CN103289537A - 一种含有丙烯酸丁酯的粉末涂料 - Google Patents
一种含有丙烯酸丁酯的粉末涂料 Download PDFInfo
- Publication number
- CN103289537A CN103289537A CN2013101607765A CN201310160776A CN103289537A CN 103289537 A CN103289537 A CN 103289537A CN 2013101607765 A CN2013101607765 A CN 2013101607765A CN 201310160776 A CN201310160776 A CN 201310160776A CN 103289537 A CN103289537 A CN 103289537A
- Authority
- CN
- China
- Prior art keywords
- parts
- butyl acrylate
- powder
- powder coating
- under
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种含有丙烯酸丁酯的粉末涂料，是由下述重量份的原料制得：聚酯树脂90-95，2402酚醛树脂30-35，有机硅消泡剂1-2，安息香1-1.5，稻壳灰1-2，脂肪族二异氰酸酯3-5，锐钛型钛白粉7-10，丙烯酸丁酯1-2，乙基纤维素1-2，无机填料90-100，抗氧剂10762-4，气相二氧化硅1-2。本发明绿色环保，机械强度高;既使用方便,又无毒无害阻燃，耐候性强。
Description
技术领域
本发明涉及涂料领域，确切地说是一种含有丙烯酸丁酯的粉末涂料。
背景技术
粉末涂料是一种新型的不含溶剂100%固体粉末状涂料。具有无溶剂、无污染、可回收、环保、节省能源和资源、减轻劳动强度和涂膜机械强度高等特点。 粉末涂料是与一般涂料完全不同的形态，它是以微细粉末的状态存在的。由于不使用溶剂，所以称为粉末涂料。粉末涂料的主要特点有：具有无公害、高效率、节省资源的特点。
发明内容
本发明的目的在于提供一种使用方便,阻燃，耐候性强的含有丙烯酸丁酯的粉末涂料。
上述目的通过以下方案实现：
一种含有丙烯酸丁酯的粉末涂料，其特征在于，是由下述重量份的原料制得：聚酯树脂 90-95，
2402酚醛树脂30-35，有机硅消泡剂 1-2，安息香 1-1.5，稻壳灰1-2，脂肪族二异氰酸酯3-5，锐钛型钛白粉7-10，丙烯酸丁酯1-2，乙基纤维素1-2，无机填料90-100，抗氧剂1076 2-4，气相二氧化硅1-2。
所述的一种含有丙烯酸丁酯的粉末涂料，其特征在于：所述的无机填料由下述重量份的原料组成：天青石粉40-45、铁矾土30-35，石灰石粉45-50、改性纳米硅藻土10-15；
所述的改性纳米硅藻土的制备方法为：将硅藻土于700-800℃下煅烧4-6小时，冷却后，破碎，过100-200目筛，然后于8-10%的乙酸溶液中浸泡5-7小时后，取出，去离子水洗涤至中性，加入相当于硅藻土重量1-2%的环氧大豆油，混匀后，烘干，研磨成纳米粉末，即得。
所述的一种含有丙烯酸丁酯的粉末涂料，其特征在于：
制备方法包括以下步骤：
（1）、按所述重量份精确称量各原料，先于500-600转/分下搅拌混合3-4分钟，于3000-3500转/分下搅拌混合8-10分钟，后于400-500转/分下搅拌混合1-2分钟，停止搅拌，得混合物料；
（2）、将混合物料用挤出机在100-115℃的温度下挤出，得挤出料；
（3）、挤出料粉碎后过100-200目筛，即得。
