CN103273789A - Process for making annual ring type decay imitating wood picture - Google Patents
Process for making annual ring type decay imitating wood picture Download PDFInfo
- Publication number
- CN103273789A CN103273789A CN2013102257063A CN201310225706A CN103273789A CN 103273789 A CN103273789 A CN 103273789A CN 2013102257063 A CN2013102257063 A CN 2013102257063A CN 201310225706 A CN201310225706 A CN 201310225706A CN 103273789 A CN103273789 A CN 103273789A
- Authority
- CN
- China
- Prior art keywords
- plank
- mud
- baffle
- wood
- annual ring
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention relates to a process for making an annual ring type decay imitating wood picture. The process is characterized by comprising the following specific process steps: A, selecting a wood plate, and adopting a protection plate to provide covering protection for a wood plate region requiring drawing; B, carrying out jetting on the region with no protection plate covering by using a high pressure water gun; C, removing the protection plate, and carrying out air-drying of the wood plate; D, adopting mud to coat the original region covered by the protection plate, such that the outer outline of the mud and the outer outline of the covered region are the same; E, carrying out a charcoal burning treatment on the region with no mud coating on the wood plate by using open fire; F, removing the mud, and removing black carbonized material on the charcoal burning surface of the wood plate; G, carrying out washing and air-drying on the wood plate; and H, carrying out a polishing treatment on the original region covered by the protection plate, and carrying out a drawing treatment on the polished region. A purpose of the present invention is to provide a process for making an annual ring type decay imitating wood picture with a good annual ring type decay imitating wood effect, wherein the picture is formed on the annual ring type decay imitating wood, and achievement is easy.
Description
Technical field
The present invention relates to a kind of technology that the imitative rotten wood of annual ring is drawn of making.
Background technology
Rotten wood is trees or the timber that rots.Because a lot of rotten wood situation in the process of corruption differs, caused differently, therefore taken a fancy to by many businessmans, handle by suitable processing, can form personalized product, for example tea table, low stool etc.Because different, be difficult to find two identical rotten wood, thereby in the present society of pursuing individuality, the commercial value of rotten wood is considerable.The formation of rotten wood has contingency, formation time is long, and because wooden problem, many rotten wood can not be used, so formation and available rotten wood have become the product that supply falls short of demand naturally.Therefore, existing rotten wood is imitative rotten wood products substantially on the market, be adopt manually chisel and carve after, with surface rubbing, not only time-consuming with sand paper, and the artificial vestige of the wooden finished product of imitative corruption that forms is obvious, look nature inadequately.Simultaneously, imitative rotten wood all is whole imitative rotten on the market, does not see local imitative rotten product, does not see that particularly with imitative rotten wood be the technology that base plate is drawn a picture.
Summary of the invention
The object of the present invention is to provide the technology that the imitative rotten wood effect of a kind of annual ring is good and imitate the imitative rotten wood picture of the making annual ring of being convenient to realize of rotten wood formation paintings at annual ring.
Purpose of the present invention is achieved through the following technical solutions: a kind of technology of making the imitative rotten wood picture of annual ring, and it is characterized in that: its concrete processing step is as follows:
A, choose plank, and the baffle that dashes spray with the ability giant hides protection in the plank zone that needs are drawn a picture;
B, will dash spray with giant to the zone that does not hide baffle through the plank of processing of step A;
C, after step B handles, remove baffle and dry plank;
D, will coat in former baffle masked areas with mud through the plank that step C handles, the outline that makes mud is with to hide the outline of distinguishing consistent;
E, the plank that will handle through step D carry out charcoal with naked light to the zone of the mud of not coating and burn and handle;
F, after step e is handled, remove mud and also remove the black carbide that the plank charcoal burns face;
G, after step F is handled, plank cleaned dries;
H, after step G handles, former baffle masked areas is polished processing, handle carrying out paintings through grinded zone then.
