CN103241057A - 牌匾制造方法 - Google Patents

牌匾制造方法 Download PDF

Info

Publication number
CN103241057A
CN103241057A CN2013101776208A CN201310177620A CN103241057A CN 103241057 A CN103241057 A CN 103241057A CN 2013101776208 A CN2013101776208 A CN 2013101776208A CN 201310177620 A CN201310177620 A CN 201310177620A CN 103241057 A CN103241057 A CN 103241057A
Authority
CN
China
Prior art keywords
board
plaque
silkwood
manufacturing
taille
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2013101776208A
Other languages
English (en)
Inventor
陆斌
赵飞
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN2013101776208A priority Critical patent/CN103241057A/zh
Publication of CN103241057A publication Critical patent/CN103241057A/zh
Pending legal-status Critical Current

Abstract

本发明提供了一种牌匾制造方法,方法包括S1、选取经干燥处理的金丝楠木并制成牌匾形状;S2、使用工具于所述金丝楠木上进行勾画;S3、浅浮雕与烙印相结合,对牌匾便面图形进行雕刻;S4、使用化学涂料上色。与现有技术相比,本发明的有益效果在于,采用干燥工艺处理的金丝楠木有效提高了牌匾的耐腐蚀性,在雕刻过程中,通过浅浮雕与烙印结合的技术,使得牌匾表面形成多图层,多图层使牌匾图案呈现远近效果,在上色过程中采用化学涂料可以有效的防止浅浮雕出现褪色等情况,延长了牌匾的使用寿命。

