CN103276827A - 聚苯砂浆保温板及聚苯砂浆的制备方法 - Google Patents

聚苯砂浆保温板及聚苯砂浆的制备方法 Download PDF

Info

Publication number
CN103276827A
CN103276827A CN2013101810209A CN201310181020A CN103276827A CN 103276827 A CN103276827 A CN 103276827A CN 2013101810209 A CN2013101810209 A CN 2013101810209A CN 201310181020 A CN201310181020 A CN 201310181020A CN 103276827 A CN103276827 A CN 103276827A
Authority
CN
China
Prior art keywords
polyphenyl
mortar
polyphenyl mortar
preparation
plate
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2013101810209A
Other languages
English (en)
Other versions
CN103276827B (zh
Inventor
史凯明
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Changzhou Feiyun Building Material Co., Ltd.
Original Assignee
CHANGZHOU FEIYUN BUILDING MATERIAL Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by CHANGZHOU FEIYUN BUILDING MATERIAL Co Ltd filed Critical CHANGZHOU FEIYUN BUILDING MATERIAL Co Ltd
Priority to CN201310181020.9A priority Critical patent/CN103276827B/zh
Publication of CN103276827A publication Critical patent/CN103276827A/zh
Application granted granted Critical
Publication of CN103276827B publication Critical patent/CN103276827B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种聚苯砂浆保温板及聚苯砂浆的制备方法，包括：基墙、保温层、噪音吸收层和饰面层，保温层包括第一聚苯砂浆板和第二聚苯砂浆板，第一聚苯砂浆板和第二聚苯砂浆板之间设置有耐碱玻纤维网格布，噪音吸收层通过粘结剂连接在保温层上，饰面层通过粘结剂连接在噪音吸收层上，聚苯砂浆制备方法包括改性聚苯颗粒的制备和改性胶粉的制备，然后在改性聚苯砂浆和改性胶粉中加入减水剂、石膏、粉煤灰和水，在40~65℃下进行充分均匀搅拌。通过上述方式，本发明能够减少聚苯砂浆板的抗剪应力，保证良好的耐候性和耐火性，增强保温板的强度，保证了建筑环境中噪音吸收率的有效提高，同时提高了保保温砂浆的致密性能和紧实程度。

