CN106221059A - A kind of PVC U feed pipe formula - Google Patents
A kind of PVC U feed pipe formula Download PDFInfo
- Publication number
- CN106221059A CN106221059A CN201610601950.9A CN201610601950A CN106221059A CN 106221059 A CN106221059 A CN 106221059A CN 201610601950 A CN201610601950 A CN 201610601950A CN 106221059 A CN106221059 A CN 106221059A
- Authority
- CN
- China
- Prior art keywords
- parts
- pvc
- feed pipe
- oatmeal
- resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of PVC U feed pipe formula, it is made up of following raw material, in terms of parts by weight: calcium zinc stabilizer 3～4 parts, paraffin 0.08～0.15 part, stearic acid 0.1～0.4 part, brightening agent 0.007～0.013 part, resin-oatmeal 140～160 parts, nano silicon 2～3 parts, titanium dioxide 3～5 parts, fine particle calcium carbonate 11～13 parts.Hinge structure, the present invention has higher shock resistance and chemical-resistance, and quality is hard, and corrosion-resistant non-scaling is easy for installation, inexpensive.
Description
Technical field
The present invention relates to feed pipe technical field, particularly to a kind of PVC-U feed pipe formula.
Background technology
Existing feed pipe, there is problems in that shock resistance is poor, in use, has UPVC monomer and interpolation
Agent is oozed out, and is not suitable for delivery, and joint adhering technique requires higher, and hardening time is longer.
Summary of the invention
The technical problem to be solved is to provide a kind of PVC-U feed pipe formula, utilize that this formula makes to
Water pipe, has higher shock resistance and chemical-resistance, and quality is hard, and corrosion-resistant non-scaling is easy for installation, inexpensive.
The technical scheme is that a kind of PVC-U feed pipe formula, by following raw material group
Become, in terms of parts by weight: calcium zinc stabilizer 3～4 parts, paraffin 0.08～0.15 part, stearic acid 0.1～0.4 part, brightening agent
0.007～0.013 part, resin-oatmeal 140～160 parts, nano silicon 2～3 parts, titanium dioxide 3～5 parts, fine particle calcium carbonate 11～13 parts.
The invention has the beneficial effects as follows: the PVC-M feed pipe utilizing this formula to make has higher impact resistance
Energy and chemical-resistance, quality is hard, corrosion-resistant non-scaling, easy for installation, inexpensive.
On the basis of technique scheme, the present invention can also do following improvement.
Further, a kind of PVC-U feed pipe formula, it is made up of following raw material, in terms of parts by weight: calcium zinc stabilizer 3.8
Part, 0.1 part of paraffin, stearic acid 0.3 part, 0.01 part of brightening agent, resin-oatmeal 150 parts, nano silicon 2.5 parts, titanium dioxide 4
Part, fine particle calcium carbonate 10 parts.
Above-mentioned further scheme is used to provide the benefit that: calcium zinc stabilizer 3.8 parts can make tubing not affect water quality, nanometer
Silicon dioxide is stablized nontoxic, pollution-free；Nano silicon 2.5 parts strengthens the wearability of its inwall, and hardness of film increases, surface
Self-cleaning ability also obtains improvement；Fine particle calcium carbonate 10 parts can reduce the weight of body, light weight, and handling and loading is convenient so that pipeline connects to be executed
Work is easy rapidly, and construction work is taken cheap.
Further, a kind of PVC-U feed pipe formula, it is made up of following raw material, in terms of parts by weight: calcium zinc stabilizer 3 parts,
0.08 part of paraffin, stearic acid 0.1 part, 0.007 part of brightening agent, resin-oatmeal 140 parts, nano silicon 2 parts, titanium dioxide 3 parts, light
Calcium 8 parts.
Above-mentioned further scheme is used to provide the benefit that: calcium zinc stabilizer 3 parts can make body more stable, less soluble
Solving, do not affect water quality, suitable for large area applications, material has good pressure performance, shock resistance and tensile strength
Performance.
Further, a kind of PVC-U feed pipe formula, it is made up of following raw material, in terms of parts by weight: calcium zinc stabilizer 4 parts,
0.15 part of paraffin, stearic acid 0.4 part, 0.013 part of brightening agent, resin-oatmeal 160 parts, nano silicon 3 parts, titanium dioxide 5 parts, light
Calcium 12 parts.
Above-mentioned further scheme is used to provide the benefit that: calcium zinc stabilizer 4 parts and resin-oatmeal 160 parts have the resistance to of excellence
Sour, alkaline-resisting, corrosion resistance.
Detailed description of the invention
Principle and feature to the present invention are described below, and example is served only for explaining the present invention, is not intended to limit
Determine the scope of the present invention.
Embodiment 1:
A kind of PVC-U feed pipe formula, is made up of following raw material, in terms of parts by weight: calcium zinc stabilizer 3.8 parts, paraffin
0.1 part, stearic acid 0.3 part, 0.01 part of Stilbene-based brightening agent, resin-oatmeal 150 parts, nano silicon 2.5 parts, titanium dioxide
4 parts, fine particle calcium carbonate 10 parts.
