CN103205606A - 一种复合铬镍合金金属的配方 - Google Patents
一种复合铬镍合金金属的配方 Download PDFInfo
- Publication number
- CN103205606A CN103205606A CN201310136674XA CN201310136674A CN103205606A CN 103205606 A CN103205606 A CN 103205606A CN 201310136674X A CN201310136674X A CN 201310136674XA CN 201310136674 A CN201310136674 A CN 201310136674A CN 103205606 A CN103205606 A CN 103205606A
- Authority
- CN
- China
- Prior art keywords
- accounts
- nickel alloy
- chrome
- metal
- hafnium
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明揭示了一种复合铬镍合金金属的配方，所述的复合铬镍合金金属的配方中包含以下金属成分：铬、镍、锆、铪、钼以及钛，所述的各金属成分所占重量百分比分别为：所述的铬占28%-37%，所述的镍占48%-53%，所述的锆占3.8%-4.6%，所述的铪占3.2%-4.4%，所述的钼占5.6%-6.7%，所述的钛占2.4%-3.3%。通过在复合铬镍合金中添加锆、铪、钼以及钛四种金属元素后，使得铬镍合金的耐腐蚀性、机械性能得到了提高，同时使得铬镍合金的熔点提高，耐高温寿命延长，使得铬镍和的电子变大，使用性能得到提升。
Description
技术领域
本发明涉及一种金属成分，具体涉及一种复合铬镍合金金属的配方。
背景技术
目前，市场上采用的铬镍合金在使用过中存在诸多不足，如电阻阻值不高，使用性能较低，耐高温性能较差，耐高温寿命短，机械强度不高等诸多限制使得铬镍合金在日常生活中的使用得不到广泛的发展。
发明内容
本发明的目的在于提供一种耐高温、高电阻、机械强度高的复合铬镍合金金属的配方。
本发明的技术方案是，一种复合铬镍合金金属的配方，所述的复合铬镍合金金属的配方中包含以下金属成分：铬、镍、锆、铪、钼以及钛，所述的各金属成分所占重量百分比分别为：所述的铬占28%-37%，所述的镍占48%-53%，所述的锆占3.8%-4.6%，所述的铪占3.2%-4.4%，所述的钼占5.6%-6.7%，所述的钛占2.4%-3.3%。
在本发明一个较佳实施例中，所述的各金属成分所占重量百分比具体比例为：所述的铬占29.6%，所述的镍占52.4%，所述的锆占4.3%，所述的铪占4.1%，所述的钼占6.4%，所述的钛占3.2%。
在本发明一个较佳实施例中，所述的各金属成分所占重量百分比具体比例为：所述的铬占35.4%，所述的镍占48.9%，所述的锆占4.1%，所述的铪占3.3%，所述的钼占5.8%，所述的钛占2.5%。
本发明所述为一种复合铬镍合金金属的配方，通过在复合铬镍合金中添加锆、铪、钼以及钛四种金属元素后，使得铬镍合金的耐腐蚀性、机械性能得到了提高，同时使得铬镍合金的熔点提高，耐高温寿命延长，使得铬镍和的电子变大，使用性能得到提升。
具体实施方式
下面对本发明的较佳实施例进行详细阐述，以使本发明的优点和特征能更易于被本领域技术人员理解，从而对本发明的保护范围做出更为清楚明确的界定。
本发明所述为一种复合铬镍合金金属的配方，所述的复合铬镍合金金属的配方中包含以下金属成分：铬、镍、锆、铪、钼以及钛，所述的各金属成分所占重量百分比分别为：所述的铬占28%-37%，所述的镍占48%-53%，所述的锆占3.8%-4.6%，所述的铪占3.2%-4.4%，所述的钼占5.6%-6.7%，所述的钛占2.4%-3.3%。
进一步地，所述的各金属成分所占重量百分比具体比例为：所述的铬占29.6%，所述的镍占52.4%，所述的锆占4.3%，所述的铪占4.1%，所述的钼占6.4%，所述的钛占3.2%。
进一步地，所述的各金属成分所占重量百分比具体比例为：所述的铬占35.4%，所述的镍占48.9%，所述的锆占4.1%，所述的铪占3.3%，所述的钼占5.8%，所述的钛占2.5%。
锆、铪、钼以及钛四种金属元素分别具有耐腐蚀、高熔点、高电阻、机械强度高等性能。
本发明所述为一种复合铬镍合金金属的配方，通过在复合铬镍合金中添加锆、铪、钼以及钛四种金属元素后，使得铬镍合金的耐腐蚀性、机械性能得到了提高，同时使得铬镍合金的熔点提高，耐高温寿命延长，使得铬镍和的电子变大，使用性能得到提升。
以上所述仅为本发明的具体实施方式，但本发明的保护范围并不局限于此，任何熟悉本领域的技术人员在本发明所揭露的技术范围内，可不经过创造性劳动想到的变化或替换，都应涵盖在本发明的保护范围之内。因此，本发明的保护范围应该以权利要求书所限定的保护范围为准。
Claims (3)
1.一种复合铬镍合金金属的配方，其特征在于：所述的复合铬镍合金金属的配方中包含以下金属成分：铬、镍、锆、铪、钼以及钛，所述的各金属成分所占重量百分比分别为：所述的铬占28%-37%，所述的镍占48%-53%，所述的锆占3.8%-4.6%，所述的铪占3.2%-4.4%，所述的钼占5.6%-6.7%，所述的钛占2.4%-3.3%。
2.根据权利要求1所述的复合铬镍合金金属的配方，其特征在于：所述的各金属成分所占重量百分比具体比例为：所述的铬占29.6%，所述的镍占52.4%，所述的锆占4.3%，所述的铪占4.1%，所述的钼占6.4%，所述的钛占3.2%。
3.根据权利要求1所述的复合铬镍合金金属的配方，其特征在于：所述的各金属成分所占重量百分比具体比例为：所述的铬占35.4%，所述的镍占48.9%，所述的锆占4.1%，所述的铪占3.3%，所述的钼占5.8%，所述的钛占2.5%。