CN103160000A - Rubber V-ribbed belt - Google Patents
Rubber V-ribbed belt Download PDFInfo
- Publication number
- CN103160000A CN103160000A CN2013101154604A CN201310115460A CN103160000A CN 103160000 A CN103160000 A CN 103160000A CN 2013101154604 A CN2013101154604 A CN 2013101154604A CN 201310115460 A CN201310115460 A CN 201310115460A CN 103160000 A CN103160000 A CN 103160000A
- Authority
- CN
- China
- Prior art keywords
- rubber
- agent
- ribbed belt
- service life
- magnesium oxide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a rubber V-ribbed belt which is prepared by mixing the following components in percentage by weight: 35% of chloroprene rubber, 30% of ethylene propylene diene monomer, 3% of chopped fiber, 5% of binding agent, 1% of anti-aging agent, 3% of reinforcing agent, 1% of plasticizer, 2% of magnesium oxide, 2% of polytetrafluoroethylene, 1% of sulfur, 2% of activating agent and the balance of oil DOP (dioctyl phthalate). The rubber V-ribbed belt has the advantages of wide application range, fewer chemical reagents in raw materials, friendliness to human, low operation noise and long service life of high-speed drive; and the molded polyurethane has excellent compactness, thereby further prolonging the service life of the V-ribbed belt.
Description
Technical field
The present invention relates to a kind of wedge band, relate in particular to the rubber multiwedge band on a kind of transmission belt that is widely used in household electrical appliance, body-building apparatus and various automobiles.
Background technology
The main glue kind that the tradition transmission belt uses is the glue kinds such as natural rubber, chloroprene rubber, terpolymer EP rubber, for satisfying the transmission requirement, need to add various chemical reagent and reinforced filling in rubber, and these chemical reagent and reinforced filling are not suitable for and the human body Long contact time; And its quality is heavier, wear resistance is relatively poor, and the work-ing life that (turns above rotating speed 6000) during high-speed cruising is also not very long; Mainly because mostly adopting the mode of polishing after moulding, it produces, due to the matrix of emery wheel through angle after sandblasting have change, add the inevitably mechanical workout factor such as when polishing machine vibration, cause angle and the belt wheel angle of transmission belt can not be in full accord, can send the noise that is difficult to accept when transmission, particularly evident when high-speed cruising.
Summary of the invention
For the deficiency that prior art exists, technical problem to be solved by this invention is, provide a kind of with low cost, technique simple, noise is little during work, wear resistance is good and the rubber multiwedge band of long service life.
1, for solving the problems of the technologies described above, the technical solution used in the present invention is: a kind of rubber multiwedge band, mixed by the composition of following weight percent and form:
Chloroprene rubber, 35%;
Terpolymer EP rubber 30%;
Staple fibre 3%;
Tackiness agent 5%;
Anti-aging agent 1%;
Strengthening agent 3%;
Softening agent 1%;
Magnesium oxide 2%;
Tetrafluoroethylene 2%;
Sulphur 1%;
Promoting agent 2%;
Lipid DOP surplus.
The advantage of rubber multiwedge band of the present invention is: have wide range of applications, chemical reagent is less in raw material, and is more friendly to the people, the operation noise is little, and the high-speed drive life-span is long.Polyurethane moulded rear density is good, has further improved the work-ing life of wedge band.
Embodiment
Below in conjunction with specific embodiment, the present invention is described in further details;
Embodiment 1:
A kind of rubber multiwedge band, mixed by the composition of following weight percent and form:
Chloroprene rubber, 35%;
Terpolymer EP rubber 30%;
Staple fibre 3%;
Tackiness agent 5%;
Anti-aging agent 1%;
Strengthening agent 3%;
Softening agent 1%;
Magnesium oxide 2%;
Tetrafluoroethylene 2%;
Sulphur 1%;
Promoting agent 2%;
Lipid DOP surplus.
Certainly, above-mentioned explanation is not to be limitation of the present invention, and the present invention also is not limited to above-mentioned giving an example; those skilled in the art; in essential scope of the present invention, the variation of making, remodeling, interpolation or replacement all should belong to protection scope of the present invention.
Claims (1)
1. rubber multiwedge band is characterized in that: mixed by the composition of following weight percent and form:
Chloroprene rubber, 35%;
Terpolymer EP rubber 30%;
Staple fibre 3%;
Tackiness agent 5%;
Anti-aging agent 1%;
Strengthening agent 3%;
Softening agent 1%;
Magnesium oxide 2%;
Tetrafluoroethylene 2%;
Sulphur 1%;
Promoting agent 2%;
Lipid DOP surplus.