Description

牌匾制造方法
技术领域
本发明涉及工艺品制造领域,尤其涉及一种在金丝楠木上进行浅浮雕的牌匾浅浮雕方法。
背景技术
牌匾是中国独有的一种商业语言、文化符号。是融汉语言、汉字书法、中国传统建筑、雕刻于一体,集思想性、艺术性于一身的综合艺术作品。但是现有技术的牌匾制作工艺中,往往是简单的经过牌匾制作成型,然后雕刻字样或花型,使得制作出来的牌匾结构较为单一,样式也不够多样;在雕刻过程中,通过烙印将图形烙印在牌匾上,再通过画笔描绘,常常在使用较长时间后出现掉色等现象;另一方面,又由于现有工艺中,牌匾表面常常为单图层设计,对于希望在牌匾上雕刻风景人物的多图层要求,较为难以满足。另外,现有的牌匾主要采用的材质耐腐蚀不强,且长期悬挂后会出现开裂,受潮等现象。
有鉴于此,应当提供一种可以在牌匾上实现多图层,且能够延长牌匾使用寿命的牌匾制造方法。
发明内容
本发明的目的是提供一种长期使用不掉色,延长牌匾使用寿命,且在牌匾上雕刻多图层的牌匾制造方法。
根据本发明的一个方面,提供了一种牌匾制造方法,方法包括
S1、选取经干燥处理的金丝楠木并制成牌匾形状;
S2、使用工具于所述金丝楠木上进行勾画;
S3、浅浮雕与烙印相结合,对牌匾便面图形进行雕刻;
S4、使用化学涂料上色。
在一些实施方式中,步骤S1中,将金丝楠木放置在干燥室中,升温干燥,在室温到100℃之间按每3小时升温10℃的速率升温,在100℃以上按每2小时升温1℃的速率升温,升温至127℃-128℃,完成干燥。该种干燥方法简单、合理,易操作,改变了阴沉金丝楠木对周围环境中水分子的敏感性,提高了牌匾材质的稳定性,解决了开裂与变形问题。
在一些实施方式中,步骤S3中,对牌匾表面图案进行远近区分,对远景采用烙印,对近景采用浅浮雕。雕刻过程中,对远景采用烙印,对近景采用浅浮雕,浅浮雕技术使得牌匾表面的多图层效果较为明显,远端背景和近端景物区分明显。
与现有技术相比,本发明的有益效果在于,采用干燥工艺处理的金丝楠木有效提高了牌匾的耐腐蚀性,在雕刻过程中,通过浅浮雕与烙印结合的技术,使得牌匾表面形成多图层,多图层使牌匾图案呈现远近效果,在上色过程中采用化学涂料可以有效的防止浅浮雕出现褪色等情况,延长了牌匾的使用寿命。
附图说明
图1为本发明一实施方式的牌匾制作方法的流程示意图。
具体实施方式
下面结合附图及具体实施例对本发明作进一步的详细描述说明。
图1示意性地显示了根据本发明一种实施方式的牌匾制造方法。方法包括:
S1、选取经干燥处理的金丝楠木并制成牌匾形状;
S2、使用工具于所述金丝楠木上进行勾画;
S3、浅浮雕与烙印相结合,对牌匾便面图形进行雕刻;
S4、使用化学涂料上色。
在本发明的该实施方式中,方法具体为
Q1、对待加工的金丝楠木进行干燥处理并制造成牌匾型;
Q2、用笔在牌匾表面勾画图层轮廓;
Q3、采用浅浮雕技术与烙印技术相结合,在烙印的同时对牌匾表面的多个图层采用浅浮雕技术进行雕刻;
Q4、使用化学涂料上色。
在步骤S1中,将阴沉金丝楠木放置在干燥室中,升温干燥,在室温到100℃之间按每3小时升温10℃的速率升温,在100℃以上按每2小时升温1℃的速率升温,升温至127℃-128℃,完成干燥;在整个干燥过程中通过调节室内水气的方式使干燥室中湿度始终保持在饱和状态。该种干燥方法简单、合理,易操作,改变了阴沉金丝楠木对周围环境中水分子的敏感性,提高了牌匾材质的稳定性,解决了开裂与变形问题。
在步骤S2中,使用画笔,工笔等工具,在牌匾表面勾画,勾出多图层大致轮廓以及局部细节。
在步骤S3中,通过常规烙印技术对步骤S2中勾画成型的牌匾进行烙印,在烙印的同时采用浅浮雕技术对牌匾表面的多个图层进行雕刻。雕刻过程中,对远景采用烙印,对近景采用浅浮雕,浅浮雕技术使得牌匾表面的多图层效果较为明显,远端背景和近端景物区分明显。
在步骤S4中,使用化学涂料对步骤S3中成型的牌匾进行上色,在上色过程中采用化学涂料可以有效的防止浅浮雕出现褪色等情况,延长了牌匾的使用寿命。
与现有技术相比,本发明的有益效果在于,采用干燥工艺处理的金丝楠木有效提高了牌匾的耐腐蚀性,在雕刻过程中,通过浅浮雕与烙印结合的技术,使得牌匾表面形成多图层,多图层使牌匾图案呈现远近效果。
应当理解,虽然本说明书按照实施例加以描述,但并非每个实施例仅包含一个独立的技术方案,说明书的这种叙述方式仅仅是为清楚起见,本领域技术人员应当将说明书作为一个整体,各实施例中的技术方案也可以经适当组合,形成本领域技术人员可以理解的其他实施例。
上文所列出的一系列的详细说明仅仅是针对本发明的可行性实施例的具体说明,它们并非用以限制本发明的保护范围,凡未脱离本发明的等效实施例或变更均应包含在本发明的保护范围之内。

Claims (3)

1.牌匾制造方法,其特征在于,方法包括
S1、选取经干燥处理的金丝楠木并制成牌匾形状;
S2、使用工具于所述金丝楠木上进行勾画;
S3、浅浮雕与烙印相结合,对牌匾便面图形进行雕刻;
S4、使用化学涂料上色。
2.根据权利要求1所述的牌匾制造方法,其特征在于,所述步骤S1中,将所述金丝楠木放置在干燥室中,升温干燥,在室温到100℃之间按每3小时升温10℃的速率升温,在100℃以上按每2小时升温1℃的速率升温,升温至127℃-128℃,完成干燥。
3.根据权利要求1所述的牌匾制造方法,其特征在于,所述步骤S3中,对牌匾表面图案进行远近区分,对远景采用烙印,对近景采用浅浮雕。
CN2013101776208A 2013-05-15 2013-05-15 牌匾制造方法 Pending CN103241057A (zh)