CN103289281A - 一种含有改性三元乙丙橡胶的电缆护套料及其制备方法 - Google Patents

一种含有改性三元乙丙橡胶的电缆护套料及其制备方法 Download PDF

Info

Publication number
CN103289281A
CN103289281A CN2013101621353A CN201310162135A CN103289281A CN 103289281 A CN103289281 A CN 103289281A CN 2013101621353 A CN2013101621353 A CN 2013101621353A CN 201310162135 A CN201310162135 A CN 201310162135A CN 103289281 A CN103289281 A CN 103289281A
Authority
CN
China
Prior art keywords
rubber
modified ept
ept rubber
preparation
terpolymer
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2013101621353A
Other languages
English (en)
Other versions
CN103289281B (zh
Inventor
董后友
章大朝
邾茂然
朱正华
徐跃伟
钱风铃
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Dongguan Qiaozi Zhoushi Electric Co.,Ltd.
Original Assignee
ANHUI GREEN ECOLOGICAL POLYMER MATERIALS TECHNOLOGY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ANHUI GREEN ECOLOGICAL POLYMER MATERIALS TECHNOLOGY Co Ltd filed Critical ANHUI GREEN ECOLOGICAL POLYMER MATERIALS TECHNOLOGY Co Ltd
Priority to CN201310162135.3A priority Critical patent/CN103289281B/zh
Publication of CN103289281A publication Critical patent/CN103289281A/zh
Application granted granted Critical
Publication of CN103289281B publication Critical patent/CN103289281B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种含有改性三元乙丙橡胶的电缆护套料及其制备方法，其组成原料为：改性三元乙丙橡胶、氢化丁腈橡胶、高炉矿渣、沸石分子筛、碳化铝、促进剂808、促进剂CZ、N-（β一氨乙基）-γ-氨丙基三甲（乙）氧基硅烷、蓖麻酸钡、抗氧剂1010、邻苯二甲酸二异丁酯和磷酸酯；本发明采用改性三元乙丙橡胶作为主料，通过对三元乙丙橡胶的改性，具有低烟、无卤、阻燃、高机械强度、高绝缘电阻的特性，而且具有良好的弹性、柔韧性，同时在原料中采用纳米凹凸棒土作为补强剂，纳米级二氧化钛和碳化铝作为填料。

Description

一种含有改性三元乙丙橡胶的电缆护套料及其制备方法
技术领域
本发明涉及一种电缆护套料，具体涉及一种含有改性三元乙丙橡胶的电缆护套料及其制备方法。
背景技术
随着经济的迅速发展，电线电缆在各个行业、领域中都得到广泛的应用，电气火灾事故的频繁发生，电线电缆的阻燃问题逐渐引起世界各国的重视，电缆燃烧时释放出大量烟雾和有毒的、腐蚀性的气体是火灾中危险因素，在火灾中妨碍了人们的安全撤离和灭火工作，使生命财产遭到严重损失，同时随着通讯事业、汽车工业和计算机工业的发展，对电缆护套料的质量要求日益增加，本发明提供一种含有改性三元乙丙橡胶的电缆护套料及其制备方法。
发明内容
本发明的目的在于提供一种含有改性三元乙丙橡胶的电缆护套料及其制备方法。
本发明采用如下技术方案：
含有改性三元乙丙橡胶的电缆护套料，其组成原料的重量份为：改性三元乙丙橡胶85-90、氢化丁腈橡胶10-15、高炉矿渣3.0-4.0、沸石分子筛20-25、碳化铝14-18、促进剂808  1.1-1.3、促进剂CZ  1.6-2.0、N-（β一氨乙基）-γ-氨丙基三甲（乙）氧基硅烷 3.8-4.5、蓖麻酸钡2.0-3.0、抗氧剂1010  0.3-0.5、邻苯二甲酸二异丁酯3.5-4.0和磷酸酯3.3-3.5。
含有改性三元乙丙橡胶的电缆护套料，其组成原料的重量份为：改性三元乙丙橡胶88、氢化丁腈橡胶12、高炉矿渣3.5、沸石分子筛22、碳化铝16、促进剂808  1.2、促进剂CZ  1.8、N-（β一氨乙基）-γ-氨丙基三甲（乙）氧基硅烷 4.2、蓖麻酸钡2.5、抗氧剂1010  0.4、邻苯二甲酸二异丁酯3.8和磷酸酯3.4。
含有改性三元乙丙橡胶的电缆护套料的制备方法，包括以下步骤：
（1）改性三元乙丙橡胶的制备：
配方（重量份）：三元乙丙橡胶25-30、马来酸酐11-13、二甲苯 35-40、丙烯酸酯2.0-2.5、顺丁烯二酸酐2.8-3.2、2,6二叔丁基对甲酚3.5-4.0、蒙脱石粉1.2-1.4和交联剂 TAIC  0.5-0.7；
制备方法如下：
a：按组成原料的重量份将三元乙丙橡胶、二甲苯、顺丁烯二酸酐在110-130℃下搅拌反应3-5小时；
b：在步骤（a）中按重量份加入马来酸酐和丙烯酸酯在150-160℃下搅拌反应1-2小时；
c：在步骤（b）中加入2,6二叔丁基对甲酚、蒙脱石粉和交联剂 TAIC在160-170℃下搅拌反应1.0-2.0小时，最后蒸馏除去二甲苯溶剂，得到改性三元乙丙橡胶；
（2）按组成原料的重量份称取步骤（1）的改性三元乙丙橡胶和其他剩余各原料，常温下低速搅拌7-9分钟，使得混合均匀，然后在温度130-150℃在密炼后1-3分钟，打三角包8-12次，完成后碾页切片并冷却。
本发明的有益效果：
本发明采用改性三元乙丙橡胶作为主料，通过对三元乙丙橡胶的改性，具有低烟、无卤、阻燃、高机械强度、高绝缘电阻的特性，而且具有良好的弹性、柔韧性，同时在原料中采用纳米凹凸棒土作为补强剂，纳米级二氧化钛和碳化铝作为填料。
具体实施方式
实施例1：含有改性三元乙丙橡胶的电缆护套料，其组成原料的重量（kg）为：改性三元乙丙橡胶88、氢化丁腈橡胶12、高炉矿渣3.5、沸石分子筛22、碳化铝16、促进剂808  1.2、促进剂CZ  1.8、N-（β一氨乙基）-γ-氨丙基三甲（乙）氧基硅烷 4.2、蓖麻酸钡2.5、抗氧剂1010  0.4、邻苯二甲酸二异丁酯3.8和磷酸酯3.4。
含有改性三元乙丙橡胶的电缆护套料的制备方法，包括以下步骤：
（1）改性三元乙丙橡胶的制备：
配方（kg）：三元乙丙橡胶28、马来酸酐12、二甲苯 38、丙烯酸酯2.2、顺丁烯二酸酐3.0、2,6二叔丁基对甲酚3.8、蒙脱石粉1.3和交联剂 TAIC  0.6；
制备方法如下：
a：按组成原料的重量份将三元乙丙橡胶、二甲苯、顺丁烯二酸酐在120℃下搅拌反应4小时；
b：在步骤（a）中按重量份加入马来酸酐和丙烯酸酯在155℃下搅拌反应1-2小时；
c：在步骤（b）中加入2,6二叔丁基对甲酚、蒙脱石粉和交联剂 TAIC在165℃下搅拌反应1.5小时，最后蒸馏除去二甲苯溶剂，得到改性三元乙丙橡胶；
（2）按组成原料的重量份称取步骤（1）的改性三元乙丙橡胶和其他剩余各原料，常温下低速搅拌8分钟，使得混合均匀，然后在温度140℃在密炼后2分钟，打三角包10次，完成后碾页切片并冷却。
通过本发明的实施例1制得的电缆料性能数据：

