CN103289501B - A kind of waterproof heat resistant coating containing acrylonitrile-butadiene-styrene copolymer - Google Patents
A kind of waterproof heat resistant coating containing acrylonitrile-butadiene-styrene copolymer Download PDFInfo
- Publication number
- CN103289501B CN103289501B CN201310216349.4A CN201310216349A CN103289501B CN 103289501 B CN103289501 B CN 103289501B CN 201310216349 A CN201310216349 A CN 201310216349A CN 103289501 B CN103289501 B CN 103289501B
- Authority
- CN
- China
- Prior art keywords
- butadiene
- styrene copolymer
- parts
- add
- acrylonitrile
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The present invention relates to a kind of waterproof heat resistant coating containing acrylonitrile-butadiene-styrene copolymer, be made up of according to weight ratio following composition: acrylonitrile-butadiene-styrene copolymer 50 ~ 60 parts, propanepoxy resin 20 ~ 30 parts, Zinic stearas 5 ~ 10 parts, dimethyl siloxane 10 ~ 20 parts, 5 ~ 10 parts, graphite, asbestos powder 5 ~ 10 parts, 5 ~ 10 parts, silicon carbide, propylene glycol 5 ~ 10 parts, dimethylbenzene 50 ~ 70 parts.The coating containing acrylonitrile-butadiene-styrene copolymer made has good waterproof heat resistant effect.
Description
Technical field
The present invention relates to a kind of waterproof heat resistant coating, particularly relate to a kind of waterproof heat resistant coating containing acrylonitrile-butadiene-styrene copolymer.
Background technology
At present, it is multifarious that Coating Market coats kind, Various Functions.For different demands.Along with the fast development of economy, client is also more and more higher to the index request of coating.Relating to the professional domain of waterproof heat resistant coating, as fields such as building, decorations, and need the field of moisture-proof heat resisting, day by day uprise to the requirement of waterproof heat resistant type coating, have at present waterproof and dampproof on the market and coating type that is high-temperature resistant result is considerably less simultaneously, therefore develop a kind of coating simultaneously with good water-repellancy and thermotolerance very urgent.
Summary of the invention
The technical problem solved: the problem that conventional coating is water-fast heat-resisting effect is poor.
Technical scheme: the present invention relates to a kind of waterproof heat resistant coating containing acrylonitrile-butadiene-styrene copolymer, be made up of according to weight ratio following composition: acrylonitrile-butadiene-styrene copolymer 50 ~ 60 parts, propanepoxy resin 20 ~ 30 parts, Zinic stearas 5 ~ 10 parts, dimethyl siloxane 10 ~ 20 parts, 5 ~ 10 parts, graphite, asbestos powder 5 ~ 10 parts, 5 ~ 10 parts, silicon carbide, propylene glycol 5 ~ 10 parts, dimethylbenzene 50 ~ 70 parts.Constantly stir by various composition is dropped in reactor, to be mixed evenly after can obtain the coating with good waterproof heat resistant effect.
Beneficial effect: after preparing the waterproof heat resistant coating containing acrylonitrile-butadiene-styrene copolymer, its water-repellancy and thermotolerance are tested, by coating even application behind tinplate surface, sample is put into water and carries out waterproof test, waterproof test duration is 50 ~ 70 days, the tinplate sample separately getting the good coating of even application carries out high temperature resistant experiment, and temperature is 700 ~ 800 DEG C, and the time is 200h.Result shows that the coating containing acrylonitrile-butadiene-styrene copolymer that the present invention makes did not ftracture foaming phenomena in 50 ~ 70 days, there is good water-repellancy, in addition at temperature is 700 ~ 800 DEG C, there is no abnormal dry and cracked or foaming phenomena within 200h, there is good heat-resisting effect yet.
Embodiment
Embodiment 1
Open reactor, get acrylonitrile-butadiene-styrene copolymer 50kg, drop in reactor, stir, add propanepoxy resin 20kg simultaneously, do not stop to stir, add Zinic stearas 5kg again, add dimethyl siloxane 10kg, then add graphite 5kg, then add asbestos powder 5kg successively, silicon carbide 5kg, propylene glycol 5kg, finally adds dimethylbenzene 50kg, can contain the coating of acrylonitrile-butadiene-styrene copolymer after thoroughly stirring.By coating even application behind tinplate surface, sample is put into water and carries out waterproof test, waterproof test duration is 50 days, and the tinplate sample separately getting the good coating of even application carries out high temperature resistant experiment, and temperature is 700 DEG C, and the time is 200h.Result shows that the coating containing acrylonitrile-butadiene-styrene copolymer that the present invention makes did not ftracture foaming phenomena in 50 days, there is good water-repellancy, in addition at temperature is 700 DEG C, there is no abnormal dry and cracked or foaming phenomena within 200h yet, there is good heat-resisting effect.
Embodiment 2
Open reactor, get acrylonitrile-butadiene-styrene copolymer 60kg, drop in reactor, stir, add propanepoxy resin 30kg simultaneously, do not stop to stir, add Zinic stearas 10kg again, add dimethyl siloxane 20kg, then add graphite 10kg, then add asbestos powder 10kg successively, silicon carbide 10kg, propylene glycol 10kg, finally adds dimethylbenzene 70kg, can contain the coating of acrylonitrile-butadiene-styrene copolymer after thoroughly stirring.By coating even application behind tinplate surface, sample is put into water and carries out waterproof test, waterproof test duration is 60 days, and the tinplate sample separately getting the good coating of even application carries out high temperature resistant experiment, and temperature is 800 DEG C, and the time is 200h.Result shows that the coating containing acrylonitrile-butadiene-styrene copolymer that the present invention makes did not ftracture foaming phenomena in 60 days, there is good water-repellancy, in addition at temperature is 800 DEG C, there is no abnormal dry and cracked or foaming phenomena within 200h yet, there is good heat-resisting effect.
Embodiment 3
Open reactor, get acrylonitrile-butadiene-styrene copolymer 55kg, drop in reactor, stir, add propanepoxy resin 25kg simultaneously, do not stop to stir, add Zinic stearas 7kg again, add dimethyl siloxane 15kg, then add graphite 8kg, then add asbestos powder 7kg successively, silicon carbide 8kg, propylene glycol 7kg, finally adds dimethylbenzene 60kg, can contain the coating of acrylonitrile-butadiene-styrene copolymer after thoroughly stirring.By coating even application behind tinplate surface, sample is put into water and carries out waterproof test, waterproof test duration is 70 days, and the tinplate sample separately getting the good coating of even application carries out high temperature resistant experiment, and temperature is 750 DEG C, and the time is 200h.Result shows that the coating containing acrylonitrile-butadiene-styrene copolymer that the present invention makes did not ftracture foaming phenomena in 70 days, there is good water-repellancy, in addition at temperature is 750 DEG C, there is no abnormal dry and cracked or foaming phenomena within 200h yet, there is good heat-resisting effect.
Claims (1)
1. the waterproof heat resistant coating containing acrylonitrile-butadiene-styrene copolymer, it is characterized in that, its preparation method is: open reactor, get acrylonitrile-butadiene-styrene copolymer 60Kg, drop in reactor, stir, add propanepoxy resin 30Kg simultaneously, do not stop to stir, add Zinic stearas 10Kg again, add dimethyl siloxane 20Kg, add graphite 10Kg again, add asbestos powder 10Kg successively again, silicon carbide 10Kg, propylene glycol 10Kg, finally add dimethylbenzene 70Kg, the coating of acrylonitrile-butadiene-styrene copolymer can be contained after thoroughly stirring.