Compared to prior art, the invention has the advantages that:
(1) utilizes the protective effect of baffle and mud, make the zone that is used for drawing a picture not be subjected to the influence of the imitative rotten wooden work of annual ring, conveniently to draw a picture; Paintings present thought-provoking visual effect under the setting off of imitative rotten timber apron;
(2) by dashing series of process such as spray, charcoal burning, the process of simulated logs corruption, the pattern that makes the imitative rotten wood of annual ring more get close to nature and form;
(3) handle by destructive engraving, make plank broken, degenerate formed broken effect naturally with the simulation plank, make the effect of the imitative rotten wood of annual ring more true to nature.
The specific embodiment
A kind of technology of making the imitative rotten wood picture of annual ring, it is characterized in that: its concrete processing step is as follows:
A, choose plank, and the baffle that dashes spray with the ability giant hides protection in the plank zone that needs are drawn a picture;
B, will dash spray with giant to the zone that does not hide baffle through the plank of processing of step A;
C, after step B handles, remove baffle and dry plank;
D, will coat in former baffle masked areas with mud through the plank that step C handles, the outline that makes mud is with to hide the outline of distinguishing consistent;
E, the plank that will handle through step D carry out charcoal with naked light to the zone of the mud of not coating and burn and handle;
F, after step e is handled, remove mud and also remove the black carbide that the plank charcoal burns face;
G, after step F is handled, plank cleaned dries;
H, after step G handles, former baffle masked areas is polished processing, handle carrying out paintings through grinded zone then.
Described baffle is that organic plates, acrylic board, iron sheet, PLASTIC LAMINATED or other have the material of protectiveness.
In order better to imitate the broken shape of rotten wood, plank had also carried out destructive engraving before carrying out step B processing handles: will carry out the destructiveness engraving with icking tool to the zone that does not hide baffle through the plank of processing of step A and handle.
The concrete operations that described destructive engraving is handled are: do not hide the engraving that the zone of baffle carries out at random at plank and destroy, make by the plate face at engraving destruction place and form tangible depression or broken hole, the plank edge then becomes irregular broken shape.Can select to use electronic icking tool in order to improve destructive carving efficiency.
After the destructiveness engraving was handled, the imitative rotten wood of the annual ring of formation had more rotten characteristic, made the imitative rotten wood of annual ring vivider more true to nature.
Baffle can be fixed on the plank by the following method in the described steps A: the air gun nail abuts in the baffle outward flange and hammers in the plank, then the air gun nail is placed on the part of baffle outer surface toward the inboard discount of baffle; Diverse location at the baffle edge repeats above-mentioned air gun nail fixation procedure as required, until baffle is fixed on the plank, guarantees that simultaneously baffle can not occur under the spray heaving or started and lose the phenomenon of protective effect dashing of giant.Can certainly be with the fixing baffle of other method.
By the said fixing method, avoided the use of glue, make the plate face of protected area of plank not contaminated, the paintings that are conducive to the later stage are handled, and convenient and swift when removing baffle, only need to remove the air gun nail and get final product.
Usually adopt the air gun nail of F30; the part that the air gun nail exceeds the baffle outer surface generally is about half of following closely length; be as the criterion to hammer into the plank appropriate depth, be unlikely that air gun nail easily comes off or the air gun ailing went into to be difficult for deeply pulling out, and have sufficient length to be used for fixedly baffle of discount.
The concrete operations of step B are: with giant the zone that the plank surface does not hide baffle is dashed spray, destroy the layer of wood on plank surface, with relative softer wooden destruction in the layer of wood, relative harder annual ring wood grain is more complete because keeping towards spray destruction than difficulty, thus formation concave-convex sense very tangible calendar year colyliform wood texture; The shower nozzle of giant adopts turbine shower nozzle or shower nozzle directly, and the turbine shower nozzle dashes the destructive strong of spray, dashes wood plate surface after the spray forming concave-convex sense very significantly in the calendar year colyliform wood texture, also can form erratic ruined; The pressure of giant is between 100 bar (bar)-300 bar (bar).
Among the step C, the purpose of drying plank is easily it not to be carried out the charcoal burning in the protection zone, and the plank moisture content after drying is preferably 10%-15%.
Among the step D, the moisture content of the mud of the usefulness of coating is 40%-55%, mud coat thickness more than 1.5mm.
