CN103320047A - 瓦椤纸板线胶糊配方及制作工艺 - Google Patents
瓦椤纸板线胶糊配方及制作工艺 Download PDFInfo
- Publication number
- CN103320047A CN103320047A CN2013102514522A CN201310251452A CN103320047A CN 103320047 A CN103320047 A CN 103320047A CN 2013102514522 A CN2013102514522 A CN 2013102514522A CN 201310251452 A CN201310251452 A CN 201310251452A CN 103320047 A CN103320047 A CN 103320047A
- Authority
- CN
- China
- Prior art keywords
- parts
- linking agent
- starch
- cross
- corrugated board
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供了一种瓦椤纸板线胶糊配方，组份和质量份数为：水：1250-1350份；淀粉：300-320份；NaOH：5-7份；硼砂：4-6份；糊料交联剂：2-5份；粘合剂：12-15份。本发明中交联剂高分子聚合物分子会取代淀粉分子中的羟基，形成稳定的交联。淀粉分子被交联剂分子包围，增强了抗热和抗剪切力的能力，从而在循环过程中保持粘度的稳定性。由于淀粉分子羟基被取代，由亲水性变为疏水性，所以干燥时易脱水，提高了干燥速度。交联剂分子易亲和纤维分子，从而帮助提高粘合强度。由于交联联剂分子的反应过程比较缓慢且不可逆，所以其粘合及防潮效果在纸板离开生产线后会逐步增加，反应完全后就完全疏水，形成坚固而防潮的浆膜。本发明还同时提供了瓦椤纸板线胶糊的制作工艺。
Description
技术领域
本发明属于胶糊制备领域，具体涉及一种瓦椤纸板线胶糊配方及制作工艺。
背景技术
众所周知，瓦楞纸板的形成离不开淀粉胶粘剂。淀粉胶粘剂的主要作用是粘合瓦楞纸和面纸，形成瓦楞纸板。现在的大部分纸箱企业所使用的淀粉胶粘剂主要是生胶。这种生胶的缺点是稳定性差、制造复杂，粘度不稳定，时有脱胶现象，损失大打样，且糊化温度较高。
发明内容
本发明针对上述现有技术的不足，提供了一种耐水性好、粘度稳定性佳的瓦椤纸板线胶糊配方；本发明同时提供了一种瓦椤纸板线胶糊的制作工艺。
本发明是通过如下技术方案实现的：
一种瓦椤纸板线胶糊配方，组份和质量份数为：水：1250-1350份；淀粉：300-320份；NaOH：5-7份；硼砂：4-6份；糊料交联剂：2-5份；粘合剂：12-15份。
本发明的进一步设置在于，所述糊料交联剂为过氧化氢。
本发明同时提供了一种瓦椤纸板线胶糊的制作工艺，包括以下步骤：
（1）给1250-1350KG水加温到31-32度，启动搅拌器加入糊料交联剂2-5KG搅拌3-5分钟；
（2）投入300-320KG淀粉和12-15KG粘合剂搅拌10-13分钟，得到复合溶液；
（3）将5-7KGNaOH兑水20KG，以及复合溶液滴入制胶桷；
（4）测量胶粘度，当胶粘度达到15mPa.s时加入糊料交联剂2-5KG，搅拌3-5分钟；
（5）加4-6KG硼砂后搅拌6-10分钟，得到瓦椤纸板线胶糊。
本发明具有如下有益效果：
1、本发明中交联剂高分子聚合物分子会取代淀粉分子中的羟基，形成稳定的交联。淀粉分子被交联剂分子包围，增强了抗热和抗剪切力的能力，从而在循环过程中保持粘度的稳定性。由于淀粉分子羟基被取代，由亲水性变为疏水性，所以干燥时易脱水，提高了干燥速度。交联剂分子易亲和纤维分子，从而帮助提高粘合强度。由于交联联剂分子的反应过程比较缓慢且不可逆，所以其粘合及防潮效果在纸板离开生产线后会逐步增加，反应完全后就完全疏水，形成坚固而防潮的浆膜。
