CN104193917A - PVC drainage pipe material - Google Patents
PVC drainage pipe material Download PDFInfo
- Publication number
- CN104193917A CN104193917A CN201410367368.1A CN201410367368A CN104193917A CN 104193917 A CN104193917 A CN 104193917A CN 201410367368 A CN201410367368 A CN 201410367368A CN 104193917 A CN104193917 A CN 104193917A
- Authority
- CN
- China
- Prior art keywords
- parts
- pvc
- drainage pipe
- pipe material
- barium sulfate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a PVC drainage pipe material. The PVC drainage pipe material is prepared from the following raw materials in parts by weight: 7-14 parts of epoxy fatty acid calcium-zinc soap, 10-15 parts of chlorinated paraffin, 5-10 parts of aluminum oxide, 15-20 parts of chlorinated polyethylene, 5-10 parts of barium sulfate, 35-55 parts of PVC resin, 10-20 parts of methacrylic propyltrimethylfluorosilane, 7-16 parts of melamine, 5-10 parts of coumarone resin, 7-14 parts of calcium carbonate and 7-12 parts of polyamide. The invention provides the PVC drainage pipe material which has the advantages of high toughness, large elongation, good anti-aging effect, good low-temperature toughness and high impact strength and tensile strength at a room temperature and high ring stiffness and Vicat softening temperature.
Description
Technical field
The present invention relates to building material technical field, be specifically related to a kind of PVC water shoot material.
Background technology
Polyvinyl chloride pipe, also claiming PVC pipe, is the tubing that the thermal plasticity high polymer that formed by polymerization of vinyl choride monomer is made, and take polyvinyl chloride (PVC) RESINS as main raw material, add appropriate antiaging agent, properties-correcting agent etc., the material forming through techniques such as mixing, calendering, vacuum formings.PVC pipe resistance to corrosion is strong, it is bonding to be easy to, PVC has very strong resistibility to oxygenant, reductive agent and strong acid.Yet it can be corroded and the also inapplicable occasion contacting with aromatic hydrocarbon, chlorinated hydrocarbon as the vitriol oil, concentrated nitric acid by dense oxidizing acid.
Summary of the invention
For the deficiencies in the prior art, technical problem to be solved by this invention is, provides a kind of toughness high, and elongation is large, and antiageing effect is good, low temperature resistant good toughness, the PVC water shoot material that the long softening temperature of normal temperature shock strength, tensile strength, ring stiffness and dimension is high.
For solving the problems of the technologies described above, the technical solution used in the present invention is: a kind of PVC water shoot material, by the raw material of following parts by weight, made: epoxyfatty acid calcium zinc soap 7-14 part, clorafin 10-15 part, aluminium sesquioxide 5-10 part, chlorinatedpolyethylene 15-20 part, barium sulfate 5-10 part, polyvinyl chloride resin 35-55 part, the fluorine-based silane 10-20 of methacrylic acid group propyl group front three part, trimeric cyanamide 7-16 part, coumarone indene resin 5-10 part, calcium carbonate 7-14 part, polymeric amide 7-12 part.
Above-mentioned PVC water shoot material, raw material by following parts by weight is made: 11 parts of epoxyfatty acid calcium zinc soaps, 12 parts of clorafins, 8 parts of aluminium sesquioxides, 17 parts of chlorinatedpolyethylenees, 8 parts, barium sulfate, 45 parts of polyvinyl chloride resins, 15 parts, the fluorine-based silane of methacrylic acid group propyl group front three, 13 parts of trimeric cyanamides, 8 parts of coumarone indene resins, 12 parts, calcium carbonate, 10 parts of polymeric amide.
PVC water shoot material advantage of the present invention is:
1, PVC water shoot material of the present invention, toughness is high, and elongation is large, and antiageing effect is good, low temperature resistant good toughness, the long softening temperature of normal temperature shock strength, tensile strength, ring stiffness and dimension is high; The tubing making has the feature of high tenacity, high mechanical strength, is better than market like product.
Embodiment
Below in conjunction with embodiment, the invention will be further described.
Embodiment 1, and a kind of PVC water shoot material is made by the raw material of following parts by weight: 7 parts of epoxyfatty acid calcium zinc soaps, 10 parts of clorafins, 5 parts of aluminium sesquioxides, 15 parts of chlorinatedpolyethylenees, 5 parts, barium sulfate, 35 parts of polyvinyl chloride resins, 10 parts, the fluorine-based silane of methacrylic acid group propyl group front three, 7 parts of trimeric cyanamides, 5 parts of coumarone indene resins, 7 parts, calcium carbonate, 7 parts of polymeric amide.
Embodiment 2, and a kind of PVC water shoot material is made by the raw material of following parts by weight: 11 parts of epoxyfatty acid calcium zinc soaps, 12 parts of clorafins, 8 parts of aluminium sesquioxides, 17 parts of chlorinatedpolyethylenees, 8 parts, barium sulfate, 45 parts of polyvinyl chloride resins, 15 parts, the fluorine-based silane of methacrylic acid group propyl group front three, 13 parts of trimeric cyanamides, 8 parts of coumarone indene resins, 12 parts, calcium carbonate, 10 parts of polymeric amide.
Embodiment 3, and a kind of PVC water shoot material is made by the raw material of following parts by weight: 14 parts of epoxyfatty acid calcium zinc soaps, 15 parts of clorafins, 10 parts of aluminium sesquioxides, 20 parts of chlorinatedpolyethylenees, 10 parts, barium sulfate, 55 parts of polyvinyl chloride resins, 20 parts, the fluorine-based silane of methacrylic acid group propyl group front three, 16 parts of trimeric cyanamides, 10 parts of coumarone indene resins, 14 parts, calcium carbonate, 12 parts of polymeric amide.
Certainly, above-mentioned explanation is not limitation of the present invention, and the present invention is also not limited to above-mentioned giving an example; those skilled in the art; in essential scope of the present invention, the variation of making, change, interpolation or replacement, all should belong to protection scope of the present invention.
Claims (2)
1. a PVC water shoot material, it is characterized in that: the raw material by following parts by weight is made: epoxyfatty acid calcium zinc soap 7-14 part, clorafin 10-15 part, aluminium sesquioxide 5-10 part, chlorinatedpolyethylene 15-20 part, barium sulfate 5-10 part, polyvinyl chloride resin 35-55 part, the fluorine-based silane 10-20 of methacrylic acid group propyl group front three part, trimeric cyanamide 7-16 part, coumarone indene resin 5-10 part, calcium carbonate 7-14 part, polymeric amide 7-12 part.
2. PVC water shoot material according to claim 1, it is characterized in that: the raw material by following parts by weight is made: 11 parts of epoxyfatty acid calcium zinc soaps, 12 parts of clorafins, 8 parts of aluminium sesquioxides, 17 parts of chlorinatedpolyethylenees, 8 parts, barium sulfate, 45 parts of polyvinyl chloride resins, 15 parts, the fluorine-based silane of methacrylic acid group propyl group front three, 13 parts of trimeric cyanamides, 8 parts of coumarone indene resins, 12 parts, calcium carbonate, 10 parts of polymeric amide.