Among the step D, the concrete preparation method of described mud is as follows:
1. get a splendid attire bucket, cover bung and tighten with 100-300 purpose paint filter cloth, red soil is placed on the paint filter cloth, with the red soil on the clear water flushing paint filter cloth, the red soil filtered fluid is kept somewhere in the splendid attire bucket, and reject residues in the residue that can't filter on the paint filter cloth; Repeat this process until the red soil filtered fluid that obtains requirement;
2. leave standstill the red soil filtered fluid, treat that the abundant post precipitation of red soil removes clear water, obtain red soil mud, make the abundant dehydration of its rapid draing with oven dry or method such as dry;
3. the strong earth a of mucosity that gets requirement is put in one and holds in the bucket, adds the 3-4 water doubly that weight is earth a weight toward holding in the bucket, pinches, rubs with the hands, washes or mechanical means is dissolved earth a in water with hand; Dissolve the water yield of usefulness very little, removing liquid is too dense can't to be filtered; The water yield is too many, and the earth a suspension water content after the filtration is too high, can cause the clay content of the mixing mud that makes to reduce;
4. will be filtered in another splendid attire bucket with 100-300 purpose paint filter cloth through the liquid that 3. step handles acquisition, obtain earth a suspension;
5. will mix with the earth a suspension that 4. obtains through step through the red soil that 2. step obtains, be deployed into mixing mud, the moisture content of mixing mud is 40%-55%; The moisture content of mixing mud is too low, and mixing mud is difficult for squeezing and coating; The mixing mud moisture content is too high, and the flowability of mixing mud is too strong, and the mixing mud that squeezing and coating go out can not meet its shape need because flowing.
Described earth a can be unselected clay, ball clay or fire clay etc.
5. will leave standstill processing through the earth a suspension that 4. step handles acquisition before handling carrying out step; After the sedimentation layering appears in earth a suspension, remove supernatant, to obtain the higher earth a suspension of earth a content.5. mix the mixing mud of acquisition like this through step, its mucosity can be stronger.
Fully the red soil moisture content after the dehydration is more low more good, can improve the earth a suspension amount of being blended into so as far as possible, is the mixing mud of 40%-55% thereby obtain moisture content.Be blended into earth a suspension more, improve the ratio of earth a in the mixing mud exactly, the mucosity of prepared like this mixing mud is just more strong, more is conducive to the squeezing and coating operation of mixing mud.
Accurately protect for convenience; avoid charcoal to burn and handle the zone that damage need be drawn a picture; among the step D; the method of coating of mud is as follows: mixing mud is packed in the pastry bag; then the mixing mud squeezing and coating on former baffle masked areas, the mixing mud profile that squeezing and coating are gone out is consistent with former baffle masked areas profile.The coat marginal portion of former baffle masked areas of squeezing and coating mixing mud is laid special stress on protecting and is subject to charcoal and burns the position of handling influence, the thicker mixing mud of coating at the position that needs are strengthened protection.Carry out mixing mud when coating, preferably with mixing mud to forming regional comprehensive complete covering and the good adhesion of paintings.
When adopting pastry bag to carry out squeezing and coating, for preventing that mud from stopping up the pastry bag outlet, the smooth and easy squeezing and coating of being convenient to of assurance mud extraction are operated, require the mud particles in the mud tiny, therefore available 100-300 purpose paint filter cloth filters, the order number of filter cloth is not The more the better, if the order number is too many, is unfavorable for filter operation on the contrary.Mixing mud coat thickness more than 1.5mm, it is more thick that mud is coated, its fire-resisting protection performance is more strong.
The red soil mucosity is not strong and water insoluble, but very easily by the aquation solution, very easily precipitate after dissolving, namely use 100-300 purpose paint filter cloth that it is filtered after, also can occur because of precipitation and/or the strong phenomenon of not stopping up mud mouth of mucosity, thereby influence the squeezing and coating operation.
