CN103242765A - 一种以聚酯薄膜为基材的胶带的制造方法 - Google Patents

一种以聚酯薄膜为基材的胶带的制造方法 Download PDF

Info

Publication number
CN103242765A
CN103242765A CN201310211935XA CN201310211935A CN103242765A CN 103242765 A CN103242765 A CN 103242765A CN 201310211935X A CN201310211935X A CN 201310211935XA CN 201310211935 A CN201310211935 A CN 201310211935A CN 103242765 A CN103242765 A CN 103242765A
Authority
CN
China
Prior art keywords
polyester film
adhesive tape
base material
manufacturing
manufacture method
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201310211935XA
Other languages
English (en)
Inventor
周志强
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
SUZHOU HUAZHOU TAPES CO Ltd
Original Assignee
SUZHOU HUAZHOU TAPES CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by SUZHOU HUAZHOU TAPES CO Ltd filed Critical SUZHOU HUAZHOU TAPES CO Ltd
Priority to CN201310211935XA priority Critical patent/CN103242765A/zh
Publication of CN103242765A publication Critical patent/CN103242765A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种以聚酯薄膜为基材的胶带的制造方法，包括步骤为：将白明胶和水按一定比例混合至所述白明胶变软，静置一定时间，再加入阿拉伯树胶、胶黄蓍树胶、甘油和剩余的水分，置于水浴中加热，最后滴加入石碳酸，搅拌得到胶状物；将所述胶状物涂布在聚酯薄膜上，将所述聚酯薄膜在烘道中加热烘干，得到以聚酯薄膜为基材的胶带。通过上述方式，本发明提供的一种以聚酯薄膜为基材的胶带的制造方法，所述胶带在使用时具有极大的柔韧性和弹性，黏贴时间长，胶接强度高，能达到7.8N/m的胶接强度，对木材、皮革、织物、纸板和塑料等材料均有良好的胶接效果。