Description

聚苯砂浆保温板及聚苯砂浆的制备方法
技术领域
本发明涉及建筑保温板领域，特别是涉及一种聚苯砂浆保温板及聚苯砂浆的制备方法。
背景技术
近年来，随着社会经济的飞速发展，建筑行业也得到了越来越广泛的发展和进步。建筑生产中外墙的保温是建筑行业的重要步骤，也是投入较大的一个环节，外墙保温性能的优异与建筑的使用寿命息息相关。
现有技术中一般都会采用保温砂浆板，但是它的抗剪性能不佳，保温砂浆的致密性能也不好，同时保温砂浆板不能很好的抵抗噪音，影响了周围环境。
发明内容
本发明主要解决的技术问题是提供一种聚苯砂浆保温板及聚苯砂浆的制备方法，能够减少聚苯砂浆板的抗剪应力，保证聚苯砂浆板良好的耐候性和耐火性，增强保温板的强度，保证了建筑环境中噪音吸收率的有效提高，同时提高了保保温砂浆的致密性能和紧实程度。
为解决上述技术问题，本发明采用的一个技术方案是：提供一种聚苯砂浆保温板，包括：基墙、保温层、噪音吸收层和饰面层，所述保温层包括第一聚苯砂浆板和第二聚苯砂浆板，所述第一聚苯砂浆板和第二聚苯砂浆板之间设置有耐碱玻纤维网格布，所述噪音吸收层通过粘结剂连接在保温层上，所述饰面层通过粘结剂连接在噪音吸收层上。
在本发明一个较佳实施例中，所述耐碱玻纤维网格布与第一聚苯砂浆板和第二聚苯砂浆板连接的两个侧面均涂覆有丙烯酸共聚液层。
在本发明一个较佳实施例中，所述耐碱玻纤维网格布通过锚栓与第一聚苯砂浆板和第二聚苯砂浆板固定设置。
在本发明一个较佳实施例中，所述噪音吸收层包括吸音泡沫板和连接在吸音泡沫板两侧的吸音棉。
在本发明一个较佳实施例中，所述饰面层采用装饰砂浆或装饰板制成。
为解决上述技术问题，本发明采用的另一个技术方案是：提供一种聚苯砂浆的制备方法，包括如下组分：胶粉料26~68g、聚苯颗粒56~105g、硅酸铝3~8g、玻化微珠2~10g、减水剂12~24g、石膏12~22g、粉煤灰10~16g和水100~266g，所述制备过程为：
1）、改性聚苯颗粒的制备：取硅酸铝和玻化微珠混配成溶液，将混配后的溶液喷涂聚苯颗粒的表面，然后加入粉煤灰均匀混合制得；
2）、改性胶粉的制备：取胶粉料和玻化微珠进行混配，然后加入石膏均匀搅拌制得；
3）、在改性聚苯砂浆和改性胶粉中加入减水剂、石膏、粉煤灰和水，然后在40~65℃下进行充分均匀搅拌即制得聚苯砂浆。
本发明的有益效果是：本发明聚苯砂浆保温板及聚苯砂浆的制备方法能够减少聚苯砂浆板的抗剪应力，保证聚苯砂浆板良好的耐候性和耐火性，增强保温板的强度，保证了建筑环境中噪音吸收率的有效提高，同时提高了保保温砂浆的致密性能和紧实程度。
附图说明
图1是本发明聚苯砂浆保温板一较佳实施例的结构示意图；
附图中各部件的标记如下：1、基墙，2、第一聚苯砂浆板，3、第二聚苯砂浆板，4、耐碱玻纤维网格布，5、丙烯酸共聚液层，6、吸音泡沫板，7、吸音棉，8、饰面层。
具体实施方式
下面结合附图对本发明的较佳实施例进行详细阐述，以使本发明的优点和特征能更易于被本领域技术人员理解，从而对本发明的保护范围做出更为清楚明确的界定。
请参阅图1，本发明实施例包括：
一种聚苯砂浆保温板，包括：基墙1、保温层、噪音吸收层和饰面层8，所述保温层包括第一聚苯砂浆板2和第二聚苯砂浆板3，所述第一聚苯砂浆板2和第二聚苯砂浆板3之间设置有耐碱玻纤维网格布4，所述噪音吸收层通过粘结剂连接在保温层上，所述饰面层8通过粘结剂连接在噪音吸收层上，所述饰面层8采用装饰砂浆或装饰板制成。
所述耐碱玻纤维网格布4通过锚栓与第一聚苯砂浆板2和第二聚苯砂浆板3固定设置，能够增强耐碱玻纤维网格布4的强度，减少聚苯砂浆板的抗剪应力。
本发明中，所述耐碱玻纤维网格布4与第一聚苯砂浆板3和第二聚苯砂浆板3连接的两个侧面均涂覆有丙烯酸共聚液层5，能够保证聚苯砂浆板良好的耐候性和耐火性。
所述噪音吸收层包括吸音泡沫板6和连接在吸音泡沫板6两侧的吸音棉7，保证了建筑环境中噪音吸收率的有效提高。
本发明中聚苯砂浆的制备方法，包括：胶粉料26~68g、聚苯颗粒56~105g、硅酸铝3~8g、玻化微珠2~10g、减水剂12~24g、石膏12~22g、粉煤灰10~16g和水100~266g。
其具体的制备过程为：
1）、改性聚苯颗粒的制备：取硅酸铝和玻化微珠混配成溶液，将混配后的溶液喷涂聚苯颗粒的表面，然后加入粉煤灰均匀混合制得；
2）、改性胶粉的制备：取胶粉料和玻化微珠进行混配，然后加入石膏均匀搅拌制得；
3）、在改性聚苯砂浆和改性胶粉中加入减水剂、石膏、粉煤灰和水，然后在40~65℃下进行充分均匀搅拌即制得聚苯砂浆。
玻化微珠能够作为保温砂浆的密实调节剂，保证了保温砂浆的致密性能良好，提高了保温砂浆的紧实程度。
实施例一
1）、改性聚苯颗粒的制备：取硅酸铝3.5g和玻化微珠2g混配成溶液，将混配后的溶液喷涂聚苯颗粒的表面，其中聚苯颗粒60g，然后加入粉煤灰12g均匀混合制得；
2）、改性胶粉的制备：取胶粉料26g和玻化微珠3g进行混配，然后加入石膏15g均匀搅拌制得；
3）、在改性聚苯砂浆和改性胶粉中加入减水剂12g、石膏3g、粉煤灰3g和水100g，然后在40℃下进行充分均匀搅拌即制得聚苯砂浆。
实施例二
1）、改性聚苯颗粒的制备：取硅酸铝6g和玻化微珠4g混配成溶液，将混配后的溶液喷涂聚苯颗粒的表面，其中聚苯颗粒84g，然后加入粉煤灰10g均匀混合制得；
2）、改性胶粉的制备：取胶粉料40g和玻化微珠4g进行混配，然后加入石膏12g均匀搅拌制得；
3）、在改性聚苯砂浆和改性胶粉中加入减水剂16g、石膏8g、粉煤灰4g和水160g，然后在50℃下进行充分均匀搅拌即制得聚苯砂浆。
实施例三
1）、改性聚苯颗粒的制备：取硅酸铝8g和玻化微珠6g混配成溶液，将混配后的溶液喷涂聚苯颗粒的表面，其中聚苯颗粒100g，然后加入粉煤灰15g均匀混合制得；
2）、改性胶粉的制备：取胶粉料66g和玻化微珠2g进行混配，然后加入石膏13g均匀搅拌制得；
3）、在改性聚苯砂浆和改性胶粉中加入减水剂18g、石膏6g、粉煤灰1g和水206g，然后在60℃下进行充分均匀搅拌即制得聚苯砂浆。
本发明聚苯砂浆保温板及聚苯砂浆的制备方法的有益效果是：
能够减少聚苯砂浆板的抗剪应力，保证聚苯砂浆板良好的耐候性和耐火性，增强保温板的强度，保证了建筑环境中噪音吸收率的有效提高，同时提高了保保温砂浆的致密性能和紧实程度。
以上所述仅为本发明的实施例，并非因此限制本发明的专利范围，凡是利用本发明说明书及附图内容所作的等效结构或等效流程变换，或直接或间接运用在其他相关的技术领域，均同理包括在本发明的专利保护范围内。

