CN103265862A - 聚氨酯保温板表面防火涂层及其制备方法 - Google Patents

聚氨酯保温板表面防火涂层及其制备方法 Download PDF

Info

Publication number
CN103265862A
CN103265862A CN2013102284272A CN201310228427A CN103265862A CN 103265862 A CN103265862 A CN 103265862A CN 2013102284272 A CN2013102284272 A CN 2013102284272A CN 201310228427 A CN201310228427 A CN 201310228427A CN 103265862 A CN103265862 A CN 103265862A
Authority
CN
China
Prior art keywords
insulation board
fire
thermal insulation
fireproof coating
coating
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2013102284272A
Other languages
English (en)
Inventor
唐志勇
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN2013102284272A priority Critical patent/CN103265862A/zh
Publication of CN103265862A publication Critical patent/CN103265862A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种组合物防火涂层，特别涉及一种应用在聚氨酯保温板表面的防火涂层及其制备方法。传统聚氨酯保温板防火等级多数只达到B1级，部分提升到复合A级的聚氨酯保温板原料价格昂贵、生产工艺复杂。本聚氨酯保温板表面防火涂层各原料组分按重量份比例由：丙烯酸乳液0.1～50、成膜助剂0.1～1、表面活性剂0.1～10、分散剂0.1～10、阻燃剂0.1～50、消泡剂0.1～20、减水剂0.1～20、水泥0.1～50、沙子0.1～50、去离子水10～40混合搅拌配制而成。本发明配方工艺合理、制备方法简单，涂覆在聚氨酯保温板上能够显著的提高其防火效果，另外还提高了聚氨酯保温板的粘接强度和保温效果。

Description

聚氨酯保温板表面防火涂层及其制备方法
技术领域
本发明涉及一种组合物防火涂层，特别涉及一种应用在聚氨酯保温板表面的防火涂层及其制备方法。
背景技术
2009年9月，《民用建筑外墙保温系统及外墙装饰防火暂行规定》颁布实施，对建筑保温材料的防火等级做了明确要求。我国普遍使用的墙体保温材料极易燃烧，如何将保温材料的高效节能与优异的防火于一身，成为一个行业性难题。聚氨酯外墙保温防火系统，具有突出的防火性能，耐火耐热，高温下不融化、无滴落物、低烟雾，尺寸稳定性好，并且具有良好的保温节能效果，将优异的防火性能和良好的节能效果于一身，适用于外墙保温等诸多领域。
防火等级国家防火建筑材料质量监督检验中心权威检测，多数聚氨酯(PIR)板防火等级达到B1级，但是随着物质生活水平的提高，人们对生活品质的要求也随之提高，希望聚氨酯外墙保温防火系统能够达到国家防火标准复合A级，高温下不熔滴，不软化，不扩散火焰穿透，从根本上杜绝外保温火灾的发生的隐患。
在这种情况下，目前市场上出现了一些防火等级提升到复合A级的聚氨酯保温板，但是其原料价格昂贵、生产工艺复杂，使得生产成本增大，限制了这些具有良好防火效果的聚氨酯保温板的广泛应用。
发明内容
本发明要解决的技术问题是如何克服现有技术的上述缺陷，提供一种能够显著提高聚氨酯保温板防火性能的聚氨酯保温板表面防火涂层。
为解决上述技术问题，本聚氨酯保温板表面防火涂层由以下组分按照所示重量份比例范围配制而成，
Figure BSA0000090914800000021
作为优选配比，本聚氨酯保温板表面防火涂层优选以下重量份比例配制，
Figure BSA0000090914800000022
作为优选配比，本聚氨酯保温板表面防火涂层优选以下重量份比例配制，
Figure BSA0000090914800000032
作为优选配比，本聚氨酯保温板表面防火涂层优选以下重量份比例配制，
作为优选配比，本聚氨酯保温板表面防火涂层优选以下重量份比例配制，
Figure BSA0000090914800000042
Figure BSA0000090914800000051
作为优选配比，本聚氨酯保温板表面防火涂层优选以下重量份比例配制，
Figure BSA0000090914800000052
作为优化，上述丙烯酸乳液为TRC-15乳液；所述成膜助剂为十二碳醇酯；上述表面活性剂为PE-100润湿剂；上述分散剂为LWJ-5040分散剂；上述阻燃剂为PU聚氨酯外墙保温材料专用A型环保阻燃剂；上述消泡剂为水泥砂浆专用消泡剂BX-835；上述减水剂为PC-1016聚羧酸高性能减水剂；上述水泥为强度等级42.5的水泥。
作为优化，上述沙子为过70/140目筛的沙子，过筛后将该沙子于97％的工业甲醇和8％的工业亚硝酸酐以重量份1000∶1的比例混合而成的混合液体中，在50℃条件下，浸泡24h。
本聚氨酯保温板表面防火涂层的制备方法是：将上述组份按照所示重量份比例混合，并于温度10℃～35℃，湿度小于≤50％的环境中，投入搅拌器搅拌或者人工搅拌，至各组分均匀混合，即得。
作为优选条件，所述制备温度为25℃，所述制备湿度为30％。
使用方法
首先将网格布覆盖到聚氨酯保温板裸板上表面，再将配制好本聚氨酯保温板表面防火涂层涂布于网格布上，最后经干燥，使本聚氨酯保温板表面防火涂层固定附着到聚氨酯保温板表面，成为一体，所述裸板为除切割成型外未进行任何额外处理的聚氨酯初始板材。
本发明聚氨酯保温板表面的防火涂层及其制备方法配方工艺合理、制备方法简单，涂覆在聚氨酯保温板上能够显著的提高其防火效果，另外还提高了聚氨酯保温板的粘接强度和保温效果。
具体实施方式
实施例1：在温度25℃，湿度30％的条件下，按照下述所示质量取下列组分投入搅拌器中搅拌，至各组分均匀混合，即得。
Figure BSA0000090914800000061
Figure BSA0000090914800000071
实施例2：在温度25℃，湿度30％的条件下，按照下述所示质量取下列组分投入搅拌器中搅拌，至各组分均匀混合，即得。
Figure BSA0000090914800000072
实施例3：在温度25℃，湿度30％的条件下，按照所示质量取下列组分投入搅拌器中搅拌，至各组分均匀混合，即得。
Figure BSA0000090914800000082
实施例4：在温度25℃，湿度30％的条件下，按照所示质量取下列组分投入搅拌器中搅拌，至各组分均匀混合，即得。
Figure BSA0000090914800000083
Figure BSA0000090914800000091
实施例5：在温度25℃，湿度30％的条件下，按照所示质量取下列组分投入搅拌器中搅拌，至各组分均匀混合，即得。
防火等级检验
(1)样品：随机抽选由依照实施例5制得的涂覆本聚氨酯保温板表面防火涂层的聚氨酯保温板1000mm×190mm×36mm20块，500×500×36mm6块。
(2)送检单位：国家防火建筑材料质量监督检验中心。
(3)送检编号：No.201110345。
(4)检验依据：GB8624-1997《建筑材料燃烧性能分级方法》
(5)检验报告：
Figure BSA0000090914800000101
(6)结论：经检验，该材料各项指标均符合不燃材料的规定要求。按GB8624-1997判定，该材料燃烧性能达到GB8624复合A级。
上述实施方式旨在举例说明本发明可为本领域专业技术人员实现或使用，对上述实施方式进行修改对本领域的专业技术人员来说将是显而易见的，故本发明包括但不限于上述实施方式，任何符合本权利要求书或说明书描述，符合与本文所公开的原理和新颖性、创造性特点的方法、工艺、产品，均落入本发明的保护范围之内。

