CN103205124A - 一种硅橡胶海绵用发泡剂 - Google Patents
一种硅橡胶海绵用发泡剂 Download PDFInfo
- Publication number
- CN103205124A CN103205124A CN2013100680424A CN201310068042A CN103205124A CN 103205124 A CN103205124 A CN 103205124A CN 2013100680424 A CN2013100680424 A CN 2013100680424A CN 201310068042 A CN201310068042 A CN 201310068042A CN 103205124 A CN103205124 A CN 103205124A
- Authority
- CN
- China
- Prior art keywords
- parts
- foaming agent
- silicone rubber
- rubber sponge
- whipping agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种硅橡胶海绵用发泡剂,由下列重量份的原料组成:偶氮二甲酰胺8-12份、三亚硝基三亚甲基三胺5-8份、3,3’-二磺酰肼二苯砜4-6份、对,对-氧双(苯磺酰氨基脲)2-3份、碳酸氢钠3-5份、柠檬酸钠2-4份、二苯胍2-4份、甘油20-30份、草酸2-5份、季戊四醇2-3份、氧化锌0.5-1.5份。本发明生产出来的发泡剂具有优良的发泡力,发泡倍率高,加工稳定性,产生的泡沫具有很好的温度适应性和分散均匀性,低成本,使用方便。采用本发明发泡剂制备的硅橡胶海绵材料质地均匀美观、力学性能良好,密度小,微孔细密分散均匀,硅橡胶海绵的孔隙率达到75%,口模膨胀率达到400%。
Description
技术领域
本发明涉及一种发泡剂,具体涉及一种硅橡胶海绵用发泡剂。
背景技术
海绵橡胶由于其结构上的特殊性,即多孔性,可以产生各种特殊的效果,因此广泛应用于密封、减震、隔热、隔音、印染乃至离子交换等多方面。在航天、航空、交通运输、石油、化工、制药、仪表、文体及日常生活等都得到了广泛应用。硅橡胶海绵,除了具有海绵橡胶所具有的减震、隔音、隔热、密封等功能外,还具有硅橡胶独特的耐高能量冲击和高电热绝缘性能等特殊性能,广泛应用于电子工业和空间技术,同时,硅橡胶海绵还具有生理惰性、无毒、无臭、无腐蚀,且模量小,柔软而富有弹性,可用作制药厂、食品厂将液体产品干燥或颗粒状的大型干燥设备的密封以及各种嵌条等。而发泡剂是硅橡胶海绵中最重要的一种助剂,发泡剂的种类、数量对泡沫的物理机械性能、泡沫密度、耐温性等有直接影响。目前橡胶硅海绵使用的发泡剂存在发泡倍率较低、稳定性较差等问题,直接影响到橡胶制品的性能,造成制品强度低,质量不稳定,总体技术质量水平低。因此,针对发泡剂所存在的问题开展研究是非常必要和迫切的。
发明内容
本发明的目的是提供一种发泡倍率高、加工稳定性好的硅橡胶海绵发泡剂。
本发明采用的技术方案如下:
一种硅橡胶海绵用发泡剂,由下列重量份的原料组成:
优选地,一种硅橡胶海绵用发泡剂,由下列重量份的原料组成:
本发明的有益效果如下:
本发明生产出来的发泡剂具有优良的发泡力,发泡倍率高,加工稳定性,产生的泡沫具有很好的温度适应性和分散均匀性,低成本,使用方便。采用本发明发泡剂制备的硅橡胶海绵材料质地均匀美观、力学性能良好,密度小,微孔细密分散均匀,硅橡胶海绵的孔隙率达到75%,口模膨胀率达到400%。
具体实施方式
下面结合实施例对本发明作进一步的说明。
实施例
一种硅橡胶海绵用发泡剂,由下列重量份的原料组成:
用本发明发泡剂作为制备硅橡胶海绵的发泡体系,按照基础实验配方制备胶料,并于180℃下进行模压发泡,测试其性能,具体见下表1。
表1
Claims (2)
1.一种硅橡胶海绵用发泡剂,其特征在于,由下列重量份的原料组成:
偶氮二甲酰胺 8-12份
三亚硝基三亚甲基三胺 5-8份
3,3’-二磺酰肼二苯砜 4-6份
对,对-氧双(苯磺酰氨基脲) 2-3份
碳酸氢钠 3-5份
柠檬酸钠 2-4份
二苯胍 2-4份
甘油 20-30份
草酸 2-5份
季戊四醇 2-3份
氧化锌 0.5-1.5份。
2.根据权利要求1所述的硅橡胶海绵用发泡剂,其特征在于,由下列重量份的原料组成:
偶氮二甲酰胺 10份
三亚硝基三亚甲基三胺 7份
3,3’-二磺酰肼二苯砜 5份
对,对-氧双(苯磺酰氨基脲) 3份
碳酸氢钠 4份
柠檬酸钠 3份
二苯胍 3份
甘油 25份
草酸 4份
季戊四醇 2份
氧化锌 1份。