Claims (6)

1.一种聚苯砂浆保温板，其特征在于，包括：基墙、保温层、噪音吸收层和饰面层，所述保温层包括第一聚苯砂浆板和第二聚苯砂浆板，所述第一聚苯砂浆板和第二聚苯砂浆板之间设置有耐碱玻纤维网格布，所述噪音吸收层通过粘结剂连接在保温层上，所述饰面层通过粘结剂连接在噪音吸收层上。
2.根据权利要求1所述的聚苯砂浆保温板，其特征在于，所述耐碱玻纤维网格布与第一聚苯砂浆板和第二聚苯砂浆板连接的两个侧面均涂覆有丙烯酸共聚液层。
3.根据权利要求1所述的聚苯砂浆保温板，其特征在于，所述耐碱玻纤维网格布通过锚栓与第一聚苯砂浆板和第二聚苯砂浆板固定设置。
4.根据权利要求1所述的聚苯砂浆保温板，其特征在于，所述噪音吸收层包括吸音泡沫板和连接在吸音泡沫板两侧的吸音棉。
5.根据权利要求1所述的聚苯砂浆保温板，其特征在于，所述饰面层采用装饰砂浆或装饰板制成。
6.一种聚苯砂浆的制备方法，其特征在于，包括如下组分：胶粉料26~68g、聚苯颗粒56~105g、硅酸铝3~8g、玻化微珠2~10g、减水剂12~24g、石膏12~22g、粉煤灰10~16g和水100~266g，所述制备过程为：
1）、改性聚苯颗粒的制备：取硅酸铝和玻化微珠混配成溶液，将混配后的溶液喷涂聚苯颗粒的表面，然后加入粉煤灰均匀混合制得；
2）、改性胶粉的制备：取胶粉料和玻化微珠进行混配，然后加入石膏均匀搅拌制得；
3）、在改性聚苯砂浆和改性胶粉中加入减水剂、石膏、粉煤灰和水，然后在40~65℃下进行充分均匀搅拌即制得聚苯砂浆。
CN201310181020.9A 2013-05-16 2013-05-16 聚苯砂浆保温板及聚苯砂浆的制备方法 Expired - Fee Related CN103276827B (zh)