CN103275429A - Water supply pipe manufactured by polyvinyl-chlorid material - Google Patents
Water supply pipe manufactured by polyvinyl-chlorid material Download PDFInfo
- Publication number
- CN103275429A CN103275429A CN2013102465418A CN201310246541A CN103275429A CN 103275429 A CN103275429 A CN 103275429A CN 2013102465418 A CN2013102465418 A CN 2013102465418A CN 201310246541 A CN201310246541 A CN 201310246541A CN 103275429 A CN103275429 A CN 103275429A
- Authority
- CN
- China
- Prior art keywords
- service pipe
- water service
- polyvinyl
- chlorid
- pipe processed
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a water supply pipe manufactured by polyvinyl-chlorid material. The composition of raw materials by weight percent is as follows: 65-80% of polyvinyl-chlorid, 1-2% of antimony sulfate, 1.5-3% of phosphite ester, 10-15% of acrylonitrile-butadiene-styrene copolymer, 3-14% of dioctyl phthalate, and 0.5-1.5% of manganese peroxide. Through the adoption of the manner, the pipe has safety, convenience, and reliability in using, can adopt hot melting homogeneity to connect, and can finish the connection of one joint in a few seconds; medium has excellent flowing property, mechanical physical property, and anti-pressure property; and a pipe body has excellent pressure-bearing ability and long service life, and reduces the trouble caused by the maintenance of the water pipe.
Description
Technical field
The present invention relates to the plastic pipe field, particularly relate to a kind of pvc material water service pipe processed.
Background technology
Polyvinyl chloride abbreviates PVC as, bright in colour, corrosion-resistant, firm and durable.In manufacturing processed, strengthen its thermotolerance, toughness, ductility etc. by increasing some subsidiary material such as softening agent, antiaging agent.In chemistry and physical property, polyvinyl chloride is to use one of plastic material the most widely on the rigidity, and pvc material is a kind of amorphism material.Pvc material has noninflammability, high strength, gasproof marquis variability and good geometrical stability, and oxygenant, reductive agent and strong acid are had very strong resistibility.
Pvc material can be used in the manufacturing water service pipe, but mechanical and physical performance commonly used is bad, and drainage under high pressure takes place easily, the flowing property of water is bad, stop up easily, leaking and stopping up all needs manually to overhaul, and has all caused the cost that uses to increase.
Summary of the invention
The technical problem that the present invention mainly solves provides a kind of pvc material water service pipe processed, and is safe and convenient to use, reliable.
For solving the problems of the technologies described above, the technical scheme that the present invention adopts is: provide a kind of pvc material water service pipe processed, by percentage to the quality, its raw material consists of:
Polyvinyl chloride 65-80%
Antimony trisulfate 1-2%
Phosphorous acid ester 1.5-3%
Acrylonitrile-butadiene-styrene copolymer 10-15%
Phthalic acid two zinc ester 3-14%
Manganse Dioxide 0.5-1.5%.
In a preferred embodiment of the present invention, by percentage to the quality, the raw material of described igelite water service pipe processed consists of:
Polyvinyl chloride 79%
Antimony trisulfate 1.8%
Phosphorous acid ester 1.5%
Acrylonitrile-butadiene-styrene copolymer 12%
Phthalic acid two zinc esters 5%
Manganse Dioxide 0.7%.
In a preferred embodiment of the present invention, by percentage to the quality, the raw material of described igelite water service pipe processed consists of:
Polyvinyl chloride 74.7%
Antimony trisulfate 1%
Phosphorous acid ester 1.5%
Acrylonitrile-butadiene-styrene copolymer 12%
Phthalic acid two zinc esters 10%
Manganse Dioxide 0.8%.
In a preferred embodiment of the present invention, by percentage to the quality, the raw material of described igelite water service pipe processed consists of:
Polyvinyl chloride 67%
Antimony trisulfate 2%
Phosphorous acid ester 2%
Acrylonitrile-butadiene-styrene copolymer 14%
Phthalic acid two zinc esters 14%
Manganse Dioxide 1%.