Calcium zinc stabilizer 3.8 parts can make tubing not affect water quality, and nano silicon is stablized nontoxic, pollution-free；Nanometer two
Silicon oxide 2.5 parts strengthens the wearability of its inwall, and hardness of film increases, and clean surfaces ability also obtains improvement；10 parts of energy of fine particle calcium carbonate
Reducing the weight of body, light weight, handling and loading is convenient so that pipeline connection construction is easy rapidly, and construction work is taken cheap；
The main component of calcium zinc stabilizer has calcium stearate, castor oil acid calcium, zinc stearate, zinc ricinate, Yi Jihuan
Oxygen soybean oil, UV absorbent.
Resin-oatmeal is the powder that resin is made.
By calcium zinc stabilizer 3.8 parts, 0.1 part of paraffin, stearic acid 0.3 part, 0.01 part of Stilbene-based brightening agent, resin-oatmeal
150 parts, nano silicon 2.5 parts, titanium dioxide 4 parts, fine particle calcium carbonate 10 parts in the high-speed mixer of 135 DEG C be blended 5 minutes, then
Cold mix 45 DEG C after take the dish out of the pot, then by extrusion molding wire casing.
Embodiment 2:
A kind of PVC-U feed pipe formula, is made up of following raw material, in terms of parts by weight: calcium zinc stabilizer 3 parts, paraffin
0.08 part, stearic acid 0.1 part, 0.007 part of Stilbene-based brightening agent, resin-oatmeal 140 parts, nano silicon 2 parts, titanium dioxide
3 parts, fine particle calcium carbonate 8 parts.
Calcium zinc stabilizer 3 parts can make body more stable, not readily dissolves, and does not affect water quality, suitable for large area applications,
Material has good pressure performance, shock resistance and tensile strength performance.
By calcium zinc stabilizer 3 parts, 0.08 part of paraffin, stearic acid 0.1 part, 0.007 part of Stilbene-based brightening agent, resin-oatmeal
140 parts, nano silicon 2 parts, titanium dioxide 3 parts, fine particle calcium carbonate 8 parts in the high-speed mixer of 135 DEG C be blended 5 minutes, the coldest
Take the dish out of the pot after mixing 45 DEG C, then by extrusion molding wire casing.
Embodiment 3:
A kind of PVC-U feed pipe formula, is made up of following raw material, in terms of parts by weight: calcium zinc stabilizer 4 parts, paraffin
0.15 part, stearic acid 0.4 part, 0.013 part of Stilbene-based brightening agent, resin-oatmeal 160 parts, nano silicon 3 parts, titanium dioxide
5 parts, fine particle calcium carbonate 12 parts.
Calcium zinc stabilizer 4 parts and resin-oatmeal 160 parts have acidproof, alkaline-resisting, the corrosion resistance of excellence.
By calcium zinc stabilizer 4 parts, 0.15 part of paraffin, stearic acid 0.4 part, 0.013 part of Stilbene-based brightening agent, resin-oatmeal
160 parts, nano silicon 3 parts, titanium dioxide 5 parts, fine particle calcium carbonate 12 parts in the high-speed mixer of 135 DEG C be blended 5 minutes, the coldest
Take the dish out of the pot after mixing 45 DEG C, then by extrusion molding wire casing.
The foregoing is only presently preferred embodiments of the present invention, not in order to limit the present invention, all spirit in the present invention and
Within principle, any modification, equivalent substitution and improvement etc. made, should be included within the scope of the present invention.
Claims (4)
1. a PVC-U feed pipe formula, it is characterised in that be made up of following raw material, in terms of parts by weight: calcium zinc stabilizer 3
～4 parts, paraffin 0.08～0.15 part, stearic acid 0.1～0.4 part, brightening agent 0.007～0.013 part, resin-oatmeal 140～160
Part, nano silicon 2～3 parts, titanium dioxide 3～5 parts, fine particle calcium carbonate 11～13 parts.
A kind of PVC-U feed pipe formula, it is characterised in that be made up of following raw material, with weight portion
Number meter: calcium zinc stabilizer 3.8 parts, 0.1 part of paraffin, stearic acid 0.3 part, 0.01 part of brightening agent, resin-oatmeal 150 parts, nano-silica
SiClx 2.5 parts, titanium dioxide 4 parts, fine particle calcium carbonate 10 parts.
A kind of PVC-U feed pipe formula, it is characterised in that be made up of following raw material, with weight portion
Number meter: calcium zinc stabilizer 3 parts, 0.08 part of paraffin, stearic acid 0.1 part, 0.007 part of brightening agent, resin-oatmeal 140 parts, nano-silica
SiClx 2 parts, titanium dioxide 3 parts, fine particle calcium carbonate 8 parts.
A kind of PVC-U feed pipe formula, it is characterised in that be made up of following raw material, with weight portion
Number meter: calcium zinc stabilizer 4 parts, 0.15 part of paraffin, stearic acid 0.4 part, 0.013 part of brightening agent, resin-oatmeal 160 parts, nano-silica
SiClx 3 parts, titanium dioxide 5 parts, fine particle calcium carbonate 12 parts.