具体实施方式
实施例1:
实施例2:
实施例3:
实施例4:
其中:上面所述的处理的碳酸钙是指:100份碳酸钙在60℃下用4份(重量份)乙烯基三甲氧基硅烷处理,而乙烯基三甲氧基硅烷是经过酒精稀释的,酒精与乙烯基三甲氧基硅烷的重量比为1:1。
由上述实施例1-4得到的低吸水的聚氯乙烯电缆料经测试具有下表所示的性能:
Claims (8)
1.一种低吸水的聚氯乙烯电缆料,其特征在于其是由以下重量份数的原料构成:
聚氯乙烯树脂 50~55份;
邻苯二甲酸二辛酯 8~12份;
对苯二甲酸二辛酯 10~ 15份;
乙烯与醋酸乙烯共聚物 5 ~8;
氯化石蜡 6~12份;
处理的碳酸钙 14~20份;
稳定剂 1.3~1.9份。
2.根据权利要求1所述的低吸水的聚氯乙烯电缆料,其特征在于所述的聚氯乙烯树脂为聚合度为130的聚氯乙烯粉。
3.根据权利要求1所述的低吸水的聚氯乙烯电缆料,其特征在于所述的邻苯二甲酸二辛酯为酯含量为99%以上并且水分含量小于0.1%邻苯二甲酸二辛酯。
4.根据权利要求1所述的低吸水的聚氯乙烯电缆料,其特征在于所述的对苯二甲酸二辛酯为酯含量大于99.5%并且水分含量小于0.1%的对苯二甲酸二辛酯。
5.根据权利要求1所述的低吸水的聚氯乙烯电缆料,其特征在于所述的乙烯与醋酸乙烯共聚物为醋酸乙烯含量为28%的乙烯与醋酸乙烯共聚物。
6.根据权利要求1所述的低吸水的聚氯乙烯电缆料,其特征在于所述的氯化石蜡为氯含量为70%的氯化石蜡。
7.根据权利要求1所述的低吸水的聚氯乙烯电缆料,其特征在于所述的处理的碳酸钙是指:100份碳酸钙在60℃下用4份的乙烯基三甲氧基硅烷处理,其中乙烯基三甲氧基硅烷是经过酒精稀释的,酒精与乙烯基三甲氧基硅烷的重量比为1:1。
8.根据权利要求1所述的低吸水的聚氯乙烯电缆料,其特征在于所述的稳定剂为铅锌稳定剂,其中硬脂酸锌与硬脂酸铅的重量比为4:6。