CN103320715A - 高耐磨高铬合金材料 - Google Patents
高耐磨高铬合金材料 Download PDFInfo
- Publication number
- CN103320715A CN103320715A CN 201310270537 CN201310270537A CN103320715A CN 103320715 A CN103320715 A CN 103320715A CN 201310270537 CN201310270537 CN 201310270537 CN 201310270537 A CN201310270537 A CN 201310270537A CN 103320715 A CN103320715 A CN 103320715A
- Authority
- CN
- China
- Prior art keywords
- alloy material
- chromium alloy
- wear
- mass percentage
- forms
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种高耐磨高铬合金材料,所述高耐磨高铬合金材料包括按质量百分比组成的下列主要成分:C:3.0%-3.3%,Cr:31.0%-33.0%,Mo:0.8%-1.0%,B:0.6%-0.7%,Cu:0.8%-1.0%,Ni:0.6%-0.7%,Al:0.3%-0.5%,Ti:0.3%-0.4%,Nb:0.6%-0.8%,以及按质量百分比组成的下列次要成分:Mg:0.005%-0.008%,Zn:0.01%-0.03%,S:≤0.025%,P:≤0.03%,其余为Fe。通过上述方式,本发明能够提高铬合金的耐高温、耐腐蚀、耐磨等性能。
Description
技术领域
本发明涉及金属材料领域,特别是涉及一种高耐磨高铬合金材料。
背景技术
铬是重要的合金元素,具有很高的耐腐蚀性,在空气中,即便是在赤热的状态下,氧化也很慢。因此,一般的高温合金中均添加一定量的Cr元素,且Cr含量越高,合金的高温抗氧化性和耐蚀性就越好。
然而,Cr在基体中的溶解度是有限的。当合金中的Cr含量达到或超过其饱和度后,在使用过程中会有复杂的组织出现而导致合金力学性能及稳定性的下降。因此,一般合金中的Cr含量都在30%以下。这类合金材料的耐温性能不够理想,无法运用于350℃以上的高温下,在一些易腐蚀的特殊环境下也无法使用,需要通过表面涂层、复合等方式来改善它的耐高温、耐腐蚀和耐磨等性能,工艺复杂,能耗大,成本高。
发明内容
本发明主要解决的技术问题是:针对现有技术的不足,提供一种高耐磨高铬合金材料,能够提高铬合金的耐高温、耐腐蚀、耐磨等性能。
为解决上述技术问题,本发明采用的一个技术方案是:提供一种高耐磨高铬合金材料,所述高耐磨高铬合金材料包括按质量百分比组成的下列主要成分:C:3.0%-3.3%,Cr:31.0%-33.0%,Mo:0.8%-1.0%,B:0.6%-0.7%,Cu:0.8%-1.0%,Ni:0.6%-0.7%,Al:0.3%-0.5%,Ti:0.3%-0.4%,Nb:0.6%-0.8%,以及按质量百分比组成的下列次要成分:Mg:0.005%-0.008%,Zn:0.01%-0.03%,S:≤0.025%,P:≤0.03%,其余为Fe。
在本发明一个较佳实施例中,所述高耐磨高铬合金材料包括按质量百分比组成的下列成分:C:3.1%,Cr:32.6%,Mo:0.8%,B:0.6%,Cu:1.0%,Ni:0.7%,Al:0.3%,Ti:0.3%,Nb:0.8%,Mg:0.007%,Zn:0.02%,S:0.02%,P:0.025%,其余为Fe。
在本发明一个较佳实施例中,所述高耐磨高铬合金材料包括按质量百分比组成的下列成分:C:3.3%,Cr:31.8%,Mo:1.0%,B:0.7%,Cu:0.9%,Ni:0.6%,Al:0.5%,Ti:0.4%,Nb:0.8%,Mg:0.005%,Zn:0.01%,S:0.02%,P:0.025%,其余为Fe。
