CN1031694C - 钢筋电渣压力焊熔炼型专用焊剂 - Google Patents
钢筋电渣压力焊熔炼型专用焊剂 Download PDFInfo
- Publication number
- CN1031694C CN1031694C CN 94115069 CN94115069A CN1031694C CN 1031694 C CN1031694 C CN 1031694C CN 94115069 CN94115069 CN 94115069 CN 94115069 A CN94115069 A CN 94115069A CN 1031694 C CN1031694 C CN 1031694C
- Authority
- CN
- China
- Prior art keywords
- welding
- flux
- solder flux
- electroslag
- reinforcing bar
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明焊剂属于焊接材料。本焊剂主要可以与钢筋电渣压力焊相匹配,解决焊剂易起弧和具有优良的焊接工艺性能的问题。本焊剂组成为(重量%): SiO2 25.0~36.0%,MnO 25.0~33.0%,TiO2 5.0~13.0%,Al2O3 5.0~12.0%,CaO 2.0~10.0%,CaF2 6.0~16.0%,MgO 2.0~8.0%,K2O+Na2O 0.1~1%。本焊剂可用于14~40mm I、II、III级热轧钢筋的电渣压力焊接。
Description
本发明的焊剂属于焊接材料,特别属于一种钢筋电渣压力焊的焊剂。
钢筋电渣压力焊目前已经得到广泛的应用,但多年来国内一直没有开发出与钢筋电渣压力焊的工艺特点相适应的焊接工艺性能优良的焊剂材料,国外也未见钢筋电渣压力焊专用焊剂的报导。
国内一般采用通用的碳素钢埋弧焊HJ431焊剂用做钢筋电渣压力焊的焊剂,但电渣压力焊接钢筋时具有起弧难、电弧稳定性差、电渣过程不稳定和不能用于III级钢筋焊接的缺点。还采用焊剂HJ350、HJ360以及日本的产品YF15等;进行工艺对比试验表明,由于这些焊剂的高温物理性能与钢筋电渣压力焊的工艺性能不匹配,因而焊接工艺不理想。
美国专利US3,518,397提出了一种用于电渣焊的焊剂,该焊剂的组成成份的百分比为:SiO2 35%,MnO 40%,Al2O35%,CaO 7%,CaF2 6%,FeO 3%,TiO2 3%,Na2O 1%
另一篇美国专利US3,258,575也提出了一种用于电渣焊的焊剂。
该焊剂的组成成分的百分比为:SiO2 46.21%,MnO 34.5%,CaF27.36%,Al2O3 5.06%,MgO 4.9%,Fe2O3 1.54%,K2O 0.06%,Na2O 0.05%,TiO2 0.05i%。
美国专利公开的这两种电渣焊焊剂是用于一般钢材,并不是钢筋电渣压力焊的专用焊剂,其起弧性能和高温物理性能等均不能满足钢筋电渣压力焊的要求。
为了改善钢筋电渣压力焊的工艺特性和焊接接头的力学性能,并且使用钢筋电渣压力焊可以推广到III级钢筋的焊接,本发明提出了一种钢筋电渣压力焊熔炼型专用焊剂。
本发明的焊剂组成成分的重量百分比为(参照GB5292-85分析方法):SiO2 25.0~36.0%,MnO 25.0~33.0%,TiO2 5.0~13.0%,Al2O3 5.0~12.0%,CaO 2.0~10.0%,CaF2 6.0~16.0%,MgO 2.0~8.0%,K2O+Na2O0.1~1%。
该焊剂与上述两个美国专利(US3,518,397和US3,258,575)公开的电渣焊焊剂相比,首先该两个美国焊剂均为高锰、低氟型焊剂,而本发明提出的焊剂属于中锰、中氟型焊剂,其次焊剂组成成分相同的组份的重量百分比含量差别很大,焊剂的配比也不相同,这些就决定了本发明的焊剂的性能明显优于两个美国专利提出的焊剂的性能。
例如本发明的焊剂组成份中加入的TiO2的量为5.0~13.0%,而两个美国专利中TiO2量仅为3%和0.05%,较高的TiO2的含量有利于改善钢筋电渣焊时的起弧性能,稳定的电弧过程,钢筋端部适宜的熔化量及良好的接头成型等等。
又如由于本发明的焊剂的特殊组成成分的配比,而使该焊剂的熔渣具有良好的高温物理性能(即1450℃时熔渣高温粘度为2泊左右,熔渣良好的导电性和相适应的表面张力等),这将使电渣压力焊工艺过程稳定,从而导致优良的接头成型和接头力学性能,这些都是两个美国专利提出的焊剂所达不到的。
采用该焊剂利用BX-500型焊机可以成功地用于电渣压力焊,焊接直径为14~40mm的I、II、III级热轧钢筋,其焊接规范为:
焊接电流:150~700A
焊接电压:电弧过程为30~35伏
电渣过程为18~23伏
起弧容易,电弧、电渣过程稳定,接头成型好,接头的力学性能符合“JGJ18-84”要求。
本发明的焊剂与现有技术相比,具有以下的优点:
1.电渣压力焊时明显改善了起弧性能,电弧过程稳定,钢筋熔化量适当,成型良好;
2.该焊剂具有良好的高温物理性能,从而保证了电渣焊过程稳定和优良的接头成型和力学性能。
实施例:
本发明推荐两个最佳的焊剂组成成分配方(重量百分比):
1.SiO2 28%,MnO 31%,TiO2 7%,Al2O3 9%,CaO 5%,CaF2 11%,MgO 8%,K2O+Na2O 1%;
2.SiO2 34%,MnO 27%,TiO2 12%,Al2O3 5%,CaO 8%,CaF2 9%,MgO 4%,K2O+Na2O 1%。
利用该焊剂可以用于电渣压力焊,焊接φ14~40mm的I、II、III级热轧钢筋,采用BX-500型焊机,参照表1所示的规范进行电渣压力焊接。表1钢筋电渣压力焊的焊接规范:
钢筋直径(mm) | 焊接电流(A) | 焊接电压(V) | 焊接通电时间(S) | ||
电弧过程U2.1 | 电渣过程U2.2 | 电弧过程t | 电渣过程T | ||
14161820222528323640 | 150~200150~200200~250250~300300~350350~450450~500550~600600~650650~700 | 30~35 | 18~23 | 14161820222532404550 | 2233444567 |
焊接时可以不加引弧球,可以保证一次性起弧。电弧过程时电弧稳定,进入电渣过程时电渣过程平稳,钢筋端部熔化量适宜。最终渣包及焊包成型好,脱渣容易,焊包大小适中,焊接接头成型好,无夹渣、咬边、气孔等缺陷。接头的力学性能符合《钢筋焊接及验收标准》JGJ18-84要求。
Claims (1)
1、一种用于钢筋电渣压力焊熔炼型专用焊剂,其特征在于,该焊剂的组成成份(参照GB5292-85分析方法)按重量百分比为:SiO2 25.0~36.0%,MnO 25.0~33.0%,TiO2 5.0~13.0%,Al2O35.0~12.0%;CaO 2.0~10.0%,CaF2 6.0~16.0%,MgO 2.0~8.0%;K2O+Na2O 0.1~1%。