CN103341340A - 一种叶腊石配方 - Google Patents
一种叶腊石配方 Download PDFInfo
- Publication number
- CN103341340A CN103341340A CN2013102546561A CN201310254656A CN103341340A CN 103341340 A CN103341340 A CN 103341340A CN 2013102546561 A CN2013102546561 A CN 2013102546561A CN 201310254656 A CN201310254656 A CN 201310254656A CN 103341340 A CN103341340 A CN 103341340A
- Authority
- CN
- China
- Prior art keywords
- pyrophillite
- pyrophyllite
- formula
- brown
- yellow
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种叶腊石配方,各成分重量比如下:青灰色叶腊石:红色和褐色叶腊石:黄色叶腊石=2:5:3。并通过粉碎、筛选、混合搅拌以及压制成块的工艺得到生产用叶腊石。本发明的有益效果是:本发明的叶腊石配方生产出来的叶腊石块,可以在性能上达到青灰色叶腊石的标准,满足正常的人造立方氮化硼和金刚石生长所需密封性、保温性、传压性、绝缘性条件,更起到降低合成终压的作用,延长设备使用寿命,节约采购成本,成本大幅下降,生产效益大幅提高。
Description
技术领域
本发明涉及超硬材料合成中所使用的密封传压介质材料领域,尤其涉及一种叶腊石配方。
背景技术
在超硬材料合成领域,叶腊石是目前迄今为止唯一可以作为组装工件的腔体,而目前最好的青灰色叶腊石产地为北京门头沟区,矿产资源在大幅减少,价格已经达到黄金矿石价格,货源紧缺。而红色叶腊石和褐色叶腊石价格便宜,但密封性能差,在生产过程中容易出现因密封不住造成“放炮”现象,企业成本极大。黄色叶腊石密封性能好而传压性能差,造成单产过低,企业效益低下。将青灰色叶腊石、红色和褐色叶腊石、加上黄色叶腊石按一定比例粉碎后配比,压制成叶腊石块,达到青灰色叶腊石的性能,满足正常生产需要,降低公司生产成本。
发明内容
为了克服上述缺陷,本发明提供一种叶腊石配方。
为了实现上述目的,本发明的技术方案是:一种叶腊石配方,各成分重量比如下:
青灰色叶腊石:红色和褐色叶腊石:黄色叶腊石=2:5:3。
一种叶腊石配方的生产工艺,步骤如下:
1)、将青灰色叶腊石、红色和褐色叶腊石以及黄色叶腊石分别进行粉碎,分三个粒度:大料、中料和细料分开储存备用;
2)、按配方比例2:5:3进行配比,青灰色叶腊石选用大料,红色和褐色叶腊石选用中料,黄色叶腊石选用细料;
3)、按5-6%的比例加入水玻璃胶,倒入搅拌机内搅拌20分钟以上后倒入料仓内备用;
4)、备用的料取出后进行压制,得到成品叶腊石。
进一步,所述的大料为1.0-1.5mm粒度;所述中料为0.3-0.8mm粒度;所述细料为小于0.3mm粒度。
本发明的有益效果是:本发明的叶腊石配方生产出来的叶腊石块,可以在性能上达到青灰色叶腊石的标准,满足正常的人造立方氮化硼和金刚石生长所需密封性、保温性、传压性、绝缘性条件,更起到降低合成终压的作用,延长设备使用寿命,节约采购成本,成本大幅下降,生产效益大幅提高。
具体实施方式
下面结合具体实施例对本发明做进一步的说明。
一种叶腊石配方,各成分重量比如下:
青灰色叶腊石:红色和褐色叶腊石:黄色叶腊石=2:5:3。
一种叶腊石配方的生产工艺,步骤如下:
1)、将青灰色叶腊石、红色和褐色叶腊石以及黄色叶腊石分别进行粉碎,分三个粒度:大料、中料和细料分开储存备用;所述的大料为1.0-1.5mm粒度;所述中料为0.3-0.8mm粒度;所述细料为小于0.3mm粒度。
2)、按配方比例2:5:3进行配比,青灰色叶腊石选用大料,红色和褐色叶腊石选用中料,黄色叶腊石选用细料;
3)、按5-6%的比例加入水玻璃胶,倒入搅拌机内搅拌20分钟以上后倒入料仓内备用;
4)、备用的料取出后进行压制,得到成品叶腊石。
本发明的技术方案不限于上述具体实施例的限制,凡是根据本发明的技术方案做出的技术变形,均落入本发明的保护范围之内。
Claims (3)
1.一种叶腊石配方,其特征在于:各成分重量比如下:
青灰色叶腊石:红色和褐色叶腊石:黄色叶腊石=2:5:3。
2.一种叶腊石配方的生产工艺,其特征在于:步骤如下:
1)、将青灰色叶腊石、红色和褐色叶腊石以及黄色叶腊石分别进行粉碎,分三个粒度:大料、中料和细料分开储存备用;
2)、按配方比例2:5:3进行配比,青灰色叶腊石选用大料,红色和褐色叶腊石选用中料,黄色叶腊石选用细料;
3)、按5-6%的比例加入水玻璃胶,倒入搅拌机内搅拌20分钟以上后倒入料仓内备用;
4)、备用的料取出后进行压制,得到成品叶腊石。
3.根据权利要求2所述的叶腊石配方额生产工艺,其特征在于:所述的大料为1.0-1.5mm粒度;所述中料为0.3-0.8mm粒度;所述细料为小于0.3mm粒度。