Description

一种以聚酯薄膜为基材的胶带的制造方法
技术领域
本发明涉及一种胶带的制造方法，特别是涉及一种以聚酯薄膜为基材的胶带的制造方法。
背景技术
胶带的表面上涂有一层粘着剂，才能令胶带能粘住物品，最早的粘着剂来自动物和植物，在十九世纪，橡胶是粘着剂的主要成份，而现代则广泛应用各种聚合物。粘着剂可以粘住东西，是由于本身的分子和欲连接物品的分子间形成键结，这种键结可以把分子牢牢地黏合在一起。胶带按他的功效分可以分为高温胶带、双面胶带、绝缘胶带、特种胶带、压敏胶带、模切胶带等，不同的功效适合不同的行业需求，人们为胶带找到了几百种用途，从补衣服到保护碰破的鸡蛋它都大有用途。传统的胶带黏着性能不好，使用时间不长，需要不断的进行更换，对于某些材料不能很好的黏着。
发明内容
本发明主要解决的技术问题是提供一种以聚酯薄膜为基材的胶带的制造方法，所述胶带黏着强度高、使用时间长。
为解决上述技术问题，本发明采用的一个技术方案是：提供一种以聚酯薄膜为基材的胶带的制造方法，包括步骤为：
（1）将白明胶和水按一定比例混合至所述白明胶变软，静置一定时间，再加入阿拉伯树胶、胶黄蓍树胶、甘油和剩余的水分，置于水浴中加热，最后滴加入石碳酸，搅拌得到胶状物；
（2）将所述胶状物涂布在聚酯薄膜上，将所述聚酯薄膜在烘道中加热烘干，得到以聚酯薄膜为基材的胶带。
在本发明一个较佳实施例中，步骤（1）中所述白明胶和所述水的比例为1g：2-3ml。
在本发明一个较佳实施例中，步骤（1）中所述静置时间为12-22小时。
在本发明一个较佳实施例中，步骤（1）中所述石碳酸的滴加速度为每秒钟2-3滴。
本发明的有益效果是：本发明的以聚酯薄膜为基材的胶带的制造方法，所述胶带在使用时具有极大的柔韧性和弹性，黏贴时间长，胶接强度高，能达到7.8 N/m的胶接强度，对木材、皮革、织物、纸板和塑料等材料均有良好的胶接效果。
具体实施方式
下面对本发明的较佳实施例进行详细阐述，以使本发明的优点和特征能更易于被本领域技术人员理解，从而对本发明的保护范围做出更为清楚明确的界定。
实施例一：
一种以聚酯薄膜为基材的胶带的制造方法，包括步骤为：
（1）将20kg白明胶和40ml的水混合至所述白明胶变软，静置14小时，再加入阿拉伯树胶、胶黄蓍树胶、甘油和剩余的水分，置于水浴中加热，最后滴加入石碳酸，所述石碳酸的滴加速度为每秒钟2滴，搅拌得到胶状物；
（2）将所述胶状物涂布在聚酯薄膜上，将所述聚酯薄膜在烘道中加热烘干，得到以聚酯薄膜为基材的胶带。
实施例二：
一种以聚酯薄膜为基材的胶带的制造方法，包括步骤为：
（1）将40kg白明胶和100ml的水混合至所述白明胶变软，静置20小时，再加入阿拉伯树胶、胶黄蓍树胶、甘油和剩余的水分，置于水浴中加热，最后滴加入石碳酸，所述石碳酸的滴加速度为每秒钟3滴，搅拌得到胶状物；
（2）将所述胶状物涂布在聚酯薄膜上，将所述聚酯薄膜在烘道中加热烘干，得到以聚酯薄膜为基材的胶带。
实施例三：
一种以聚酯薄膜为基材的胶带的制造方法，包括步骤为：
（1）将30kg白明胶和90ml的水混合至所述白明胶变软，静置16小时，再加入阿拉伯树胶、胶黄蓍树胶、甘油和剩余的水分，置于水浴中加热，最后滴加入石碳酸，所述石碳酸的滴加速度为每秒钟3滴，搅拌得到胶状物；
（2）将所述胶状物涂布在聚酯薄膜上，将所述聚酯薄膜在烘道中加热烘干，得到以聚酯薄膜为基材的胶带。
本发明揭示的以聚酯薄膜为基材的胶带的制造方法，所述胶带在使用时具有极大的柔韧性和弹性，黏贴时间长，胶接强度高，能达到7.8 N/m的胶接强度，对木材、皮革、织物、纸板和塑料等材料均有良好的胶接效果。
以上所述仅为本发明的实施例，并非因此限制本发明的专利范围，凡是利用本发明说明书所作的等效结构或等效流程变换，或直接或间接运用在其他相关的技术领域，均同理包括在本发明的专利保护范围内。

Claims (4)

1.一种以聚酯薄膜为基材的胶带的制造方法，其特征在于，包括步骤为：
（1）将白明胶和水按一定比例混合至所述白明胶变软，静置一定时间，再加入阿拉伯树胶、胶黄蓍树胶、甘油和剩余的水分，置于水浴中加热，最后滴加入石碳酸，搅拌得到胶状物；
（2）将所述胶状物涂布在聚酯薄膜上，将所述聚酯薄膜在烘道中加热烘干，得到以聚酯薄膜为基材的胶带。
2.根据权利要求1所述的以聚酯薄膜为基材的胶带的制造方法，其特征在于，步骤（1）中所述白明胶和所述水的比例为1g：2-3ml。
3.根据权利要求1所述的以聚酯薄膜为基材的胶带的制造方法，其特征在于，步骤（1）中所述静置时间为12-22小时。
4.根据权利要求1所述的以聚酯薄膜为基材的胶带的制造方法，其特征在于，步骤（1）中所述石碳酸的滴加速度为每秒钟2-3滴。
CN201310211935XA 2013-05-31 2013-05-31 一种以聚酯薄膜为基材的胶带的制造方法 Pending CN103242765A (zh)