本发明的有益效果是:通过对合金元素的合理优化匹配,严格控制Cr元素的含量,使合金具有高强度、高硬度、高弹性、高耐磨、抗冲击、抗冲刷、无磁等功能,且具有优良的抗氧化性能,耐腐蚀能力,可以具有高强度、高硬度、高弹性、耐磨、抗冲击、抗冲刷、无磁,可以运用于高温、强腐蚀以及强碳等特殊环境中。
具体实施方式
下面对本发明的较佳实施例进行详细阐述,以使本发明的优点和特征能更易于被本领域技术人员理解,从而对本发明的保护范围做出更为清楚明确的界定。
本发明实施例包括:
一种高耐磨高铬合金材料,所述高耐磨高铬合金材料包括按质量百分比组成的下列主要成分:C:3.0%-3.3%,Cr:31.0%-33.0%,Mo:0.8%-1.0%,B:0.6%-0.7%,Cu:0.8%-1.0%,Ni:0.6%-0.7%,Al:0.3%-0.5%,Ti:0.3%-0.4%,Nb:0.6%-0.8%,以及按质量百分比组成的下列次要成分:Mg:0.005%-0.008%,Zn:0.01%-0.03%,S:≤0.025%,P:≤0.03%,其余为Fe。
实施例一:
一种高耐磨高铬合金材料,所述高耐磨高铬合金材料包括按质量百分比组成的下列主要成分:C:3.1%,Cr:32.6%,Mo:0.8%,B:0.6%,Cu:1.0%,Ni:0.7%,Al:0.3%,Ti:0.3%,Nb:0.8%;以及按质量百分比组成的下列次要成分:Mg:0.007%,Zn:0.02%,S:0.02%,P:0.025%;其余为Fe。
实施例二:
一种高耐磨高铬合金材料,所述高耐磨高铬合金材料包括按质量百分比组成的下列主要成分:C:3.3%,Cr:31.8%,Mo:1.0%,B:0.7%,Cu:0.9%,Ni:0.6%,Al:0.5%,Ti:0.4%,Nb:0.8%;以及按质量百分比组成的下列次要成分:Mg:0.005%,Zn:0.01%,S:0.02%,P:0.025%;其余为Fe。
本发明的高耐磨高铬合金材料,由于合金中的Cr元素含量在30%以上,因此其具有优良的耐高温、抗氧化性介质腐蚀能力,在不同条件的HNO 、饱和HS溶液中都是稳定的,无需表面涂层处理,适用于航空、化工等行业,可以用作航空元件、耐磨构件、受冲击件等等。
本发明揭示了一种高耐磨高铬合金材料,通过对合金元素的合理优化匹配,严格控制Cr元素的含量,使合金具有高强度、高硬度、高弹性、高耐磨、抗冲击、抗冲刷、无磁等功能,且具有优良的抗氧化性能,耐腐蚀能力,可以具有高强度、高硬度、高弹性、耐磨、抗冲击、抗冲刷、无磁,可以运用于高温、强腐蚀以及强碳等特殊环境中。
以上所述仅为本发明的实施例,并非因此限制本发明的专利范围,凡是利用本发明说明书内容所作的等效结构或等效流程变换,或直接或间接运用在其他相关的技术领域,均同理包括在本发明的专利保护范围内。
Claims (3)
1.一种高耐磨高铬合金材料,其特征在于,所述高耐磨高铬合金材料包括按质量百分比组成的下列主要成分:C:3.0%-3.3%,Cr:31.0%-33.0%,Mo:0.8%-1.0%,B:0.6%-0.7%,Cu:0.8%-1.0%,Ni:0.6%-0.7%,Al:0.3%-0.5%,Ti:0.3%-0.4%,Nb:0.6%-0.8%,以及按质量百分比组成的下列次要成分:Mg:0.005%-0.008%,Zn:0.01%-0.03%,S:≤0.025%,P:≤0.03%,其余为Fe。
2.根据权利要求1所述的高耐磨高铬合金材料,其特征在于,所述高耐磨高铬合金材料包括按质量百分比组成的下列成分:C:3.1%,Cr:32.6%,Mo:0.8%,B:0.6%,Cu:1.0%,Ni:0.7%,Al:0.3%,Ti:0.3%,Nb:0.8%,Mg:0.007%,Zn:0.02%,S:0.02%,P:0.025%,其余为Fe。
3.根据权利要求1所述的高耐磨高铬合金材料,其特征在于,所述高耐磨高铬合金材料包括按质量百分比组成的下列成分:C:3.3%,Cr:31.8%,Mo:1.0%,B:0.7%,Cu:0.9%,Ni:0.6%,Al:0.5%,Ti:0.4%,Nb:0.8%,Mg:0.005%,Zn:0.01%,S:0.02%,P:0.025%,其余为Fe。