CN103171013A - 一种木材深度碳化的工艺 - Google Patents

一种木材深度碳化的工艺 Download PDF

Info

Publication number
CN103171013A
CN103171013A CN2013101093761A CN201310109376A CN103171013A CN 103171013 A CN103171013 A CN 103171013A CN 2013101093761 A CN2013101093761 A CN 2013101093761A CN 201310109376 A CN201310109376 A CN 201310109376A CN 103171013 A CN103171013 A CN 103171013A
Authority
CN
China
Prior art keywords
timber
carbonization
hot press
wood
heating platen
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2013101093761A
Other languages
English (en)
Other versions
CN103171013B (zh
Inventor
孙磊
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ANHUI MEIYUAN DECORATION TECHNOLOGY Co Ltd
Original Assignee
ANHUI MEIYUAN DECORATION TECHNOLOGY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ANHUI MEIYUAN DECORATION TECHNOLOGY Co Ltd filed Critical ANHUI MEIYUAN DECORATION TECHNOLOGY Co Ltd
Priority to CN201310109376.1A priority Critical patent/CN103171013B/zh
Publication of CN103171013A publication Critical patent/CN103171013A/zh
Application granted granted Critical
Publication of CN103171013B publication Critical patent/CN103171013B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种木材深度碳化的工艺，所述的碳化的步骤为：A.将导热油在加热炉体内烧至350℃-600℃，加热后的导热油持续流动到热压机的热压板上，使热压板的表面温度达到350℃-600℃；B.将烘干后的木材排放在热压板上，放置时需保证排放在热压板上的木材厚度一致；C.木材排放好后使热压板对木材进行压紧，压紧压力为1.5-2.0Mpa；D.热压板对木材压紧20-25分钟后，使热压机加压力提升到2.5-3.0Mpa；E.然后继续碳化35-40分钟，将热压板打开，取出木材，完成碳化过程。有益效果是使木材深层次的碳化，从而减少木材使用时膨胀或变形开裂情况发生。

Description

一种木材深度碳化的工艺
技术领域
本发明涉及一种木材深度碳化的工艺，属于木材加工技术领域。
背景技术
木材主要由纤维素、半纤维素组成，纤维素在木材细胞壁中起骨架作用，其化学性质和超分子结构对木材的强度有重要影响。纤维素中的羟基和水分子也可形成氢键，不同部位的羟基之间存在的氢键直接影响着木材的吸湿和解吸过程。大量的氢键可以提高木材的强度，减少吸湿性，降低化学反应性等，且纤维素的吸湿性直接影响到限位的尺寸稳定性和强度。木材经过碳化工艺后，使羟基的浓度减少，化学结构发生复杂的变化，从而使木材的吸湿性降低，尺寸稳定性提高。半纤维素是细胞壁中与细胞膜紧密联结的物质，起粘结作用，是基体物质，半纤维素吸湿性强、耐热性差、容易水解，在外界条件作用下易于发生变化，是木材中吸湿性最大的组分，是使木材产生吸湿膨胀、变形开裂的因素之一，通过碳化可以使半纤维素被破坏，因而可降低木材的吸湿性，减少木材的膨胀与收缩，提高了碳化木的尺寸稳定性。现有的木材碳化技术主要是通过将木材放入大型的圆筒内，然后在底部进行加热，这样的碳化过程，只能使木材的表面碳化，无法深层次的对木材进行碳化，使得木材使用时间长后，就会膨胀或变形开裂。
发明内容
针对上述现有技术存在的问题，本发明提供一种木材深度碳化的工艺，使木材能够深层次的碳化，从而减少木材使用时膨胀或变形开裂情况的发生。
为了实现上述目的，本发明采用的技术方案是：一种木材深度碳化的工艺，该工艺的具体步骤是：
（1）选材：选择中性密度的木材；
（2）切割：通过电锯机将木材切割成长方体型；
（3）烘干：将切割后的木材放入烘干机内进行烘干；
（4）碳化：将烘干好的木材进行碳化；
所述的碳化的步骤为：
A．将导热油在加热炉体内烧至350℃-600℃，加热后的导热油持续流动到热压机的热压板上，使热压板的表面温度达到350℃-600℃；
B.将烘干后的木材排放在热压板上，放置时需保证排放在热压板上的木材厚度一致；
C．木材排放好后使热压板对木材进行压紧，压紧压力为1.5-2.0Mpa，木材开始受热受压进行碳化；
D．热压板对木材压紧20-25分钟后，使热压机加压力提升到2.5-3.0Mpa，使木材受力紧缩增加木材的密度；
E．然后继续碳化35-40分钟，将热压板打开，取出木材，完成碳化过程。
优选的，导热油是400#的导热油。
与现有技术相比，本发明采用热压机和导热油相结合的碳化过程，这样在温度超过350摄氏度的同时，能更施加原有窑内无法达到的压力值，从而使木材密度增加，另外本发明再碳化过程中采用二次加压的过程，这样的工艺过程可以使木材深层次的碳化，从而减少木材使用时膨胀或变形开裂情况发生。
具体实施方式
下面对本发明作进一步说明。
本发明的具体步骤是：
（1）选材：选择中性密度的木材；
（2）切割：通过电锯机将木材切割成长方体型；
（3）烘干：将切割后的木材放入烘干机内进行烘干；
（4）碳化：将烘干好的木材进行碳化；
所述的碳化的步骤为：
A．将导热油在加热炉体内烧至350℃-600℃，加热后的导热油持续流动到热压机的热压板上，使热压板的表面温度达到350℃-600℃；
B.将烘干后的木材排放在热压板上，放置时需保证排放在热压板上的木材厚度一致；
C．木材排放好后使热压板对木材进行压紧，压紧压力为1.5-2.0Mpa，木材开始受热受压进行碳化；
D．热压板对木材压紧20-25分钟后，使热压机加压力提升到2.5-3.0Mpa，使木材受力紧缩增加木材的密度；
E．然后继续碳化35-40分钟，将热压板打开，取出木材，完成碳化过程。
导热油的型号有许多种，优选的导热油是400#的导热油，采用这种型号的导热油热传递效率高，从而使热压板能更快的达到所需的温度，便于后续木材碳化的进行。
上述的碳化方法不仅局限于中性密度木材，还可适用于各种密度不同的木材，可根据木材密度的大小不同，适当调整热压碳化的时间，从而完成碳化。

Claims (2)

1.一种木材深度碳化的工艺，该工艺的具体步骤是：
（1）选材：选择中性密度的木材；
（2）切割：通过电锯机将木材切割成长方体型；
（3）烘干：将切割后的木材放入烘干机内进行烘干；
（4）碳化：将烘干好的木材进行碳化；
其特征在于，所述的碳化的步骤为：
A．将导热油在加热炉体内烧至350℃-600℃，加热后的导热油持续流动到热压机的热压板上，使热压板的表面温度达到350℃-600℃；
B.将烘干后的木材排放在热压板上，放置时需保证排放在热压板上的木材厚度一致；
C．木材排放好后使热压板对木材进行压紧，压紧压力为1.5-2.0Mpa；
D．热压板对木材压紧20-25分钟后，使热压机加压力提升到2.5-3.0Mpa；
E．然后继续碳化35-40分钟，将热压板打开，取出木材，完成碳化过程。
2.根据权利要求1所述的木材深度碳化的工艺，其特征在于，所述的导热油是400#的导热油。
CN201310109376.1A 2013-03-29 2013-03-29 一种木材深度碳化的工艺 Expired - Fee Related CN103171013B (zh)