所述的一种含有丙烯酸丁酯的粉末涂料，其特征在于：所述的有机硅消泡剂固含量为25%，所述的聚酯树脂为羟基型聚酯，酸值 30-40mk KOH/g， 粘度 5000-7000mPa.S， 固化温度 180-200℃。
本发明的有益效果为：本发明绿色环保，机械强度高;既使用方便,又无毒无害阻燃，耐候性强。
具体实施方式
一种含有丙烯酸丁酯的粉末涂料，是由下述重量份（kg）的原料制得：聚酯树脂 95，2402酚醛树脂35，固含量为25%的有机硅消泡剂 1，安息香 1.5，稻壳灰1，脂肪族二异氰酸酯5，锐钛型钛白粉7，丙烯酸丁酯1，乙基纤维素2，无机填料100，抗氧剂1076 4，气相二氧化硅2。
所述的无机填料由下述重量份(kg)的原料组成：天青石粉40、铁矾土35，石灰石粉50、改性纳米硅藻土15；
所述的改性纳米硅藻土的制备方法为：将硅藻土于800℃下煅烧6小时，冷却后，破碎，过200目筛，然后于10%的乙酸溶液中浸泡7小时后，取出，去离子水洗涤至中性，加入相当于硅藻土重量2%的环氧大豆油，混匀后，烘干，研磨成纳米粉末，即得。
所述的一种含有丙烯酸丁酯的粉末涂料，
制备方法包括以下步骤：
（1）、按所述重量份精确称量各原料，先于500转/分下搅拌混合4分钟，于3500转/分下搅拌混合10分钟，后于400转/分下搅拌混合1分钟，停止搅拌，得混合物料；
（2）、将混合物料用挤出机在115℃的温度下挤出，得挤出料；
（3）、挤出料粉碎后过200目筛，即得。
所述的聚酯树脂为羟基型聚酯，酸值 30-40mk KOH/g， 粘度 5000-7000mPa.S， 固化温度 180-200℃。
将本实施例所得涂料采用高压静电喷涂于铸件上，电压为60KV，平均膜厚为65-75微米，固化条件为180℃烘烤20分钟；
性能指标如下：
按照GB/T1732测试，抗冲击性 ≥50kg.cm；
按照GB/T6739测试，铅笔硬度≥H级；
480h QUV-B加速光老化试验测试得，保光率达92%。
所得涂层表面平整，无气泡，颗粒、缩孔、针孔。
Claims (4)
1.一种含有丙烯酸丁酯的粉末涂料，其特征在于，是由下述重量份的原料制得：聚酯树脂 90-95，2402酚醛树脂30-35，有机硅消泡剂 1-2，安息香 1-1.5，稻壳灰1-2，脂肪族二异氰酸酯3-5，锐钛型钛白粉7-10，丙烯酸丁酯1-2，乙基纤维素1-2，无机填料90-100，抗氧剂1076 2-4，气相二氧化硅1-2。
2.根据权利要求1所述的一种含有丙烯酸丁酯的粉末涂料，其特征在于：所述的无机填料由下述重量份的原料组成：天青石粉40-45、铁矾土30-35，石灰石粉45-50、改性纳米硅藻土10-15；
所述的改性纳米硅藻土的制备方法为：将硅藻土于700-800℃下煅烧4-6小时，冷却后，破碎，过100-200目筛，然后于8-10%的乙酸溶液中浸泡5-7小时后，取出，去离子水洗涤至中性，加入相当于硅藻土重量1-2%的环氧大豆油，混匀后，烘干，研磨成纳米粉末，即得。
3.根据权利要求1所述的一种含有丙烯酸丁酯的粉末涂料，其特征在于：
制备方法包括以下步骤：
（1）、按所述重量份精确称量各原料，先于500-600转/分下搅拌混合3-4分钟，于3000-3500转/分下搅拌混合8-10分钟，后于400-500转/分下搅拌混合1-2分钟，停止搅拌，得混合物料；
（2）、将混合物料用挤出机在100-115℃的温度下挤出，得挤出料；
（3）、挤出料粉碎后过100-200目筛，即得。
4.根据权利要求1所述的一种含有丙烯酸丁酯的粉末涂料，其特征在于：
所述的有机硅消泡剂固含量为25%，所述的聚酯树脂为羟基型聚酯，酸值 30-40mk KOH/g， 粘度 5000-7000mPa.S， 固化温度 180-200℃。