The invention has the beneficial effects as follows: pvc material of the present invention water service pipe processed, described water service pipe is safe and convenient to use, reliable, can adopt the hot melt homogeneity to connect, can finish a joint in several seconds and connect, the good flowing properties of medium has good mechanical and physical performance, the compressive resistance performance is good, body has good bearing capacity, and long service life has reduced the trouble that the water pipe inspection and repair shop causes.
Embodiment
Below preferred embodiment of the present invention is described in detail, thereby so that advantages and features of the invention can be easier to be it will be appreciated by those skilled in the art that protection scope of the present invention is made more explicit defining.
Embodiment one:
Provide a kind of pvc material water service pipe processed, by percentage to the quality, its raw material consists of:
Polyvinyl chloride 79%
Antimony trisulfate 1.8%
Phosphorous acid ester 1.5%
Acrylonitrile-butadiene-styrene copolymer 12%
Phthalic acid two zinc esters 5%
Manganse Dioxide 0.7%.
Embodiment two:
Provide a kind of pvc material water service pipe processed, by percentage to the quality, its raw material consists of:
Polyvinyl chloride 74.7%
Antimony trisulfate 1%
Phosphorous acid ester 1.5%
Acrylonitrile-butadiene-styrene copolymer 12%
Phthalic acid two zinc esters 10%
Manganse Dioxide 0.8%.
Embodiment three:
Provide a kind of pvc material water service pipe processed, by percentage to the quality, its raw material consists of:
Polyvinyl chloride 67%
Antimony trisulfate 2%
Phosphorous acid ester 2%
Acrylonitrile-butadiene-styrene copolymer 14%
Phthalic acid two zinc esters 14%
Manganse Dioxide 1%.
The pvc material water service pipe processed that the present invention discloses, described water service pipe is safe and convenient to use, reliable, can adopt the hot melt homogeneity to connect, can finish a joint in several seconds and connect, the good flowing properties of medium has good mechanical and physical performance, the compressive resistance performance is good, body has good bearing capacity, and long service life has reduced the trouble that the water pipe inspection and repair shop causes.
The above only is embodiments of the invention; be not so limit claim of the present invention; every equivalent structure or equivalent flow process conversion that utilizes description of the present invention to do; or directly or indirectly be used in other relevant technical fields, all in like manner be included in the scope of patent protection of the present invention.
Claims (4)
1. a pvc material water service pipe processed is characterized in that, by percentage to the quality, the raw material of described igelite water service pipe processed consists of:
Polyvinyl chloride 65-80%
Antimony trisulfate 1-2%
Phosphorous acid ester 1.5-3%
Acrylonitrile-butadiene-styrene copolymer 10-15%
Phthalic acid two zinc ester 3-14%
Manganse Dioxide 0.5-1.5%.
2. pvc material according to claim 1 water service pipe processed is characterized in that, by percentage to the quality, the raw material of described igelite water service pipe processed consists of:
Polyvinyl chloride 79%
Antimony trisulfate 1.8%
Phosphorous acid ester 1.5%
Acrylonitrile-butadiene-styrene copolymer 12%
Phthalic acid two zinc esters 5%
Manganse Dioxide 0.7%.
3. pvc material according to claim 1 water service pipe processed is characterized in that, by percentage to the quality, the raw material of described igelite water service pipe processed consists of:
Polyvinyl chloride 74.7%
Antimony trisulfate 1%
Phosphorous acid ester 1.5%
Acrylonitrile-butadiene-styrene copolymer 12%
Phthalic acid two zinc esters 10%
Manganse Dioxide 0.8%.
4. pvc material according to claim 1 water service pipe processed is characterized in that, by percentage to the quality, the raw material of described igelite water service pipe processed consists of:
Polyvinyl chloride 67%
Antimony trisulfate 2%
Phosphorous acid ester 2%
Acrylonitrile-butadiene-styrene copolymer 14%
Phthalic acid two zinc esters 14%
Manganse Dioxide 1%.