CN103289460B - A kind of waterproof heat resistant coating containing rosin MALEIC ANHYDRIDE ester - Google Patents
A kind of waterproof heat resistant coating containing rosin MALEIC ANHYDRIDE ester Download PDFInfo
- Publication number
- CN103289460B CN103289460B CN201310216086.7A CN201310216086A CN103289460B CN 103289460 B CN103289460 B CN 103289460B CN 201310216086 A CN201310216086 A CN 201310216086A CN 103289460 B CN103289460 B CN 103289460B
- Authority
- CN
- China
- Prior art keywords
- parts
- maleic anhydride
- anhydride ester
- add
- rosin maleic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The present invention relates to a kind of waterproof heat resistant coating containing rosin MALEIC ANHYDRIDE ester, be made up of according to weight ratio following composition: rosin MALEIC ANHYDRIDE ester 30 ~ 40 parts, benzene emulsion 20 ~ 30 parts, glycerol 10 ~ 20 parts, 10 ~ 20 parts, aluminium sesquioxide powder, Calucium Silicate powder 10 ~ 20 parts, mica powder 5 ~ 10 parts, terra alba 5 ~ 10 parts, titanium dioxide 5 ~ 10 parts, N-BUTYL ACETATE 5 ~ 10 parts, propyl carbinol 50 ~ 70 parts.The coating containing rosin MALEIC ANHYDRIDE ester made has good waterproof heat resistant effect.
Description
Technical field
The present invention relates to a kind of waterproof heat resistant coating, particularly relate to a kind of waterproof heat resistant coating containing rosin MALEIC ANHYDRIDE ester.
Background technology
Along with the development of society, coating industry also obtains significant progress thereupon.In evolution, the demand of people to coating is increasing, is also more and more higher to the requirement of coating simultaneously.Relating to the professional domain of waterproof heat resistant coating, as fields such as building, decorations, and need the field of moisture-proof heat resisting, day by day uprise to the requirement of waterproof heat resistant type coating, the coating type simultaneously on the market at present with waterproof and heat-resisting effect is less, therefore develops a kind of coating simultaneously with good water-repellancy and thermotolerance and has boundless market outlook.
Summary of the invention
The technical problem solved: the problem that conventional coating is water-fast heat-resisting effect is poor.
Technical scheme: the present invention is a kind of waterproof heat resistant coating containing rosin MALEIC ANHYDRIDE ester, it is made up of according to weight ratio following composition: rosin MALEIC ANHYDRIDE ester 30 ~ 40 parts, benzene emulsion 20 ~ 30 parts, glycerol 10 ~ 20 parts, 10 ~ 20 parts, aluminium sesquioxide powder, Calucium Silicate powder 10 ~ 20 parts, mica powder 5 ~ 10 parts, terra alba 5 ~ 10 parts, titanium dioxide 5 ~ 10 parts, N-BUTYL ACETATE 5 ~ 10 parts, propyl carbinol 50 ~ 70 parts.Constantly stir by various composition is dropped in reactor, to be mixed evenly after can obtain the coating with good waterproof heat resistant effect.
Beneficial effect: after preparing the waterproof heat resistant coating containing rosin MALEIC ANHYDRIDE ester, its water-repellancy and thermotolerance are tested, by coating even application behind tinplate surface, sample is put into water and carries out waterproof test, waterproof test duration is 30 ~ 50 days, the tinplate sample separately getting the good coating of even application carries out high temperature resistant experiment, and temperature is 800 ~ 1000 DEG C, and the time is 300h.Result shows that the coating containing rosin MALEIC ANHYDRIDE ester that the present invention makes did not ftracture foaming phenomena in 30 ~ 50 days, there is good water-repellancy, in addition at temperature is 800 ~ 1000 DEG C, there is no abnormal dry and cracked or foaming phenomena within 300h yet, there is good heat-resisting effect.
