CN103296098A - 双层二氧化钛复合氧化锌薄膜电极的制备方法 - Google Patents

双层二氧化钛复合氧化锌薄膜电极的制备方法 Download PDF

Info

Publication number
CN103296098A
CN103296098A CN2013102269041A CN201310226904A CN103296098A CN 103296098 A CN103296098 A CN 103296098A CN 2013102269041 A CN2013102269041 A CN 2013102269041A CN 201310226904 A CN201310226904 A CN 201310226904A CN 103296098 A CN103296098 A CN 103296098A
Authority
CN
China
Prior art keywords
titanium dioxide
membrane electrode
layer titanium
zinc oxide
dioxide composite
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2013102269041A
Other languages
English (en)
Inventor
祝平
Original Assignee
SUZHOU NUOXIN INNOVATION ENERGY CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by SUZHOU NUOXIN INNOVATION ENERGY CO Ltd filed Critical SUZHOU NUOXIN INNOVATION ENERGY CO Ltd
Priority to CN2013102269041A priority Critical patent/CN103296098A/zh
Publication of CN103296098A publication Critical patent/CN103296098A/zh
Pending legal-status Critical Current

Abstract

本发明提供了一种双层二氧化钛复合氧化锌薄膜电极的制备方法，包括以下步骤：（1）将醋酸锌溶解到无水酒精中，搅拌至溶解形成乳白色溶液；（2）将二氧化钛单层薄膜浸入乳白色溶液中20-120分钟，取出用甲醇清洗，干燥；（3）将干燥后的粗品升温到预设温度，保温一定时间，以每分钟30摄氏度的速率进行冷却，获得双层二氧化钛复合氧化锌薄膜电极半成品；（4）将双层二氧化钛复合氧化锌薄膜电极半成品放入染料中进行浸泡，获得双层二氧化钛复合氧化锌薄膜电极成品。相较于现有技术，本发明的制备方法所获得的双层二氧化钛复合氧化锌薄膜电极致密度较高，有助于提高电池的效率。

Description

双层二氧化钛复合氧化锌薄膜电极的制备方法
技术领域
本发明涉及一种制备方法，尤其涉及一种双层二氧化钛复合氧化锌薄膜电极的制备方法。
背景技术
电池已经广泛应用在众多场合和产品上，其中电池的效率一直是人们想要提高的目标。人们从各方面进行了努力，以希望提高电池的效率，例如从新材料、新制备方法等，有人采用了二氧化钛薄膜应用在电池中，然而目前的二氧化钛薄膜电极致密度不足，从而影响电池效率
发明内容
本发明主要解决的技术问题是目前的二氧化钛薄膜电极致密度不足，从而影响电池效率。
为了解决上述技术问题，本发明实施例公开了一种双层二氧化钛复合氧化锌薄膜电极的制备方法，包括以下步骤：
（1）将醋酸锌溶解到无水酒精中，搅拌至溶解形成乳白色溶液；
（2）将二氧化钛单层薄膜浸入乳白色溶液中20-120分钟，取出用甲醇清洗，干燥；
（3）将干燥后的粗品升温到预设温度，保温一定时间，以每分钟30摄氏度的速率进行冷却，获得双层二氧化钛复合氧化锌薄膜电极半成品；
（4）将双层二氧化钛复合氧化锌薄膜电极半成品放入染料中进行浸泡，获得双层二氧化钛复合氧化锌薄膜电极成品。
在本发明的一较佳实施例中，步骤（1）的醋酸锌的纯度大于等于98.5%，无水酒精的纯度大于等于99%，搅拌时间为20-40分钟。
在本发明的一较佳实施例中，步骤（3）的预设温度为500摄氏度，保温时间为1小时。
相较于现有技术，本发明的制备方法所获得的双层二氧化钛复合氧化锌薄膜电极致密度较高，有助于提高电池的效率。
具体实施方式
下面将对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅是本发明的一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其它实施例，都属于本发明保护的范围。
本发明实施例公开了一种双层二氧化钛复合氧化锌薄膜电极的制备方法，包括以下步骤：
（1）将醋酸锌溶解到无水酒精中，搅拌至溶解形成乳白色溶液；
（2）将二氧化钛单层薄膜浸入乳白色溶液中20-120分钟，取出用甲醇清洗，干燥；
（3）将干燥后的粗品升温到预设温度，保温一定时间，以每分钟30摄氏度的速率进行冷却，获得双层二氧化钛复合氧化锌薄膜电极半成品；
（4）将双层二氧化钛复合氧化锌薄膜电极半成品放入染料中进行浸泡，获得双层二氧化钛复合氧化锌薄膜电极成品。
在本发明的一较佳实施例中，步骤（1）的醋酸锌的纯度大于等于98.5%，无水酒精的纯度大于等于99%，搅拌时间为20-40分钟。
在本发明的一较佳实施例中，步骤（3）的预设温度为500摄氏度，保温时间为1小时。
相较于现有技术，本发明的制备方法所获得的双层二氧化钛复合氧化锌薄膜电极致密度较高，有助于提高电池的效率。
以上所述仅为本发明的实施例，并非因此限制本发明的专利范围，凡是利用本发明说明书内容所作的等效结构或等效流程变换，或直接或间接运用在其它相关的技术领域，均同理包括在本发明的专利保护范围内。

Claims (3)

1.一种双层二氧化钛复合氧化锌薄膜电极的制备方法，其特征在于，包括以下步骤：
（1）将醋酸锌溶解到无水酒精中，搅拌至溶解形成乳白色溶液；
（2）将二氧化钛单层薄膜浸入乳白色溶液中20-120分钟，取出用甲醇清洗，干燥；
（3）将干燥后的粗品升温到预设温度，保温一定时间，以每分钟30摄氏度的速率进行冷却，获得双层二氧化钛复合氧化锌薄膜电极半成品；
（4）将双层二氧化钛复合氧化锌薄膜电极半成品放入染料中进行浸泡，获得双层二氧化钛复合氧化锌薄膜电极成品。
2.根据权利要求1所述的双层二氧化钛复合氧化锌薄膜电极的制备方法，其特征在于，步骤（1）的醋酸锌的纯度大于等于98.5%，无水酒精的纯度大于等于99%，搅拌时间为20-40分钟。
3.根据权利要求1所述的双层二氧化钛复合氧化锌薄膜电极的制备方法，其特征在于，步骤（3）的预设温度为500摄氏度，保温时间为1小时。
CN2013102269041A 2013-06-08 2013-06-08 双层二氧化钛复合氧化锌薄膜电极的制备方法 Pending CN103296098A (zh)