Earth a, as unselected clay, ball clay or fire clay etc., mucosity is strong, but be difficult for by the aquation solution, dissolve the back and form suspension, sedimentation is slow, even the high-concentration suspension liquid that obtains after sedimentation also contains a large amount of moisture, it is obviously unrealistic to make its dehydration make mud with air drying, must take methods such as heating or oven dry to make its quick dehydration; But fast can form more stiff clod because dehydration is inhomogeneous in the dehydration process, clod is in case form and just be difficult to dissolve, particularly in the few mud of moisture with regard to more difficult dissolving; Like this, the single earth a mud of making can stop up the pastry bag outlet because containing clod, influences the squeezing and coating operation.
In red soil, add the mixing mud that forms behind the earth a suspension and not only be difficult for precipitation and strengthened mucosity, during squeezing and coating mud extraction smooth and easy, be conducive to the enforcement of the method for coating of this mud.
The concrete operations of step e are: with gasoline flame gun or oxy arc rifle the do not coat zone of mud, plank surface is carried out charcoal and burnt and handle, when charcoal burns to burn redwood material surface degree of being, handle the vestige of artificially carving and/or dash spray before to such an extent that more be tending towards nature, imitate the state after timber is degenerated naturally.Can certainly carry out charcoal with other thermal-flame and burn processing.Relatively softer wooden by more burning in the timber layer of wood, harder relatively annual ring wood grain is by less burning.
When charcoal burn to be handled, carry out edge charcoal burning to being positioned at the coat plank surface of outer rim of the pattern that forms of mud earlier, then comprehensive charcoal burning is carried out on the plank surface in the mud zone of not coating.When carrying out the processing of charcoal burning with gasoline flame gun or oxy arc rifle, the edge charcoal burns uses flammule, and charcoal burns and uses big flame comprehensively.
The zone at mud edge is being carried out charcoal when burning, mud can reduce or lose anti-flammability because of dehydration, can constantly add water in mud at this moment, is coated in the anti-flammability that the first-class method of mud is kept mud as getting wet with writing brush.
The concrete operations of step F are: after step e is handled, the mud that sticks to the plank surface is struck off; When removing carbide; adopt brass wire brush, scrub-brush, iron wire brush, brush machine or sander along grain direction wood surface to be carried out brushing back and forth; need brush carbide or till the black carbide that makes charcoal burning place is brushed by making; this moment, not protected plank area surfaces was mellow and full; artificial engraving and/or the vestige that the dashes spray nature that becomes is imitateed the state after timber is degenerated naturally before.Because of the different wooden burning degree difference of soft or hard in the timber layer of wood, through brushing back and forth, presented the tangible pseudo-classic style of concave-convex sense calendar year colyliform wood texture by the wood plate surface at charcoal burning place again.
Among the step G, the plank moisture content after drying is preferably 10%-15%.
Among the step G, after with soft hairbrush plank being scrubbed, dry again.
It can be the techniques of painting such as combination picture that adopt pyrography, traditional Chinese Painting, watercolor, oil painting or the two or more technique of painting to form that paintings are handled.
Picture and the combination of imitating rotten timber apron present thought-provoking visual effect.
Claims (10)
1. make the technology that the imitative rotten wood of annual ring is drawn for one kind, it is characterized in that: its concrete processing step is as follows:
A, choose plank, and the baffle that dashes spray with the ability giant hides protection in the plank zone that needs are drawn a picture;
B, will dash spray with giant to the zone that does not hide baffle through the plank of processing of step A;
C, after step B handles, remove baffle and dry plank;
D, will coat in former baffle masked areas with mud through the plank that step C handles, the outline that makes mud is with to hide the outline of distinguishing consistent;
E, the plank that will handle through step D carry out charcoal with naked light to the zone of the mud of not coating and burn and handle;
F, after step e is handled, remove mud and also remove the carbide that the plank charcoal burns face;
G, after step F is handled, plank cleaned dries;
H, after step G handles, former baffle masked areas is polished processing, handle carrying out paintings through grinded zone then.
2. a kind of annual ring of making according to claim 1 is imitated the technology that rotten wood is drawn, and it is characterized in that: plank had also carried out destructive engraving processing before carrying out step B processing: will carry out the destructiveness engraving with icking tool to the zone that does not hide baffle through the plank of processing of step A and handle.