Embodiment
Embodiment 1
Open reactor, get rosin MALEIC ANHYDRIDE ester 30kg, drop in reactor, stir, add benzene emulsion 20kg simultaneously, do not stop to stir, add glycerol 10kg again, add aluminium sesquioxide powder 10kg, then add Calucium Silicate powder 10kg, add mica powder 5kg successively again, terra alba 5kg, titanium dioxide 5kg, N-BUTYL ACETATE 5kg, finally add propyl carbinol 50kg, the coating of rosin MALEIC ANHYDRIDE ester can be contained after thoroughly stirring.By coating even application behind tinplate surface, sample is put into water and carries out waterproof test, waterproof test duration is 30 days, and the tinplate sample separately getting the good coating of even application carries out high temperature resistant experiment, and temperature is 800 DEG C, and the time is 300h.Result shows that the coating containing rosin MALEIC ANHYDRIDE ester that the present invention makes did not ftracture foaming phenomena in 30 days, there is good water-repellancy, in addition at temperature is 800 DEG C, there is no abnormal dry and cracked or foaming phenomena within 300h yet, there is good heat-resisting effect.
Embodiment 2
Open reactor, get rosin MALEIC ANHYDRIDE ester 40kg, drop in reactor, stir, add benzene emulsion 30kg simultaneously, do not stop to stir, add glycerol 20kg again, add aluminium sesquioxide powder 20kg, then add Calucium Silicate powder 20kg, add mica powder 10kg successively again, terra alba 10kg, titanium dioxide 10kg, N-BUTYL ACETATE 10kg, finally add propyl carbinol 70kg, the coating of rosin MALEIC ANHYDRIDE ester can be contained after thoroughly stirring.By coating even application behind tinplate surface, sample is put into water and carries out waterproof test, waterproof test duration is 50 days, and the tinplate sample separately getting the good coating of even application carries out high temperature resistant experiment, and temperature is 1000 DEG C, and the time is 300h.Result shows that the coating containing rosin MALEIC ANHYDRIDE ester that the present invention makes did not ftracture foaming phenomena in 50 days, there is good water-repellancy, in addition at temperature is 1000 DEG C, there is no abnormal dry and cracked or foaming phenomena within 300h yet, there is good heat-resisting effect.
Embodiment 3
Open reactor, get rosin MALEIC ANHYDRIDE ester 35kg, drop in reactor, stir, add benzene emulsion 25kg simultaneously, do not stop to stir, add glycerol 15kg again, add aluminium sesquioxide powder 15kg, then add Calucium Silicate powder 15kg, add mica powder 7kg successively again, terra alba 7kg, titanium dioxide 7kg, N-BUTYL ACETATE 7kg, finally add propyl carbinol 60kg, the coating of rosin MALEIC ANHYDRIDE ester can be contained after thoroughly stirring.By coating even application behind tinplate surface, sample is put into water and carries out waterproof test, waterproof test duration is 40 days, and the tinplate sample separately getting the good coating of even application carries out high temperature resistant experiment, and temperature is 900 DEG C, and the time is 300h.Result shows that the coating containing rosin MALEIC ANHYDRIDE ester that the present invention makes did not ftracture foaming phenomena in 40 days, there is good water-repellancy, in addition at temperature is 900 DEG C, there is no abnormal dry and cracked or foaming phenomena within 300h yet, there is good heat-resisting effect.
Claims (1)
1. the waterproof heat resistant coating containing rosin MALEIC ANHYDRIDE ester, it is characterized in that, preparation method's step of coating is as follows: open reactor, get rosin MALEIC ANHYDRIDE ester 40kg, drop in reactor, stir, add benzene emulsion 30kg simultaneously, do not stop to stir, add glycerol 20kg again, add aluminium sesquioxide powder 20kg, add Calucium Silicate powder 20kg again, add mica powder 10kg successively again, terra alba 10kg, titanium dioxide 10kg, N-BUTYL ACETATE 10kg, finally add propyl carbinol 70kg, the coating of rosin MALEIC ANHYDRIDE ester can be contained after thoroughly stirring.