Claims (3)

1.一种含有改性三元乙丙橡胶的电缆护套料，其特征在于其组成原料的重量份为：改性三元乙丙橡胶85-90、氢化丁腈橡胶10-15、高炉矿渣3.0-4.0、沸石分子筛20-25、碳化铝14-18、促进剂808  1.1-1.3、促进剂CZ  1.6-2.0、N-（β一氨乙基）-γ-氨丙基三甲（乙）氧基硅烷 3.8-4.5、蓖麻酸钡2.0-3.0、抗氧剂1010  0.3-0.5、邻苯二甲酸二异丁酯3.5-4.0和磷酸酯3.3-3.5。
2.根据权利要求1所述的含有改性三元乙丙橡胶的电缆护套料，其特征在于其组成原料的重量份为：改性三元乙丙橡胶88、氢化丁腈橡胶12、高炉矿渣3.5、沸石分子筛22、碳化铝16、促进剂808  1.2、促进剂CZ  1.8、N-（β一氨乙基）-γ-氨丙基三甲（乙）氧基硅烷 4.2、蓖麻酸钡2.5、抗氧剂1010  0.4、邻苯二甲酸二异丁酯3.8和磷酸酯3.4。
3.一种如权利要求1所述的含有改性三元乙丙橡胶的电缆护套料的制备方法，其特征在于包括以下步骤：
（1）改性三元乙丙橡胶的制备：
配方（重量份）：三元乙丙橡胶25-30、马来酸酐11-13、二甲苯 35-40、丙烯酸酯2.0-2.5、顺丁烯二酸酐2.8-3.2、2,6二叔丁基对甲酚3.5-4.0、蒙脱石粉1.2-1.4和交联剂 TAIC  0.5-0.7；
制备方法如下：
a：按组成原料的重量份将三元乙丙橡胶、二甲苯、顺丁烯二酸酐在110-130℃下搅拌反应3-5小时；
b：在步骤（a）中按重量份加入马来酸酐和丙烯酸酯在150-160℃下搅拌反应1-2小时；
c：在步骤（b）中加入2,6二叔丁基对甲酚、蒙脱石粉和交联剂 TAIC在160-170℃下搅拌反应1.0-2.0小时，最后蒸馏除去二甲苯溶剂，得到改性三元乙丙橡胶；
（2）按组成原料的重量份称取步骤（1）的改性三元乙丙橡胶和其他剩余各原料，常温下低速搅拌7-9分钟，使得混合均匀，然后在温度130-150℃在密炼后1-3分钟，打三角包8-12次，完成后碾页切片并冷却。
CN201310162135.3A 2013-05-06 2013-05-06 一种含有改性三元乙丙橡胶的电缆护套料及其制备方法 Active CN103289281B (zh)