2、本发明所述的瓦椤纸板线胶糊具有优异的粘合强度及渗透性，可帮助降低上糊量，由于上糊量降低，从而具有容易干燥，使纸板易烘干，保持纸板的平整及硬度的优异性能。
3、本发明所述的瓦椤纸板线胶糊的粘度稳定性佳，上糊降低及薄膜强度高，可相对降低板的偏软和弯翘的现象；有关的损耗如贴合不良、上浆过多等现象，都能得到有效的降低。
4、本发明所述的瓦椤纸板线胶糊，不仅能抑制细菌的生长，且能保护淀粉在糊料过夜储存后，仍能维持正常的贴合性及糊料性能，糊料的保质期大概为4-7天。
5、本发明所述的瓦椤纸板线胶糊，有优异的成膜性，使糊料具备了良好的初期粘合能力。
具体实施方式
实施例一：
本发明提供了一种瓦椤纸板线胶糊配方，组份和质量份数为：水：1250份；淀粉：300份；NaOH：5份；硼砂：4份；过氧化氢：2份；粘合剂：12份。
上述瓦椤纸板线胶糊的制作工艺，包括以下步骤：
（1）给1250水加温到31度，启动搅拌器加入过氧化氢2KG搅拌3分钟；
（2）投入300KG淀粉和12KG粘合剂搅拌10分钟，得到复合溶液；
（3）将5KGNaOH兑水20KG，以及复合溶液滴入制胶桷；
（4）测胶粘度达到15mPa.s时加入糊料交联剂2KG，搅拌3分钟；
（5）加4KG硼砂后搅拌6分钟即可使用。
实施例二：
本发明提供了一种瓦椤纸板线胶糊配方，组份和质量份数为：水：1350份；淀粉：320份；NaOH：7份；硼砂：6份；过氧化氢：5份；粘合剂：15份。
上述瓦椤纸板线胶糊的制作工艺，包括以下步骤：
（1）给1350KG水加温到32度，启动搅拌器加入过氧化氢5KG搅拌5分钟；
（2）投入320KG淀粉和15KG粘合剂搅拌13分钟，得到复合溶液；
（3）将7KGNaOH兑水20KG，以及复合溶液滴入制胶桷；
（4）测胶粘度达到15mPa.s时加入糊料交联剂5KG，搅拌5分钟；
（5）加6KG硼砂后搅拌10分钟即可使用。
实施例三：
本发明提供了一种瓦椤纸板线胶糊配方，组份和质量份数为：水：1300份；淀粉：310份；NaOH：6份；硼砂：5份；过氧化氢：4份；粘合剂：14份。
上述瓦椤纸板线胶糊的制作工艺，包括以下步骤：
（1）给1300KG水加温到31.5度，启动搅拌器加入过氧化氢4KG搅拌4分钟；
（2）投入310KG淀粉和14KG粘合剂搅拌12分钟，得到复合溶液；
（3）将6KGNaOH兑水20KG，以及复合溶液滴入制胶桷；
（4）测胶粘度达到15mPa.s时加入糊料交联剂4KG，搅拌4分钟；
（5）加5KG硼砂后搅拌8分钟即可使用。
本发明可改变为多种方式对本领域的技术人员是显而易见的，这样的改变不认为脱离本发明的范围。所有这样的对所述领域的技术人员显而易见的修改，将包括在本权利要求的范围之内。
Claims (3)
1.一种瓦椤纸板线胶糊配方，其特征在于，组份和质量份数为：水：1250-1350份；淀粉：300-320份；NaOH：5-7份；硼砂：4-6份；糊料交联剂：2-5份；粘合剂：12-15份。
2.根据权利要求1所述的瓦椤纸板线胶糊配方，其特征在于，所述糊料交联剂为过氧化氢。
3.一种瓦椤纸板线胶糊的制作工艺，包括以下步骤：
（1）给1250-1350KG水加温到31-32度，启动搅拌器加入糊料交联剂2-5KG搅拌3-5分钟；
（2）投入300-320KG淀粉和12-15KG粘合剂搅拌10-13分钟，得到复合溶液；
（3）将5-7KGNaOH兑水20KG，以及复合溶液滴入制胶桷；
（4）测量胶粘度，当胶粘度达到15mPa.s时加入糊料交联剂2-5KG，搅拌3-5分钟；
（5）加4-6KG硼砂后搅拌6-10分钟，得到瓦椤纸板线胶糊。