3. a kind of annual ring of making according to claim 2 is imitated the technology that rotten wood is drawn; it is characterized in that: the concrete operations that described destructive engraving is handled are: do not hide the engraving that the zone of baffle carries out at random at plank and destroy; make by the plate face at engraving destruction place and form tangible depression or broken hole, the plank edge then becomes irregular broken shape.
4. a kind of annual ring of making according to claim 1 is imitated the technology that rotten wood is drawn, it is characterized in that: baffle is fixed on the plank by the following method in the described steps A: the air gun nail abuts in the baffle outward flange and hammers in the plank, then the air gun nail is placed on the part of baffle outer surface toward the inboard discount of baffle; Diverse location at the baffle edge repeats above-mentioned air gun nail fixation procedure as required, until baffle is fixed on the plank, guarantees that simultaneously baffle can not occur under the spray heaving or started and lose the phenomenon of protective effect dashing of giant.
5. a kind of annual ring of making according to claim 1 is imitated the technology that rotten wood is drawn; it is characterized in that: the concrete operations of step B are: with giant the zone that the plank surface does not hide baffle is dashed spray; destroy the layer of wood on plank surface; with relative softer wooden destruction in the layer of wood; relative harder annual ring wood grain is more complete because keeping towards spray destruction than difficulty, with formation concave-convex sense very tangible calendar year colyliform wood texture.
6. a kind of annual ring of making according to claim 1 is imitated the technology that rotten wood is drawn, it is characterized in that: the concrete operations of step e are: with gasoline flame gun or oxy arc rifle the do not coat zone of mud, plank surface is carried out charcoal and is burnt and handle, when charcoal burns to burn redwood material surface degree of being.
7. a kind of annual ring of making according to claim 1 is imitated the technology that rotten wood is drawn, and it is characterized in that: the concrete operations of step F are: after step e is handled, the mud that sticks to the plank surface is struck off; When removing carbide, adopt brass wire brush, scrub-brush, iron wire brush, brush machine or sander along grain direction wood surface to be carried out brushing back and forth, till the black carbide that makes charcoal burning place is brushed.
8. according to any described a kind of technology that the imitative rotten wood of annual ring is drawn of making of claim 1-7, it is characterized in that: among the step D, the concrete preparation method of described mud is as follows:
1. get a splendid attire bucket, cover bung and tighten with 100-300 purpose filter cloth, red soil is placed on the filter cloth, with the red soil on the clear water washing and filtering cloth, the red soil filtered fluid is kept somewhere in the splendid attire bucket, and reject residues in the residue that can't filter on the filter cloth; Repeat this process until the red soil filtered fluid that obtains requirement;
2. leave standstill the red soil filtered fluid, treat that the abundant post precipitation of red soil removes clear water, obtain red soil mud, make the abundant dehydration of its rapid draing with drying or drying;
3. the strong earth a of mucosity that gets requirement is put in one and holds in the bucket, adds the 3-4 water doubly that weight is earth a weight toward holding in the bucket, pinches, rubs with the hands, washes or mechanical means is dissolved earth a in water with hand;
4. will be filtered in another splendid attire bucket with 100-300 purpose filter cloth through the liquid that 3. step handles acquisition, obtain earth a suspension;
5. will mix with the earth a suspension that 4. obtains through step through the red soil that 2. step obtains, be deployed into mixing mud, the moisture content of mixing mud is 40%-55%.
9. a kind of technology that the imitative rotten wood of annual ring is drawn of making according to claim 8 is characterized in that: will leave standstill processing through the earth a suspension that 4. step handles acquisition before 5. handling carrying out step; After the sedimentation layering appears in earth a suspension, remove supernatant, to obtain the higher earth a suspension of earth a content.
10. a kind of annual ring of making according to claim 8 is imitated the technology that rotten wood is drawn; it is characterized in that: among the step D; the method of coating of mud is as follows: mixing mud is packed in the pastry bag; then the mixing mud squeezing and coating on former baffle masked areas, make the outer contour shape of the mixing mud that squeezing and coating go out consistent with the outer contour shape of former baffle masked areas.