CN103320885B - 多功能纺织纤维的制造方法 - Google Patents
多功能纺织纤维的制造方法 Download PDFInfo
- Publication number
- CN103320885B CN103320885B CN201310215977.0A CN201310215977A CN103320885B CN 103320885 B CN103320885 B CN 103320885B CN 201310215977 A CN201310215977 A CN 201310215977A CN 103320885 B CN103320885 B CN 103320885B
- Authority
- CN
- China
- Prior art keywords
- master batch
- textile fiber
- mica
- sediment
- fiber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明涉及一种纺织纤维的制造方法,具体是一种多功能纺织纤维的制造方法。该方法依次包括以下步骤:a.将天然独山石粉碎,加清水,取漂浮的云母烘干待用,去除悬浮物;b.对上一步骤的沉淀物烘干后粉碎至800-850目,加重量浓度5%的盐水比重液进行分层处理,去除漂浮物;c.将步骤b剩余的沉淀物烘干后与步骤a获得的云母混合,粉碎至5微米以下,形成功能粉末;d.将上一步骤获得的功能粉末与涤纶树脂均匀混合制成母粒,将所述母粒与其他能够形成纺织纤维的树脂原料混合后拉成纤维。本发明能够将天然独山石与纺织纤维进行结合,进而使纺织织物具有发射远红外线和产生负离子能力、有利于人体保健。
Description
技术领域
本发明涉及一种纺织纤维的制造方法,具体是一种多功能纺织纤维的制造方法。
背景技术
以高分子材料为原料的纺织纤维已广泛用于服装、床上用品等纺织品的面料中,但现有的此类纺织纤维仅具有构成织物的单一功能。
天然独山石是由斜长石、黝帘石、铬云石、透辉石、闪石、黑云母、榍石、帘石、沸石、葡萄石、电气石、绢云母、方解石、石英等较多的矿物质组成的天然材料,其部分组成成份相配合具有产生远红外线和负离子的能力,其能够产生消除异味和抗菌效果,但尚无将其与纺织纤维相结合的记载。
发明内容
本发明所要解决的技术问题是,提供一种能够将天然独山石与纺织纤维进行结合,进而使纺织织物具有发射远红外线和产生负离子能力、有利于人体保健的多功能纺织纤维的制造方法。
本发明多功能纺织纤维的制造方法依次包括以下步骤:
a.将天然独山石粉碎至20-40目,加清水进行沉浮处理,取漂浮的云母烘干待用,同时去除悬浮物;
b.对上一步骤的沉淀物烘干后用气流烘干机进行粉碎,粉碎至800-850目,加重量浓度5%的盐水比重液进行分层处理,去除漂浮物;
c.将步骤b剩余的沉淀物烘干后与步骤a获得的云母混合,进入气流粉碎机进行粉碎,粉碎至5微米以下,形成功能粉末;
d.将上一步骤获得的功能粉末与涤纶树脂均匀混合制成母粒,将所述母粒与其他能够形成纺织纤维的树脂原料混合后拉成可用于织物的长丝或短丝纤维;所述功能粉末在母粒中的重量含量为15-18%;所述母粒在纺织纤维原料总量中的重量含量为15-18%。
本发明能够获得纺织纤维,用其织造形成的纤维具有永久远红外发射的特性,经检测其发射光波波长为8-14微米,其法向的发射率为80-90%,其可作用增强人体的血液微循环,加快新陈代谢,增强人体免疫力;另外,经测试,本发明获得的纤维能提高周围负离子浓度,能激活人体的细胞、排除人体内的毒素,提高人体的抗菌能力和免疫能力;本发明获得的纤维还具有抗菌作用和除异味作用,对白色念珠菌、金黄色葡萄球菌、大肠杆菌、肺炎克雷白菌的抗菌能力可达到99%,并且去除甲醛、氨气、硫化氢气体的能力可达到85%-90%。
具体实施方式
本发明实施例的制造方法依次包括以下步骤:
a.将天然独山石粉碎至30目,加清水进行沉浮处理,取漂浮的云母烘干待用,同时去除悬浮物;
b.对上一步骤的沉淀物烘干后用气流烘干机进行粉碎,粉碎至800目,加重量浓度5%的盐水比重液进行分层处理,去除漂浮物;
c.将步骤b剩余的沉淀物烘干后与步骤a获得的云母混合,进入气流粉碎机进行粉碎,粉碎至5微米以下,形成功能粉末;
d.将上一步骤获得的功能粉末与涤纶树脂均匀混合制成母粒,将所述母粒与其他能够形成纺织纤维的树脂原料混合后拉成可用于织物的长丝或短丝纤维;所述功能粉末在母粒中的重量含量为15%;所述母粒在纺织纤维原料总量中的重量含量为15%。
经测试,本发明实施例获得的纤维所产生的负离子浓度为2130-2400(检测标准:TTC.F024-2007);该纤维还具有抗菌作用和除异味作用,对白色念珠菌、金黄色葡萄球菌、大肠杆菌、肺炎克雷白菌的抗菌能力可达到99%,并且去除甲醛、氨气、硫化氢气体的能力可达到85%-90%。
Claims (1)
1.一种多功能纺织纤维的制造方法,其特征是:依次包括以下步骤,
a.将天然独山石粉碎至20-40目,加清水进行沉浮处理,取漂浮的云母烘干待用,同时去除悬浮物;
b.对上一步骤的沉淀物烘干后用气流烘干机进行粉碎,粉碎至800-850目,加重量浓度5%的盐水比重液进行分层处理,去除漂浮物;
c.将步骤b剩余的沉淀物烘干后与步骤a获得的云母混合,进入气流粉碎机进行粉碎,粉碎至5微米以下,形成功能粉末;
d.将上一步骤获得的功能粉末与涤纶树脂均匀混合制成母粒,将所述母粒与其他能够形成纺织纤维的树脂原料混合后拉成可用于织物的长丝或短丝纤维;所述功能粉末在母粒中的重量含量为15-18%;所述母粒在纺织纤维原料总量中的重量含量为15-18%。