Claims (10)

1.一种聚氨酯保温板表面防火涂层，其特征是：所述涂层由以下组分按照所示重量份比例范围配制而成，
Figure FSA0000090914790000011
2.根据权利要求1所述的聚氨酯保温板表面防火涂层，其特征是：所述涂层由以下组分按照所示重量份比例配制而成，
Figure FSA0000090914790000012
Figure FSA0000090914790000021
3.根据权利要求1所述的聚氨酯保温板表面防火涂层，其特征是：所述涂层由以下组分按照所示重量份比例配制而成，
4.根据权利要求1所述的聚氨酯保温板表面防火涂层，其特征是：所述涂层由以下组分按照所示重量份比例配制而成，
Figure FSA0000090914790000031
5.根据权利要求1所述的聚氨酯保温板表面防火涂层，其特征是：所述涂层由以下组分按照所示重量份比例配制而成，
Figure FSA0000090914790000032
6.根据权利要求1所述的聚氨酯保温板表面防火涂层，其特征是：所述涂层由以下组分按照所示重量份比例配制而成，
Figure FSA0000090914790000041
7.根据权利要求1-6任一所述的聚氨酯保温板表面防火涂层，其特征是：所述丙烯酸乳液为TRC-15乳液；所述成膜助剂为十二碳醇酯；所述表面活性剂为PE-100润湿剂；所述分散剂为LWJ-5040分散剂；所述阻燃剂为PU聚氨酯外墙保温材料专用A型环保阻燃剂；所述消泡剂为水泥砂浆专用消泡剂BX-835；所述减水剂为PC-1016聚羧酸高性能减水剂；所述水泥为强度等级42.5的水泥。
8.根据权利要求1-6任一所述的聚氨酯保温板表面防火涂层，其特征是：所述沙子为过70/140目筛的沙子。
9.一种氨酯保温板表面防火涂层的制备方法，其特征是：所述氨酯保温板表面防火涂层为权利要求1-7任一所述的氨酯保温板表面防火涂层，其制备方法是：将权利要求1-6任一所述组份按照所示重量份比例混合，并于温度10℃～35℃，湿度小于≤50％的环境中，投入搅拌器搅拌或者人工搅拌，至各组分均匀混合，即得。
10.根据权利要求9所述的氨酯保温板表面防火涂层的制备方法，其特征是：所述温度为25℃，所述湿度为30％。
CN2013102284272A 2013-06-09 2013-06-09 聚氨酯保温板表面防火涂层及其制备方法 Pending CN103265862A (zh)